• Korean Journal of Materials Research
• /
• v.6 no.9
• /
• pp.900-904
• /
• 1996

비정질 실리콘의 표면에 Ni과 Pd를 형성하여 측면으로의 결정화 속도를 향상시켰다. Ni에 의해 비정질 실리콘이 측면으로 결정화될 때 그 성장 속도는 50$0^{\circ}C$에서 3w$\mu\textrm{m}$/hour였으며 이때의 활성화 에너지는 2.87eV로 나타났다. Pd의 경우는 Pd2Si의 형성에 의해 압축 응력이 유발되어 Pdrks의 간격이 좁을수록 측면으로의 결정화 속도가 증가하였다. Ni과 Pd을 각각 다른 부분에 증착시키고 결정화시키면 Ni에 의해 측면으로 결정화되는 속도가 Ni만으로 결정화시킬 때 보다 약 2배 이상의 측면결정화 속도를 보였다.

• Korean Journal of Materials Research
• /
• v.17 no.7
• /
• pp.376-381
• /
• 2007

Fluorine-doped tin oxide (FTO) thin film was coated on aluminosilicate glass at $450^{\circ}C$ by spray pyrolysis method. In the range of 0-2.7 molar ratio of F/Sn, the variations of electrical conductivity and visible light transmission were investigated. At the F/Sn ratio of 1.765, the film showed the lowest electrical resistivity value of $3.0{\times}10^{-4}{\Omega}\;cm$, the highest carrier concentration of $2.404{\times}10^{21}/cm^3$, and about $8\;cm^2/V{\cdot}sec$ of electronic mobility. The FTO film showed a preferred orientation of (200) plane parallel to the substrate. X-ray photoelectron spectroscopy analysis results indicated that the contents of $Sn^{4+}-O$ bonding are the highest at 1.765 of F/Sn molar ratio.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.07a
• /
• pp.185-190
• /
• 2003

In this paper, it was demonstrated that the organic thin film transistors were fabricated by the organic gate insulators with vapor deposition polymerization (VDP) processing. In order to form polyimide as a gate insulator, vapor deposition polymerization process was also introduced instead of spin-coating process, where polyimide film was co-deposited by high-vacuum thermal evaporation from 4,4'-oxydiphthalic anhydride (ODPA) and 4,4'-oxydianiline (ODA) and 2,2-bis(3,4-dicarboxyphenyl)hexafluoropropane dianhydride (6FDA) and ODA, and cured at $150^{\circ}C$ for 1hr. Electrical output characteristics in our organic thin film transistors using the staggered-inverted top-contact structure obtained to the saturated slop in the saturation region and the subthreshold non-linearity in the triode region. Field effect mobility, threshold voltage, and on-off current ratio in $0.45\;{\mu}m$ thick gate dielectric layer were about $0.17\;cm^2/Vs$, -7 V, and $10^6\;A/A$, respectively. Details on the explanation of compared to organic thin-film transistors (OTFTS) electrical characteristics of ODPA-ODA and 6FDA-ODA as gate insulators by fabricated thermal co-deposition method.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.17 no.9
• /
• pp.947-952
• /
• 2004

Tb-doped lead zirconate titanate(Pb(Zr$\_$0.6/,Ti$\_$0.4/)O$_3$; PZT) thin films on Pt(111)/Ti/SiO$_2$/Si(100) substrates were fabricated by the sol-gel method. The effect on the structural and electrical properties of films measured according to Tb content. The dielectric and ferroelectric properties of Tb-doped PZT thin films were altered significantly by Tb-doping. The PZT thin film with higher dielectric constant and improved leakage current characteristic was obtained by adding 0.3 mol% Tb. The relative dielectric constant and the dielectric loss of the 0.3 mol% Tb-doped PZT thin film were 1611 and 0.024, respectively. Typical value of the swichable remanent poaraization(2Pr) and the coercive filed of the PZT film capacitor for 0.3 mol% Tb-doped were 61.4 ${\mu}$C/cm$^2$ and 61.9 kV/cm, respectively. Tb-doped PZT thin films showed improved fatigue characteristics comparing to the undoped PZT thin film.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2017.05a
• /
• pp.134.2-134.2
• /
• 2017

