• The Journal of Korean Academy of Prosthodontics
• /
• v.44 no.6
• /
• pp.740-750
• /
• 2006

Statement of problems. In an attempt to reduce screw loosening, dry lubricant coatings such as pure gold or tefron have been applied to the abutment screw. However, under repeated tightening and loosening procedures, low wear resistance and adhesion strength of coating material produced free particles on the surface of abutment screw and increased frictional resistance resulting in screw tightening problems. Purpose. The aim of this study was to compare friction coefficient, adhesion strength, vickers hardness and evaluate coating surface of titanium alloy specimens coated with TiN(titanium nitride), ZrN(zirconium nitride) and WC(tungsten carbide). Material and method. Titanium alloy(Ti-6Al-4V) discs of 12mm in diameter and 1mm in thickness divided into 4 groups. TiN, ZrN and WC was coated for the specimens of 3 groups respectively, and those of 1 group were not coated. Each group was made up of 4 specimens. In this study, sputtering method was used among the PVD(Physical Vapor Deposition) techniques available for TiN, ZrN and WC coatings. Friction coefficient, adhesion strength, vickers hardness and coating surface of 4 groups were measured. Results. 1. For all three coating conditions, friction coefficient was significantly decreased. Especially, ZrN coated surface showed the lowest value. $TiN(0.39{\pm}0.02)$, $ZrN(0.24{\pm}0.01)$, $WC(0.31{\pm}0.03)$. 2. TiN coating showed the highest adhesion strength, however ZrN coating had the lowest value. $TiN(25.3N{\pm}1.6)$, $ZrN(14.8N{\pm}0.6)$, $ WC(18.4N{\pm}0.7)$. 3. Vickers hardness of all three coatings was remarkably increased as compared with that of none coated specimen. TiN coating had the highest Vickers hardness, however WC coating showed the lowest value. $TiN(1865.2{\pm}33.8)$, $ZrN(1814.4{\pm}18.6)$, $WC(1008.5{\pm}35.9)$. 4. The ZrN or WC coated specimen showed a homogeneous and smooth surface, however the rough surface with defects was observed for TiN coating. Conclusions. When TiN, ZrN and WC coating applied to the abutment screw, frictional resistance would be reduced, as a result, the greater preload and prevention of the screw loosening could be expected.

• Journal of the Korean Ceramic Society
• /
• v.32 no.9
• /
• pp.977-988
• /
• 1995

Several oxide (ZrO2, Al2TiO5, reactive Al2O3) and nonoxide (SiC, Si3N4, "ALON" (5AlN.9Al2O3)) additives were used as a microfiller for alumina based LCC (Low-Cement-Castable). High temperature prooperties (HMOR, softening under load) and the phase changes of developed LCC on various sintering temperatures were examined. In addition, thermal shock test and corrosion test were accomplished. Based on these data the effects of each microfiller on the properties of LCC were established comparing to those of the commercial LCC with amorphous silica as a microfiller. The castables, containing reactive alumina, ZrO2 and "ALON" (5AlN.9Al2O3) as a first portion, exhibited considerably higher HMOR-values over 100$0^{\circ}C$, better creep behavior, and thermal shock resistance than those of castables with amorphous silica. The LCC with 5% Al2TiO5 showed no corrosion against molten aluminum.nst molten aluminum.

• Proceedings of the KAIS Fall Conference
• /
• 2001.05a
• /
• pp.40-46
• /
• 2001

The thermal stability of $Al_2TiO_{5}$ ceramics was improved by formation of solid solution with MgO, such as $MgAl_2O_4$ spinel through electrofusion in an arc furnance, and by limitation of grain size and microcracks with $SiO_2$, $ZrO_2$ and ${\alpha}$-$Al_2O_3$. The low thermal expansion properties of $Al_2TiO_{5}$ composites show the thermal hysteresis curves due to the strong anisotropy of $Al_2TiO_{5}$. These phenomena are explained by the opening and closing of microcracks. The relation between thermal hysteresis, microstructures and sintering temperature were studied by dilatometry.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.05c
• /
• pp.157-160
• /
• 2001

