• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11b
• /
• pp.209-212
• /
• 2001

Polyimide(PI) films have been considered as the interlayer dielectric materials due to low dielectric constant, low water absorption, high gap-fill and planarization capability. The PI mm Was etched with using inductively coupled plasma (ICP). The etching characteristics such as etch rate and selectivity were evaluated to gas mixing ratio. High etch rate was $8300{\AA}/min$ and vertical profile was approximately acquired $90^{\circ}$ at $CF_{4}/(CF_{4}+O_{2})$ of 0.2. The selectivies of polyimide to PR and $SiO_{2}$ were 1.2, 5.9, respectively. The etching profiles of PI films with an aluminum pattern were measured by a scanning electron microscope (SEM). The chemical states on the PI film surface were investigated by x-ray photoelectron spectroscopy (XPS). Radical densities of oxygen and fluorine in different gas mixing ratio of $O_{2}/CF_{4}$ were investigated by optical emission spectrometer (OES).

• Electrical & Electronic Materials
• /
• v.7 no.1
• /
• pp.57-63
• /
• 1994

Aluminum oxide($Al_2{O_3}$) offers some unique advantages over the conventional silicon dioxide( $SiO_{2}$) gate insulator: greater resistance to ionic motion, better radiation hardness, possibility of obtaining low threshold voltage MOS FETs, and possibility of use as the gate insulator in nonvolatile memory devices. We have undertaken a study of the dielectric breakdown of $Al_2{O_3}$ on Si deposited by GAIVBE technique. In our experiments, we have varied the $Al_2{O_3}$ thickness from 300.angs. to 1400.angs. The resistivity of $Al_2{O_3}$ films varies from 108 ohm-cm for films less than 100.angs. to 10$_{13}$ ohm-cm for flims on the order of 1000.angs. The flat band shift is positive, indicating negative charging of oxide. The magnitude of the flat band shift is less for negative bias than for positive bias. The relative dielectric constant was 8.5-10.5 and the electric breakdown fields were 6-7 MV/cm(+bias) and 11-12 MV/cm (-bias).

• Transactions of the Society of Information Storage Systems
• /
• v.3 no.2
• /
• pp.94-112
• /
• 2007

Nano-sized inverted domain dots in ferroelectric materials have potential application in ultrahigh-density rewritable data storage systems. Herein, a data storage system is presented based on scanning non-linear dielectric microscopy and a thin film of ferroelectric single-crystal lithium tantalite. Through domain engineering, we succeeded to form an smallest artificial nano-domain single dot of 5.1 nm in diameter and artificial nano-domain dot-array with a memory density of 10.1 Tbit/$inch^2$ and a bit spacing of 8.0 nm, representing the highest memory density for rewritable data storage reported to date. Sub-nanosecond (500psec) domain switching speed also has been achieved. Next, long term retention characteristic of data with inverted domain dots is investigated by conducting heat treatment test. Obtained life time of inverted dot with the radius of 50nm was 16.9 years at $80^{\circ}C$. Finally, actual information storage with low bit error and high memory density was performed. A bit error ratio of less than $1\times10^{-4}$ was achieved at an areal density of 258 Gbit/inch2. Moreover, actual information storage is demonstrated at a density of 1 Tbit/$inch^2$.

• Proceedings of the KIEE Conference
• /
• 2000.11c
• /
• pp.455-457
• /
• 2000

In this work the electrical characteristics of organic TFTs with the semiconductor-insulator interfaces, where the gate dielectrics were treated by the two methods which are the deposition of Octadecyltrichlorosilane (OTS) on the insulator and rubbing the insulator surface. Pentacene is used as an active semiconducting layer. The semiconductor layer of pentacene was thermally evaporated in vacuum at a pressure of about $2{\times}10^{-7}$ Torr and at a deposition rate of $0.3{\AA}/sec$. Aluminum and gold were used for the gate and source/drain electrodes. OTS is used as a self-alignment layer between $SiO_2$ and pentacene. The gate dielectric surface was rubbed before pentacene is deposited on the insulator. In order to confirm the changes of the surface morphology the atomic force microscopy (AFM) was utilized. The characteristics of the fabricated TFTs are measured to clarify the effects of the surface treatment.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.21 no.4
• /
• pp.354-361
• /
• 2008

The dielectric characteristics of low-k interlayer dielectric materials was fabricated by plasma enhanced chemical vapor deposition (PECVD). BTMSM precursor was evaporated and introduced with the flow rates from 16 sccm to 25 sccm by 1sccm step in the constant flow rate of 60 sccm $O_2$ in process chamber. Manufactured samples are analyzed components by measuring FT/IR absorption lines. Decomposition each Microscopic structures through two-dimensional correlation analysis about mechanisms for the formation of SiOCH in $SiOCH_3$, Si-O-Si and Si-$CH_3$ bonding group and analyzed correlation between the micro-structure of each group. It is a tendency that seems to be growing of Si-O-Ci(C) bonding group and narrowing of Si-O-$CH_3$ bonding group relative to the increasing flow-rate BTMSM. The order of changing sensitivity about changes of flow-rate in Si-O-Si(C) bonding group is cross link mode$(1050cm^{-1})$ $\rightarrow$ open link mode$(1100cm^{-1})\rightarrow$ cage link mode $(1140cm^{-1})$.

