• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.20 no.5
• /
• pp.81-86
• /
• 2019

Metal oxide/graphene composites have been known as promising functional materials for advanced applications such as high sensitivity gas sensor, and high capacitive secondary battery. In this study, tin dioxide ($SnO_2$) nanostructures were grown on chemically synthesized graphene nanosheets using a two-zone horizontal furnace system. The large area graphene nanosheets were synthesized on Cu foil by thermal chemical vapor deposition system with the methane and hydrogen gas. Chemically synthesized graphene nanosheets were transferred on cleaned $SiO_2$(300 nm)/Si substrate using the PMMA. The $SnO_2$ nanostuctures were grown on graphene nanosheets at $424^{\circ}C$ under 3.1 Torr for 3 hours. Raman spectroscopy was used to estimate the quality of as-synthesized graphene nanosheets and to confirm the phase of as-grown $SnO_2$ nanostructures. The surface morphology of as-grown $SnO_2$ nanostructures on graphene nanosheets was characterized by field-emission scanning electron microscopy (FE-SEM). As the results, the synthesized graphene nanosheets are bi-layers graphene nanosheets, and as-grown tin oxide nanostructures exhibit tin dioxide phase. The morphology of $SnO_2$ nanostructures on graphene nanosheets exhibits complex nanostructures, whereas the surface morphology of $SnO_2$ nanostructures on $SiO_2$(300 nm)/Si substrate exhibits simply nano-dots. The complex nanostructures of $SnO_2$ on graphene nanosheets are attributed to functional groups on graphene surface.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.05c
• /
• pp.99-102
• /
• 2003

Tin dioxide thin films were deposited at $375^{\circ}C$ on alumina substrate by metal-organic chemical vapor deposition process to find the relationship between physicochemical properties and the annealing treatments. The small grains with heat treatments grew to the bunch of grains and then showed the hillocks on the film surface. The thickness decreased with annealing treatment. The measured binding energy (BE) and branching ratio of the Sn 3d spin-orbital doublet were typical of oxidized states of Sn and the BE of the O1s core level of about 530~530.65eV also confirmed the presence of O-Sn bonds. The BE of oxygen and tin with annealing treatment shifted to higher position. O/Sn atomic ratios of films deposited at $375^{\circ}C$ for 2min and 4min were 1.99 and 2.01, respectively. The value of the atomic ratio O/Sn of films deposited at $375^{\circ}C$ for 2min changed from 1.99 to 2.45 with annealing treatment. Gas sensitivity depended on annealing temperature, the sensitivity increased with increasing annealing temperature.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.11a
• /
• pp.250-251
• /
• 2005

Tin dioxide (SnO$_2$) thin films have been prepared on Si wafer (100) by Plasma Enhanced Chemical Vapor Deposition (PECVD). SnO$_2$ thin films were prepared from mixtures of dibutyltin diacetate as a precursor, oxygen as an oxidant at 275, 325, 375, 425$^{\circ}C$, respectively. The microstructure of deposited films was characterized by X-ray diffraction and field emission scanning electron microscopy. Structural characteristics of prepared SnO$_2$ thin films were investigated with different substrate temperature. The deposition rate was linearly increased with substrate temperature. Surface morphology and uniformity of prepared thin film was excellent at 375$^{\circ}C$ and grain size was averagely 25nm.

• Journal of the Korean Society for Heat Treatment
• /
• v.26 no.4
• /
• pp.173-177
• /
• 2013

Separation and recovery of valuable metals such as zinc, nickel or tin from copper alloy dross has recently attracted from the viewpoints of environmental protection and resource recycling. In this report, preliminary study on concentration and separation of tin from copper alloy dross using selective dissolution method was performed. The tin in the copper alloy dross did not dissolve in the nitric acid solution which could allow the concentration and separation of the tin from the copper alloy dross. Precipitation of tin as $H_2SnO_3$ (metastannic acid) occurred in the solution and transformed to tin dioxide ($SnO_2$) after drying process. The dried sample was heat-treated at low temperature and its phase characteristics, surface morphology and chemical composition were investigated.

• Journal of the Korean Chemical Society
• /
• v.56 no.4
• /
• pp.484-490
• /
• 2012

The tin (IV) oxide nanoparticles are prepared by controlled precipitation method and calcined at temperatures of $200-600^{\circ}C$. The prepared $SnO_2$ nanoparticles characterized by XRD patterns, TEM image, IR and UV-Vis spectra. The XRD patterns and TEM image show the tetragonal structure and spherical morphology for $SnO_2$ nanoparticles, respectively. The photocatalytic activity of the prepared $SnO_2$ nanoparticles studied in degradation reaction of methylene blue (MB). The results show the size of nanoparticles, band-gap energy and photocatalytic activity of $SnO_2$ depends on the calcinations temperature. The $SnO_2$ nanoparticles calcined at $500^{\circ}C$ indicated the highest photoreactivity. Also, the zero-valent tin (ZVT) nanoparticles with tetragonal structure are prepared by a reducing agent and used as a catalyst in degradation of MB. In basic pH of 11, the degradation >95% of MB at time 150 min obtained at presence of ZVT nanoparticles.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.24 no.2
• /
• pp.84-87
• /
• 2014

