• Clean Technology
• /
• v.19 no.2
• /
• pp.75-83
• /
• 2013

In the present paper, we review recycling and applications of titanium binary alloy scraps. The recycling techniques are to successfully prepare low oxygen content ingots using hydrogen plasma arc melting (HPAM) and to produce low oxygen content titanium alloy powders by Hydrogenation-dehydrogenation (HDH) and Deoxidation in solid state (DOSS) process. In addition, as applications of the titanium binary alloy scraps, Ti based solid-solution carbide powders, which would be used for producing Ti based solid-solution cermets with high toughness, were prepared using the titanium binary alloy scraps. These results confirmed that the titanium alloy scraps could be recycled and refined using the HPAM. The resulting oxygen content of the titanium alloy powders were below 1,000 ppm after powderizing. Finally, we had confirmed that the refined titanium alloy powders were able to be utilized as raw materials for preparing the toughened cermets.

• Korean Journal of Materials Research
• /
• v.32 no.1
• /
• pp.44-50
• /
• 2022

Transition metal carbides (TMCs) are used to process difficult-to-cut materials due to the trend of requiring superior wear and corrosion properties compared to those of cemented carbides used in the cutting industry. In this study, TMC (TiC, TaC, Mo₂C, and NbC)-based cermets were consolidated by spark plasma sintering at 1,300 ℃ (60 ℃min) with a pressure of 60 MPa with Co addition. The sintering behavior of TMCs depended exponentially on the function of the sintering exponent. The Mo₂C-6Co cermet was fully densified, with a relative density of 100.0 %. The Co-binder penetrated the hard phase (carbides) by dissolving and re-precipitating, which completely densified the material. The mechanical properties of the TMCs were determined according to their grain size and elastic modulus: TiC-6Co showed the highest hardness of 1,872.9 MPa, while NbC-6Co showed the highest fracture toughness of 10.6 MPa^*m^1/2. The strengthened grain boundaries due to high interfacial energy could cause a high elastic modules; therefore, TiC-6Co showed a value of 452 ± 12 GPa.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.07b
• /
• pp.834-838
• /
• 2002

In this paper, we have fabricated 4H-SiC schottky diodes utilizing a metal-oxide overlap structure for electric filed termination. The barrier height and Ideality factor were measured by current-voltage, capacitance-voltage characteristics. Schottky barrier height(SBH) were 1.41ev for Ni and 1.35eV for Pt, 1.52eV for Pt/Ti at room temperature and Pt/Ti Schottky diode exhibited Ideality factor was 1.06 to 1.4 in the range of $25^{\circ}C{\sim}200^{\circ}C$. To improve the reverse bias characteristics, an edge termination technique is employed for Pt/Ti/4H-SiC Schottky rectifiers and the device show excellent characteristics with higher blocking voltage up to 780V compared with unterminated devices.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11b
• /
• pp.521-524
• /
• 2001

In this letter. we report on the investigation of Ti. Pt/Si/Ti Ohmic contacts to p-type 4H-SiC. The contacts were formed by a 2-step vacuum annealing at $500^{\circ}C$ for 1h. $950^{\circ}C$ for 10 min respectively. The contact resistances were measured using the transmission line model method. which resulted in specific contact resistivities in the $3.5{\times}10^{-3}$ and $6.2{\times}10^{-4}ohm/cm^{2}$, and the physical properties of the contacts were examined using x-ray diffraction. microscopy. AES(auger electron spectroscopy). AES analysis has shown that, at this anneal temperature, there was a intermixing of the Ti and Si. migration of into SiC. Overlayer of Pt had the effect of decreasing the specific contact resistivity and improving the surface morphology of the annealed contact.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.9 no.1
• /
• pp.81-86
• /
• 2010

