• 한국정밀공학회지
• /
• 제13권11호
• /
• pp.32-37
• /
• 1996

Using the are ion plating(AIP) process, TiN coating was deposited onto high speed steel substrates. The effects of coating thickness, titanisum interlayer and shield on wear resisting capability of the coated tools were investigated. In order to promote good adhesion between the substrate and the TiN coating a thin Ti interlayer was deposited. A shield was set up also between Ti target and high speed steel substrates to prevent molten droplets from reaching the substrate. Three series of varying thickness of TiN coated layer were prepared with or without the Ti interlayer, and with or without the shield. The tools with the Ti layer and the shield showed longer tool lifes than those of other series of tools and the commercially available TiN coated HSS tools, by up to 70%.

• 대한치과교정학회지
• /
• 제23권3호
• /
• pp.327-340
• /
• 1993

The purpose of this study was to estimate the possibility of practical application of TiN ion-plating method on orthodontic appliances. TiN was coated on the surface of orthodontic stainless steel roll band by means of ion-plating method, and colorimetric properties of its obtained TiN film were investigated by using color analyzer. Also its corrosion and discoloration properties were compared with those of non ion-plated stainless steel roll band by using immersion test, which was done in 1N HCl solution for 10 days. Both weight changes and surface corrosion appearances of specimens for each day were respectively investigated by using electronic weighing machine and SEM(Scanning Electron Microscope). The discoloration degress of TiN-coated specimens immersed in 1N HCl solution were investigated by using color analyzer and then judged by N.B.S.(National Bureau of Standard) Unit. The results of this study were summarized as follows. o TiN ion-plated films showed the hue of 5Y, the value of 7, and the chroma of 3 by Munsell notations. o The weight losses and surface changes of TiN ion-plated specimens immersed in 1N HCl solution were less than those of non ion-plated specimens. It was shown, therefore, that the corrosion resistance was significantly improved by TiN ion-plating. o The discoloration degrees of non ion-plated specimens were too significant to be examined by color analyzer, while those of TiN ion-plated specimens were slight when judged by N.B.S. Unit. It was also apparent, therefore, that the anti-discoloration property was significantly improved by TiN ion-plating.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1995년도 추계학술대회 논문집 학회본부
• /
• pp.364-366
• /
• 1995

We investigated the Electromigration characteristics in Cu alloyed Al line and the effect of Ti/TiN barrier layer on the characteristics. Test structures were fabricated by wafer level and 50% failure times were tested in the condition of j= 2 MA/$cm^3$, T= 300$^{\circ}C$. The reliability of Al line was improved which was 0.5%Cu Alloyed, but Ti/TiN under layer deteriorated the reliability while TiN over layer improved the characteristics.

• 열처리공학회지
• /
• 제2권4호
• /
• pp.11-18
• /
• 1989

To investigate the influence of $TiCl_4$, $N_2$ inlet fraction on the TiN layer, TiN film was deposited onto the STC3 and STD11 steel from gas mixtures of $TiCl_4/N_2/H_2$ by the radio frequency plasma assisted chemical vapor deposition. The films were deposited at various $TiCl_4$, $N_2$ inlet fractions. The results showed that the film thickness was increased with $TiCl_4$ inlet fraction. However, while the thickness was increased with $N_4$ inlet fraction under 0.4 the thickness was decreased with increasing $N_2$ inlet fraction over 0.4. The density of deposited films was varied as $TiCl_4$, $N_2$ inlet fraction and its maximum value was about $5.6g/cm^3$. The contents of chlorine were increased with increasing $TiCl_4$ inlet fraction and nearly constant with increasing $N_2$ inlet fraction.

• International Journal of Ocean System Engineering
• /
• 제2권2호
• /
• pp.106-115
• /
• 2012

In the present study, TiN and CrN films were coated by arc ion plating equipment onto aluminum alloy substrate, A2024. The film thickness was about 4.65 ${\mu}m$. TiN and CrN films were analyzed by X-ray diffraction and energy dispersive X-ray equipments. The Young's modulus and the micro-Vickers hardness of aluminum substrate were modified by the ceramic film coatings. The difference in Young's modulus between substrate and coating film would affect on the wear resistance. The critical load, Lc, was 75.8 N for TiN and 85.5 N for CrN. It indicated from the observation of optical micrographs for TiN and CrN films that lots of cracks widely propagated toward the both sides of scratch track in the early stage of MODE I. TiN film began to delaminate completely at MODE II stage. The substrate was finally glittered at MODE III stage. For CrN film, a few crack can be observed at MODE I stage. The delamination of film was not still occurred at MODE II and then was happened at MODE III. This agrees with critical load measurement which the adhesive strength was greater for CrN film than for TiN film. Consequently, it was difficult for CrN to delaminate because the adhesive strength was excellent against Al substrate. The wear process, which the film adheres and the ball transfers, could be enhanced because of the increase in loading. The wear weight of ball was less for CrN than for TiN. This means that the wear damage of ball was greater for TiN than for CrN film. It is also obvious that it was difficult to delaminate because the CrN coating film has high toughness. The coefficient of friction was less for CrN coating film than for TiN film.

