• Journal of the Korean Electrochemical Society
• /
• v.12 no.3
• /
• pp.251-257
• /
• 2009

In this study, we fabricated nickel oxide thin film for lithium based electrolyte using sol-gel method. This film was deposited by dip-coating method with mixed solvent of DameH (N,N-dimethylaminoethanol) and DI water. As changing the ratio between DmaeH and DI water, nickel oxide thin film was presented in different charge density and optical transmittance because they were shown various thickness. It was accounted for changing viscosity and density by the ratio of DmaeH and DI water. The thin film synthesized with 1 : 1 ratio of DmaeH and DI water was expressed best electrochromic performance in lithium based electrolyte, because of thick thickness but porous structures.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.07a
• /
• pp.185-190
• /
• 2003

In this paper, it was demonstrated that the organic thin film transistors were fabricated by the organic gate insulators with vapor deposition polymerization (VDP) processing. In order to form polyimide as a gate insulator, vapor deposition polymerization process was also introduced instead of spin-coating process, where polyimide film was co-deposited by high-vacuum thermal evaporation from 4,4'-oxydiphthalic anhydride (ODPA) and 4,4'-oxydianiline (ODA) and 2,2-bis(3,4-dicarboxyphenyl)hexafluoropropane dianhydride (6FDA) and ODA, and cured at $150^{\circ}C$ for 1hr. Electrical output characteristics in our organic thin film transistors using the staggered-inverted top-contact structure obtained to the saturated slop in the saturation region and the subthreshold non-linearity in the triode region. Field effect mobility, threshold voltage, and on-off current ratio in $0.45\;{\mu}m$ thick gate dielectric layer were about $0.17\;cm^2/Vs$, -7 V, and $10^6\;A/A$, respectively. Details on the explanation of compared to organic thin-film transistors (OTFTS) electrical characteristics of ODPA-ODA and 6FDA-ODA as gate insulators by fabricated thermal co-deposition method.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.18 no.2
• /
• pp.159-163
• /
• 2005

This paper gives characterization of ZnO thin film deposited by RF magnetron sputtering method, which is concerned in deposition process and device fabrication process, to fabricate solidly mounted resonator(SMR)-type film bulk acoustic resonator(FBAR). A piezoelectric layer of 1.1${\mu}{\textrm}{m}$ thick ZnO thin films were grown on thermally oxidized SiO$_2$(3000 $\AA$)/Si substrate layers by RF magnetron sputtering at the room temperature. The highly c-axis oriented ZnO thin film was obtained at the conditions of 265 W of RF power, 10 mtorr of working pressure, and 50/50 of Ar/O$_2$ gas ratio. The piezoelectric-active area was 50 ${\mu}{\textrm}{m}$${\times}$50${\mu}{\textrm}{m}$, and the thickness of ZnO film and Al-3 % Cu electrode were 1.4 ${\mu}{\textrm}{m}$ and 180${\mu}{\textrm}{m}$, respectively. Its series and parallel frequencies appeared at 2.128 and 2.151 GHz, respectively, and the qualify factor of the resonator was as high as 401.8$\pm$8.5.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.11a
• /
• pp.72-73
• /
• 2005

Stress behavior was studied to investigate the internal behaviors of boron, carbon, and nitrogen in the 1000${\AA}$-thick tungsten boron carbon nitride (W-B-C-N) thin films. The impurities in the W-B-C-N thin films provide stuffing effects that were very effective for preventing the interdiffusion between interconnection metal and silicon substrate during the subsequent high temperature annealing process. The resistivity of W-B-C-N thin film decreases as an annealing temperature increase. The W-B-C-N thin films have compressive stress, and the stress value decreased up to $4.11\times10^{10}dyne/cm^2$ as an $N_2$ flow rate increases up to 3 sccm.

• Korean Journal of Materials Research
• /
• v.19 no.1
• /
• pp.24-27
• /
• 2009

Indium Gallium Zinc Oxide (IGZO) thin films were deposited onto 300 nm-thick oxidized Si substrates and glass substrates by direct current (DC) magnetron sputtering of IGZO targets at room temperature. FESEM and XRD analyses indicate that non-annealed and annealed IGZO thin films exhibit an amorphous structure. To investigate the effect of an annealing treatment, the films were thermally treated at $300^{\circ}C$ for 1hr in air. The IGZO TFTs structure was a bottom-gate type in which electrodes were deposited by the DC magnetron sputtering of Ti and Au targets at room temperature. The non-annealed and annealed IGZO TFTs exhibit an $I_{on}/I_{off}$ ratio of more than $10^5$. The saturation mobility and threshold voltage of nonannealed IGZO TFTs was $4.92{\times}10^{-1}cm^2/V{\cdot}s$ and 1.46V, respectively, whereas these values for the annealed TFTs were $1.49{\times}10^{-1}cm^2/V{\cdot}$ and 15.43V, respectively. It is believed that an increase in the surface roughness after an annealing treatment degrades the quality of the device. The transmittances of the IGZO thin films were approximately 80%. These results demonstrate that IGZO thin films are suitable for use as transparent thin film transistors (TTFTs).

