• 대한의용생체공학회:의공학회지
• /
• 제21권3호
• /
• pp.273-277
• /
• 2000

순 티타늄(공업용 순 티타늄, 2급)의 0.5M에서 0.7M 농도의 $H_3PO_4$ 용액에서 $0.3\~l.0 A/dm^2$의 정전류 밀도변화에 따른 anodizing 거동을 관찰하였다. 이때 형성된 산화피막을 SEM과 XRD로 관찰, 분석하였다. 실험결과 0.05M $H_3PO_4$ 용액의 조건에서 전압-시간 (V-T)곡선의 초기에는 직선적인 관계를 보였고, 전류밀도가 증가함에 따라 포물선의 형태를 나타내었다. 그리고 V-T곡선의 형태는 전해질의 농도의 증가에 따라 큰 변화가 없었지만, 최종적인 전압은 감소하였다. 티타늄의 산화피막은 전해질 농도와 전류밀도가 증가할수록 미세한 입자 형태에서 눈꽃과 같고 층을 이룬 입자들로 구성된 구조를 나타내었다. 산화막과 전해질의 계면에서의 방전에 의해 산화피막의 국소적인 침착과 용해를 동반하였다. 산화피막의 결정성은 anodizing 전압이 증가할수록 증가하였고 전해질의 농도가 증가할수록 감소하는 경향을 보였다.

• 한국재료학회지
• /
• 제13권11호
• /
• pp.761-768
• /
• 2003

The corrosion resistance and cytotoxicity behavior of Ti alloys were studied as a function of Nb contents(3wt.%Nb, 20wt.%Nb, 40wt.%Nb). Ti-Nb alloys were melted by vacuum arc furnace and then rolled to 50% reduction ratio after homogenized at 105$0^{\circ}C$ for 24hrs. The corrosion resistance of Ti-Nb alloys were investigated by potentiodynamic polarization test in the 0.9% NaCl and 5% HCI solution. Biocompatibility of Ti-Nb alloys was evaluated by cytotoxicity test. The results can be summarized as follows 1) The microstructure change from equiaxial to acicular and the increased $\beta$ phase in Ti-Nb alloys were obtained as the Nb content increased. 2) For the corrosion test in the solution of 0.9% NaCl and 5% HCI, the corrosion behavior of Ti-Nb alloys was similar to ASTM grade 2 CP Ti. 3) For the cytotoxicity test, Ti-Nb alloys showed excellent biocompatibility compared to ASTM grade 2 CP Ti, 316L STS and Co-Cr alloys.

• 대한치과보철학회지
• /
• 제51권4호
• /
• pp.261-268
• /
• 2013

연구 목적: 본 연구는 납형의 크기 및 형태 변화가 티타늄의 주조성에 어떠한 영향을 미치는지 확인하고자 하였다. 연구 재료 및 방법: 납형의 크기에 따라 Small Pattern군과 Large Pattern군으로 나누었고, 각각 Flat, Semicircular, Horse-shoe 및 V-shape형으로 납형의 형태에 따라 4개의 하위군으로 나누어 총 8개의 군으로 분류하였다. 모든 납형의 주입선은 Runner-bar형으로 하였다. 티타늄 주조 전용 매몰재인 실리카계 매몰재(Rematitan Plus$^{(R)}$, Dentarum, Germany)를 이용하여 매몰하였고, 아크용융 방식의 원심 주조기(Ti Cast Super R$^{(R)}$, Selec, Japan)를 사용하여 주조하였다. 주조성 평가는 완전한 형태로 주조 된 격자의 개수를 척도로 재현 정도를 확인하였다. 통계처리는 SPSS ver. 19.0 for WIN (SPSS. Inc. Chicago, IL, USA)를 사용하였다. 납형의 크기 및 형태에 따른 티타늄의 주조성을 이원변량 분산분석(Two-way ANOVA)을 이용하여 분석하였다. 결과:납형의 평균 재현율은 Small Pattern군은 95.14%, Large Pattern군은 94.30%로 Small Pattern군의 주조성이 유의하게 높았다(P<.05). 납형의 형태 변화에 따른 주조성은 Small Pattern군에서 Semicircular군 133.20개(96.52%), Horse-shoe군 132.40개(95.94%), Flat군 132.00개(95.65%), V-shape군 127.60개(92.46%) 순으로 감소하였다. Large Pattern군은 Flat군 198.60개(95.94%), V-shape군 197.80개(95.56%), Semicircular군 196.40개(94.88%), Horse-shoe군 188.00개(90.82%)순으로 감소하였다. Small Pattern군과 Large Pattern군 모두에서 납형의 형태변화에 따른 주조성은 유의할 만한 차이를 보이지 않았다(P>.05). 결론:주조체의 크기가 작을수록 주조성이 높아짐을 알 수 있었고 형태에 따른 주조성에서는 큰 영향을 받지 않는 것을 알 수 있었다.

