• Title/Summary/Keyword: UO2

Search Result 620, Processing Time 0.031 seconds

The Effect of PVA-Al(III) Complex on Pore Formation and Grain Growth of $UO_2$ Sintered Pellet (II) (PVA-A(III) 착물이 $Uo_2$ 소결체의 기공형성과 결정립성장에 미치는 영향(II))

  • 이신영;김형수;노재성
    • Journal of the Korean Ceramic Society
    • /
    • v.36 no.8
    • /
    • pp.782-790
    • /
    • 1999
  • The compressibility sinterability sintering behaviour and thermal stability of AlOOH added UO2 pellt and PVA-Al(III) complex added UO2 pellet were investigated respectively. Compared with characteristics of AlOOH added UO2 pellet the green density and the sintered density of PVA-Al(III) complex added UO2 pellet were lowered but the grain size and the pore size of that were more increased in accordance with higher compacting pressure. The AlOOH added UO2 pellet had the grain size of about 14${\mu}{\textrm}{m}$ with monomodal pore size distribution while the PVA-Al(III) complex added UO2 pellet had the grain size of about 42 ${\mu}{\textrm}{m}$ with bimodal pore size distribution. The PVA-A(III) complex added UO2 pellet had a similiar open porosity to the AlOOH added UO2 pellet and a lower resintered density change than the AlOOH added UO2 pellet.

  • PDF

Measurement of Melting Temperatures of $UO_2,\;(U,Gd)O_2\;and\;(U,Er)O_2$ Fuels

  • Kang Ki Won;Yang Jae Ho;Kim Keon Sik;Kim Jong Hun;Lee Young Woo;Song Kun Woo
    • Nuclear Engineering and Technology
    • /
    • v.36 no.1
    • /
    • pp.104-111
    • /
    • 2004
  • The melting temperatures of $UO_2,\;UO_2-6wt\%Gd_{2}O_3,\;UO_2-12wt\%Gd_{2}O_3,\;UO_2-2wt\%Er_{2}O_3,\;and\;UO_2-4wt\%Er_{2}O_3$ fuels were measured. Fuel materials were loaded in a tungsten capsule of which shape met the black body condition. The melting temperature was measured by the thermal arrest method during heating of the capsule in an induction furnace. The measured melting temperature of $UO_2$ fuel was $2815{\pm}20^{\circ}C$. The solidus and liquidus temperatures of $UO_2-Gd_{2}O_3\;and\;UO_2-Er_{2}O_3$ had also been measured, and it was observed that the solidus temperatures of them were lower than the liquidus temperature by $15{\sim}25^{\circ}C$. Measured melting temperatures of $UO_2,\;UO_2-Gd_{2}O_3\;and\;UO_2-Er_{2}O_3$ fuels were as follows:

첨가제에 의한 $UO_2$$UO_2$-4wt% 의 미세구조 변화

  • 김한수;김시형;이영우
    • Proceedings of the Korean Nuclear Society Conference
    • /
    • 1995.05a
    • /
    • pp.668-673
    • /
    • 1995
  • $UO_2$-CeO$_2$ 모의혼합분말에 첨가제를 미량 첨가하여 소결체의 미세구조 변화를 $UO_2$분말의 경우와 비교, 관찰하였다. 소결 첨가제로서 Ta, Ti 및 Nb를 사용하였으며, 이들을 미세한 산화물의 형태로 $UO_2$$UO_2$-CeO$_2$에 첨가하여 환원성 및 산화성 분위기에서 각각 소결하였다. Ta, Ti 및 Nb는 환원소결에서 $UO_2$의 결정립을 성장시켰으나 산화소결에서는 첨가효과가 크게 나타나지 않았다. $UO_2$-0.lw%TiO$_2$$UO_2$-0.6w%Ta$_2$O$_{5}$의 환원소결체에서 eutectic phase가 관찰되었으나 산화소결체에서는 나타나지 않았다. $UO_2$-4wt%CeO$_2$의 환원소결에서는 Ti만이 결정립성장에 기여하는 것으로 나타났으며 Ta, Nb와 같이 $UO_2$에 치환형으로 고유되는 원소는 Ce 이온과 Cluster를 형성함으로 결정립성장에 거의 기여하지 못하고, Ti와 같이 UO2$_2$ 침입형으로 고용되는 원소는 일부가 인접한 Ce$_{U}$' 이온과 cluster를 형성하더라도 나머지가 V$_{U}$'의 형성에 기여하므로서 결정립을 성장시킬 수 있다.

