• Journal of the Korean institute of surface engineering
• /
• v.41 no.2
• /
• pp.57-62
• /
• 2008

Electrochemical properties of Ti-30Ta-$(3{\sim}15)$Nb alloys coated by HA/Ti compound layer have been studied by various electrochemical method. Ti-30Ta binary alloys contained 3, 7, 10, and 15 wt% Nb contents were manufactured by the vacuum furnace system. The specimens were homogenized for 24 hrs at $1000^{\circ}C$. The samples were cut and polished for corrosion test and coating. It was coated with HA/Ti compound layer by magnetron sputter. The HA/Ti non-coated and coated morphology of Ti alloy were analyzed by x-ray diffractometer(XRD) and filed emission scanning electron microscope(FE-SEM). The corrosion behaviors were investigated using potentiodynamic method in 0.9% NaCl solution at $36.5{\pm}1^{\circ}C$. The homoginazed Ti-30Ta-$(3{\sim}15wt%$)Nb alloys showed the ${\alpha}+{\beta}$ phase, and ${\beta}$ phase peak was predominantly appeared with increasing Nb content. The microstructure of Ti alloy was transformed from needle-like structure to equiaxed structure as Nb content increased. HA/Ti composite surface showed uniform coating layer with 750 nm thickness. The corrosion resistance of HA/Ti composite coated Ti-alloys were higher than those of the non-coated samples in 0.9% NaCl solution at $36.5{\pm}1^{\circ}C$. Especially, corrosion resistance of Ti-Ta-Nb system increased as Nb content increased.

• Journal of Technologic Dentistry
• /
• v.24 no.1
• /
• pp.95-104
• /
• 2002

For biomedical applications, Ti-X%Zr-Y%Nb-0.2%Pd(X:10$\sim$20, Y:2$\sim$8) alloys not containing harmful Al and V were newly designed, and the effect of alloy composition and heat treatment on the microstructure and mechanical properties was investigated. From the results, it was shown that the mechanical properties were enhanced with the addition of Zr or Nb. The effect of heat treating on room temperature strength was investigated by aging treatment after solution treatment. The mechanical properties of Ti-20%Zr-4%Nb-0.2%Pd alloy aged at 400$^{\circ}C$ for 10hrs was found to be superior to those of the pure Ti and Ti-6%Al-4%V ELI alloy.

• Journal of Korea Foundry Society
• /
• v.41 no.2
• /
• pp.127-131
• /
• 2021

Based on its good compatibility with high-temperature environments, the Ti-48Al-2Cr-2Nb alloy is used for high-temperature materials of industrial equipment. In this study, a Ti-48Al-2Cr-2Nb alloy turbocharger turbine wheel was fabricated by a vacuum centrifugal casting method. The conditions that prevent misrun defects of the turbocharger turbine wheel blade from centrifugal casting using alumina molds were investigated. The microstructure of the alloy prepared by vacuum centrifugal casting was studied by means of optical microscopy (OM), with a micro-Vickers hardness analyzer (HV), by X-ray diffraction (XRD) and by SEM-EDS. The HV and SEM-EDS examinations of the as-cast Ti-48Al-2Cr-2Nb alloy showed that the thickness of the oxide layer (α-case) was typically less than 50 ㎛. At a high preheating temperature of 1,100℃, a moderate RPM of 260, and with an alumina mold with a large gate size, there were almost no misrun defects. Therefore, it was confirmed that a Ti-48Al-2Cr-2Nb alloy turbocharger turbine wheel with fewer misrun defects could be achieved through a high preheating temperature, a moderate RPM, a large gate size and an alumina mold to suppress the formation of alpha-case components.

• Journal of Technologic Dentistry
• /
• v.27 no.1
• /
• pp.19-25
• /
• 2005

Ti6Al4V alloy have been mainly used as implant materials. Ti-6Al-4V alloy instead of pure Ti is being widely used as biomaterials has some characteristics such as high fatigue strength, tensile strength. But it has been reported recently that vanadium component expresses cytotoxicity and carcinogenicity and aluminium component is related with dementia of Alzheimer type. In order to overcome their detrimental effects, $\beta$-phase stabilizer Nb was chosen in the present study, in addition Ta and Hf were added to Ti-40wt.%Nb alloy to improve its mechanical properties. This paper was described the influence of heat treatment of Ti-40Nb alloys with 2wt%Ta, 2wt%Hf on the mechanical properties. Specimens of Ti alloys were melted in vacuum arc furnace and homogenized at 1050$^{\circ}C$ for 24 hr. and then were aged after solution heat treat at $\alpha+\beta$ and $\beta$ regions. The mechanical properties of Ti alloys were analysed by hardness test, tensile test, elongation test and SEM test. The results can be summarized as follows: 1. The mechanical properties Ti-40wt.%Nb were improved when 2wt.% Ta and 2wt.%Hf were added. 2. The higher tensile strength value and elongation at solution heat treat was higher than solution heat treat and then were aged.