최근 고성능, 저 전력 반도체 소자를 위한 미세 공정 기술이 발전함에 따라, gate oxide의 두께 및 선폭이 감소하고, aspect ratio가 증가하고 있는 추세이다. 따라서 얇아진 gate oxide를 통한 채널 물질로의 boron 확산을 막기 위한 고농도 질화 막 증착의 필요성이 높아지고 있으며, high aspect ratio의 gate oxide에 적용 가능한 우수한 step coverage의 질화막 또한 요구되고 있다. 이러한 요구조건을 만족시키기 위해 일반적인 13.56MHz의 플라즈마 소스를 이용한 질화연구들이 선행되어져 왔으나, 높은 binding energy(~24 eV)를 가지고 있는 N2 molecule gas를 효과적으로 dissociation 하지 못해 충분한 질화공정이 수행되어질 수 없었을 뿐만 아니라 높은 공정온도($>200^{\circ}C$에서 진행되어 반도체소자에 손상을 줄 수 있다. 본 연구에서는 이러한 문제들을 해결하기 위해 VHF (162MHz)를 이용한 플라즈마를 통해 고밀도에서 낮은 전자온도와 높은 진동온도의 플라즈마를 구현하여 20%이상의 높은 질화율을 얻을 수 있었고, multi-tile push-pull 플라즈마 소스를 통해 VHF 사용 시 나타나는 standing wave effect를 제어하여 high aspect ratio의 gate sidewall spacer에 우수한 step coverage의 질화막을 형성시킬 수 있었다.

• Journal of Powder Materials
• /
• v.17 no.4
• /
• pp.276-280
• /
• 2010

In the present work, ethylene glycol-based (EG) copper oxide nanofluids were synthesized by pulsed wire evaporation method. In order to explode the pure copper wire, high voltage of 23 kV was applied to the both ends of wire and argon/oxygen gas mixture was used as reactant gas. EG-based copper oxide nanofluids with different volume fraction were prepared by controlling explosion number of copper wire. From the transmission electron microscope (TEM) image, it was found that the copper oxide nanoparticles exhibited an average diameter about 100 nm with the oxide layer of 2~3 nm. The synthesized copper oxide consists of CuO/$Cu_2O$ phases and the Brunauer Emmett Teller (BET) surface area was estimated to be $6.86\;m^2\;g^{-1}$. From the analyses of thermal properties, it is suggested that viscosity and thermal conductivity of EG-based copper oxide nanofluids do not show temperature-dependent behavior over the range of 20 to $90^{\circ}C$. On the other hand, the viscosity and thermal conductivity of EG-based copper oxide nanofluids increase with volume fraction due to the active Brownian motion of the nanoparticles, i.e., nanoconvection.

• Journal of the Korean Electrochemical Society
• /
• v.5 no.2
• /
• pp.43-46
• /
• 2002

Commercial titanium rod was anodized in three types of electrolytes such as 0.06 mol/L $\beta-glycerophosphate+0.3mol/L$ calcium acetate, 0.06mol/L $\beta-glycerophosphate+0.3mol/L$ sodium acetate and 0.06 mol/L $\beta-glycerophosphate+5mol/L$ calcium phosphate. The titanium oxide layer $(TiO_2)$ was characterized by scanning electron microscope (SEM), X-ray diffraction (XRD) and electron spectroscopy chemical analysis (ESCA). Numerous micropores were observed on the titanium oxide layer by SEM. The diameter of micropores increased with the increase of electrolytic voltage. The titanium oxide layer was composed of anatase structure. The phosphorous element was detected at 130 eV binding energy, but calcium was not found in the oxide layer because of lower contents. After anodizing the oxide layer was etched in the 30g/L NaOH solution at $80^{\circ}C$ for 1hr. The surroundings of micropores were much more smoothed and rounded than before alkaline etching.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.08a
• /
• pp.241-241
• /
• 2010

