• Applied Chemistry for Engineering
• /
• v.16 no.3
• /
• pp.449-455
• /
• 2005

Electron beam (EB) and ultraviolet (UV) curable monomers (AF-1 with mono functionality and AF-2 with tetra functionality) containing hydroxy and acrylate group for anti-fogging coating were synthesized and applied to EB and UV-curable coating systems. The synthesized reactive AF-1 and AF-2 monomers were first formulated into UV-curable system and the optimization of film properties for anti-fogging coating was investigated. The 5:17.5 ratio for AF-1 and AF-2 was found to be the best optimized formulation for anti-fogging coating without destroying the other essential properties such as hardness, solvent resistance, and adhesion. The optimized formulation was applied to the EB-curable system, and EB and UV-curable systems were compared. The results demonstrated that both EB and UV-cured films coated on PC sheet showed excellent anti-fogging properties; however, the EB-cured film exhibited better hardness, adhesion, and water repellent properties than the UV-cured film.

• Korean Chemical Engineering Research
• /
• v.55 no.6
• /
• pp.754-761
• /
• 2017

UV-curable hydrophilic coating solutions were prepared by mixing colloidal silica dispersed in alcohol with an acrylic monomer, pentaerythritol triacrylate (PETA). Hydrophilic coating films were also prepared by spin coating the hydrophilic coating solutions on PC substrates and UV curing for 10 minutes subsequently. The effect of the amount of colloidal silica in the coating solutions, which was varied from 10 g to 50 g, was investigated on the hydrophilic properties of UV-cured coating films. The results showed that the amount of colloidal silica had a great influence on the hydrophilic properties of UV-cured coating films and the coating film prepared with 30 g of colloidal silica showed a lowest contact angle of $37^{\circ}$ and an excellent pencil hardness of H.

• Journal of the Korean Applied Science and Technology
• /
• v.28 no.2
• /
• pp.240-246
• /
• 2011

UV-Curable hybrid coatings were synthesized to improve the surface properties of plastic film. Organic-inorganic coating solutions were prepared by the sol-gel method using urethane-acrylate oligomer, acrylate monomer, photo initiator and tetraethoxysilane (TEOS). Methacryloyloxypropyltrimethoxysilane(MPTMS) was used as a silane coupling agent to improve chemical interaction between inorganic phases and UV curable acrylate. In this study, the surface hardness and adhesive properties were improved with the use of inorganic component. The experimental results showed that UV-Curable hybrid films containing aliphatic urethane oligomer, hexanedioldiacrylate, trimethylolpropanetriacrylate, hydroxy dimethyl acetophenone exhibited good surface properties. Also, the optimum curing conditions were investigated.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2010.05a
• /
• pp.699-700
• /
• 2010

• Journal of the Semiconductor & Display Technology
• /
• v.13 no.1
• /
• pp.35-41
• /
• 2014

UV curable transparent hard coating materials have been developed to improve the mechanical and optical properties of PET substrate. The coating materials were synthesized using various urethane acrylate oligomers, monomers, photo initiators, and leveling agents. The materials were coated on PET substrates and UV cured. The hard coated PET films were shown to have the good scratch resistance and transparency. When the urethane acrylate oligomer with more functional groups was introduced into the coating solution, the mechanical and optical properties were improved. However the higher concentration of 9-functional oligomer resulted in the decrease of workability. The addition of trimethylolpropane ethoxylate$(EO/OH)_9$ triacrylate(TMPETA) to coating solution improved the workability and properties. As a result, the UV cured film from the formulation of urethane acrylate oligomer with 9-functional groups, TMPETA as a monomer, IRACURE 754 as a photo initiator and BYK-340 as a leveling agent showed the best mechanical and optical properties in this study.

