Annealing Effect on $SnO_2$ Thin Films Properties

$SnO_2$ 박막 특성에 미치는 annealing 효과

Tin dioxide thin films were deposited at $375^{\circ}C$ on alumina substrate by metal-organic chemical vapor deposition process to find the relationship between physicochemical properties and the annealing treatments. The small grains with heat treatments grew to the bunch of grains and then showed the hillocks on the film surface. The thickness decreased with annealing treatment. The measured binding energy (BE) and branching ratio of the Sn 3d spin-orbital doublet were typical of oxidized states of Sn and the BE of the O1s core level of about 530~530.65eV also confirmed the presence of O-Sn bonds. The BE of oxygen and tin with annealing treatment shifted to higher position. O/Sn atomic ratios of films deposited at $375^{\circ}C$ for 2min and 4min were 1.99 and 2.01, respectively. The value of the atomic ratio O/Sn of films deposited at $375^{\circ}C$ for 2min changed from 1.99 to 2.45 with annealing treatment. Gas sensitivity depended on annealing temperature, the sensitivity increased with increasing annealing temperature.