• Transactions on Electrical and Electronic Materials
• /
• v.5 no.2
• /
• pp.66-70
• /
• 2004

The Sr$\_$0.7/Bi$\_$2.3/Ta$_2$O$\_$9/(SBT)thin films are deposited on Pt-coated electrode (Pt/TiO$_2$/SiO$_2$/Si) using a RE magnetron sputtering method. The ferroelectric properties of SBT capacitors with annealing times were studied. As a result of conducting the X-ray diffraction analysis and the electron microscopy analysis, the perovskite phase began to grow from 10 minutes after annealing the specimen, and excellent crystallization was accomplished at 60 minutes after annealing the specimen. The remanet polarization (2P$\_$r/) value and the coercive electric field (E$\_$c/) of the SBT thin film specimen showed the most excellent characteristics at 60 minutes after annealing the specimen, which were approximately 12.40 C/$\textrm{cm}^2$ and 30 kV/cm, respectively. The leakage current density of the SBT thin film specimen as annealed for 60 minutes was approximately 2.81${\times}$10$\^$－9/A/$\textrm{cm}^2$.

• Applied Chemistry for Engineering
• /
• v.10 no.8
• /
• pp.1129-1135
• /
• 1999

The reduction of $SO_2$ by CO over supported cobalt catalysts was investigated within the temperature range of $350{\sim}550^{\circ}C$, initial $SO_2$ concentration of 1000~10000 ppm, $CO/SO_2$ molar ratio of 1.0~3.0 and space velocity of $5000{\sim}15000h^{-1}$. Several types of supports such as ${\gamma}-Al_2O_3$, $TiO_2$ were tested. The $SO_2$ conversion and selectivity to elemental sulfur were investigated using a differential fixed bed reactor at atmospheric pressure. The catalyst prepared by wet impregration of 5 wt % cobalt on ${\gamma}-Al_2O_3$ showed $SO_2$ conversion higher than 90% and COS yield lower than 6% at temperature above $400^{\circ}C$. The optimum $CO/SO_2$ molar ratio was investigated as 2.0. At higher $CO/SO_2$ molar ratio, the $SO_2$ conversion became higher but the main product was COS. The effect of $SO_2$ concentration and space velocity over $SO_2$ conversion and COS yield was not appreciable in the experimental range. The activated cobalt phase was detected as $CoS_2$ and the $CoS_2$ phase unchanged even after reaction.

• Journal of the Korean Ceramic Society
• /
• v.39 no.8
• /
• pp.721-727
• /
• 2002

In order to overcome trade-off among compositions, process and properties of the glasses with high PbO-base composition for PDP Rib, we studied glass crystallization and crystallization kinetics by Differential Thermal Analysis(DTA). Glass powder was obtained through melting/cooling/grinding, with 3 wt%TiO2 addition for the crystal nucleation and growth in $62PbO-19B_2O_3-10SiO_2-9(Al_2O_3-K_2O-BaO-ZnO)$(in wt%) composition glass. This powder was heat-treated for 1 to 10 h at $445^{\circ}C$ for nucleation. DTA measurements were performed to obtain the crystallization peak with $5∼25^{\circ}C/min$ heating rates. DTA crystallization peak temperature increased with increasing the heating rate and decreased with increasing the heating time. Because the Avrami parameter (n) was approximately 1, the surface crystallization occurred. The maximum nucleation time was 2 h.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.07a
• /
• pp.39-42
• /
• 2000

The effect of excess Pb contents on the etching of PZT thin films and their electrical properties has been investigated. Ferroelectric PZT(53/47) thin films were prepared by the metal alkoxide-based Sol-Gel method, in which they were spin-coating on P7Ti/Si02/Si substrate using the PZT(53/47) stock solutions with various excess Pb contents. Etching of PZT film was performed using planar inductively coupled Ar/Cl$_2$/BCl$_3$ plasma. The etch rate of PZT film was 2450 $\AA$/min at Ar(20)/BCl$_3$(80) gas mixing ratio and substrate temperature of 8$0^{\circ}C$.

• Journal of Korea Foundry Society
• /
• v.5 no.3
• /
• pp.5-12
• /
• 1985

Many researchers have studied the eutectic solidification of CV Graphite Cast Iron qualitatively. However quantative studies have not been done. The type of eutectic solidification of CV Graphite Cast Iron treated with CG Alloy (Fe-Si-Mg-5Ti-Ca-Ce) was studied quantitatively through M.D.E. value (Mushy Degree of Eutectic Solidification) = $t_2/t_1)$, where $t_1$ is the difference of the eutectic solidification starting time between surface and center part of the casting sample, and $t_2$ is the time of eutectic solidification of the center part. Following results were obtained. (1) The M.D.E. value of CV graphite cast iron lies between that of spheroidal graphite and that of flake graphite cast iron but is closer to that of Flake graphite cast iron. (2) The M.D.E. value of CV graphite cast iron depends upon CV ratio. (3) The time required for eutectic solidification increases as graphite form is changed from Flake, CV. to spheroidal graphite. (4) The M.D.E. value increases as cooling rate increases.

