• Journal of Conservation Science
• /
• v.27 no.1
• /
• pp.115-121
• /
• 2011

A Urethane resin restoration material was made to be used in the restoration of stone cultural assets. The Urethane resin restoration material showed strong adhesive strength and tensile strength similar to epoxy recovery material, which had been mainly used for the recovery of stone cultural assets. The sealing property, anti-shrinking property and paint-ability of Urethane resin restoration material are also similar to existing epoxy system restoration materials. Especially, this Urethane resin restration material is expected to give permanence and continuous stability in the restoration of cultural assets made in stone by resolving the two big issues of existing epoxy recovery material, which are 'yellowing' and 'ir-reversibility'. This Urethane resin restration material had been directly applied as a filling material and adhesive and it was dissolved again. The Urethane resin, which had been used for the recovery, was able to be perfectly removed, which means that this Urethane resin recovery material has perfect reversibility. This Urethane resin restoration material also has enhanced convenience since user can adjust the working-life dependent on work environment. It is believed that this Urethane resin restoration material can also be used as a filling material or adhesive for other cultural assets made of ceramic or metal heritage, in addition to stone, since it has strong adhesive strength and tensile strength.

• International Journal of Concrete Structures and Materials
• /
• v.2 no.2
• /
• pp.83-90
• /
• 2008

Permeability to vapor and water among other performances required for finishing materials is dealt with in this study. The relative moisture content of concrete coated/covered with a finishing material was experimentally investigated while changing the environmental conditions including temperature, relative humidity, and rainfall. An organic paint (water-based urethane), organic synthetic resin emulsion-type film coating (film coating E), and inorganic porcelain tiles were selected as the finishing materials. When compared from the aspect of vapor and water permeability, the vapor permeability and water permeability of water-based urethane were high and low, respectively; those of film coating E were high and high, respectively; and those of porcelain tiles were low and low, respectively. This means that the moisture state of concrete structures is governed not only by the environmental conditions but also by the performance of finishing materials. It is therefore of paramount importance to appropriately select a finishing material to address the specific deteriorative factors involved in the concrete structure to be finished.

• Journal of Fisheries and Marine Sciences Education
• /
• v.22 no.4
• /
• pp.501-507
• /
• 2010

The ceramic contained paint was made to replace the lead sinker for gill-net with coated lead sinker. The ceramic contained paints were coated in various conditions on the lead sinker with 19g of weight and the optimal coating condition was studied. The adaptability of the coated lead sinker was checked through the anti durability test and fishing operation with gill-net. The case of "Main material 70 wt% + Urethane thinner 30 wt% (Main material 700 $m{\ell}$ + Thinner 300 $m{\ell}$)" showed the best in the coating characteristics depending on the combination ratio of the ceramic paint contained. The coated lead sinker dried at $100^{\circ}C$ inside oven was superior to the drying in the room temperature in its surface glossiness and anti durability and faster drying time than the one dried in normal temperature. The quadruple layers of coating on lead sinker with 4 times of dipping and drying application showed the super anti durability in the coating characteristics depending on the frequency of dipping. When press is applied to the coated lead sinker, the coated layer is not detached from the sinker. In addition, the coated lead sinker was not damaged or peeled at the fishing operation about 2 months in various depths within 50m and by the materials at the bottom (sand, stone and gravel stone) and it was in good condition.

• Journal of the Korean Applied Science and Technology
• /
• v.38 no.2
• /
• pp.476-487
• /
• 2021

