• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2012년도 춘계학술발표대회
• /
• pp.111.1-111.1
• /
• 2012

Interest in flexible transparent conducting films (TCFs) has been growing recently mainly due to the demand for electrodes incorporated in flexible or wearable displays in the future. Indium tin oxide (ITO) thin films, which have been traditionally used as the TCFs, have a serious obstacle in TCFs applications. SWNTs are the most appropriate materials for conductive films for displays due to their excellent high mechanical strength and electrical conductivity. In this work, the fabrication by the spraying process of transparent SWNT films and reduction of its sheet resistance on PET substrates is researched Arc-discharge SWNTs were dispersed in deionized water by adding sodium dodecyl sulfate (SDS) as surfactant and sonicated, followed by the centrifugation. The dispersed SWNT was spray-coated on PET substrate and dried on a hotplate. When the spray process was terminated, the TCF was immersed into deionized water to remove the surfactant and then it was dried on hotplate. The TCF film was then was doped with Au-ionic doping treatment, rinsed with deionized water and dried. The surface morphology of TCF was characterized by field emission scanning electron microscopy. The sheet resistance and optical transmission properties of the TCF were measured with a four-point probe method and a UV-visible spectrometry, respectively. This was confirmed and discussed on the XPS and UPS studies. We show that 87 ${\Omega}/{\Box}$ sheet resistances with 81% transmittance at the wavelength of 550nm. The changes in electrical and optical conductivity of SWNT film before and after Au-ionic doping treatments were discussed. The effect of Au-ion treatment on the electronic structure change of SWNT films was investigated by Raman and XPS.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2009년도 하계학술대회 논문집
• /
• pp.106-107
• /
• 2009

In this study, We investigated the effects of substrate temperature on the electrical and optical properties of Ga-, B-codoped ZnO(GZOB) thin films. GZOB thin films were deposited on glass substrate with various substrate temperature in the range from R.T. to $500\;^{\circ}C$ by DC magnetron sputtering. In the reslt, GZOB films at $400\;^{\circ}C$ exhibited a low resistivity value of $8.67\;{\times}\;10^{-4}\;{\Omega}-cm$, and a visible transmission of 80% with a thickness of 300 nm. This result indicated that the addition of Ga and B in ZnO films leads to the improvement of conductivity and transparent. From the result, we can confirm the possibility of the application as transparent conductive electrodes.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2011년도 제42회 하계학술대회
• /
• pp.1430-1431
• /
• 2011

To develope the transparent conducting oxide(TCO) films is one of the essential technologies to improve various properties of electro-optical devices such as dye-sensitized solar cells(DSCs). ITiO thin film is considered one of the candidates as TCO electrodes of DSCs because it shows many advantages such as the high transparency in long wavelength range above 700nm and excellent properties of electrical necking between nanoporous TiO2 and ITiO transparent electrode. This paper presents the effect of sputtering processes on the structural, electrical and optical properties of ITiO thin film deposited by r.f. magnetron sputtering. The effect of doping concentration of Ti on the chemical compounds and C axis-orientation properties of were mainly studied experimentally. The morphology and electrical properties were greatly influenced by deposition processes, especially by the doping concentration of Ti. The $3.8{\times}10^{-4}{\Omega}{\cdot}cm$ of minimum volume resistivity were obtained under the experimental conditions of gas pressure 7mTorr, substrate temperature $300^{\circ}C$, and 2.5% of Ti doping concentration.

• 전기학회논문지P
• /
• 제58권4호
• /
• pp.615-618
• /
• 2009

In order to apply for transparent conductive oxide(TCO), we deposited ZnO thin film on the glass at room temperature by RF magnetron sputtering method. Deposition conditions for low resistivity were optimized in our previous studies. Under the deposition condition with the RF power of 800 [W]. Sheet resistance and surface roughness of ITO and ZnO thin film were measured by Hall-effect measurement system and AFM, respectively. The sheet resistance of ITO and ZnO thin film were 7.290 [$\Omega$] and 4.882 [$\Omega$], respectively. and surface roughness were 3.634 [nm] and 0.491 [nm], respectively. Green OLED was fabricated with the structure of TPD(400 [$\AA$])/Alq3(600 [$\AA$])/LiF(5 [$\AA$])/Al(1200 [$\AA$]). Turn-on voltage of green OLED applied ITO was 7 [V] and luminance was 7,371 [$cd/m^2$]. And, Turn-on voltage of green OLED applied ZnO was 14 [V] and luminance was 6,332 [$cd/m^2$].

• 한국전기전자재료학회논문지
• /
• 제23권4호
• /
• pp.327-332
• /
• 2010

We report on the effect of PET substrate preheating on the characteristics of the flexible and transparent indium tin oxide (ITO) electrode grown by a specially designed roll-to-roll sputtering system for touch panel applications. It was found that electrical and optical properties of the roll-to-roll sputter grown ITO film were critically dependent on the preheating of the PET substrate. In addition, the roll-to-roll sputter-grown ITO film after post annealing test at $140^{\circ}C$ for 90 min showed stable electrical and optical properties. The low sheet resistance and high optical transmittance of the ITO film grown on the preheated PET substrate demonstrate that the preheating process before ITO sputtering is one of the effective way to improve the characteristics of ITO/PET film. Furthermore, the superior flexibility of the ITO electrode grown on the preheated PET substrate indicates that the preheating treatment is a promising technique to obtain robust ITO/PET sample for touch panel applications.

