• Korean Journal of Materials Research
• /
• v.13 no.10
• /
• pp.640-644
• /
• 2003

NiCr thin films were fabricated by rf magnetron sputtering for applying to both the top electrode and absorption layer on Pb(Zr, Ti)O$_3$(PZT) thin films for infrared sensors. The rms roughness and resistivity of NiCr films prepared with Ni power of 80 W and Cr power of 50 W showed the most stable oxidation resistance after annealing at $600^{\circ}C$ for 5 min in oxygen ambient. The rms roughness and resistivity of NiCr films annealed at $V^{\circ}C$ in oxygen ambient were about 2$0\AA$ and $70 \mu$Ω-cm, respectively. As-deposited Ni/PZT/Pt and NiCr (Ni 80 W, Cr 50 W)/PZT/Pt structures showed well saturated hysteresis loops. However, in case of the samples annealed at $500^{\circ}C$ in oxygen ambient, only NiCr/PZT/Pt showed saturated loops having a remanent polarization of 20$\mu$C/$\textrm{cm}^2$. Ultra-thin NiCr films showed a possibility as a top electrode for infrared sensors.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.14 no.5
• /
• pp.356-361
• /
• 2001

The structureal, dielectric and piezoelectric properties of Pb[(Sb$\_$1/2/Nb$\_$1/2/)$\_$x/-(Ni$\_$1/3/Nb$\_$2/3/)$\_$0.15-x/-(Zr$\_$y/Ti$\_$1-y/)$\_$0.85/]O$_3$(x=0∼0.05, y=0.47∼0.52) ceramics were investigated with the substitution of Pb(Sb$\_$1/2/Nb$\_$1/2/)O$_3$(abbreviated PSN) and the Zr/Ti ratio. At Zr/Ti ratio of 50/50, tetragonality was decreased and grain size abruptly decreased with the increase of PSN substitution. Curie temperature was decreased and dielectric constant increased with the substitution of PSN. The coercive field increased and remnant polarization decreased with the substitution of PSN. Electromechanical coupling factor(k$\_$p/) showed the highest value of 0.622 at 1mol% PSN, but mechanical quality factor(Q$\_$m/) showed the minimum value at that composition. Dielectric constant and electromechanical coupling factor with the Zr/Ti ratio showed maximum values at Zr/Ti ratio of 50/50 and mechanical quality factor showed minimum values near the Zr/Ti ratio of 50/50.

• Journal of Hydrogen and New Energy
• /
• v.5 no.1
• /
• pp.1-8
• /
• 1994

Lattice structure, hydrogen absorption characteristics, discharge capacity and cycle life of $V_{22}Ti_{16}Zr_{16}Ni_{39}X_7$(X= Cr, Co, Fe, Mn, Al) alloys were investigated. The matrix phases of these alloys were the C14 Laves phase. Chromium-containing alloy had a vanadium-rich phase in addition to the Laves phase. The chromium, maganese, or aluminum-containing alloys had lower hydrogen equilibrium pressure and larger hydrogen absorption content than the cobalt or iron-containing alloys. The discharge capacities of these alloys were 270~330mAh/g. The discharge capacity according to the alloying element X decreased in the order of Mn>Cr>Co, Al)Fe. The charge/discharge cycle lives of the chromium, cobalt or iron-containing alloys were longer than those of maganese or aluminum-containing alloys due to the lower vanadium dissolution rate.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.06a
• /
• pp.330-330
• /
• 2008

$Fe_2O_3$ added Pb$(Ni_{1/3}Nb_{2/3})O_3-PbTiO_3-PbZrO_3 $ (PNN-PT-PZ) ceramics were produced in order to use them as a bimoph acturator for energy harvesting. Especially, the 0.25 wt% $Fe_2O_3$ added 0.4PNN-0.357PT-0.243PZ, having the composition of morphotropic phase boundary, showed good piezoelectric properties of $d_{33}$ of 810 pC/N, $k_p$ of 77% and $Q_m$ of 55 along with a high Curie temperature of $210^{\circ}C$. A bimorph actuator, composed of the two piezoelectric layers bonded together with a phosphorous bronze layer as a central metallic electrode, was successfully fabricated. The bimorph actuator, vibrated with a 1.3 mm amplitude at 68 Hz, produced high electric power of approximately 60 mW.