• Korean Journal of Metals and Materials
• /
• v.49 no.2
• /
• pp.121-127
• /
• 2011

The mechanical properties of the various heat treatment conditions on Ti-15Mo-3Nb-3Al-0.2Si alloy plates were examined. XRD patterns from the surface of Ti-15Mo-3Nb-3Al-0.2Si were analyzed as a solution-treated Ti alloy has the single-phase ${\beta}$ structure whereas the aged Ti alloys have the ${\beta}$ matrix embedded with ${\alpha}$ needles. High strength (~1500 MPa) with decent ductility (7%) was obtained by the Ti alloy double aged at $300^{\circ}C$ and $520^{\circ}C$ for 8 hours each. The double-aged alloy exhibits the finer structure than the single-aged alloy at $300^{\circ}C$ for 8 hours because of the higher nucleation rate of ${\alpha}$ needles at an initial low aging temperature ($320^{\circ}C$). TEM observation revealed that the fine nanostructure with ${\alpha}$ needles in the ${\beta}$ matrix ensured the excellent mechanical properties in the double aged Ti-15Mo-3Nb-3Al-0.2Si alloy. In the solution treated alloy, the yield drop, stress-serrations and the ductility minimum typically associated with dynamic strain aging can be attributed to the dynamic interaction between dislocations and oxygen atoms. The yield drop and the stress serration were not observed in aged samples because the geometrically introduced dislocations due to phase precipitates suppressed the dynamic strain aging.

• 한국신재생에너지학회:학술대회논문집
• /
• 2006.11a
• /
• pp.324-324
• /
• 2006

Nb and Ti were added to 316 stainless steel, and then heat-treatments and surface treatments were performed on the 316 stainless steel and the Nb- and Ti-added alloys. All samples indicated enhanced electrical conductivity after surface treatments, whereas they showed low electrical conductivity before surface treatments due to the existence of non-conductive passive film on the alloy surface. In particular, the Hb- and Ti-added alloys showed remarkable enhancement of electrical conductivity compared to the original alloy, 316 stainless steel. Surface characterization revealed that small carbide particles formed on the alloy surface after surface treatments, while the alloys indicated flat surface structure before surface treatments. $Cr_{23}C_6$ mainly formed on the 316 stainless steel, and NbC and TiC mainly formed on the Nb- and Ti-added alloys, respectively. We attribute the enhanced electrical conductivity after surface treatments to the formation of these carbide particles, possibly acting as a means of electro-conductive channel through the passive film. Furthermore, NbC and TiC are supposed to be more effective carbides than $Cr_{23}C_6$ as electro-conductive channels of stainless steel

• Journal of Korea Foundry Society
• /
• v.22 no.5
• /
• pp.252-256
• /
• 2002

Ni-Nb-Ti-Zr amorphous alloys were manufactured using melt-spinning methods. Amorphous formability, the supercooled liquid region before crystallization and mechanical properties were examined. The value of the reduced glass transition temperature and the supercooled liquid region of $Ni_{62}Nb_{10}Ti_{13}Zr_{15}$ alloy were relatively high and were 0.612 and 76 K respectively. However, amorphous bulk alloy rod was not formed using the Cu-mold die casting. The mechanical properties were in the range of $800{\sim}900DPN$ of hardness and $2.5{\sim}2.8$ GPa of tensile strength in the whole composition range.

• Journal of the Korean Society for Heat Treatment
• /
• v.18 no.2
• /
• pp.91-98
• /
• 2005

Both commercially pure titanium and Ti-6Al-4V alloy have been widely used as biomaterials because of their excellent biocompatibility, corrosion resistance and mechanical properties. However, in recent years, vanadium has been found to cause cytotoxic effects and adverse tissue reactions, while aluminium has been associated with potential neurological disorders. A newly designed ${\alpha}+{\beta}$ type Ti alloy, Ti-10Ta-10Nb alloy showed superior properties to CP Ti and Ti-6Al-4V alloy in the point of biomaterial, and elucidated the future uses as a biomaterial. Microstructural changes of Ti-10Ta-10Nb alloy after hot-rolling, warm-rolling, solution and aging treatment were investigated. According to TEM results, the microstructures after solution treatment were composed of mostly ${\alpha}$ phase with a trace of ${\beta}$ phase due to adding ${\beta}$-phase stabilizer tantalum and niobium. The microstructures after warm-rolling is coarse and elongated ${\alpha}$ phase and hot rolling resulted in very fine ${\alpha}$ widmanst$\ddot{a}$tten. The highest value of hardness was obtained by aging treatment at $400^{\circ}C$ for 20hr in which microstructure consisted of very fine ${\alpha}$ phase in ${\beta}$ matrix.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2003.06a
• /
• pp.1374-1377
• /
• 2003

Ti-8Ta-3Nb is made for biomaterial. The experimental speciments are as-cast Ti-8Ta-3Nb and Ti-8Ta-3Nb swaged. The solution treatment in the range 760-96$0^{\circ}C$have been carried out. The microstructural investigations have been carried out on the specimens after the solution treatment. and the hardness have been measured. And the specific heat and the dilatometer of Ti-8Ta-3Nb swaged have been measured. From the result, the $\beta$ transus of the alloy was determined to be 880-86$0^{\circ}C$.

• Membrane Journal
• /
• v.22 no.1
• /
• pp.1-7
• /
• 2012

We make a studyof the hydrogen permeability and chemical stability of $Nb_{56}Ti_{23}Ni_{21}$ metal alloy membrane. For this purpose, we produced the $Nb_{56}Ti_{23}Ni_{21}$ membrane which has 10 mm diameter and 0.5 mm thick, and experiment the hydrogen transport properties under two kinds of feed gas ($H_2$ 100%; $H_2$ 60% + $CO_2$ 40%) at $450^{\circ}C$C with variation of absolute pressure.The maximum hydrogen permeation flux was $5.58mL/min/cm^2$ in the absolute pressure 3 bar under pure hydrogen. And each case of feed gases about gas composition, the permeation fluxes were satisfied with Sievert's law, and the hydrogen permeation flux decreased with decrease of hydrogen partial pressure irrespective of temperature and pressure. After permeation test, we experiment the stability and durability of $Nb_{56}Ti_{23}Ni_{21}$ alloy membrane for carbon dioxide by XRD analysis.