• Journal of the Korean institute of surface engineering
• /
• v.41 no.3
• /
• pp.88-93
• /
• 2008

Ir-Re thin films with Ti interlayer were deposited onto the tungsten carbide substrate by ion beam assisted DC magnetron sputtering. The Ir-Re films were prepared with targets of having two atomic percent of 7:3 and 5:5. The microstructure and surface analysis of the specimen were conducted by using SEM, XRD and AFM. Mechanical properties such as hardness and adhesion strength of Ir-Re thin film also were examined. The interlayer of pure titanium was formed with 100 nm thickness. The film growth of Ir-30at.%Re was faster than that of Ir-50at.%Re in the same deposition conditions. Ir-Re thin films consisted of dense and columnar structure irrespective of the different target compositions. The values of hardness and adhesion strength of Ir-30at.%Re thin film coated on WC substrate were higher than those of Ir-50at.%Re thin film.

• Korean Journal of Materials Research
• /
• v.31 no.1
• /
• pp.8-15
• /
• 2021

Transparent, photocatalytic, and self-cleaning TiO2 thin film is developed by TiO2 sol-gel coating on glass and polycarbonate (PC) substrates. Acetyl acetone (AcAc) suppresses the precipitation of TiO2 by forming a yellowish (complex) transparent sol-gel. XPS analysis confirms the presence of Ti2p and O1s in the thin films on glass and PC substrates. The TiO2-sol is prepared by stabilizing titanium (IV) isopropoxide (TTIP) with diethylamine and methyl alcohol. The addition of AcAcsilane coupling solution to the TiO2-sol instantaneously turns to yellowish color owing to the complexing of titanium with AcAc. The AcAc solution substantially improves the photocatalytic property of the TiO2 coating layer in MB solutions. The coated TiO2 film exhibits super hydrophilicity without and with light irradiation. The TiO2 thin film stabilized by adding 8.7 wt% AcAc shows the highest photo-degradation for methylene blue (MB) solution under UV light irradiation. Also, the optimum photocatalytic activity is obtained for the 8.7 wt% AcAc-stabilized TiO2 coating layer calcined at 450 ℃. The thin-films on glass exhibit fast self-cleaning from oleic acid contamination within 45 min of UV-light irradiation. The appropriate curing time at 140 ℃ improves the anti-fogging and thermal stability of the TiO2 film coated on PC substrate. The watermark-free PC substrate is particularly beneficial to combat fogging problems of transparent substrates.

• Korean Journal of Materials Research
• /
• v.5 no.7
• /
• pp.775-780
• /
• 1995

Thin films of titanium nitride are formed using the tetrakis-dimethyl-amino-titanium (TDMAT(Ti[N($CH_3$)$_2$]$_4$)) under various conditions. The formation of TiN films has been obtained from the thermal decomposition of the Ti-precursor and the gas phase reaction between TDMAT and ammonia(NH$_3$). The resistivity of the MOCVD film can be attributed to their impurity. Especially the curve fitting graph of XPS data is revealed that main impurities in the films as carbon and oxygen make various interstitial compounds which has influenced physical and electrical properties of the film. In the contact hole with the aspect ratio of 3:1 and the diameter of 0.5${\mu}{\textrm}{m}$, the SEM morphology shows that the step coverage is more decreased in the films formed y flowing ammonia additionally than the films formed by pyrolysis of TDMAT and the phenomenon is probably related with the activation energy.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.10 no.6
• /
• pp.418-424
• /
• 2000

Pure $TiO_2$and 10 mol % Pb-doped $TiO_2(Pb_xTi_{1-x}O_2$(x = 0.1)) powder and thin films have been prepared by the sol-gel method. Titanium isopropoxide and ethanol are used for pure $TiO_2$, lead acetate trihydrate and titanium triisopropoxide monoacethylacetonate are used for Pb-doped $TiO_2$, respectively. Films are coated on p-type Si(100) wafer and ITO glass substrates by the sol-gel spin-coating method. The powder and multi-coated films are annealed at different temperature (400~$800^{\circ}C$) for phase formation and crystallization. TGA/DTA, XRD analysis, SEM and UV-visible transmission spectroscopy have been used to study the characteristics of the powder and films. XRD results show that the films are polycrystalline, anatase type and oriented predominantly to the A(101) plane. A slight shift in the d-spacing for the Pb-doped film indicates the incorporation of the Pb into $TiO_2$lattice. A shift of the absorption wavelength in the transmission spectrum towards longer wavelength has been observed about $Pb_xT_{1-x}O_2$(x = 0.1) thin film, which indicates a decrease in the bandgap of $TiO_2$upon Pb-doping.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.24 no.4
• /
• pp.361-369
• /
• 2008