To prepare acrylic resin coatings containing 70% of solids, we used n-butyl methacrylate(BMA), methyl methacrylate(MMA), 2-hydroxyethyl methacrylate(2-HEMA), and acetoacetoxyethyl acrylate(AAEA), caprolactone acrylate(CLA) as raw materials, the glass transition temperature(T_g) of acrylic copolymer was adjusted around 50 ℃. The viscosity and molecular weight of the acrylic resins was increased with increasing OH values. Di-tert-amyl peroxide was found to be the suitable initiator to get high-solids acrylic resins. The optimum reaction conditions found in the study are 5 wt% of initiator, 4 wt% of chain transfer agent, 4 hrs of dropping time, and 140 ℃ of reaction temperature. The structure of the synthesized resins were characterized by FT-IR and ¹H-NMR spectroscopy. Number average molecular weight of 1900~2600 and molecular wight distribution of 1.4~2.1 were obtained. Crosslinked acrylic urethane clear coatings were obtained by curing reaction between the synthesized acrylic resins and hexamethylene diisocyanate trimer(Desmodur N-3300), the equivalent ratio of NCO/OH was 1.2/1.0. The physical properties from the following studies were carried out: viscosity(Zahn cup #2), adhesion, drying time, pot-life, pensil hardness, and 60° specular gloss. Various properties of the acrylic urethane clear coatings were also evaluated on the coating specimens. Adhesion property to a substrate, drying time, pot-life, pencil hardness, and 60° specular gloss of prepared paint showed quite good properties. Futhermore, prepared paint containing 10% of CLA showed quite good properties for adhesion, low viscosity and high hardness.

• Journal of The Korean Society of Agricultural Engineers
• /
• v.46 no.4
• /
• pp.39-46
• /
• 2004

This experiment was carried out to study on the effect of surface coating on thermal insulation of farm structures to improve thermal resistance and reflective effect of solar radiation. Nine different types of experimental specimen were compared in the temperature variations of inside and outside; A, B, C, D. E and F types are box container and G, H and I types are drum container. The size of these containers is $1,500{\times}2,000{\times}2,500$ mm and ${\varphi}$ $280{\times}330$ mm, respectively. Specimen of 3-type box(A, B, C) is galvanized steel sheet of thickness 0.45 mm. D, E and F types are sandwich panel of the thickness 50 mm inserted with urethane, glass wool and polystyrene form, respectively. G, H and I types are paint pot using in general. The surface of A. D, E, F and I types didn't any treatment, B, C and G types were treated with thermal insulation coating on the outside surface(B, G) or the inside and outside surface(C). And H type was treated with water paint coating on the only outside surface. In general, the experimental results showed the following tendencies; In case of A, B and C types. it was found that the thermal insulation effect of types coated with thermal insulation coating was improved remarkably than that of no treatment. And the thermal insulation effect between steel sheet and sandwich panel type was nearly similar There was not a significant difference of thermal insulation effect between thermal insulation coating and water paint coating. In time of drum container filled with rough rice, The difference of heat transfer tendency and temperature variation among surface treatments was nearly similar that of box types of galvanized steel sheet. And there was time lag about 6 hours between the temperature of middle part of rice and that of inside or outside surface.

• Applied Chemistry for Engineering
• /
• v.20 no.1
• /
• pp.52-61
• /
• 2009

In this study, TAPEH (t-amyl peroxy 2-ethyl hexanoate) was selected for the reaction initiator which is a core factor for developing acrylic polyol binder. Tone M100 (caprolactone acrylate), 4HBA (4-hydroxy butyl acrylate), and 2HEMA (2-hydroxy ethyl methacrylate) were used for hydroxy-monomers. To check the applicability of raw materials mentioned above into the binders of 2 components acrylic polyurethane paint and reduce the VOC, the reactivity and film performance by different kinds of aliphatic polyisocyanate hardeners which are already generalized were reviewed. As the Tin-based catalyst has been regulated, the comparison test of reactivity and performance between the conventional catalyst and non-toxic metal catalyst recommended as the alternative was conducted as well. As a result, we were able to obtain the basic data which are necessary for applying 2 components high solid polyurethane paint and also reached a conclusion that it can be applied for developing new paints in terms of high performance, workability and environmental care.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 1997.10a
• /
• pp.295-298
• /
• 1997

Recycl ing of PP/EPR based bumper coated with polyester urethane paint has been per formed by chemical decoating method. Electronic Speckle Pattern Interferometry (ESP11 has been applied to characterize the deformation of polyolef in based bumper. In additon, physical properties and processability of recycled materials have been investigated by dynamic mechanical thermal analysis, impact test and melt flower index measurement. The results show that the deformation ratio of recycled material is higher than that of virgin one. The morphological change of EPR, degree of distribution and dispersion during the recycling process seem to be the most important factor for the deformation and the mechanical properties of recycled materials. The experimental results obtained show that ESPI is very powerful technique to study the thermal mechanical property of polyolefin bumper system.