• KIEE International Transactions on Electrophysics and Applications
• /
• v.4C no.4
• /
• pp.165-169
• /
• 2004

This paper reports a miniaturized conductor-backed CPW (CBCPW) bandpass filter based on a thin film polyimide layer coated on CMOS-grade silicon. With a 20 ${\mu}{\textrm}{m}$-thick polyimide interface layer and back metallization on the CMOS-grade silicon, the interaction of electromagnetic fields with the lossy silicon substrate has been isolated, and as a result a low-loss and low-dispersive CBCPW line has been obtained. Measured attenuation constant at 20 GHz is below 1.2 ㏈/cm, which is compatible with the CPW on GaAs. In addition, by using the proposed CBCPW geometry, miniaturized BPF for Ku band application is designed and its measured frequency response shows excellent agreement with the predicted value with validating the performances of the proposed CBCPW geometry for RFIC interconnects and filter applications.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.26 no.5
• /
• pp.347-350
• /
• 2013

By inserting a very thin metal layer of Ag between two outer oxide layers of amorphous silicon indium zinc oxide (SIZO), we fabricated a highly transparent SIZO/Ag/SIZO multilayer on a glass substrate. In order to find the optimized thickness of Ag layers, we investigated the variation of optical properties depending on Ag thickness. It was found that the transition of Ag layer from island formation to a continuous film occurred at a critical thickness. Continuity of the Ag film is very important for optical properties in SIZO/Ag/SIZO multilayer. With about 15 nm thick Ag layer, the multilayer showed a high optical transmittance of 80% at 550 nm and low emissivity in IR.

• Journal of the Korean institute of surface engineering
• /
• v.50 no.5
• /
• pp.392-397
• /
• 2017

The Young's modulus of a nanoscale titanium (Ti) thin-film was evaluated using a high-speed microcantilever resonating at the megahertz frequency in the present study. A 350 nm thick Ti film was deposited on the surface of a silicon microcantilever, and the morphology of the film was analyzed using the atomic force microscopy. The microcantilever was excited to resonate using an ultrasonic pulser that generates tone burst signals and the resonance frequency shift induced by the deposition of Ti was measured using a Michelson interferometer. The Young's modulus was determined through a modal analysis using the finite element method and the result was validated by the nanoindentation testing, showing good agreement within a relative error of 1.0%. The present study proposes a nanomechanical characterization technique with enhanced accuracy and sensitivity.

• Journal of the Korean institute of surface engineering
• /
• v.51 no.1
• /
• pp.62-70
• /
• 2018

Sulfamate plating solution containing a small amount of chloride bath was fabricated to study the properties of the electrodeposited Ni thin films. Effects of the changes of current density and additive concentration on current efficiency, residual stress, surface morphology and microstructure of Ni thin films electrodeposited from Ni sulfamate-chloride baths were investigated. The current efficiency was measured to be more than about 95%, independent of the changes of current density and saccharin concentration in the baths. Residual stress of Ni thin film was appeared to be the compressive stress modes in the range of $5{\sim}30mA/cm^2$ current density. Maximum compressive stress was observed at the current density of $10mA/cm^2$. Compressive stress values of Ni thin/thick films were increased to be about -85~-100 MPa with increasing saccharin concentration from 0 to 0.0195 M(4 g/L). Surface morphology was changed from smooth to nodule surface appearance with increasing the current density. Smooth surface morphology of Ni thin films electrodeposited from the baths containing saccharin was observed, independent of the saccharin concentration. Ni thin/thick films consist of FCC(111), FCC(200), FCC(220), FCC(311) and FCC(222) peaks. It was revealed that the FCC(200) peak of Ni thin films is the preferred orientation in the range of $5{\sim}30mA/cm^2$ current density. The intensity of FCC(200) peak was gradually decreased and the intensity of FCC(111) peak was increased with increasing saccharin concentration in the baths.

• Bulletin of the Korean Chemical Society
• /
• v.23 no.2
• /
• pp.225-228
• /
• 2002

Amorphous $Ga_2O_3$ films have been grown on Si(100) substrates by metal organic chemical vapor deposition (MOCVD) using gallium isopropoxide, $Ga(O^iPr)_3$, as single precursor. Deposition was carried out in the substrate temperature range 400-800 $^{\circ}C$. X-ray photoelectron spectroscopy (XPS) analysis revealed deposition of stoichiometric $Ga_2O_3$ thin films at 500-600 $^{\circ}C$. XPS depth profiling by $Ar^+$ ion sputtering indicated that carbon contamination exists mostly in the surface region with less than 3.5% content in the film. Microscopic images of the films by scanning electron microscopy (SEM) and atomic force microscopy (AFM) showed formation of grains of approximately 20-40 nm in size on the film surfaces. The root-mean-square surface roughness from an AFM image was ${\sim}10{\AA}$. The interfacial layer of the $Ga_2O_3$/Si was measured to be ${\sim}35{\AA}$ thick by cross-sectional transmission electron microscopy (TEM). From the analysis of gaseous products of the CVD reaction by gas chromatography-mass spectrometry (GC-MS), an effort was made to explain the CVD mechanism.