• Transactions on Electrical and Electronic Materials
• /
• v.16 no.6
• /
• pp.308-311
• /
• 2015

V₂O₅/Mn₃O₄/Nb₂O₅ codoped zinc oxide varistor ceramics were sintered at a temperature range as low as 875~950℃. The voltage clamping characteristics of V₂O₅/Mn₃O₄/Nb₂O₅ codoped zinc oxide varistor ceramics were investigated at a pulse current range of 1~50 A. The sintering temperature had a significant effect on clamp voltage ratio, which exhibits surge protection capabilities. The varistor ceramics sintered at 875℃ exhibited the best clamping characteristics, in which the clamp voltage ratio was 2.69 at a pulse current of 50 A. The varistor ceramics sintered at 900℃ exhibited the highest electrical stability, where = 3,824 V/cm (initial 3,909 V/cm), and E_{1 mA/cm²} = 27 (initial 39) after application of a pulse current of 100 A.

• Journal of the Korean Electrochemical Society
• /
• v.3 no.1
• /
• pp.44-48
• /
• 2000

Amorphous $V_2O_5$ cathode thin films were prepared by DC-magnetron sputtering at room temperature and the thin film rechargeable lithium batteries were fabricated with the configuration of $V_2O_5/LIPON/Li$ using sequential ex-situ thin film deposition techniques. The electrochemical characteristics of $V_2O_5$ cathode materials Prepared at 80/20 of $Ar/O_2$ ratio showed high capacity and cycling behaviors by half cell test. LIPON solid electrolytes films were prepared by RF-magnetron sputtering using the self-made $Li_3PO_4$ target in pure $N_2$ atmosphere, and it was very stable for lithium contact in the range of 1.2-4.0 V vs. Li. Metallic lithium were deposited on LIPON electrolyte by thermal evaporation methode in dry room. Vanadium oxide based full cell system showed the initial discharge capacity of $150{\mu}A/cm^2{\mu}m$ in the range of $1.2\~3.5V$.

• Journal of Environmental Science International
• /
• v.16 no.9
• /
• pp.1077-1083
• /
• 2007

[ $V_2O_5/TiO_2$ ] catalyst impregnated ceramic candle filters are in principle, capable of performing shallow-bed dust filtration plus a catalytic reaction, promoted by a catalytic deposited in their inner structure. Pilot-scale $V_2O_5/TiO_2$ catalyst impregnated ceramic candle filters were prepared, characterized and tested for their activity towards the SCR reaction. The effect on NO conversion of operating temperature, gas hourly space velocity, amount of deposited catalyst, pressure drops and long-term experiment (life of catalytic filter) was determined. The following effects of $V_2O_5/TiO_2$ catalyst impregnated ceramic candle filters in SCR reaction are observed: (1) It increases the activity and widens the temperature window for SCR. (2) When the content of $V_2O_5$ catalyst increases further from 3 to 9wt.%, activity of NO increases. (3) NO conversion at first increases with temperature and then decreases at high temperatures (above $400^{\circ} over), possibly due to the occurrence of the ammonia oxidation reaction.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.13 no.9
• /
• pp.751-757
• /
• 2000

The r.f. power effect for Pt doping is investigated on structural and electrochemical properties of amorphous vanadium oxide(V$_2$O$_{5}$) film, grown by direct current (d.c.) magnetron sputtering. Room temperature charge-discharge measurements based on a half-cell with a constant current clearly indicated that the Pt doping could improve the cyclibility of V$_2$O$_{5}$ cathode film. Using glancing angle x-ray diffraction(GXRD) and high-resolution transmission electron microscopy (HRTEM) analysis, we found that the Pt doping with 10W r.f. power induces more random amorphous structure than undoped V$_2$O$_{5}$ film. As the r.f. power of Pt target increases. large amount of Pt atoms incorporates into the amorphous V$_2$O$_{5}$ film and makes $\alpha$-PtO$_2$microcrystalline phase in the amorphous V$_2$O$_{5}$ matrix. These results suggest that the semiconducting $\alpha$-PtO$_2$ microcrystalline phase in amorphous matrix lead to a drastically faded cyclibility of 50W Pt doped V$_2$O$_{5}$ cathode film. Possible explanations are given to describe the Pt doping effect on cyclibillity of the amorphous V$_2$O$_{5}$ cathode film battery. film battery.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.11a
• /
• pp.335-338
• /
• 2000

Carbon is an attractive candidate for use in eletrochemical supercapacitors that depend on charge storage in the electrode/electrolyte international double layer. Property of an electrical double layer capacitor depend both on the technique used to prepare the electrode and on the current collector structure. The study is to research that V$_2$O$_{5}$-flyash-AC composite electrode for supercapacitor. The discharge capacitance of V$_2$O$_{5}$-flyash-AC(70wt%) in 1st and 50th cycle was 18.6F/g and 15.13F/g at current density of 0.5mA/cm$^2$. The discharge process of V$_2$O$_{5}$-flyash (3 : 97)-AC composite electrode is larger than that others.thers.