• Proceedings of the KIEE Conference
• /
• 2009.07a
• /
• pp.1425_1426
• /
• 2009

In this study, commercially available polyethylene terephthalate(PET), which is widely used as a substrate of flexible electronic devices, was modified by dielectric barrier discharge(DBD) method in an air condition at atmospheric pressure, and aluminium - doped zinc oxide (ZnO:Al) transparent conducting film was deposited on PET substrate by r. f. magnetron sputtering method. Surface analysis and characterization of the plasma-treated PET substrate was carried out using contact angle measurements, X-ray Photoelectron Spectroscopy(XPS) and Atomic Force Microscopy (AFM). Especially the effect of surface state of PET substrate on some important properties of ZnO:Al transparent conducting film such as electrical and morphological properties and deposition rate of the film, was studied experimentally. The results showed that the contact angle of water on PET film was reduced significantly from $62^{\circ}$ to $43^{\circ}$ by DBD surface treatment at 20 min. of treatment time. The plasma treatment also improved the deposition rate and electrical properties. The deposition rate was increased almost linearly with surface treatment time. The lowest electrical resistivity as low as $4.97{\times}10^{-3}[\Omega-cm]$ and the highest deposition rate of 234[${\AA}m$/min] were obtained in ZnO:Al film with surface treatment time of 5min. and 20min., respectively.

• Journal of the Korean Vacuum Society
• /
• v.18 no.1
• /
• pp.49-53
• /
• 2009

The chemical properties of SiOC film was studied for inter-layer insulator. SiOC film was formed with non polarity due to the appropriate union by the alkyl and hydroxyl group. An amorphous structure of non polarity can induce the low dielectric constant materials. The chemical properties of thin film can define the bonding structure owing to the ionic variation, and the analysis of chemical properties was researched by the carbon content using the FTIR spectra, and induced the film with non polarity. The electrical properties is the electron flow, and is always not the same as the chemical properties. The electrical properties of SiOC film with various flow rate ratios was analyzed and researched the correlation between the chemical properties. SiOC film showed the increasing of the leakage current after annealing process, and abruptly increased the carbon content at some samples. But the sample with increasing the carbon content decreased the leakage current. It means that the chemical properties is not the same as the electrical properties, and the carbon is related with the variation of the bonding structure, and does not contribute the current flow.

• Journal of the Korean Vacuum Society
• /
• v.5 no.4
• /
• pp.359-364
• /
• 1996

$SrTiO_3$ thin films were deposited on Pt/Ti/$SiO_2$/Si substrates at low temperatures below $300^{\circ}C$ by r.f. magnetron sputtering. The materials and the electrical properties of the deposited films were investigated with controlling deposition parameters such as substrate temperature(T_s) and positive substrate d.c. bias voltage. Stoichiometric $SrTiO_3$ films were obtained at Ts of $300^{\circ}C$, but Sr content in the film was less than that of a target when Ts was lower than $300^{\circ}C$, resulting in poor electrical properties. By introducing a positive substrate d.c. bias during deposition, the crystallinity and the dielectric properties of the films were markedly improved. 400 nm thick $SrTiO_3$, films deposited at $300^{\circ}C$ with a positive substrate d.c. bias of 20V showed a columnar structure with <211> crystallographic direction and a dielectric constant of 98.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.05a
• /
• pp.469-472
• /
• 1999

CeO$_2$ thin films have used in wide applications such as SOI, buffer layer, antirflection coating, and gate dielectric layer. CeO$_2$takes one of the cubic system of fluorite structure and shows similar lattice constant (a=0.541nm) to silicon (a=0.543nm). We investigated CeO$_2$films as buffer layer material for nonvolatile memory device application of a single transistor. Aiming at the single transistor FRAM device with a gate region configuration of PZT/CeO$_2$ /P-Si , this paper focused on CeO$_2$-Si interface properties. CeO$_2$ films were grown on P-type Si(100) substrates by 13.56MHz RF magnetron sputtering system using a 2 inch Ce metal target. To characterize the CeO$_2$ films, we employed an XRD, AFM, C-V, and I-V for structural, surface morphological, and electrical property investigations, respectively. This paper demonstrates the best lattice mismatch as low as 0.2 % and average surface roughness down to 6.8 $\AA$. MIS structure of CeO$_2$ shows that breakdown electric field of 1.2 MV/cm, dielectric constant around 13.6 at growth temperature of 200 $^{\circ}C$, and interface state densities as low as 1.84$\times$10$^{11}$ cm $^{-1}$ eV$^{-1}$ . We probes the material properties of CeO$_2$ films for a buffer layer of FRAM applications.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07a
• /
• pp.74-77
• /
• 2004

[ $HfO_2$ ] dielectric layers were grown on the p-type Si(100) substrate by metalorganic molecular beam epitaxy(MOMBE). Hafnium $t-butoxide[Hf(O{\cdot}t-C_4H_9)_4]$ was used as a Hf precursor and Argon gas was used as a carrier gas. The thickness of the layers was measured by scanning electron microscopy (SEM) and high-resolution transmission electron measurement(HR-TEM). The properties of the $HfO_2$ layers were evaluated by X-ray diffraction(XRD), high frequency capacitance-voltage measurement(HF C-V), current-voltage measurement(I-V), and atomic force measurement(AFM). HF C-V measurements have shown that $HfO_2$ layer grown by MOMBE has a high dielectric constant(k=19-21). The properties of $HfO_2$ films are affected by various process variables such as substrate temperature, bubbler temperature, Ar, and $O_2$ gas flows. In this paper, we examined the relationship between the $O_2/Ar$ gas ratio and the electrical properties of $HfO_2$.