  • PDF

$Li_2O$ 첨가에 따른 $UO_2$$UO_2-3.23wt%CeO_2$분말의 소결거동 연구

  • 김시형;김한수;나상호;이영우;손동성
    • Proceedings of the Korean Nuclear Society Conference
    • /
    • 1997.05b
    • /
    • pp.74-79
    • /
    • 1997
  • $UO_2$$UO_2$-3.23wt%CeO$_2$가 128$0^{\circ}C$에서 소결되면 밀도는 각각 93%T.D., 91.2%T.D.이었으나, Li$_2$O가 0.lwt%씩 첨가된 경우에는 소결밀도가 95.5%T.D., 95.1%T.D.로 증가하였다. 소결온도가 증가함에 따라서 $UO_2$$UO_2$-3.23wt%CeO$_2$의 소결밀도는 현저하게 증가되는 반면에, Li$_2$O가 첨가된 경우에는 저온에서도 이미 치밀화가 많이 일어났기 때문에 소결밀도의 증가폭이 완만하였다. Li$_2$O가 첨가된 분말에서는 소결온도가 더 높아지면, 결정립성장이 주로 일어나게 되어 168$0^{\circ}C$에서 소결되었을 때, $UO_2$$UO_2$-0.1wt%Li$_2$O의 결정립크기가 각각 8.7$\mu\textrm{m}$, 120$\mu\textrm{m}$ 이고, $UO_2$-3.23wt%CeO$_2$$UO_2$-3.23wt%CeO$_2$-0.lwt%Li$_2$O는 각각 10.9$\mu\textrm{m}$, 34$\mu\textrm{m}$ 이었다. $UO_2$$UO_2$-3.23wt%CeO$_2$ 그리고, 두 조성에 Li$_2$O가 각각 첨가된 경우, Ar-4vol.%H$_2$ 분위기보다 H$_2$분위기에서 소결했을 때 밀도가 더 높았다. 그러나, 결정립은 $UO_2$$UO_2$-Li$_2$O의 경우, 수소분위기에서 소결했을 때, (U,Ce)O$_2$와 (U,Ce)O$_2$-Li$_2$O에서는 Ar-4vol.%H$_2$분위기에서 소결했을 때 더욱 성장하였다.

  • PDF

The Comparison of Sintering Characteristics between the PVA-Al(III) Complex added $UO_2$Pellet and AlOOH added $UO_2$pellet (PVA-Al(III) 착물 첨가 $UO_2$소결체와 AlOOH 첨가 $UO_2$소결체의 소결 특성 비교)

  • Lee, Sin-Yeong;Yu, Ho-Sik;Lee, Seung-Jae;Kim, Hyeong-Su;Bae, Gi-Gwang
    • Korean Journal of Materials Research
    • /
    • v.10 no.1
    • /
    • pp.55-61
    • /
    • 2000
  • The sintering characteristics of PVA-Al(III) complex added $UO_2$ pellet and AlOOH added $UO_2$pellet were compared. The major phase of PVA-Al(III) complex and AlOOH decomposed at $1000^{\circ}C$ in $H_2$atmosphere was $\theta-Al_2O_3$. Compared with the apparent density of pure $UO_2$, that of AlOOH added $UO_2$ powder was higher but that of PVA-Al(III) complex was lower. the densification of AlOOH added $UO_2$ pellet was initiated at about $800^{\circ}C$, the densification of PVA-Al(III) complex added $UO_2$ pellet was initiated at about $900^{\circ}C$ respectively. In a view of pore size distribution, the PVA-Al(III) complex added $UO_2$ pellet appeared as monomodal type, whereas the AlOOH added $UO_2$ pellet appeared as bimodal type. The grain size of AlOOH added $UO_2$ pellet was about $13\mu\textrm{m}$ but the grain size of PVA-Al(III) complex added $UO_2$ pellet was increased up to about $36\mu\textrm{m}$.

  • PDF

Properties of Compacts and Pellets Made Using Bimodal- Sized $UO_2$ Powder

  • Kim, Keon-Sik;Song, Kun-Woo;Kang, Ki-Won;Kim, Jong-Hun;Kim, Young-Min
    • Nuclear Engineering and Technology
    • /
    • v.31 no.6
    • /
    • pp.608-617
    • /
    • 1999
  • The powder mixture which has a bimodal size distribution, with a large mode corresponding to AUC-UO$_2$ powder and a small one corresponding to ADU-UO$_2$ powder, was prepared, pressed into compacts, and sintered at 1680t for 4 hours in hydrogen gas. The compact density of the powder mixture increases with increasing ADU-UO$_2$content within a content of 20 wt %, since small ADU-UO$_2$ particles can fill interstices between large AUC-UO$_2$particles. The UO$_2$ pellet made using the powder mixture has a lower open porosity than that made using AUC-UO$_2$ powder alone. The mechanism for the formation of a flake-like pore is proposed, and the decrease in open porosity may be ascribed to the decrease in the number of flake-like pores.