We have investigated the Dielectric and Piezoelectric properties of $xPb(R_{1/2}Ta_{1/2})O_3-(1-x)Pb(Zr_{0.52}Ti_{0.48})O_3$ (R=Al,Y) solid solutions in which R ions are substituted for Al and Y ions. The maximum value of electromechanical coupling factor kp of 55% and 51% were obtained at the composition of 5mol% PAT and 5mol% PYT. However mechanical quality factor$(Q_m)$ had a minimum value of 44 and 69 at the composition of 5mol% PAT and 5mol% PYT. Also, the maximum value of piezoelectctric constant of $d_{33}(329[pC/N])$ and $d_{33}(310[pC/N])$ were obtained at the composition of 5mol% PAT and 5mol% PYT.

• Transactions on Electrical and Electronic Materials
• /
• v.11 no.2
• /
• pp.54-60
• /
• 2010

Polymer-assisted deposition is a chemical solution route to high quality thin films. In this process, the polymer controls the viscosity and binds metal ions, resulting in a homogeneous distribution of metal precursors in the solution and the formation of crack-free and uniform films after thermal treatment. We review our recent effort to epitaxially grow metal-nitride thin films, such as hexagonal GaN, cubic TiN, AlN, NbN, and VN, mixed-nitride $Ti_{1-x}Al_xN$, ternary nitrides tetragonal $SrTiN_2$, $BaZrN_2$, and $BaHfN_2$, hexagonal $FeMoN_2$, and nanocomposite TiN-$BaZrN_2$.

• Transactions of Materials Processing
• /
• v.18 no.7
• /
• pp.544-549
• /
• 2009

This study aimed to elucidate the deformation mechanism during low-temperature superplasticity of fine-grained Ti-6Al-2Sn-4Zr-2Mo-0.1Si alloy in the context of constitutive equation. For this purpose, initial coarse equiaxed microstructure was refined to $2.2{\mu}m$ via dynamic globularization. Globularized microstructure exhibited large superplastic elongations(434-826%) at temperatures of $650-750^{\circ}C$ and strain rate of $10^{-4}s^{-1}$. It was found that the main deformation mechanism of fine-grained material was grain boundary sliding accommodated by dislocation motion with both stress exponent (n) and grain size exponent (p) values of 2. When the alpha grain size, not sub-grain size, was considered to be an effective grain size, the apparent activation energy for low-temperature superplasticity of the present alloy(169kJ/mol) was closed to that of Ti-6Al-4V alloy(160kJ/mol).

• Proceedings of the Korean Vacuum Society Conference
• /
• 2016.02a
• /
• pp.166.2-166.2
• /
• 2016

최근 생산 장비의 발달로 인해 절삭공구, 전기전자 부품, 항공 및 자동차 부품 생산에 필요한 생산 장비의 수명연장, 고속 절단 및 고성능화가 중요시 되면서 우수한 내구성, 내마모성 및 고온 안정성을 갖는 기계부품 및 공구를 요구하게 되었다. 내마모성을 가지는 표면을 얻기 위해서는 TiN, TiC, AlN, Al2O3, CrN, ZrO2와 같은 경도 높은 물질을 증착하여 특성을 개선시키는 방법이 있다. 특히 AlN은 비교적 우수한 경도와 고온 안정성을 가지고 있어, 생산 장비의 고속 절단 및 반복되는 정밀 작업으로 인한 열충격과 마모를 완화시키는 역할을 하는 코팅재로 사용하기 적합하다. 본 실험에서는 RF-magnetron sputtering 방법을 이용하여 AlN 박막을 파워 150W, 질소가스 분압비에 따라 25%, 50%, 75%, 100%의 조건으로 금속기판 위에 증착하였다. 금속 기판 위에 제작된 AlN막은 XRD (X-ray Diffraction)을 사용하여 배향성을 확인하였고, HM-220 (Micro-vickers hardness tester)을 사용하여 AlN박막의 경도를 측정하였으며, SEM (Scanning Electron Microscope), AFM (Atomic Force Microscope)을 이용하여 표면의 구조와 거칠기를 측정하였다. 이 실험을 통하여 우수한 물성과, 치밀한 조직의 AlN박막이 고속 절삭 공구, 유공압 실린더, 베어링과 같은 금속부품의 코팅소재로 적용가능 할 것으로 기대된다.

