• Korean Chemical Engineering Research
• /
• v.55 no.6
• /
• pp.754-761
• /
• 2017

UV-curable hydrophilic coating solutions were prepared by mixing colloidal silica dispersed in alcohol with an acrylic monomer, pentaerythritol triacrylate (PETA). Hydrophilic coating films were also prepared by spin coating the hydrophilic coating solutions on PC substrates and UV curing for 10 minutes subsequently. The effect of the amount of colloidal silica in the coating solutions, which was varied from 10 g to 50 g, was investigated on the hydrophilic properties of UV-cured coating films. The results showed that the amount of colloidal silica had a great influence on the hydrophilic properties of UV-cured coating films and the coating film prepared with 30 g of colloidal silica showed a lowest contact angle of $37^{\circ}$ and an excellent pencil hardness of H.

• Textile Coloration and Finishing
• /
• v.22 no.3
• /
• pp.239-245
• /
• 2010

Breathable waterproof PET fabrics were prepared by the UV coating of UV-curable polyurethaneacrylate(PUA) formulation mixed with polyethyleneglycol(PEG) as a water soluble pore former. The dispersed PEG in the UV-cured coating was extracted by warm water, which can generate individual circular pores uniformly distributed all over the coating instead of pore channels. Accordingly the moisture permeability of the microporously coated fabrics increased substantially with increasing PEG addition without significant reduction of hydrostatic pressure. Also the silicone diacrylate addition in the formulation was beneficial in increasing the hydrostatic pressure. The UV-based microporous coating can be an alternative to conventional thermal curing of solventborne polyurethane coating owing to the enhanced environment friendliness and energy saving.

• Journal of the Korean Institute of Illuminating and Electrical Installation Engineers
• /
• v.26 no.4
• /
• pp.35-40
• /
• 2012

In this study, the ultraviolet (UV) intensity of polymer insulator was measured using the Anti-Reflective (AR) coating lens on the occurrence of corona discharge. The UV intensity was compared before and after the AR coating. Under the 200-260[nm] of UV lens, the reflection rate before AR coating was 7.5~5.5[%] with 85-89[%] of transmission rate. After AR coating, however, the reflection rate decreased to 1.3~1.22[%] with improved transmission (97.4~97.6[%]). Then, the UV intensity by distance was measured in the polymer insulator. According to the measurement, the UV intensity increased 6.5 times at 37.5[%] of Vm/Vbd with 5[m] of distance. As distance increased, the growth rate declined. As high voltage increased, in addition, AR coating was less effective due to the count error caused by the UV sensor pulse signal overlap. Therefore, it appears that it would be more effective to detect corona discharge with 5[m] or less of distance at diagnosis of power facilities by AR coating and UV sensor sensitivity.

• Korean Membrane Journal
• /
• v.7 no.1
• /
• pp.19-27
• /
• 2005

PP hollow fiber membrane was hydrophilized by EVOH dip coating followed by low temperature plasma treatment and UV irradiation. EVOH coating attained high water flux without any prewetting but its stability did not guaranteed at high water permeation rate. At high water permeation rate, water flux declined gradually due to swelling and delamination of the EVOH coating layer causing pore blocking effect. However, plasma treatment reduces the swelling, which suppress delamination of the EVOH coating layer from PP support result in relieving the flux decline. Also, UV irradiation helped the crosslinking of the EVOH coating layer to enhance the performance at low water permeation rate. FT-IR and ESCA analyses reveal that EVOH dip coating performed homogeneously through not only membrane surface but also matrix. Thermogram of EVOH film modified plasma treatment and W irradiation show that crosslinking density of EVOH layer increased. Chemical modification by plasma treatment and UV irradiation stabilized the hydrophilic coating layer to increase the critical flux of the submerged membrane.