• Bulletin of the Korean Chemical Society
• /
• v.17 no.12
• /
• pp.1123-1127
• /
• 1996

Crystalline compound RbV2SeO7, a Rb analogue of KV2SeO7, was synthesized from a hydrothermal reaction of V2O5, V2O3, SeO2, and Rb2CO3 in the mole ratio 3: 1: 15: 6 (in millimoles) at 230℃. RbV2SeO7 crystallizes in an orthorhombic space group Pnma (No. 62) with a=18.444(8), b=5.415(3), c=7.070(4) Å, Z=8. The two structures of KV2SeO7 and RbV2SeO7 are almost the same except that bond lengths in the latter are slightly longer than in the former. The magnetic susceptibility measurement for RbV2SeO7 in the temperature range 4-300 K showed an antiferromagnetic ordering with TN=45 K, higher than that for KV2SeO7 of 27 K. The origin of the magnetic coupling and the different ordering temperatures in the two phases are discussed in relation to the crystal structures.

• Applied Chemistry for Engineering
• /
• v.22 no.5
• /
• pp.582-585
• /
• 2011

In this study, surface-adsorbed species of 1,2-dichlorobenzene (1,2-DCB) on mesoporous $V_2O_5/TiO_2$ catalysts synthesized by spray pyrolysis were investigated through the adsorption/desorption performed using in situ FT-IR cell. Also, the comparison of adsorbed species with $TiO_2$ and $V_2O_5/TiO_2$ synthesized by the incipient wetness was carried out.

• Proceedings of the KIEE Conference
• /
• 2008.07a
• /
• pp.1252-1253
• /
• 2008

The $V_{1.8}W_{0.2}O_5$ thin films deposited on $Pt/Ti/SiO_2/Si$ substrates by RF sputtering method with different $Ar/O_2$ ratio. The $V_{1.8}W_{0.2}O_5$ thin films were measured electrical and structural properties, fairly good Temperature coefficient of resistance(TCR). It was found that electrical and structural properties, TCR properties of thin films were strongly dependent upon the $Ar/O_2$ ratio. The dielectric constant of the $V_{1.8}W_{0.2}O_5$ thin films with 50/20 ratio were 93 with a dielectric loss of 0.535, respectively. Also, the TCR values of the $V_{1.8}W_{0.2}O_5$ thin films with 50/20 ratio were -3.15%/$^{\circ}C$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.05c
• /
• pp.295-298
• /
• 2003

The principal problems in development of dielectric paste materials for PDP(plasma display panel)are PbO free paste and low melting temperature. We prepared PbO free paste from glasses in the system BaO-ZnO-$B_2O_3-V_2O_5$. DTA, XRD and SEM were used to study and characterize BaO-ZnO-$B_2O_3-V_2O_5$ glasses. PbO free paste developed at this paper has thermal expansion of $74{\times}10^{-7}/^{\circ}C$, DTA transformation point of $460^{\circ}C$, and firing condition of $560^{\circ}C$, 10min.

• Journal of the Korean Ceramic Society
• /
• v.48 no.4
• /
• pp.303-306
• /
• 2011

[ $V_2O_5$ ]doped Karrooite pigments were synthesized by the solid state method to get stabilized brown pigment in oxidation and reduction atmosphere. Optimum substitution condition and limited dopant with $V_2O_5$ for Karrooite pigment was investigated. With calcination at $1250^{\circ}C{\sim}1400^{\circ}C$, compositions were designed varying $V_2O_5$ molar ratio by increasing 0.02mole to the formula $Mg_1-xTi_2-xM_{2x}O_5$(x = 0.01~0.09 mole). Synthesized pigments were analyzed by XRD, Raman spectroscopy and UV-vis. When $V_2O_5$ was doped from 0.01 to 0.05 mole, single phase of Karrooite was observed at temperature $1300^{\circ}C$ and soaking time 4h by Raman spectroscopy. However, it was found that excess $VO_2$ peak appeared with 0.07 and 0.09 mole of $V_2O_5$ doped to $MgTi_2O_5$. This result indicated that the maximum limit of solid solution is 0.05 mole $V_2O_5$. Karrooite pigments were applied as a ceramic pigment to achieve brown colors in lime magnesia glaze and lime barium graze at both of oxidation and reduction atmosphere. CIE color coordinates are $L^*$ = 40.34, $a^*$ = 9.94, $b^*$ = 21.40 in lime magnesia glaze.