• Fibers and Polymers
• /
• 제2권4호
• /
• pp.184-189
• /
• 2001

Continuous photografting/crosslinking of polyethyleneglycol dimethacrylate oligomers onto cotton using a water-soluble benzophenone photoinitiator was investigated. Photografting increased with increasing irradiation dose, oligomer concentration and photoinitiator concentration. Maximum grafting efficiency of DM 400 and 600 were 83% and 79%, respectively. the photografting increased the wrinkle resistance of cotton implying surface crosslinking of cotton. bothsurface crosslinking and bulk crosslinking of cotton were accomplished via dual curing of a mixed formulation containing both a thermally curable component (BTCCA/SHP) and a UV-curable component. The wrinkle resistance of the crosslinked cotton was found to be higher when cured by thermal curing due to the facile post-polymerization of the UV active component. The presence of crosslinks in the dually crosslinked cotton was verified with FT-IR and thermogravimetric analysis.

• 한국지반공학회:학술대회논문집
• /
• 한국지반공학회 2001년도 봄 학술발표회 논문집
• /
• pp.419-424
• /
• 2001

In the KOESWall system, non-woven geotextiles are placed at the face of reinforced earth until the facing blocks are built up. And when this system is used as temporary structure, geotextiles facings are exposed to sunlight during service lifetime. During these periods, degradation of nonwoven geotextiles are occurred by UV light. So the UV-resistance of nonwoven geotextiles must be assessed correctly, in considering of the site conditions. In this study, laboratory test and the field test have been performed to evaluate the UV resistance of non-woven geotextiles used in KOESWall system and the results are expressed in terms of tensile characteristics & SEM photographs.

• 대한환경공학회지
• /
• 제32권11호
• /
• pp.1063-1068
• /
• 2010

본 연구는 유효한 분변오염의 지표 미생물로서 제안되고 있는 E.coli와, 병원성 바이러스에 대한 지표 미생물로 추천되는 $Q{\ss}$ 파지의 UV 및 UV/$H_2O_2$에 대한 내성을 비교하였다. 이 결과에 의거, 병원성 바이러스 관리를 위한 E.coli 규제의 유효성을 고찰하였다. 또한, 병원성 바이러스에 대한 대체 지표 미생물로써, $Q{\ss}$ 파지, T4 및 lambda 파지의 실제 하수 2차 처리 수중에서의 UV 불활성화를 비교하였다. 실험결과, $Q{\ss}$ 파지와 E.coli는 UV에 대해 거의 동등한 내성을 보였으나, UV/$H_2O_2$ 공정에 대해서는 E.coli보다 $Q{\ss}$ 파지가 더 높은 내성을 보였다. 이로부터, $Q{\ss}$ 파지가 모든 병원성 바이러스의 UV 또는 UV/$H_2O_2$에 대한 내성을 대표한다고 할 수는 없을지라도, 지표 미생물로써 E.coli의 불활성화 효과에만 의존하는 것은, 소독공정에 따라서는 바이러스류에 대해 충분한 소독효과를 얻지 못할 수도 있음을 알 수 있었다. 한편, T4 및 lambda 등 DNA 파지와 불활성화를 비교하였을 경우, $Q{\ss}$ 파지가 UV에 대해 더 낮은 내성을 보였다. 따라서, 불활성화에 대한 지표 바이러스로써 $Q{\ss}$ 파지의 이용은 낮은 UV 조사량의 도입에 의해 결과적으로 불충분한 소독효과를 초래할 수도 있을 것 같다. 이 결과는, 병원성 바이러스류에 대해 보다 충분한 불활성화를 달성하기 위해서는 RNA 파지인 $Q{\ss}$보다 T4 및 lambda 등 DNA 파지가 지표 바이러스로써 보다 유효할 수 있음을 보여준다.

• 미생물학회지
• /
• 제27권3호
• /
• pp.297-303
• /
• 1989

Attempts to isolate the naturally occurring ultra-violet resistant bacteria from environmental sources were made. The isolates, designated No.29, 100, and 107, among numbers of bacterial isolates revealed a remarkable resistance to UV ray, whose degree of resistance in dose/response kinetics was comparable to that of an endospore-former, Bacillus subtilis. In a range of 100-300 $Jm^{-2}$/min of UV irradiation, the isolates exhibited 500-1000 fold resistance compated with E. coli. The isolated appeared to possiss cell-bound pigment of organge or crimson-red. The isolate 29 is spherical in pairs or tetrads, whereas the isolates 100 and 107 are rod. All are Gram-gositive bacteria and seemed to be non-endospore-bearer. A number of biochemical studies pursued on the isolates suggested that they are quite different to each other. Electron microscopic examination and the physiological characters of the isolate 29 suggested that this UV resistant spherical bacterium might be one species of Deinococcus, probably Deinococus radiophilus. Since there is no documents on UV resistant, Gram-positive, non-sporeformer bacillus so far, the isolates 100 and 107 might be turned out as new kinds of UV resistant bacteria occurring in nature by further investigation.