The purpose of this study is to make porous oxide film on the surfaces of pure Ti through anodic spark discharge in electrolytic solution containing calcium and phosphate ions, to improve osseointergration by treating fluoride agent. In addition, it is to evaluate the fluoride modified effect on the surface. Commercial pure Ti plate with $20{\times}10{\times}2mm$ and Ti wire with a diameter of 1.5mm and a total length of 15mm were used. After making titanium oxide films converted by anodic spark discharge, anodizing was performed. Fluoride was spreaded to titanium laboratory plate and maintained for 30 minutes after anodizing breakdown. Fluoride ion discharge amount was measured per 24 hours after dipping titanium plate into saline (10ml) and sustaining 90rpm in a pyrostat. Some plates and wires were dipped in Hanks solutions for a month to examine biocompatibility using SEM and XRD. $TiO_2$ film formed by anodic discharge technique showed great roughness and uniform pores which were $1{\sim}3{\mu}m$ in a diameter. Roughness of the films treated with anodic discharge after blasting were higher than the turned ones(P<0.05). Rapid surface activity was observed in the samples treated with $TiF_3$ agent, which immersed in Hanks solution for 30 days. Taking the results into consideration, the fluoride modified implant with anodic discharge demonstrates that it makes uniformly porous oxide film on the surface of implant and properly increase roughness for osseointegration. The implants will achieve greater bone integration after short healing time by improving surface activity.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.9 no.1
• /
• pp.23-28
• /
• 1999

Au fine particles dispersed $TiO_{2}$ film was prepared on silica glass substrate by sol-gel dipping and firing process. The $TiO_{2}$ films were fabricated from the system of titanium tetraisopropoxide-EtOH-HCl-$H_{2}O$-hydrogen tetrachloroaurat (III) tetrahydrate. The conditions for the formation of clear solution and dissolving high concentration of Au compound were examined. Photoreduction process was adopted to control the size of gold metal particles. Phase evolution of matrix $TiO_{2}$ and variation of Au particle with UV irradiation were investigated by XRD, SEM, TEM and UV-visible spectrophotometer. The effect of CPCl (Cetylpyridinium chloride monohydrate) as a dispersion agent was evaluated.

• Korean Journal of Materials Research
• /
• v.12 no.5
• /
• pp.353-358
• /
• 2002

The microstructure and growth behaviors of anodic oxide layers on titanium were investigated. $TiO_2$ oxide films were prepared by anodizing at constant voltages of 180 and 200V in sulfuric acid electrolyte. The anodic $TiO_2$ layer formed at 200V showed a cell structure with more irregular pore shapes around the interface between the anodic oxide layer and the substrate titanium compared with that formed at 180V. Irregular shape of pores at the initial stage of anodization seemed to be attributed to spark discharge phenomena which heavily occurred during increasing voltages. The thickness of the anodic oxide film increased linearly at a rate of $1.9{\times}10^{ -1}\mu\textrm{m}$/min. The oxide layers formed at 180 and 200V were composed mainly of anatase structure, and the anodizing process could be suggested as one of fabrication methods of photocatalytic $TiO_2$.

• Korean Journal of Metals and Materials
• /
• v.46 no.6
• /
• pp.370-376
• /
• 2008

The formation of anodic oxide film of titanium (Ti) was studied at a variety of electrolyte concentrations and current density to clarify their effects on morphology, microstructure and composition of Ti oxide layer. For the analysis of the Ti oxide films, a scanning electron microscopy (SEM), X-ray diffractometer (XRD), and X-ray photoelectron spectroscopy (XPS) were used. The results showed that the concentration of phosphoric acid played a crucial role in the crystalline structure of the Ti oxide layer while the current density gave a critical effect on the thickness and diameter of its pore. In particular, the crystalline anatase phase with a thickness larger than $2{\mu}m$, which is quite desirable for a dental implant application, could be readily prepared at the phosphoric acid concentration of 0.5 M and current density higher than $2.0A/dm^2$.

• Corrosion Science and Technology
• /
• v.17 no.6
• /
• pp.310-316
• /
• 2018

The effect of passive film on corrosion of metals and alloys in a static corrosive environment has been studied by many researchers and is well known, however few studies have been conducted on the electrochemical measurement of metals and alloys during cavitation corrosion conditions, and there are no test standards for electrochemical measurements 'During cavitation' conditions. This study used commercially additive manufactured(AM) pure titanium in tests of anodic polarization, corrosion potential measurements, AC impedance measurements, and repassivation. Tests were performed in 3.5% NaCl solution under three conditions, 'No cavitation', 'After cavitation', and 'During cavitation' condition. When cavitation corrosion occurred, the passive current density was greatly increased, the corrosion potential largely lowered, and the passive film revealed a small polarization resistance. The current fluctuation by the passivation and repassivation phenomena was measured first, and this behavior was repeatedly generated at a very high speed. The electrochemical corrosion mechanism that occurred during cavitation corrosion was based on result of the electrochemical properties 'No cavitation', 'After cavitation', and 'During cavitation' conditions.

• Journal of Powder Materials
• /
• v.29 no.4
• /
• pp.297-302
• /
• 2022

This study compares the characteristics of a compact TiO₂ (c-TiO₂) powdery film, which is used as the electron transport layer (ETL) of perovskite solar cells, based on the manufacturing method. Additionally, its efficiency is measured by applying it to a carbon electrode solar cell. Spin-coating and spray methods are compared, and spray-based c-TiO₂ exhibits superior optical properties. Furthermore, surface analysis by scanning electron microscopy (SEM) and atomic force microscopy (AFM) exhibits the excellent surface properties of spray-based TiO₂. The photoelectric conversion efficiency (PCE) is 14.31% when applied to planar perovskite solar cells based on metal electrodes. Finally, carbon nanotube (CNT) film electrode-based solar cells exhibits a 76% PCE compared with that of metal electrode-based solar cells, providing the possibility of commercialization.