• Conservation Science in Museum
• /
• v.27
• /
• pp.67-90
• /
• 2022

A C-46 transport aircraft, which can be thought of as a large cultural heritage item from the modern period, was subjected to paint analysis and conservation treatment in preparation for its exhibition. The C-46 is the first aircraft ever dispatched to overseas combat zones by the Korean Air Force and carried out missions during the Vietnam War. The aircraft is mainly made of aluminum and shows signs of corrosion on its surface, including pitting and etching, as well as gray and white powdery attachments. In the analysis of the paint, diatomite(SiO₂·nH₂O) was confirmed in the red paint, titanium dioxide(TiO₂) was identified in the white paint, black iron oxide(Fe₃O₄) was detected in the black paint, and colcothar(Fe₃O₄) mixed with putty was confirmed in the blue paint. Infrared spectroscopy revealed the use of alkyd resin in the paint on the main body and nitrocellulose in the Taegeuk pattern. During the conservation treatment, mechanical cleaning, such as sanding, was conducted to remove paint and varnish from the surface. Corrosion was removed by sanding and cleaning with chemical solvents, and new paints and varnishes were applied. Through the paint analysis and conservation treatment, the aircraft was made available for exhibition in a stable condition.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.32 no.3
• /
• pp.229-233
• /
• 2019

Pure $BiFeO_3$ (BFO) and (Eu, V) co-doped $Bi_{0.9}Eu_{0.1}Fe_{0.975}V_{0.025}O_{3+{\delta}}$ (BEFVO) thin films were deposited on $Pt(111)/Ti/SiO_2/Si(100)$ substrates by chemical solution deposition. The effects of co-doping were observed by X-ray diffraction, Raman spectroscopy, and scanning electron microscopy (SEM). The electrical properties of the BEFVO thin film were improved as compared to those of the pure BFO thin film. The remnant polarization ($2P_r$) of the BEFVO thin film was approximately $26{\mu}C/cm^2$ at a maximum electric field of 1,190 kV/cm with a frequency of 1 kHz. The leakage current density of the co-doped BEFVO thin film ($4.81{\times}10^{-5}A/cm^2$ at 100 kV/cm) was two orders of magnitude lower than of that of the pure BFO thin film.

• Transactions on Electrical and Electronic Materials
• /
• v.6 no.1
• /
• pp.10-13
• /
• 2005

$Sr_{0.6}Ba_{0.4}Nb_{2}O_{6}$, hereafter SBN60, thin films of 300 nm thickness were deposited using ion beam sputtering technique, in which sintered ceramic target of the same composition was utilized and the $Ar:O_{2}$ gas ratio was controlled during deposition onto $Pt(100)/TiO_{2}/SiO_{2}/Si$ substrate. Crystallization and orientation behavior as well as electrical properties of the films were examined after annealing treatment at $650{\sim}800{\cric}C$. It was found that the film orientation was dependent upon $Ar:O_{2}$ratio, in which strong (00l) orientation was developed when the gas ratio was about 1:4 at $4.3{\times}10^{-4}$ torr. Typical remanent polarization (2Pr), the coercive field (Ec) and the dielectric constant of Pt/SBN60/Pt thin film capacitor were approximately $10{\mu}C/cm^{2}$, 60 kV/cm, and 615, respectively.

• Journal of the Korean Vacuum Society
• /
• v.5 no.2
• /
• pp.107-112
• /
• 1996

Thin films of $Pb(Zr_xTi_{1-x})O_3$)PZT) were grown on $Pt/SiO_2/Si(100)$ at various temperatures by RF magnetron sputtering method. Surface morphology of these films were studied by using Atomic Force Microscopy(AFM). These films were also analyzed by using Atomic Force Microscopy(AFM). These films were also analyzed by using X-ray photoemission spectroscopy(XPS) for determining their chemical composition and their depth profile. It was found that the films grown at the substrated temperature of $300^{\circ}C$ have much more smooth surface characteristics in comparison to those films grown at room temperature, which may be explained in terms of surface mobility of ad-atoms such as Pb. It was also found that Pb enrichment in the near surface region enhanced for the films grown at higher substate temperature.

• KSBB Journal
• /
• v.23 no.1
• /
• pp.83-89
• /
• 2008

Food wastewater derived from the three-stage methane fermentation system developed in this lab contained high concentration organic substances. The organic wastewater should be treated through advanced wastewater treatment system to satisfy the "Permissible Pollutant Discharge Standard of Korea". In order to treat the organic wastewater efficiently, several optimum operation conditions of a modified $UV/TiO_{2}$ photocatalytic system have been investigated. In the first process, wastewater was pre-treated with $FeCl_{3}$. The optimum pH and coagulant concentration were 4.0 and 2000mg/L, respectively. Through this process, 52.6% of CODcr was removed. The second process was $UV-TiO_{2}$ photocatalytic reaction. The optimum operation conditions for the system were as follows: UV lamp wavelength, 254 nm; wastewater temperature, $40^{\circ}C$; pH 8.0; and air flow rate, 40L/min, respectively. Through the above two combined processes, 69.7% of T-N and 70.9% of CODcr contained in the wastewater were removed.