• Corrosion Science and Technology
• /
• v.9 no.6
• /
• pp.265-269
• /
• 2010

This paper describes the exfoliation and surface modification of muscovite mica for UV coating formulation. For the exfoliation of the mica, hydrothermal process was used in the presence of lithium nitrate ($LiNO_3$). After the cation exchange with $Li^+$ ions, the surface of the mica was modified with several amphiphilic substances to increase compatibility and storage stability in UV coating formulation. Such a hydrophobic surface modification affected colloidal stability as well as dispersibility of the exfoliated mica in UV coating solution. Anticorrosive property of mica/UV coated steel plates was tested by salt spray test (SST) and compared with sodium montmorillonite ($Na^+$-MMT)/UV coated steel plates.

• Journal of the Semiconductor & Display Technology
• /
• v.13 no.1
• /
• pp.35-41
• /
• 2014

UV curable transparent hard coating materials have been developed to improve the mechanical and optical properties of PET substrate. The coating materials were synthesized using various urethane acrylate oligomers, monomers, photo initiators, and leveling agents. The materials were coated on PET substrates and UV cured. The hard coated PET films were shown to have the good scratch resistance and transparency. When the urethane acrylate oligomer with more functional groups was introduced into the coating solution, the mechanical and optical properties were improved. However the higher concentration of 9-functional oligomer resulted in the decrease of workability. The addition of trimethylolpropane ethoxylate$(EO/OH)_9$ triacrylate(TMPETA) to coating solution improved the workability and properties. As a result, the UV cured film from the formulation of urethane acrylate oligomer with 9-functional groups, TMPETA as a monomer, IRACURE 754 as a photo initiator and BYK-340 as a leveling agent showed the best mechanical and optical properties in this study.

• Polymer(Korea)
• /
• v.38 no.3
• /
• pp.391-396
• /
• 2014

Polymer microneedles can be fabricated by a micromolding method, an easy and cost-effective method. However, it is not easy to achieve uniform coating with an aqueous coating solution due to hydrophobic surface of polymer microneedles. 3-Dimensional coating polymer microneedles could deliver more than twice as much dose as in-plane metal microneedles by increasing coating area and the number of microneedles per unit area. A uniform coating was not obtained by addition of coating additives in the coating solution. The satisfied coating was achieved by treatment of surface of polymer microneedle with metal deposition and UV/ozone, and UV/ozone treatment was an ultimate surface treatment method based on biological safety. Calcein coating polymer microneedles were prepared by using UV/ozone treatment and followed dip-coating, and they delivered calcein in porcine skin successfully after 15 min of insertion.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2010.05a
• /
• pp.699-700
• /
• 2010

• Proceedings of the KAIS Fall Conference
• /
• 2009.12a
• /
• pp.80-83
• /
• 2009

Application of UV curing technique for poly vinyl chloride (PVC) floor tiles coating has improved the quality of PVC floor. Various formulations including acrylated oligomers based on a polyurethane were blended with reactive monomers, photoinitiators and other additives. The used oligomers are commercial aliphatic urethane acrylates. Thin films were prepared on PVC tiles by bar coating with different formulations using UV radiation. The coating resins were characterized by FTIR. The properties of UV-cured films such as gloss grade and adhesion were examined. The properties of UV-cured films dependent on the influence of composition and processing conditions was studied. The investigation was conducted to achieve an optimal domain of composition and desired coating effect.

• Journal of Adhesion and Interface
• /
• v.13 no.1
• /
• pp.31-37
• /
• 2012

In this study, we investigated the curing properties of UV-LED curable color coating. Specially, the effects of UV-LED wavelength (365, 395, and 405 nm), inert gas, the concentration of photosensitizer, and dual curing on the curing behavior of UV-LED coating systems were studied. The photopolymerization behaviors and the unreacted acrylate groups at Film-air (FA) interface and Film-substrate (FS) interface were investigated by photo differential scanning calorimetry (Photo-DSC) and Fourier-transform infrared spectroscopy with attenuated total reflection (FT-IR/ATR), respectively. Photo-DSC results showed that the heat flow and the ultimate conversion for coating system cured by 405 nm UV-LED were higher than the corresponding values for coating systems cured by 395 and 365 nm UV-LED. FT-IR/ATR results showed that the UV-LED curing systems improved interior and through curing of the coating film, but significantly are affected by oxygen inhibition at FA-interface. The inert environment such as nitrogen purging and the dual curing improved the surface and interior curing of the coating films.