• Journal of the Korean institute of surface engineering
• /
• v.29 no.4
• /
• pp.261-267
• /
• 1996

The characteristics and adhesion strength of TiN layer deposited by D. C. magnetron sputtering were investigated. Three types of TiN layers were deposited on STS304 stainless steel. Scratch tests were performed to determine the effect of deposition temperature, the thickness of coated TiN layer and the titanium inter-layer on the adhesion strength. TiN multilayer with titanium inter-layer showed the highest critical load in the deposition temperature range of $25^{\circ}C$ to $300^{\circ}C$. Adhesion strength of TiN multilayer with titanium inter-layer was raised from 15N to 20N by raising deposition temperature from $25^{\circ}C$ to $400^{\circ}C$. Adhesion strength was raised from 18N to 38N by increasing the thickness of outer layer of TiN multilayer from 2.1 $\mu\textrm{m}$ to 9.5 $\mu\textrm{m}$.

• Korean Journal of Materials Research
• /
• v.13 no.5
• /
• pp.338-342
• /
• 2003

Adhesion between Cu and low-k films has been investigated. Low-k films deposited using a mixture of hexamethyldisilane(HMDS) and Para-xylene had a dielectric constant as low as 2.7, showing the thermally stable properties up to $400^{\circ}C$. In this study, Ti glue layer, boron dopant, and $N_2$plasma treatment were used to improve adhesion property of between Cu and low-k films. Ti glue layer slightly improved adhesion property. After $N_2$plasma treatment, the adhesion property was significantly improved due to the increased roughness and the formation of new binding states between Ti and plasma-treated PPpX : HMDS. However, $300^{\circ}C$ annealing of $N_2$plasma treated sample caused the diffusion of Cu into the PPpX : HMDS, degrading the low-k properties. In the case of Cu(B)/Ti/PPpX : HMDS, the adhesion was remarkably increased. This enhanced adhesion was attributed to formation of Ti-boride at the Cu-Ti interface. It is because the formed Ti-boride prevented the diffusion of Cu into the PPpX : HMDS and the Cu-Ti reaction at the Ti interface.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.26 no.12
• /
• pp.867-871
• /
• 2013

The Ti adhesion layers were deposited onto the glass substrate for transparent capacitors using $Bi_2Mg_{2/3}Nb_{4/3}O_7$ (BMNO) dielectric thin films. Graphene was transferred onto the Ti/glass substrate after growing onto the Ni/$SiO_2$/Si using rapid-thermal pulse CVD (RTPCVD). The BMNO dielectric thin films were investigated for the microstructure, dielectric and leakage properties in the case of capacitors with and without Ti adhesion layers. Leakage current and dielectric properties were strongly dependent on the Ti adhesion layers grown for graphene bottom electrode.

• Journal of the Korean Society for Heat Treatment
• /
• v.13 no.5
• /
• pp.324-329
• /
• 2000

Microstructure, mechanical and fatigue behaviors of TiCN and TiN/TiCN thin films, deposited on quenched and tempered STD61 tool steel, were investigated by using XRD, XPS, hardness, adhesion and fatigue tests. The TiCN thin film is grown along the (100), (111) orientation, whereas the TiN/TiCN thin film is grown along the (111) orientation. The preferred orientation of TiN/TiCN thin film strongly depends on the TiN buffer layer whose orientation is (111), as is well-known. The TiN/TiCN thin film showed the higher adhesion compared with TiCN single layer because the TiN buffer layer, having good toughness, reduces the effects of the lower hardness of substrate. In the high cycle tension-tension fatigue test, the fatigue life of the TiCN and the TiN/TiCN coated steel increased approximately two to four times and five to nine times respectively compared with uncoated specimens. The TiN buffer layer in multilayer thin films plays an important role in reducing residual stress and fatigue crack initiation, and then in restraining the fatigue propagation.

• Korean Journal of Materials Research
• /
• v.3 no.6
• /
• pp.593-597
• /
• 1993

Adhesion of CVD W to the TiN glue layer in the blanket W process which is a promising candidate for filing contact holes in subhalfmicron ULSIs has been investigated. The adhesion was enhanced with increasing the W film thickness due to the decrease of the TiN film stress. The adhesion strength was increased by the sputter etching of the TiN surface prior to the W deposition owing to the removal of contaminants and the increase of the surface roughness. The adhesion of the W film to the TiN glue layer property was also improved by Ar ion implantation of the TiN surface owing to the activation of the TiN surface.