• 한국재료학회지
• /
• 제26권6호
• /
• pp.306-310
• /
• 2016

To produce 4N grade high-purity silica powder from natural ore, the mineralogical characteristics of natural silica ore were investigated and their effects on the purification process were revealed. The Chinese silica mineral ore used was composed of iron and aluminum as main impurities and calcium, magnesium, potassium, sodium, and titanium as trace impurities; these trace impurities generally exist as either single oxides or complex oxides. It was confirmed that liberation and acidic washing of the impurities were highly dependent on the particle size of the ground silica ore and on its mineralogical characteristics such as the distribution and phases of existing impurities. It is suggested that appropriate size reduction of silica ore should be realized for optimized purification according to the origin of the natural silica ore. A single step purification process, the mechano-chemical washing (MCW) process, was proposed and verified in comparison with the conventional multi step washing process.

• 한국재료학회지
• /
• 제19권9호
• /
• pp.473-480
• /
• 2009

In order to provide the mechanism of nozzle clogging, recovered nozzles for high strength steel grade were examined carefully after continuous casting. The thickness of clogged material in SEN is increased in the following order: from the bottom to the top of the nozzle, upper part of slag line, and the pouring hole. Nozzle clogging material begins to form due the adhesion of metal to nozzle wall, the decarburization, and reduction of oxide in the refractory by Al and Ti in the melt. The reduction of oxide in the refractory by Al and Ti improves the wettability of the melt on the refractory and forms a thin Al-Ti-O layer. Metal containing micro alumina inclusions is solidified on the Al-Ti-O layer, and the solid layer grows due to the heat evolution through the nozzle wall. Thermodynamic calculation has been made for the related reactions. The effect of superheat to the nozzle clogging is discussed on ultra low carbon steel and low carbon steel.

• The Journal of Advanced Prosthodontics
• /
• 제10권2호
• /
• pp.163-166
• /
• 2018

PURPOSE. The marginal bone loss of implants with laser treated surface was investigated after six weeks of loading after implant installation to the mandible molar area. MATERIALS AND METHODS. A total of 23 implants were placed in the edentulous molar area of the mandible: 13 implants were immediately loaded and 10 implants were early loaded. The implants used were made of titanium grade 23, screw shaped, 4.2 mm in diameter, and 10 mm in length. Patients were evaluated with resonance frequency analysis at implant fixture installation and 1, 2 (final prosthesis installation), 3, 5, 8, and 14 months later. X-rays were taken at 2 months after fixture installation and 1, 2, 3 years after to measure the marginal bone loss. RESULTS. The mean ISQ value measured at the implant installation was over 70 at all-time points. The average of marginal bone loss was average 0.33 mm. CONCLUSION. Immediate implant loading for laser treated implants would be possible.

• 한국기계가공학회지
• /
• 제3권1호
• /
• pp.72-78
• /
• 2004

In this paper, mechanical behaviors of developed pedicle screw system, made of bio-mechanical materials(Ti-6Al-4V, Grade 5), ale predicted using FEM analysis. As a first step, morphologic construction of normal Korean spines and surgical operation convenience are considered to design optimum pedicle screw system. In this step, various design variables are considered as design parameters to develop optimized models. As a next step, tension and bending tests are performed to improve the structural performance of the developed system using finite element method. In this step, required Static compression and bending test specifications by ASTM F-04 25 04 01 are applied to understand the bio-mechanical behaviors of the designed spinal implant system under various load types. As the results of this research, it is possible to develop efficient pedicle screw system, having enough rigidity and fixation to stand any spinal damage under allowable stress conditions.

