Abstract
The structureal, dielectric and piezoelectric properties of Pb[(Sb$\_$1/2/Nb$\_$1/2/)$\_$x/-(Ni$\_$1/3/Nb$\_$2/3/)$\_$0.15-x/-(Zr$\_$y/Ti$\_$1-y/)$\_$0.85/]O$_3$(x=0∼0.05, y=0.47∼0.52) ceramics were investigated with the substitution of Pb(Sb$\_$1/2/Nb$\_$1/2/)O$_3$(abbreviated PSN) and the Zr/Ti ratio. At Zr/Ti ratio of 50/50, tetragonality was decreased and grain size abruptly decreased with the increase of PSN substitution. Curie temperature was decreased and dielectric constant increased with the substitution of PSN. The coercive field increased and remnant polarization decreased with the substitution of PSN. Electromechanical coupling factor(k$\_$p/) showed the highest value of 0.622 at 1mol% PSN, but mechanical quality factor(Q$\_$m/) showed the minimum value at that composition. Dielectric constant and electromechanical coupling factor with the Zr/Ti ratio showed maximum values at Zr/Ti ratio of 50/50 and mechanical quality factor showed minimum values near the Zr/Ti ratio of 50/50.