  • PDF

Effect of $UO_2$ Powder Property and Oxygen Potential on Sintering Characteristics of $UO_2-Gd_2O_3$ Fuel

  • Song, Kun-Woo;Kim, Keon-Sik;Yoo, Ho-Sik;Jung, Youn-Ho
    • Nuclear Engineering and Technology
    • /
    • v.30 no.2
    • /
    • pp.128-139
    • /
    • 1998
  • The effect of UO$_2$ powder property and oxygen potential on characteristics of sintered UO$_2$-Gd$_2$O$_3$ fuel pellets has been investigated. Two types of powder, mixture of AUC-UO$_2$ and Gd$_2$O$_3$powders (type I) and mixture of ADU-UO$_2$ and Gd$_2$O$_3$powders (type II), have been prepared, pressed, and sintered at 168$0^{\circ}C$ for 4 hours. Four sintering atmospheres with different mixing ratios of $CO_2$to H$_2$ gas ranging from 0 to 0.3 have been used. UO$_2$-Gd$_2$O$_3$ fuel has lower sintered density than UO$_2$ fuel, and the density drop is larger for powder type I than for powder type II. As the oxygen potential increases, the sintered density of UO$_2$-2wt% Gd$_2$O$_3$pellets increases but that of UO$_2$-10wt% Gd$_2$O$_3$ pellets decreases. It is found that pores are newly formed in UO$_2$-10wt% Gd$_2$O$_3$ pellets in accordance with the decrease in density. The grain size of UO$_2$-Gd$_2$O$_3$ fuel increases and a short range G4 distribution becomes homogeneous as the oxygen potential increases. A long range ed distribution and grain structure are inhomogeneous for powder type II. The lattice parameter of (U,Gd)O$_2$solid solution decreases linearly with Gd$_2$O$_3$ content. The dependence of UO$_2$-Gd$_2$O$_3$fuel characteristics on powder type and sintering atmosphere have been discussed.

  • PDF

Uranium Recovery from Nuclear Fuel Powder Conversion Plant Filtrate and its Thermal Decomposition Characteristics (핵연료분말 제조공정에서 발생된 여액으로부터 우라늄 회수 및 회수된 우라늄 화합물의 열분해 특성)

  • Jeong, Kyung-Chai;Jeong, Ji-Young;Kim, Byung-Ho;Kim, Tae-Joon;Choi, Jong-Hyeun
    • Journal of the Korean Ceramic Society
    • /
    • v.39 no.2
    • /
    • pp.204-209
    • /
    • 2002
  • In this study, $UO_4{\cdot}2NH_4F$, the precipitates which has low solubility, was obtained by chemical precipitation method to recover and reuse the trace uranium from the liquid waste producing in AUC process and for this compound it was characterized by means of chemical analysis, TG-DTA, XRD and FT-IR analyses. This compound was analyzed as $UO_4{\cdot}2NH_4F$ and shape of this precipitate was hexagonal type, having the size of 2∼3 ${\mu}m$. Also, the intermediates were obtained as $UO_4F,\;UO_4,\;UO_3,\;and\;U_3O_8$ by the thermal decomposition over the temperature of 220, 310, 515 and 640$^{\circ}C$, respectively. It is concluded that under the condition of a constant heating rate of 5$^{\circ}C$/min in air atmosphere range of between room temperature and 800$^{\circ}C$, thermal decomposition reaction mechanism of $UO_4{\cdot}2NH_4F$ is as follow; $UO_4{\cdot}2NH_4F{\rightarrow}UO_4F{\rightarrow}UO_4{\rightarrow}UO_3{\rightarrow}U_3O_8$.

The Conceptual Design of a Hybrid $UO_2$-MOX Pellet

  • Shin, Ho-Cheol;Bae, Sung-Man;Kim, Yong-Bae;Lee, Sang-Hee
    • Proceedings of the Korean Nuclear Society Conference
    • /
    • 1997.05a
    • /
    • pp.45-50
    • /
    • 1997
  • The conventional MOX fuel shows adverse controllability in view of its neutronic characteristics such as decreased soluble boron worth and effective delayed-neutron fraction compared to the UO$_2$ fuel. In order to mitigate these disadvantages, we devised a new concept of the hybrid UO$_2$-MOX fuel pellet with dual structure such that its outer annular section contains. UO$_2$ fuel and its inner cylindrical bar contains MOX fuel. The lattice physics code HELIOS was used to evaluate the neutronic characteristics of three different types of fuel pellets ; UO$_2$ fuel pellet, MOX fuel pellet, and hybrid UO$_2$-MOX fuel pellet. Results show that the hybrid UO$_2$-MOX fuel pellet generally has intermediate neutronic tendency between UO$_2$ fuel and MOX which could diminish the problems arising from the use of the conventional MOX fuel.

  • PDF