• 한국광물학회지
• /
• 제23권1호
• /
• pp.25-37
• /
• 2010

경남 하동군과 산청군 일대는 선캄브리아기 회장암체 내 티탄철석 광상이 배태됨이 잘 열려져 있다. 이 연구는 하동군 옥종면 월횡리에 위치하는 하동 티타늄 광산지역과 산청군 단성변 일대 6개 광구지역(단성 지적 64, 65, 74, 75, 84, 85호)에 대한 조사를 통하여 티탄철석광체의 배태양상을 규명 하고자 시도되었다. 옥종면 월횡리 티타늄 광체는 맥상으로 발달하며 북북동 주향과 북서 경사방향으로 폭 약 10~50 m, 연장 약 100 m로 발달한다. 이 지역에서 고품위 광체 ($TiO_2$ 20 wt% 내외)는 폭약 7m로 간극 누적형 회장암체 내 발달하기도 한다. 각력화 및 전단조직이 뚜렷하고 티탄철석은 기질부에서 각섬석과 수반됨이 특징이다. 산청군 단성면 일대는 엽리상 회장암체 내 티탄철석 광화작용이 초래되어 수m부터 수십m까지 다양한 폭으로 여러 매 교호 발달하는 성층형을 나타낸다. 티탄철석은 기질부에 광염되어 있으며 신장되거나 굴곡되어 산출하며 대체적으로 저품위 ($TiO_2$ 1.0~6.0 wt%)이다. 연구지역에서 티탄철석 광체는 맥상과 성층상으로 산출함이 확인되었으며 맥상광체가 성층상 광체보다는 고품위를 나타냄이 특징이다.

• 대한치과보철학회지
• /
• 제48권2호
• /
• pp.122-127
• /
• 2010

연구목적: 본 연구는 machined 임플란트와 골유도능이 있는 calcium phosphate를 electron-beam deposition으로 coating처리한 임플란트의 골/임플란트 접촉률을 조직형태계측학적으로 비교하는 것이다. 연구 재료 및 방법:여섯 마리의 수컷 New Zealand white rabbit과직경3.3 mm, 길이 5 mm의 임플란트 24개를 준비하였다. Machined 임플란트 (대조군)와 calcium phosphate coated 임플란트(실험군)를 좌, 우 경골에 2개씩 총 4개를 식립하고 임플란트 주위에 부하가 가해지지 않도록 하여 3주, 6주의 치유기간을 두었다. 식립 3주와 6주후, 각각 3마리의 토끼를 희생하여 조직시편을 제작하였다. 제작된 시편을 광학현미경 하에서 골/임플란트 접촉률 (BIC ratio)을 계산하고 paired t-test로 두 군을 비교하였다. 결과:골/임플란트 접촉률은 임플란트 식립 3주후, 대조군에서 평균과 표준편차는$44.1{\pm}16.5%$ 이었고 실험군은 $70.8{\pm}18.9%$로 실험군이 통계적으로 유의하게 높았다 (P= 0.0264). 6주후의경우, machined 임플란트는 $78.6{\pm}15.1%$, calcium phosphate coated 임플란트는 $79.0{\pm}26.0%$로 두 군 간 통계적으로 유의한 차이는 없었다. 결론: Calcium phosphate coated 임플란트는 machined 티타늄 임플란트에 비해 빠른 초기 골반응을 나타냈다. 그러므로, 임상적으로 calcium phosphate coated 임플란트를 사용했을 때, 수술 후 치유 기간을 단축하여 조기 부하가 가능할 것으로 사료된다.

• 대한치과보철학회지
• /
• 제49권1호
• /
• pp.65-72
• /
• 2011

연구 목적: 이 연구의 목적은 티타늄 지대주와 비귀금속 보철물이 접촉한 경우를 가정하여 이종 금속간 접촉에 의한 갈바닉 부식으로 인해 발생하는 표면 거칠기 변화를 비교, 평가하고자 하였다. 연구 재료 및 방법: 성분과 조성이 다른 3종의 Ni-Cr합금 (T3, Bella bond plus, Tilite)과 cp 티타늄 Grade 2를 이용하여 $13{\times}13{\times}1.5\;mm$의 크기로 시편을 각 군당 6개씩 제작하였다. 연마과정 후 절연 테이프로 직경 6 mm만을 노출시켜 potentiostat (Parastat 2273A)를 이용하여 동전위 분극 시험과 갈바닉 부식 시험을 시행하였으며, 표면 거칠기 측정기(Surftester SV-3000)를 이용하여 부식 전 후 거칠기를 평가하였다. 측정값을 paired t-test와 One-way ANOVA로 분석하였다. 결과: 티타늄과 접촉한 모든 Ni-Cr 시편의 표면 거칠기는 통계적으로 유의하게 증가하였다. 증가량은 베릴륨을 포함한 T3합금 ($0.016{\pm}.007\;{\mu}m$)이 가장 컸으며, 베릴륨을 포함하지 않은 Bella bond plus ($0.012{\pm}.003\;{\mu}m$), 티타늄을 첨가한 Tilite ($0.012{\pm}.002\;{\mu}m$)는 큰 차이를 보이지 않았다. 금속 종류에 따른 거칠기 증가는 유의한 차이를 보이지 않았다. 결론: 티타늄과 접촉한 비귀금속 합금은 갈바닉 부식에 의해 표면 거칠기가 증가하였다.