적외선 센서는 빛의 유무에 관계없이 물체 또는 인체에서 발산하는 적외선을 감지한다. 이러한 센서를 전자 및 디스플레이 시스템과 연동하면 열영상 시스템이 되는데, 이는 전방 감시, 플랜트 감시, 보안, 방범용으로 많이 사용되며, 특히 자동차 야간 운전자 보조용으로 사용되어 최첨단, 고부가가치를 지니고 있는 핵심부품이다. 비냉각형 적외선 센서인 마이크로볼로미터는 상온에서 작동하므로 극저온 Cooler가 불필요하며, 무게와 부피가 작아 각종 시스템에 부착가능하다. 특히 볼로미터형 적외선 센서는 용량이 적은 TE cooler로 상온으로 안정화를 시키며, 진공으로 유지되는 금속 또는 세라믹 패키지를 사용하게 된다. 본 연구에서는 마이크로 볼로미터용 진공패키지를 제작하여 패키지 조립 및 측정기술에 대해 조사하였다. 패키지는 금속재질인 kovar를 사용하여 제작되었고, 내부에 TE Cooler와 장수명 진공유지를 위한 getter, 그리고 온도센서 및 볼로미터 센서 칩을 장착하여 조립하였다. 패키지 Cap ass'y와 base envelop의 솔더링 공정은 약 $200^{\circ}C$에서 수행하였으며, evacuation system을 이용하여 5일 동안 패키지 bake-out 공정을 수행하였다. 이 후 getter를 활성화시키고, seal-off 공정으로 진공 기밀을 유지하였다. 진공 패키지의 기밀성은 $6{\times}10^{-9}\;std.cm^3/sec$로 기밀성을 유지하였다. 볼로미터 센서의 반응도는 $10^2\;V/W$ 이상을 나타내었으며, 탐지도는 $2{\times}10^8\;cm-Hz^{1/2}/W$를 나타내었다.

• Journal of the Korean Wood Science and Technology
• /
• v.42 no.2
• /
• pp.172-182
• /
• 2014

Extraction is a necessary element in the bioconversion of lignocellulosics to fuels and chemicals. Although various forms of chemical pretreatment of cellulosic materials have been proposed, their effectiveness varies depending on the treatment conditions and substrate. In this study, mixed hardwood (MH) and loblolly pine (LP) were pretreated with dilute acid in a 100 mL accelerated solvent extraction (ASE) at the predetermined optimal conditions: temperature: $170^{\circ}C$, acid concentration: 0.5% (w/v), and reaction time: 2~64 min. This method was highly effective for extracting the hemicellulose fraction. Total xmg (defined as the sum of xylose, mannose, and galactose) can be extracted from milled MH and LP through pressurized dilute acid treatment in maximum yields of 12.6 g/L and 15.3 g/L, respectively, representing 60.5% and 70.4% of the maximum possible yields, respectively. The crystallinity index increased upon pretreatment, reflecting the removal of the amorphous portion of biomass. The crystalline structure of the cellulose in the biomass, however, was not changed by the ASE extraction process.

• Korean Journal of Veterinary Research
• /
• v.40 no.1
• /
• pp.35-41
• /
• 2000

We established a new method to analyze abamectin using HPTLC (high performance thin layer chromatography) in order to obtain its pharmacokinetic profiles in pigs. Recovery of abamectin in pig serum after fluorescence derivatization was $80.01{\pm}3.82%$ at 0.1ppm and $83.67{\pm}3.63%$ at 10ppm, respectively. Detection reproducibility in terms of coefficient variation (c.v.) was 3.09% and 2.74% (intra-day), and 3.71% and 51.7%(inter-day), for 0.1 and 10ppm, respectively. Pharmacokinetics of abamectin was studied in five Yorkshire-Landrace mixed bred male pigs ($35.0{\pm}2.7kg$) administered intramuscularly 0.3mg/kg b.w. Pharmacokinetic profiles of abamectin in pigs were described by the 1-compartment open model with first-order absorption and first-order elimination. AUC (area under the curve) was $262.65{\pm}16.44ng{\cdot}day/ml$ and the biological elimination half-life ($t_{1/2},\;k_e$) was $5.28{\pm}0.84$ days, indicating somewhat high bioavailability and long half-life by the intramuscular route. We suggest intramucular injection of abamectin could be also used in place of the recommended route of its subcutaneous administration so far.