• 한국전기전자재료학회논문지
• /
• 제25권4호
• /
• pp.304-308
• /
• 2012

Transparent thin film transistors (TTFT) were fabricated using the rf magnetron sputtered ZnO-$SnO_2$ films as active layers. A ceramic target whose Zn atomic ratio to Sn is 2:1 was employed for the deposition of ZnO-$SnO_2$ films. To study the post-annealing effects on the properties of TTFT, ZnO-$SnO_2$ films were annealed at $200^{\circ}C$ or $400^{\circ}C$ for 5 min before In deposition for source and drain electrodes. Oxygen was added into chamber during sputtering to raise the resistivity of ZnO-$SnO_2$ films. The effects of oxygen addition on the properties of TTFT were also investigated. 100 nm $Si_3N_4$ film grown on 100 nm $SiO_2$ film was used as gate dielectrics. The mobility, $I_{on}/I_{off}$, interface state density etc. were obtained from the transfer characteristics of ZnO-$SnO_2$ TTFTs.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2014년도 제46회 동계 정기학술대회 초록집
• /
• pp.331-331
• /
• 2014

3족 질화물에 기반한 발광다이오드는 비소화물이나 인화물에 비해 여러 가지 장점을 가져 각광받아왔다. 특히, (Al)GaN 에 기반한 자외선 영역 발광 다이오드는 자외선 경화, 소독 등의 여러 가지 응용 가능성을 가진다 [1]. 하지만, 심자외선 영역으로 갈수록 높은 접촉 저항과 투명전극에서의 광흡수에 의해 전류주입 효율과 광추출 효율이 감소하여 결국 외부양자 효율이 더욱 열화되는 특성을 보인다. 이는 넓은 밴드갭을 가지는 물질을 이용하여 p-(Al)GaN 층에서 오믹접촉을 이루어야만 해결이 가능하지만 아직까지 이러한 결과가 보고된 바 없다. 본 연구에서는, 우리는 넓은 밴드갭을 가지는 silicon dioxide (SiO2) 에 전기장을 인가하여 p-GaN, and p-AlGaN 층에 전도성 필라멘트를 형성하여 전기전도도를 부여하는 연구를 진행하였다. p-GaN 과 p-AlGaN 위에서 5 nm 두께의 SiO2는 schottky 한 특성과 280 nm의 파장대역에서 약 97%의 투과율을 보였다. 비록 schottky 장벽이 형성되었지만, 전기전도도가 크게 향상되었으며 심자외선 영역에서 매우 낮은 흡수율을 보였다. 이는 기존의 증착후 열처리를 거쳐 제조된 전극에 비하여 우수한 특성을 지니며 향후 심자외선 영역 발광다이오드의 p-(Al)GaN 층 위에 오믹접촉을 이룰수 있는 가능성을 제시한다.

• 한국재료학회지
• /
• 제27권2호
• /
• pp.69-75
• /
• 2017

To establish low-temperature process conditions, process-property correlation has been investigated for Ga-doped ZnO (GZO) thin films deposited by pulsed DC magnetron sputtering. Thickness of GZO films and deposition temperature were varied from 50 to 500 nm and from room temperature to $250^{\circ}C$, respectively. Electrical properties of the GZO films initially improved with increase of temperature to $150^{\circ}C$, but deteriorated subsequently with further increase of the temperature. At lower temperatures, the electrical properties improved with increasing thickness; however, at higher temperatures, increasing thickness resulted in deteriorated electrical properties. Such changes in electrical properties were correlated to the microstructural evolution, which is dependent on the deposition temperature and the film thickness. While the GZO films had c-axis preferred orientation due to preferred nucleation, structural disordering with increasing deposition temperature and film thickness promoted grain growth with a-axis orientation. Consequently, it was possible to obtain a good electrical property at relatively low deposition temperature with small thickness.

• 센서학회지
• /
• 제22권2호
• /
• pp.105-110
• /
• 2013

We fabricated an a-IGZO thin film transistor (TFT) with AZO/Ag/AZO transparent multilayer source/drain contacts by rf magnetron sputtering. a-IGZO TFT with AZO/Ag/AZO multilayer S/D electrodes (W/L = 400/50 ${\mu}m$) showed a subs-threshold swing of 3.78 V/dec, a minimum off-current of $10^{-12}$ A, a threshold voltage of 0.41 V, a field effect mobility of $10.86cm^2/Vs$, and an on/off ratio of $9{\times}10^9$. From the ultraviolet photoemission spectroscopy, it was revealed that the enhanced electrical performance resulted from the lowering of the Schottky barrier between a-IGZO and Ag due to the insertion of an AZO layer and thus the AZO/Ag/AZO multilayer would be very appropriate for a promising S/D contact material for the fabrication of high performance TFTs.

• 한국세라믹학회지
• /
• 제44권6호
• /
• pp.303-307
• /
• 2007

Transparent In-doped zinc oxide (IZO) thin films are deposited with variation of pulsed DC power at Ar atmosphere on coming 7059 glass substrate by pulsed DC magnetron sputtering. A c-axis oriented IZO thin films were grown in perpendicular to the substrate. The optical transmittance spectra showed high transmittance of over 80% in the UV-visible region and exhibited the absorption edge of about 350 nm. Also, the IZO films exhibited the resistivity of ${\sim}10^{-3}{\Omega}\;cm$ and the mobility of ${\sim}6cm/V\;s$. Organic Light-emitting diodes (OLEDs) with IZO/N,N'-diphenyl-N, N'-bis(3-methylphenl)-1, 1'-biphenyl-4,4'-diamine (TPD)/tris (8-hydroxyquinoline) aluminum ($Alq_3$)/LiF/Al configuration were fabricated. LiF layer inserted is used as an interfacial layer to increase the electron injection. Under a current density of $100\;mA/cm^2$, the OLEDs show an excellent efficiency (9.4 V turn-on voltage) and a good brightness ($12000\;cd/m^2$) of the emission light from the devices. These results indicate that IZO films hold promise for anode electrodes in the OLEDs application.