This paper investigated into process characteristics of AlTiN coated layers for machining to the direction of upper and lower in plastic mold material (KP-4) with the cemented carbide ball endmill with the diameter of 8mm coated AlTiN layers (1~4) step by step using machining center. The material used in experiments was KP-4 that was machined by three types of inclined angles; $15^{\circ}$, $30^{\circ}$ and $45^{\circ}$ As estimated mechanical properties of AlTiN coated layers, it was shown the most result in the condition of three layered coating that the coating that the coating depth, the hardness of the coated layer and the surface roughness of the coated layer were $13{\mu}m$, Hv 3027.3 and $0.042{\mu}m$, respectively. The cutting component was better at the condition of upper direction than that of lower direction in all experimental conditions and indicated to be less which the bigger angle of the material was increased the effective diameter of the tool.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11a
• /
• pp.521-524
• /
• 2001

In this letter, we report on the investigation of Ti, Pt/Si/Ti Ohmic contacts to p-type 4H-SiC. The contacts were formed by a 2-step vacuum annealing at 500$^{\circ}C$ for 1h, 950$^{\circ}C$ for 10 min respectively. The contact resistances were measured using the transmission line model method, which resulted in specific contact resistivities in the 3.5x10$\^$-3/ and 6.2x10$\^$-4/ ohm/$\textrm{cm}^2$, and the physical properties of the contacts were examined using x-ray diffraction, microscopy, AES(auger electron spectroscopy). AES analysis has shown that, at this anneal temperature, there was a intermixing of the Ti and Si, migration of into SiC. Overlayer of Pt had the effect of decreasing the specific contact resistivity and improving the surface morphology of the annealed contact.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.3 no.2
• /
• pp.115-119
• /
• 2002

This study was performed to improve mechanical properties of rotor and bushing materials. SACD and SKD11 steels as rotor and bushing materials were investigated. Gas nitriding and TiN coating were carried out on SACM and SKD11 steels. TiN coating was deposited on SKD11 steel by reactive sputtering process. This coated layer was picked off during the operation because of insufficient adhesion. Gas nitriding was carried out on SACM and SKD11 steels in an ammonia atmosphere at 51$0^{\circ}C$ for 72 hrs. These gas nitrided parts showed good mechanical properties. SKD11 steels were heat-treated to obtain optimum carbide size and distribution. As a results, the hardness increased.

• Journal of the Korean Society for Heat Treatment
• /
• v.30 no.3
• /
• pp.99-105
• /
• 2017

This study was carried out to investigate the effect of heat treatment on the microstructure and mechanical properties in 90% hot forged Incoloy 825 alloy. With increasing solution treatment temperature, the grain size increased and the volume fraction of total precipitates decreased, and the precipitates disappeared at $1,000^{\circ}C$. With increasing aging time at $700^{\circ}C$, the volume fraction of precipitate increased and the precipitates size increased. Most of the precipitates consist $Cr_{23}C_6$ carbide, and a small amount of TiC carbide was also observed. With decreasing solution treatment temperature and increasing aging time, tensile strength and hardness increased, and the elongation and impact value decreased. With increasing aging time, the impact value decreased sharply by the increased of the precipitate size.

• Journal of Powder Materials
• /
• v.13 no.6 s.59
• /
• pp.445-449
• /
• 2006

The experimental data from the central composite design runs were utilized for mathematical models far the drilling characteristics containing linear, quadratic and interactive effects of the parameters such as volume fraction of TiC in the composites, drill speed, feed rate and drill diameter. The models were developed via stepwise selection where the insignificant effects were removed using t-test. The models were subjected to optimization of maximizing drill life and satisfying the other constraints.

• Korean Journal of Materials Research
• /
• v.16 no.1
• /
• pp.50-57
• /
• 2006

Phase mixtures of Titanium boride, nitride, and carbide powder were produced by the reduction of a mixture of titanium and boron oxides with carbon via a gas-solid phase reaction. Boron oxides produce a vapour phase or decompose to a metal sub-oxide gaseous species when reduced at elevated temperature. The mechanism of BO sub-oxide gas formation from $B_2O_3$ and its subsequent reduction to titanium diboride for the production of uniform size hexagonal platelets is explained. These gaseous phases are critical for the formation of boride, nitride and carbide ceramics. For the production of ceramic phase composite microstructures, the nitrogen partial pressure was the most critical factor. Some calculated equilibrium phase fields has been verified experimentally. The theoretical approach therefore identifies conditions for the formation of phase mixtures. The thermodynamic and kinetic factors that govern the phase constituents are also discussed.