• Electrical & Electronic Materials
• /
• v.5 no.2
• /
• pp.207-215
• /
• 1992

본 연구에서 xPb(A $l_{0.5}$N $b_{0.5}$) $O_{3}$-(1-x)Pb(Z $r_{0.52}$ $Ti_{o.48}$) $O_{3}$계의 조성변화에 따른 유전 및 압전특성에 관해 실험한 결과 다음과 같은 결론을 얻었다. PAN의 첨가량이 증가함에 따라 c축은 수축되고 a축은 팽창하여 tetragonality는 감소하였고 grain의 크기와 Curie온도 또한 PAN의 첨가량에 따라 감소하였으나 밀도와 유전상수는 PAN의 양이 5mol%까지 증가하다가 그 이상에서는 감소하는 경향을 보였다. PAN의 첨가량이 증가함에 따라 시편의 비저항은 증가하였고 Kp는 PAN의 양이 5mol%첨가시 60%로 최대치를 보였으나 Qm은 최소치를 나타내었다.다.

• Korean Journal of Materials Research
• /
• v.14 no.4
• /
• pp.293-299
• /
• 2004

Transition metal ions doped $TiO_2$ nanostructured powders were prepared with simply heating aqueous $TiOCl_2$ solutions, contained various metal ions (Ni, Al, Fe, Zr, and Nb) of 1.47 mol% added as metal-chlorides, at $100^{\circ}C$ for 4 hrs by homogeneous precipitation process under suppressing conditions of water vaporization. The characterizations for prepared $TiO_2$ powders were carried out to observe doping of metal ions, their concentrations and microstructures using XRD, UV-VIS (DRS), XPS, SEM, TEM and ICP. Also, photo-oxidative abilities were evaluated by decomposition of 4-chlorophenol (4CP) under ultraviolet light irradiations. No secondary oxide phases were formed in all the $VTiO_2$ powders, showing doping with various transition metal ions. When adding ions ($Ni^{2+}$ or$ Al^{3+ }$ and $Zr^{4+}$ ) having valance states or ionic radii greatly different from those of $Ti^{4+}$ , the $TiO_2$ powders of mixed anatase and rutile phases were formed, whereas in the case of additions of $^Fe{3+ }$ and $Nb^{ 5+}$ as well as no addition of metal ion the powders with pure rutile phase alone were formed. Among the prepared $TiO_2$ powders, Ni$^{2+}$ doped $TiO_2$ powders, containing a small amount of anatase phase, showed excellent photo-oxidative ability in 4CP decomposition because of relative decreases in electron-hole recombination and poisoning of $TiO_2$ surface during the photoreaction.n.

• Journal of Welding and Joining
• /
• v.16 no.1
• /
• pp.88-97
• /
• 1998

The surface characteristics of 13Cr stainless steel systems by plasma nitriding were investigated. The plasma nitriding for the 13Cr steels, in which the nitriding forming elements such as Ti, V, W, Nb, Al, Zr and Si were added about 2~3wt.%, respectively, was performed. In all nitrided specimens, .epsilon.-F $e_{2-3}$N, UPSILON.'-F $e_{4}$N and CrN were detected as the nitrides with the a-Fe in the nitrided layer. VN and .betha.- $W_{2}$N were also detected in 13Cr-3V and 13Cr-3W alloys. The growth of the nitrided layer was controlled by the diffusion process. The thickness of the nitrided layer was similar in the 13Cr-2Nb and 3Zr specimens to that of 13Cr(BM) specimen, while the others exhibited the thinner layer. The activation energy for the growth of the nitrided layer in the temperature range of 773-873K was about 130kJ/mol in 13Cr(BM), 13Cr-2Ti, 3W, 3Al, 3Zr and 3Si alloys. The hardness of the nitrided specimens was significantly increased above Hv1000, comparing to the non-nitrided specimen. The specimens with the nitrided forming elements revealed much higher hardness values and, especially, 13Cr-3Al, 3V and 3Si specimens were significantly hardened up to Hv1300.v1300.0.