• Proceedings of the KIEE Conference
• /
• 1994.11a
• /
• pp.193-195
• /
• 1994

In this study, the structural, dielectric and piezoelectrical properties of $xPb(Mg_{1/2}W_{1/2})O_3-(1-x)[0.41Pb(Ni_{1/3}Nb_{2/3})O_3-0.36PbTiO_3-0.23P Zr)_3]$ (x=0, 0.01, 0.02, 0.03, 0.04, 0.05) system ceramics were investigated. The dielectric constant ${\varepsilon_{33}}^{\tau}$ at loon temperature increased up to 3mol% PMW and decreased with further PMW content. The specimen with 1mol% $Pb(Mg_{1/2}W_{1/2})O_3$, which has the ${\varepsilon_{33}}^{\tau}=5509$, kp=59[%] and $d_{33}=758{\times}10^{-12}[C/N]$, exhibits good characteristics.

• Korean Journal of Materials Research
• /
• v.15 no.11
• /
• pp.697-704
• /
• 2005

The deformation behavior of a bulk amorphous and crystallized amorphous $Zr_{22.5}Ti_{14}Cu_{12.5}Ni_{10}Be_{22.5}$ alloy extracted from a commercial golf club head was characterized at room temperature ana $300^{\circ}C$. At room temperature, amorphous specimens revealed higher yield stress and ductility than partially crystallized alloy specimens. Amorphous alloy displayed some plasticity before fracture, which resulted from strain hardening and repeated crack initiation and propagation. The fracture is mainly localized on one major shear band, and the compressive fracture angle of the amorphous specimen between the stress axis and the fracture plane was about $40^{\circ}$ Scanning electron microscope observations revealed mainly a vein-like structure in the amorphous alloy But the fracture surface of partially crystallized amorphous alloy consisted of vein-like and featureless fracture structure. The partially crystallized alloy extracted from the thick part of the club fractured in the elastic region, at a much lower stress level than the amorphous, suggesting that relatively coarse crystal particles formed during cooling cause the brittle fracture.

• Proceedings of the Korean Magnestics Society Conference
• /
• 2008.12a
• /
• pp.141.2-141.2
• /
• 2008

• Journal of Hydrogen and New Energy
• /
• v.7 no.2
• /
• pp.137-145
• /
• 1996

The Zr-based $AB_2$ type Laves phase hydrogen storage alloys have some promising properties, long cycle life, high discharge capacity, as electrode materials in reversible metal hydride batteries. However, when these alloys are used as negative electrode for battery, there is a problem that their rate capabilities are worse than those of commercialized $AB_5$ type hydrogen storage alloys. In this work, we tried to develop the Zr-based $AB_2$ type Laves phase hydrogen storage alloys which have high capacity and, especially, high rate capability.

• Journal of Hydrogen and New Energy
• /
• v.10 no.3
• /
• pp.185-189
• /
• 1999

Effects of alloy modification with the $Zr_{0.6}Ti_{0.4}V_{0.4}Ni_{1.2}Mn_{0.4}$ alloy for an electrode use have been investigated. For the alloy composition, a part of Mn was substituted by Co, Cr and Fe. The experimental results showed that Co accelerated activation of alloy, and Fe and Cr improved the discharge capacity. These results agree with P-C-T curves of each alloy. But substituting Fe for Mn showed the decrease of the discharge capacity when discharged at high rate (60mA, about 1C rate). Considering both the discharge capacity and the high rate discharge property, $Zr_{0.6}Ti_{0.4}V_{0.4}Ni_{1.2}Mn_{0.3}Cr_{0.1}$ alloy was found to be the best alloy among the alloys subjected to the test.

• Journal of the Korean Ceramic Society
• /
• v.39 no.11
• /
• pp.1017-1022
• /
• 2002

$(Ba_{1-x}Ca_x)(Ti_{1-y}Zr_y)O_3(BCTZ)$ powders for the Ni-electrode Multilayer Ceramic Capacitor(MLCC) were synthesized via hydrothermal treatment using mixed aqueous solutions of $BaCl_2{\cdot}2H_2O,\Ca(NO_3)2{\cdot}4H_2O,\ ZrOCl_2{\cdot}8H_2O$ and $TiCl_4$. Two component and three component systems were also extensively studied for basic data. BT, CT and BZ powders were crystalline but CZ was determined to be amorphous under the same synthetic condition. In BTZ system, Zr and Ti were completely soluble and Ca would be substituted for Ba up to ∼6 mol% in BCT. The submicron-sized $(Ba_{0.95}Ca_{0.05})(Ti_{0.80}Zr_{0.20})O_3$ powder of the target composition was successfully synthesized at $150{\circ}$ for 12h.