• Journal of the Korean GEO-environmental Society
• /
• v.11 no.9
• /
• pp.55-60
• /
• 2010

This study are carried out to an lab model tests to develop a construction method that solidifies high-water content cohesive soil by using filter type drain and vacuum pressure, and that stabilizes the ground by accelerating horizontal drain at incline or in tunnel. The calibration chamber was designed within length of 1.5m and height of 50cm, and a drainage hole for preconsolidation, a switchgear and a piezometer were installed at the bottom part of the chamber. Also, a settlement gage was installed at the top part so that it can measure the settlement by time. The calibration ground basis was made in a form of thin layer from kaolinite and bentonite in 9:1 ratio stirred at 130% water content condition. A filter type drain was installed at chamber center and a vacuum pressure of 0.8MPa was applied through a hose linked to the cap at the top part, then, the settlement was measured in every 1 hour interval. After experiment, the moisture contents were measured by position, then, verified the increase of solidity of the ground through a triaxial compression test on undisturbed profile. After 11 days from the effective date, it was observed that the settlement decreased by maximum 35mm and the water content ratio was reduced by 38% at most while the solidity of the ground increased by 5~8 times greater than before preconsolidation.

• Journal of the Korean institute of surface engineering
• /
• v.36 no.2
• /
• pp.200-205
• /
• 2003

Thermoelectric p-type $Fe_{0.98}$ $Mn_{ 0.02}$$Si_2$ bulk specimens have been produced by mechanical alloying and consolidation by vacuum hot pressing. The subsequent isothermal annealing was not able to fully transform the mestastable as -milled powders into the $\beta$ $-FeSi_2$ phase, so that the obtained matrix consisted of not only thermoelectric semiconducting $\beta$-FeSi$_2$ but also some residual, untransformed metallic $\alpha$ $- Fe_2$$Si_{ 5}$ and $\varepsilon$-FeSi mixtures. Interestingly, $\beta$ - $FeSi_2$ was more easily obtained in the low density specimen when compared to the high density specimen. The oxidation at 700 and $800^{\circ}C$ in air led to the phase transformation of the above described iron - silicides and the formation of a thin silica surface layer.

• Nuclear Engineering and Technology
• /
• v.45 no.5
• /
• pp.683-688
• /
• 2013

Candidate coating materials for re-usable metallic nuclear fuel crucibles, TaC, TiC, ZrC, $ZrO_2$, and $Y_2O_3$, were plasmasprayed onto a niobium substrate. The microstructure of the plasma-sprayed coatings and thermal cycling behavior were characterized, and U-Zr melt interaction studies were carried out. The TaC and $Y_2O_3$ coating layers had a uniform thickness, and high density with only a few small closed pores showing good consolidation, while the ZrC, TiC, and $ZrO_2$ coatings were not well consolidated with a considerable amount of porosity. Thermal cycling tests showed that the adhesion of the TiC, ZrC, and $ZrO_2$ coating layers with niobium was relatively weak compared to the TaC and $Y_2O_3$ coatings. The TaC and $Y_2O_3$ coatings had better cycling characteristics with no interconnected cracks. In the interaction studies, ZrC and $ZrO_2$ coated rods showed significant degradations after exposure to U-10 wt.% Zr melt at $1600^{\circ}C$ for 15 min., but TaC, TiC, and $Y_2O_3$ coatings showed good compatibility with U-Zr melt.

• Korean Journal of Materials Research
• /
• v.25 no.8
• /
• pp.386-390
• /
• 2015

Fe-base superalloy powders with $Y_2O_3$ dispersion were prepared by high energy ball milling, followed by spark plasma sintering for consolidation. High-purity elemental powders with different Fe powder sizes of 24 and 50 mm were used for the preparation of $Fe-20Cr-4.5Al-0.5Ti-O.5Y_2O_3$ powder mixtures (wt%). The milling process of the powders was carried out in a horizontal rotary ball mill using a stainless steel vial and balls. The milling times of 1 to 5 h by constant operation (350 rpm, ball-to-powder ratio of 30:1 in weight) or cycle operation (1300 rpm for 4 min and 900 rpm for 1 min, 15:1) were applied. Microstructural observation revealed that the crystalline size of Fe decreased with an increase in milling time by cyclic operation and was about 15 nm after 3 h, forming a FeCr alloy phase. The cyclic operation had an advantage over constant milling in that a smaller-agglomerated structure was obtained. The milled powders were sintered at $1100^{\circ}C$ for 30 min in vacuum. With an increase in milling time, the sintered specimen showed a more homogeneous microstructure. In addition, a homogenous distribution of Y-compound particles in the grain boundary was confirmed by EDX analysis.

• Korean Journal of Materials Research
• /
• v.10 no.6
• /
• pp.403-408
• /
• 2000

The Al-Cr-Zr composite metal powders were prepared by mechanical alloying and consolidated by vacuum hot pressing. The microstructural characteristics and the thermal stability of the MA Al-Cr-Zr alloys were evaluated by means of microhardness measurement, XRD and TEM in order to develop high temperature, high strength aluminum alloys. The mechanical alloying was conducted in attritor with 300rpm for 20 hours. The density of the vacuum hot pressed Al-Cr-Zr alloy reached at 97% of theoretical one. After exposing at $300^{\circ}C$ for 100 hours, there is almost no variation in hardness change of the MA alloys. Even after exposing at $ 500^{\circ}C$ for 100 hours, the hardness of the alloy was decreased within 6% of the initial value. The fine stable $Al_3Zr\;and\; Al_{13}Cr_2$ intermetallics were formed at the stage of consolidation and heat treatment in aluminum matrix. The good thermal stability of the MA Al-Cr-Zr alloy can ab attributed to the role of the dispersoids, inhibiting grain growth of nanocrystalline, and the final grain size after heat treatment was less than 150nm.