• Korean Journal of Materials Research
• /
• v.18 no.10
• /
• pp.558-563
• /
• 2008

TiAlN films were deposited on WC-5Co substrates with different buffer layers by D.C. magnetron sputtering. The films were evaluated by microstructural observations and measuring of preferred orientation, hardness value, and adhesion force. As a process variable, various buffer layers were used such as TiAlN single layer, TiAlN/TiAl, TiAlN/TiN and TiAlN/CrN. TiAlN coating layer showed columnar structures which grew up at a right angle to the substrates. The thickness of the TiAlN coating layer was about $1.8{\mu}m$, which was formed for 200 minutes at $300^{\circ}$. XRD analysis showed that the preferred orientation of TiAlN layer with TiN buffer layer was (111) and (200), and the specimens of TiAlN/TiAl, TiAlN/CrN, TiAlN single layer have preferred orientation of (111), respectively. TiAlN single layer and TiAlN/TiAl showed good adhesion properties, showing an over 80N adhesion force, while TiAlN/TiN film showed approximately 13N and the TiAlN/CrN was the worst case, in which the layer was destroyed because of high internal residual stress. The value of micro vickers hardness of the TiAlN single layer, TiAlN/TiAl and TiAlN/TiN layers were 2711, 2548 and 2461 Hv, respectively.

• Journal of the Korean Society for Heat Treatment
• /
• v.4 no.4
• /
• pp.1-14
• /
• 1991

In PECVD(Plasma-Enhanced Chemical Vapor Deposition) process, titanium nitride is thin and its adhesion is poor for the protective coatings. Therefore it has been studied that intermediate layer forms between substrate and TiN thin film. Using R.F. plasma nitriding, nitride layer was first formed, then TiN thin film coated by PECVD. The chemical composition of the coatings has been characterized using AES, EDS and their crystallographic structure by means of XRD. Mechanical properties such as microhardness and film adhesion have also been determined by vickers hardness test, scratch test and indentation test. As a result, there was no difference in chemical composition and structure between the TiN deposition only and the composite of TiN deposition on nitrided steel. It was found that nitrided substrate increased the hardness of TiN coatings and was beneficial in preventing the plastic deformation in the substrate. Therefore the effective load bearing capacity of the TiN coatings on nitrided steel was increased and their adhesion was improved as well. According to the results of this study, the processes that lead to the formation of composite layers characterized by good working properties, i.e., high microhardness, adhesion and resistance to deformation.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2003.10a
• /
• pp.59-59
• /
• 2003

In recent, various functional coatings on artificial tooth implants have been conducted to enhance the bonding strength between implants and bones. Despite of these efforts, some previous reports argued that an adhesion strength between titanium implant and the final coatings like hydroxyapatite(HA) is weaker than the strength between coating and bone. In order to increase the adhesion force between the final coating and implant surface, TiN/DLC based functionally graded coating, which has higher mechanical strength than the titanium implant, was applied as a middle layer between titanium implant and final coating. Particularly we finally coated a biocompatible hydroxyapatite film on the DLC layer and examined the mechanical properties. As a result, TiN/DLC based functionally graded coating showed the higher adhesion strength compared with hydroxyapatite single layer coating on the titanium implant.

• Journal of the Korean institute of surface engineering
• /
• v.38 no.2
• /
• pp.79-82
• /
• 2005

This study investigated the effect of nitriding on the hardness and adhesion properties of $TiB_2$ coatings. Inductively coupled plasma (ICP) was used for both nitriding and deposition. By applying ICP, H13 steel was nitrided at a high rate of $50\;{\mu}m/hr$. After nitriding, a Fe4N compound layer or a diffusion layer was formed according to the hydrogen/nitrogen ratio. Both layers could improve the load-bearing capacity of the substrate by increasing the substrate hardness. The adhesion of the $TiB_2$ coatings increased to $\~30N$ after nitriding, but the hardness of the coating was lowered to 20-30 GPa. However, the adhesion of the $TiB_2$ coatings with a high hardness (>60 GPa) could not be improved substantially by nitriding due to the large difference in hardness between the coating and the substrate. The grain size of the $TiB_2$ coating was larger on the nitrided substrates, resulting in a decrease in the hardness of the coating.

• Journal of the Korean Society for Heat Treatment
• /
• v.12 no.3
• /
• pp.199-205
• /
• 1999

The quaternary Ti-Al-V-N films have been grown on glass substrates by reactive dc and rf magnetron sputter deposition from a Ti-6Al-4V target in mixed Ar-$N_2$ discharges. The Ti-Al-V-N films were investigated by means of X-ray diffraction(XRD), electron probe microanalysis(EPMA) and scratch tester. Both XRD and EPMA results indicated that the Ti-Al-V-N films were of single B1 NaCl phase having columnar structure with the (111) preferred orientation. Scratch tester results showed that the adhesion strength of Ti-Al-V-N films which treated with substrate heating and vacuum annealing was superior to that of as-deposited film. The good adhesion strength was also achieved in the double-layer structure of Ti-Al-V-N/Ti-Al-V/Glass.