• 한국염색가공학회지
• /
• 제14권4호
• /
• pp.223-228
• /
• 2002

Cotton fabric was treated with $TiO_2$-PEG600 dispersion colloid by pad-dry-cure and wet-fixation process to improve the performance properties as well as UV-cut effect. As the concentration of $TiO_2$/PEG increased tensile strength, crease resistance, stiffness of treated cotton fabric increased. Application of wet-fixation method provided a further improvement in tensile strength, crease resistance, stiffness of treated cotton fabric. Cotton fabric treated with $TiO_2$/PEG was more efficient in UV-cut property than untreated cotton.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1997년도 추계학술대회 논문집
• /
• pp.221-224
• /
• 1997

In this study we investigated the acting characteristics of Polymers for electrical insulation by UV radiation and salt water spray treatment. We used the Polymers such as EPDM, SR. PTFE. EVA. We measured contact angle and surface resistance to know the aging characteristic of Polymer surface. And we use SEM to observe the change of the surface shape. Dry flashover voltage test impulse voltage test were carried for the polymer insulator(EVA) . Through this experiment and the analysis we could know the polymers have a good resistance to weathering conditions like as salt spray UV irradiation and mix of them. And we can compare the aging characteristics between Polymers. As a result, we could know that the surface characteristics of PTFE is better than the other. And the degree, electrical characteristics is affected by change of surface shape is not big.

• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 2002년도 추계학술발표대회 논문집
• /
• pp.261-264
• /
• 2002

Interfacial evaluation, damage sensing and cure monitoring of single carbon fiber/thermosetting composite with different curing processes was investigated using electro-micromechanical test. After curing, residual stress was monitored by measurement of electrical resistance (ER) and then it was compared to correlate with various curing processes. In thermal curing, curing shrinkage appeared significantly by matrix shrinkage and residual stress due to the difference in thermal expansion coefficient (TEC). The change in electrical resistance (ΔR) on thermal curing was higher than that on ultraviolet (UV) curing. For thermal curing, apparent modulus was the highest and reaching time until same strain was faster. So far thermal curing shows strong durability on the IFSS after boiling test.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2008년도 하계학술대회 논문집 Vol.9
• /
• pp.495-496
• /
• 2008

This paper describes the influence of Ultra-violet irradiation on time to tracking resistance of epoxy insulating materials by use of the inclined plane test. And, the influence of surface degradation was evaluated through several method such as measurement of contact angle, surface roughness, using a scanning electron microscopy. As the 1000 hours of the surface degradation with UV-CON, the flashover time decreases at different rates depending on epoxy resin and silicone rubber specimen. As the duration of the surface degradation with UV-CON is prolonged, the contact angle of epoxy resin decreases at the rate of degradation time, while that of silicone rubber was not exchanged. It is assumed that this phenomenon is related to the decrease in hydrophobicity of the surface of the materials. Also, as to epoxy resin, the decrease of hydrophobicity due to surface degradation with UV-CON is greater than that resulting from surface degradation with WOM. The UV radiation produced chalking and crazing on the surface of the insulating materials specimen.

• 한국지반신소재학회논문집
• /
• 제3권1호
• /
• pp.37-42
• /
• 2004

보강토 옹벽시스템에서, 부직포 지오텍스타일은 블럭이 시공될 때 보강토체의 전면에 노출, 포설되어 있다. 임시구조물에 보강토 옹벽이 적용될 때 지오텍스타일은 시공기간 중 일광에 노출되게 된다. 이 기간 중, 자외선에 의해 부직포 지오텍스타일의 분해가 발생하게 된다. 따라서 현장시공의 관점에서 부직포 지오텍스타일의 자외선 저항성이 명확하게 평가되어야만 한다. 본 연구에서는 실험실 및 현장시험을 수행하여 KOESWall 시스템에 사용되는 부직포 지오텍스타일의 자외선 저항성이 평가되었고, 그 결과를 SEM 사진과 인장특성으로 나타내었다.

• 한국표면공학회지
• /
• 제47권6호
• /
• pp.297-302
• /
• 2014

ZnS nanowires were synthesized in order to investigate $NO_2$ gas sensing properties. They were grown on the sapphire substrate using ZnS powders. SEM (scanning electron microscopy) showed the diameter and length of the ZnS nanowires were approximately in the range of 50 - 100 nm and a few $10s\;{\mu}m$, respectively. They were also found to be composed of Wurtzite- structured single crystals from TEM (transmission electron microscopy) analysis. $NO_2$ gas sensing performance of the ZnS nanowire was measured with electrical resistance changes caused by $NO_2$ gas with a concentration of 1-5ppm. The sensor was UV treated with an intensity of $1.2mW/cm^2$ to facilitate charge carrier transfer. The responses of the ZnS nanowires to the $NO_2$ gas at room temperature, treated with UV of two different wavelengths of 365 nm and 254 nm, are measured to be 124.53 - 206.87 % and 233.97 - 554.83%, respectively. In the current work, the effect of UV treatment on the gas sensing performance of the ZnS nanowires was studied. And the underlying mechanism for the electrical resistance changes of the ZnS nanowires by $NO_2$ gas was also discussed.