• 한국표면공학회지
• /
• 제54권3호
• /
• pp.133-138
• /
• 2021

Ternary Ti-X-N coatings, where X = Al, Si, Cr, O, etc., have been widely used for machining tools and cutting tools such as inserts, end-mills, and etc. Ti-Al-N-O coatings were deposited onto silicon wafer and WC-Co substrates by a cathodic arc evaporation (CAE) technique at various negative substrate bias voltages. In this study, the influence of substrate bias voltages during deposition on the microstructure and mechanical properties of Ti-Al-N-O coatings were systematically investigated to optimize the CAE deposition condition. Based on results from various analyses, the Ti-Al-N-O coatings prepared at substrate bias voltage of -80 V in the process exhibited excellent mechanical properties with a higher compressive residual stress. The Ti-Al-N-O (-80 V) coating exhibited the highest hardness around 30 GPa and elastic modulus around 303 GPa. The improvement of mechanical properties with optimized bias voltage of -80 V can be explained with the diminution of macroparticles, film densification and residual stress induced by ion bombardment effect. However, the increasing bias voltage above -80 V caused reduction in film deposition rate in the Ti-Al-N-O coatings due to re-sputtering and ion bombardment phenomenon.

• 한국표면공학회지
• /
• 제34권2호
• /
• pp.105-114
• /
• 2001

$Al_2$$O_3$ coatings were deposited on M2 high speed steels by the plasma enhanced chemical vapor deposition (PECVD) process, using a gas mixture of AlC1$_3$, $H_2$, $CO_2$ and Ar $Al_2$$O_3$ coatings had interference color and showed amorphous phase. $A1_2$X$A1_3$/($Ti_{0.5}$ /$Al_{0.5}$ )N double layer coatings were produced in the sequence of substrate $NH_3$ plasma pretreatment, ($Ti_{0.5}$$Al_{0.5}$)N depoition process, $Al_2$$O_3$ deposition process. $Al_2$ $O_3$/( $Ti_{0.5}$A $l_{0.5}$)N double layer coatings showed NaCl structure in ( $Ti_{0.5}$A $l_{0.5}$)N layer and amorphous phase in A1$_2$ $O_3$ layer. It was shown that $Al_2$ $O_3$ columns continuously grew onto ( $Ti_{0.5}$A $l_{0.5}$)N columns. ( $Ti_{0.5}$A $l_{0.5}$)N single coating and $Al_2$ $O_3$/( $Ti_{0.5}$A $l_{0.5}$)N double layer coating were oxidized at $700^{\circ}C$, 80$0^{\circ}C$, 90$0^{\circ}C$ for 1hr, 3hr in atmosphere. At 80$0^{\circ}C$, single layer coatings were oxidized, which were examined substrate oxide particle. But $Al_2$ $O_3$/ ( $Ti_{0.5}$A $l_{0.5}$)N double layer coatings maintained the asdeposited state. Therefore, $Al_2$ $O_3$/ ( $Ti_{0.5}$A $l_{0.5}$)N double layer coatings have moreexcellent oxidation resistance than ( $Ti_{0.5}$A $l_{0.5}$)N single layer coatings.X> 0.5/)N single layer coatings.s.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2015년도 춘계학술대회 논문집
• /
• pp.131-132
• /
• 2015

$Ti_{0.26}Al_{0.16}Si_{0.01}N_{0.57}$ (at%) coatings were synthesized on stainless steel 304 by using arc ion plating systems (AIPS). Targets employed for the deposition were Ti, AlSi(67:33at%) and AlSi(82:18at%). The thickness of TiAlSiN coatings is $4{\mu}m$. The oxidation characteristics of the deposited coatings were studied by thermogravimetric analysis (TGA) in air between 800 and $900^{\circ}C$ for 75 hr. The oxide scale formed on the TiAlSiN coatings consisted of $rutile-TiO_2$ layer and ${\alpha}-Al_2O_3$. At $800^{\circ}C$, the coatings oxidized relatively slowly, and the scales were thin and adherent. When oxidized above $900^{\circ}C$, $TiO_2$ grew fast over the mixed oxide layer, and the oxide scale formed on TiAlSiN coatings was prone to spallation. Microstructural changes of the TiAlSiN coatings that occurred during high temperature oxidation were investigated by EPMA, XRD, SEM and TEM.