• Proceedings of the Korean Reliability Society Conference
• /
• 2002.06a
• /
• pp.115-115
• /
• 2002

최근 중장비용 도료의 외관 즉 색상 및 광택의 변화는 상품가치를 결정하는 중요한 요소의 하나로 대두되고 있다. 이와 관련 도장 품질향상을 위해서 각종의 신도료가 개발되고 있고 물성 확인은 필수적이다. 특히 검사 항목중 내후성 확인은 Field에서 2년 이상 장시간의 시험기간이 필요하나 검증기간 단축을 위해 시험실에서 Weathering test를 시행하고 있다. 그러나 이러한 Lab. test 결과와 실제 Field data와의 상관관계를 알 수 없어 추정에 그치는 것이 현실이었다. 본 연구에서는 중장비용 우레탄도료의 내후성에 영향을 미치는 인자를 고려, 물성을 대폭 향상시킨 도료에 대해 시험실 Weathering test 결과와 옥외폭로시험 결과, 실제 장비에 적용한 Data를 토대로 중장비용 우레탄 도료의 내후성시험 가속계수를 도출하여 개발도료의 내후성 검증기간을 단축하고자 하였다.

• Journal of the Korea Institute of Military Science and Technology
• /
• v.14 no.6
• /
• pp.974-978
• /
• 2011

The beam-matter interaction with various coating effects has received continued attention in the high power laser community. Previous works suggest that coatings promote target damage when compared to beaming on uncoated surface. Three types of paint coatings(Acrylic urethane, Silicone alkyd and Stealth blend) and a water coat on metals(Al, Ti and STS) are irradiated with a $CO_2$ laser. Both strain and temperature measurements are provided for assessing the instantaneous response characteristics of each coating on different metals. A selective combination of surface coats with metals has proven effective in either preventing or enhancing damage, both thermal and mechanical, associated with focused beaming on a target.

• Journal of Korean Society of Occupational and Environmental Hygiene
• /
• v.30 no.2
• /
• pp.134-152
• /
• 2020

Objectives: The objective of this study was to evaluate volatile organic compounds (VOCs) and toluene diisocyanates (TDIs) exposure among polyurethane waterproofing workers in the construction industry. Methods: Task-based personal air samplings were carried out at seven construction sites using organic vapor monitor for VOCs (n=88) and glass fiber filters coated with 1-(2-pyridyl)piperazine(1-2PP) for TDIs (n=81). The concentration of VOCs and TDIs were shown for four different work types(mixing paint, primer roller painting, urethane resin spread painting, painter assistant) at five different worksites (rooftop, ground parking lot, piloti, bathroom, and swimming pool). The two TDI sampling methods (filter vs impinger) were evaluated in parallel to compare the concentrations. Results: The geometric mean(GM) concentration of VOCs Exposure Index (EI) was highest for primer roller painting (1.4), followed in order by, urethane resin spread painting (0.85), mixing paint (0.53), and painter assistant (0.35) by work types. The GM of VOCs EI was highest for bathroom (1.4) followed in order by, swimming pool (0.85), piloti (0.89), ground parking lot (0.82) and rooftop (0.57) by worksites. The GM of 2,4-/2,6-TDI concentration was 0.052 ppb and 0.432 ppb each. There was no statistical difference in TDIs concentrations among worksites. The concentration of 2,6-TDI was ten times higher than that of 2,4-TDI. The concentration of 2,6-TDI by impinger method was 5.7 times higher than that by filter method. Conclusions: In this study, we found 38.6% of the VOCs samples exceeded the occupational exposure limits and 19.8% of the 2,6-TDI samples exceeded 1 ppb among polyurethane waterproofing workers. The most important determinants that increase the concentration of VOCs and TDIs was indoor environment and primer painting work.