• Proceedings of the KAIS Fall Conference
• /
• 2010.11a
• /
• pp.478-481
• /
• 2010

Antimony doped tin oxide (ATO) nanoparticles were added as nanofillers to UV-curable polyester-acrylate (PEA) resin for coating to improve thermal, mechanical, and electrical properties. In this study, ATO nanoparticles were grafted by 3-glycidyloxypropyltrimethoxysilane and 3-methacryloxypropyltrimethoxysilane respectively to improve dispersion and interfacial adhesion. The physical properties and surface scratch hardness of the UV-curable nanocomposite coating were improved considerably by introducing the modified ATO nanoparticles.

• Journal of the Korean Graphic Arts Communication Society
• /
• v.16 no.3
• /
• pp.61-80
• /
• 1998

To investigate in influence of photosensitizer used with benzophenone(BP) in the curing rate and physical properties of UV curable hard coating on plastic, we prepared UV curable clear and pigmented coatings with DEA, DMA, NPM and TEA as photosensitizer, respectively. The curing rate calculated from the decrease of the absorbance of acrylic double bond measured by FT-IR spectroscopy increased s follows; DEA>DMA>NPM>TEA. this order could be explained by the reactivity of diethylamino group of DEA and the ease of formation of activated complex between BP and photosensitizer during the curing process. In UV curable pigmented coatings, the order of curing rate increased as follows; DEA>DMA>TEA>NPM. It was found that the curing rate of the pigmented coating can be increased by light scattering of TiO$_2$. The hardness of coating film cured by photosensitization of DEA and DMA is higher than other photosensitizers due to the crosslinking reaction of DEA and DMA radical bound to polymer backbone.

• Journal of the Korean Wood Science and Technology
• /
• v.32 no.6
• /
• pp.23-35
• /
• 2004

The goal of study was to investigate the influence of the acrylated urethane oligomer on mechanical properties, the chemical resistance and thermal resistance of the UV curable urethane acrylate coatings for fancy veneer overlayed plywood flooring. The pencil hardness and abrasion resistance of the coated fancy veneer overlayed plywood floorings increased with increasing the acrylate functionality of the acrylated urethane oligomer. In the case of the UV cured film containing hexa-functional acrylated aliphatic urethane oligomer, high discoloration of the coated fancy veneer overlayed plywood flooring was observed near the cracks at the beginning of the chemical treatment. In this study, it was found that the degradation of the UV cured film caused by an alkaline reagent was higher than that of the UV cured film caused by an acidic treatment.

• Journal of the Korean Graphic Arts Communication Society
• /
• v.19 no.2
• /
• pp.68-78
• /
• 2001

UV-curable resin has the properties of quick-drying, thigh productivity at low temperature, energy savint, space saving, solventless, non-polluting and low-stinking, and thus, UV-curing system has been widely used in the fields of printing inks, adhesives, paints and coating agents. This study has been executed to micro-patterning used UV-curable resin, The micro-patterning properties of this photoresist were investigated under irradiation of UV light low pressure mercury lamp. When the exposed photoresist film was developed by pure water developer, the resolution of this photoresist was about 50$\mu\textrm{m}$.

• Journal of Adhesion and Interface
• /
• v.9 no.2
• /
• pp.32-37
• /
• 2008

A series of UV-curable powder coatings with different contents of photoinitiator (0.5 wt%, 1 wt%, 2 wt%) were formulated and measured gel content, tensile strength of cured film. Heat-sensitive substrates such as MDF, plywood and PVC were coated UV-curable powder and cured coatings were measured physical properties by pendulum hardness tester, glossmeter, pull-off adhesion tester. With increasing photoinitiator content, adhesion force between coating and substrate decreased because of crosslinking density increasing. The results of pendulum hardness was not significantly changed but gloss was changed according to different substrates. Adhesion of UV-curable coatings was enough to apply for heat-sensitive substrates. From these results, we concluded that contents of photoinitiator was a effective factor in UV-curable powder coatings. UV-curable coatings was a portential candidate for heat-sensitive substrates.