• 한국표면공학회지
• /
• 제37권3호
• /
• pp.152-157
• /
• 2004

Ti-Al-N ($Ti_{75}$ $Al_{25}$ N) and Ti-Al-Si-N ($Ti_{69}$ $Al_{23}$ $Si_{8}$N) coatings synthesized by a DC magnetron sputtering technique were studied comparatively with respect to phase characterization and high-temperature oxidation behavior. $Ti_{69}$ $Al_{23}$ $Si_{ 8}$N coating had a nanocomposite microstructure consisting of nanosized(Ti,Al,Si)N crystallites and amorphous $Si_3$$N_4$, with smooth surface morphology. Ti-Al-N coating of which surface $Al_2$$O_3$ layer formed during oxidation suppressed further oxidation. It was sufficiently stable against oxidation up to about $700^{\circ}C$. Ti-Al-Si-N coating showed better oxidation resistance because both surface Ab03 and near-surface $SiO_2$ layers suppressed further oxidation. XRD, GDOES, XPS, and scratch tests were performed.

• 한국표면공학회지
• /
• 제54권5호
• /
• pp.230-237
• /
• 2021

In this study, the influence of silicon contents on the microstructure, mechanical and tribological properties of Ti-Al-Si-N coatings were systematically investigated for application of cutting tools. The composition of the Ti-Al-Si-N coatings were controlled by different combinations of TiAl₂ and Ti₄Si composite target powers using an arc ion plating technique in a reactive gas mixture of high purity Ar and N₂ during depositions. Ti-Al-Si-N films were nanocomposite consisting of nanosized (Ti,Al,Si)N crystallites embedded in an amorphous Si₃N₄/SiO₂ matrix. The instrumental analyses revealed that the synthesized Ti-Al-Si-N film with Si content of 5.63 at.% was a nanocomposites consisting of nano-sized crystallites (5-7 nm in dia.) and a three dimensional thin layer of amorphous Si₃N₄ phase. The hardness of the Ti-Al-Si-N coatings also exhibited the maximum hardness value of about 47 GPa at a silicon content of ~5.63 at.% due to the microstructural change to a nanocomposite as well as the solid-solution hardening. The coating has a low friction coefficient of 0.55 at room temperature against an Inconel alloy ball. These excellent mechanical and tribological properties of the Ti-Al-Si-N coatings could help to improve the performance of machining and cutting tool applications.

• 대한치과교정학회지
• /
• 제51권4호
• /
• pp.270-281
• /
• 2021

Objective: The aim of this in vitro study was to evaluate the changes in friction between orthodontic brackets and archwires coated with aluminum oxide (Al₂O₃), titanium nitride (TiN), or chromium nitride (CrN). In addition, the resistance of the coatings to intraoral conditions was evaluated. Methods: Stainless steel canine brackets, 0.016-inch round nickel-titanium archwires, and 0.019 × 0.025-inch stainless steel archwires were coated with Al₂O₃, TiN, and CrN using radio frequency magnetron sputtering. The coated materials were examined using scanning electron microscopy, an X-ray diffractometer, atomic force microscopy, and surface profilometry. In addition, the samples were subjected to thermal cycling and in vitro brushing tests, and the effects of the simulated intraoral conditions on the coating structure were evaluated. Results: Coating of the metal bracket as well as nickel-titanium archwire with Al₂O₃ reduced the coefficients of friction (CoFs) for the bracket-archwire combination (p < 0.01). When the bracket and stainless steel archwire were coated with Al₂O₃ and TiN, the CoFs were significantly lower (0.207 and 0.372, respectively) than that recorded when this bracket-archwire combination was left uncoated (0.552; p < 0.01). The friction, thermal, and brushing tests did not deteriorate the overall quality of the Al₂O₃ coatings; however, some small areas of peeling were evident for the TiN coatings, whereas comparatively larger areas of peeling were observed for the CrN coatings. Conclusions: Our findings suggest that the CoFs for metal bracket-archwire combinations used in orthodontic treatment can be decreased by coating with Al₂O₃ and TiN thin films.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2013년도 춘계학술대회 논문집
• /
• pp.119-120
• /
• 2013