Separation/recovery of valuable metals such as zinc, nickel or tin from copper alloy dross has recently attracted from the viewpoints of environmental protection and resource recycling. In this study, preliminary investigation on separation of tin (Sn) from copper alloy dross using selective dissolution method was performed. The tin in the copper alloy dross did not dissolve in an aqueous nitric acid solution which could allow the concentration/separation of tin from the copper alloy dross. Precipitation of tin as $H_2SnO_3$ (meta stannic acid)occurred in the solution and transformed to tin dioxide ($SnO_2$) after drying process. The dried sample was heat-treated at low temperature and its crystal structure, surface morphology and chemical composition were investigated.

• Korean Journal of Materials Research
• /
• v.13 no.7
• /
• pp.442-446
• /
• 2003

Tin dioxide ($SnO _2$) thin films were deposited at $375^{\circ}C$ on alumina substrate by metal-organic chemical vapor deposition. A few hillocks like a cauliflower were observed and the number of hillock on thin film surface increased with annealing temperature in air atmosphere. The oxygen content and the binding energy during air annealing at$ 500^{\circ}C$ came to close the stoichiometric $SnO_2$. The cauliflower hillocks seem to be the result of the continuous migration of the tiny grains to release the stress of an expanded grain. Sensitivity of CO gas depended on annealing temperature and increased with increasing annealing temperature.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.19 no.10
• /
• pp.1-7
• /
• 2018

Tin dioxide, $SnO_2$, is applied as an anode material in Li-ion batteries and a gas sensing materials, which shows changes in resistance in the presence of gas molecules, such as $H_2$, NO, $NO_2$ etc. Considerable research has been done on the synthesis of $SnO_2$ nanostructures. Nanomaterials exhibit a high surface to volume ratio, which means it has an advantage in sensing gas molecules and improving the specific capacity of Li-ion batteries. In this study, $SnO_2$ nanostructures were grown on a Si substrate using a thermal CVD process with the vapor transport method. The carrier gas was mixed with high purity Ar gas and oxygen gas. The crystalline phase of the as-grown tin oxide nanostructures was affected by the oxygen gas flow rate. The crystallographic property of the as-grown tin oxide nanostructures were investigated by Raman spectroscopy and XRD. The morphology of the as-grown tin oxide nanostructures was confirmed by scanning electron microscopy. As a result, the $SnO_2$ nanostructures were grown directly on Si wafers with moderate thickness and a nanodot surface morphology for a carrier gas mixture ratio of Ar gas 1000 SCCM : $O_2$ gas 10 SCCM.

• Bulletin of the Korean Chemical Society
• /
• v.33 no.8
• /
• pp.2535-2538
• /
• 2012

$SnO_2@carbon$ tube-core nanowire was synthesized via a facile self-organized method, which was in situ by one step via Chemical Vapor Deposition. The resulting composite was characterized by scanning electron microscopy, X-ray diffraction and transmission electron microscope. The diameter of the single nanowire is between 5 nm and 60 nm, while the length would be several tens to hundreds of micrometers. Then X-ray diffraction pattern shows that the composition is amorphous carbon and tin dioxide. Transmission electron microscope images indicate that the nanowire consists of two parts, the outer carbon tube and the inner tin dioxide core. Meanwhile, the possible growth mechanism of $SnO_2@carbon$ tube-core nanowire is also discussed.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.20 no.4
• /
• pp.497-502
• /
• 2019

Metal oxide nanostructures are promising materials for advanced applications, such as high sensitive gas sensors, and high capacitance lithium-ion batteries. In this study, tin oxide (SnO) nanostructures were grown on a Si wafer substrate using a two-zone horizontal furnace system for a various substrate temperatures. The raw material of tin dioxide ($SnO_2$) powder was vaporized at $1070^{\circ}C$ in an alumina crucible. High purity Ar gas, as a carrier gas, was flown with a flow rate of 1000 standard cubic centimeters per minute. The SnO nanostructures were grown on a Si substrate at $350{\sim}450^{\circ}C$ under 545 Pa for 30 minutes. The surface morphology of the as-grown SnO nanostructures on Si substrate was characterized by field-emission scanning electron microscopy (FE-SEM) and atomic force microscopy (AFM). Raman spectroscopy was used to confirm the phase of the as-grown SnO nanostructures. As the results, the as-grown tin oxide nanostructures exhibited a pure tin monoxide phase. As the substrate temperature was increased from $350^{\circ}C$ to $424^{\circ}C$, the thickness and grain size of the SnO nanostructures were increased. The SnO nanostructures grown at $450^{\circ}C$ exhibited complex polycrystalline structures, whereas the SnO nanostructures grown at $350^{\circ}C$ to $424^{\circ}C$ exhibited simple grain structures parallel to the substrate.