• 열처리공학회지
• /
• 제2권4호
• /
• pp.1-10
• /
• 1989

To investigate the influence of temperature on the TiN film, it was deposited on the STC-3 steel and Si-wafer from $TiCl_4/N_2/H_2$ gas mixture by using the radio frequency plasma assisted chemical vapor deposition. The deposition was performed at temperature of $400^{\circ}C-500^{\circ}C$. The results showed that crystalline TiN film was deposited over $480^{\circ}C$, and all specimens showed the crystalline TiN X-ray diffraction peaks after vacuum heat treatment for 3 hrs, at $1000^{\circ}C$, $10^{-5}torr$. While the film thickness was increased above $480^{\circ}C$, it was decreased under $480^{\circ}C$ as temperature increased. And the contents of titanium were increased and it of chlorine were decreased as temperature increased. Because temperature increase was attributed to the increase in the density of TiN film, surface hardness of TiN film was increased with temperature.

• 한국전기전자재료학회논문지
• /
• 제25권9호
• /
• pp.681-685
• /
• 2012

We investigated the dry etching characteristics of TiN in $TiN/Al_2O_3$ gate stack using a inductively coupled plasma system. TiN thin film is etched by BCl3/He plasma. The etching parameters are the gas mixing ratio, the RF power, the DC-bias voltages and process pressures. The highest etch rate is in $BCl_3/He$ (25%:75%) plasma. The selectivity of TiN thin film to $Al_2O_3$ is pretty similar with $BCl_3/He$ plasma. The chemical reactions of the etched TiN thin films are investigated by X-ray photoelectron spectroscopy. The intensities of the Ti 2p and the N 1s peaks are modified by $BCl_3$ plasma. Intensity and binding energy of Ti and N could be changed due to a chemical reaction on the surface of TiN thin films. Also we investigated that the non-volatile byproducts such as $TiCl_x$ formed by chemical reaction with Cl radicals on the surface of TiN thin films.

• 열처리공학회지
• /
• 제3권1호
• /
• pp.1-7
• /
• 1990

To investigate the influence of r.f. power and electrode distance on the TiN deposition, TiN films were deposited onto STC3, STD11 steel and Si-wafer from gas mixtures of $TiC_4/N_2/H_2$ using the radio frequency plasma assisted chemical vapor deposition. The crystallinity of TiN film could be improved by the increase of r.f. power and the decrease of electrode distance. The TiN coated layer contains chlorine, its content were decreased with increasing r.f. power as well as decreasing electrode distance. And the thickness of deposited TiN was largely affected by r.f. power and electrode distance. The hardness of deposited TiN reached a maximum value of about Hv 2,000.

• 열처리공학회지
• /
• 제4권1호
• /
• pp.19-29
• /
• 1991

This study was to investigate the influence of the substrate hardness on the hardness and adhesion of TiN thin film deposited by R.F. PACVD. Although the substrate hardness changed, chemical composition, stoichiometry and structure of TiN thin film did not change. ISE index was 1.96-1.99 for the substrate and was 1.57-1.79 for TiN thin film. And ISE index of TiN thin film was inverse proportion to the substrate hardness. When the substrate hardness was low, TiN thin film had many cracks around the indentation. But as the substrate hardness increased, TiN thin film had a few cracks and the deformation was limited within indentation. In having measured the adhesion of TiN thin film by SAT, the critical load (Lc) generally increased as the substrate hardness decreased.

• 한국재료학회지
• /
• 제3권1호
• /
• pp.12-18
• /
• 1993

단결정 실리콘위에 스퍼터법으로 증착된 티타니움막을 급속가열로에서 고상반응에 의해 형성시킨 면저항 1.2 ohm/sq. 내외의 TiS$i_2$ 박막에 있어서 열안정성을 상부절연막의 유무 및 종류에 따라 조사하였다. 상부절연막은 상압 CVD로 증착한 USG(Undoped Silicate Glass, Si$i_2$) 막과 플라즈마 CVD법으로 증착한 PE-SiN(S$i_3$$N_4$)막을 사용했다. 열안정성 평가는 90$0^{\circ}C$에서 시간을 달리하여 TiS$i_2$막, PE-SiN막, USG막의 스트레스는 각각 1.3${\times}{10^{9}}$, 1.25 ${\times}{10^{10}}$, 2.26 ${\times}{10^{10}}$ dyne/c$m^2$의 인장응력을 나타내었다. 응집현상은 TiS$i_2$의 응집현상은 Nabarro-Herring 마이크로 크리프에 의한 원자의 확산관점에서 검토되었다.