공구, 다이몰드 등에 널리 쓰이는 TiC, TiN, CrN, TiCrN, TiAlN 코팅의 산화특성을 비교하기 위하여 $600^{\circ}C-900^{\circ}C$에서 대기중 산화시험을 실시하였다. 내산화성은 (TiC, TiN), TiAlN, TiCrN, CrN 코팅의 순서로 증가하였다. 코팅원소중 Ti는 $TiO_2$로, Cr은 $Cr_2O_3$로, Al은 $Al_2O_3$로 산화되었다.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2018년도 춘계학술대회 논문집
• /
• pp.35-35
• /
• 2018

물리적 증착법에 의해 제조되는 초고경도 박막은 나노다층과 나노복합 구조가 대표적이며, 본 연구에서는 음극 아크 증착법으로 TiAlN과 AlTiiN 층 조합을 이용하여 나노다층구조를 포함하는 다층막 시편을 제작하였다. 초격자 두께 주기 12.1 ~ 15.6 nm에서 35 ~ 55 GPa의 경도값을 가졌으며, 절삭공구 코팅분야에 적용할 예정이다.

• Journal of Ceramic Processing Research
• /
• 제13권spc1호
• /
• pp.149-153
• /
• 2012

Ti2AlN MAX-phase films were synthesized through the post-annealing process of as-deposited Ti-Al-N films. Near amorphous or quasi-crystalline ternary Ti-Al-N films were deposited on Si and Al2O3 substrates by sputtering a Ti2AlN MAX-phase target at room temperature, 300 ℃ and 450 ℃, respectively. A vacuum annealing of those films at 800 ℃ for 1 hour changed those films to crystalline Ti2AlN MAX-phase. The polycrystalline Ti2AlN MAX-phase films exhibited very excellent oxidation resistance due to its characteristics microstructure (nanolaminates), which has potential applications for high-temperature protective coatings. The microstructure and composition of Ti2AlN MAX-phase films were investigated using with a variety of characterization tools.

• 한국결정성장학회지
• /
• 제22권4호
• /
• pp.183-189
• /
• 2012

고온 열수송용 재료로 이용되는 Hastelloy X의 표면처리에 따른 고온물성 개선에 대한 연구를 수행하였다. Hastelloy X 기판 상에 각각 PVD법인 Arc discharge 및 Sputtering을 이용하여 TiAlN 및 $Al_2O_3$ 박막을 표면 코팅(overlay coating) 하였고, 분위기 분말을 이용하여 Al을 금속표면을 통해 확산시키는 방법인 Pack cementation법을 이용한 Al 확산코팅(diffusion coating: aluminiding)법을 이용한 표면처리를 수행하였다. 이들 표면처리가 Ni-Cr계 합금의 고온열처리에서 생성되는 두꺼운 불균질 산화물($Cr_2O_3$)형성 억제에 미치는 효과와 조성 및 표면미세구조가 물성에 미치는 영향에 대해 알아보기 위해, 표면처리 된 Hastelloy X 샘플들을 공기 및 헬륨가스 분위기에서 $1000^{\circ}C$로 열처리 하였으며, 열처리된 전후 시편들에 대해 상형성, 미세구조 및 고온 물성 변화를 측정하였다. 이러한 실험결과를 통하여 표면코팅법에 의한 TiAlN 및 $Al_2O_3$ 박막에 비해 Al 확산코팅한 경우 두꺼운 불균질 산화물($Cr_2O_3$)형성이 억제되어 보다 균질한 미세구조와 높은 내마모성 등 높은 고온 안정성을 보여주는 것을 확인할 수 있었다.