• Korean Journal of Metals and Materials
• /
• v.50 no.9
• /
• pp.653-657
• /
• 2012

In this study, a molybdenum disilicide ($MoSi_2$) coating process was investigated by hydrogen reduction and Si-pack cementation. At first, the metallic Mo coating was carried out by hydrogen reduction of $MoO_3$ powder at $750^{\circ}C$ for various holding times (1, 2, 3 h) in hydrogen atmosphere. A $4.3{\mu}m$ thick metallic molybdenum thin film was formed at 3 h. $MoSi_2$ was obtained by Si-pack cementation on molybdenum thin film through hydrogen reduction processing. It was carried out using $Si:Al_2O_3:NH_4Cl=5:92:3$ (wt%) packs at $900^{\circ}C$ for various holding times (30, 60, 90 min) in Ar atmosphere. When the holding time was 90 min, a $MoSi_2$ layer was coated successfully and a $15.4{\mu}m$ thickness was observed.

• Parasites, Hosts and Diseases
• /
• v.60 no.3
• /
• pp.173-179
• /
• 2022

Malaria remains a global health threat. Approximately 97% of the population is at risk in sub-Saharan countries, particularly Nigeria. This study compared the performance of 2 diagnostic methods in assessing malaria endemicity in the rural communities of Ebonyi State, Nigeria. A total of 1,140 study participants were screened for malaria parasite using Rapid Diagnostic Test kits (RDT) in the field, while thick and thin films for microscopy were examined in the laboratory. Our result showed that malaria prevalence was 56.8 by RDT and 38.6% by microscopic test. Age group under 10 years had the highest prevalence of 28.9% (RDT) and 23.6% (microscopy), respectively. The highest prevalence of 19.5% by RDT was recorded in Onicha Local Government Area, while the highest prevalence of 13.4% with microscopy was recorded in Ezza North Local Government Area. The sensitivity and specificity of microscopic examination were both 100%, while those of RDT were 95.5% and 75.9%, respectively.

• Progress in Superconductivity and Cryogenics
• /
• v.11 no.4
• /
• pp.20-24
• /
• 2009

YBCO coated conductors (CC) on the $CeO_2$-buffered IBAD-MgO template were fabricated by metal-organic deposition (MOD) Process with Ba-trifluoroacetate and fluorine-free Y and Cu precursor materials. The precursor solution was coated on $CeO_2$-buffered IBAD MgO templates using the multiple dip-coating method, decomposed into inorganic precursors by pyrolysis up to $400^{\circ}C$ within 3 h, and finally fired at $740{\sim}800^{\circ}C$ in a reduced oxygen atmosphere. Microstructure, texture, and superconducting properties of YBCO films were found highly sensitive to both the firing temperature and time. The high critical current density ($J_C$) of $1.15\;MA/cm^2$ at 77.3K in the self-field could be obtained from $1\;{\mu}m$ thick YBCO CC, fired at $740^{\circ}C$ for 3.5 h, implying that high performance YBCO CC is producible on IBAD MgO template. Further enhancement of $J_C$ values is expected by improving the in-plane texture of $CeO_2$-buffer layer and avoiding the metal substrate contamination.

• Current Optics and Photonics
• /
• v.7 no.6
• /
• pp.714-720
• /
• 2023

Laser cleaning has the advantages of environmental protection, precision, and high efficiency, and has good prospects for application in removing oxide films on the surface of aluminum alloy. This paper discusses the cleaning threshold and cleaning mechanism of aluminum alloy surface oxide film. A nanosecond pulsed laser was used to remove a 5-㎛-thick oxide film from the surface of 7A04 aluminum alloy, and the target surface temperature and cleaning depth were simulated. The effects of different laser energy densities on the surface morphology of the aluminum alloy were analyzed, and the plasma motion process was recorded using a high-speed camera. The temperature measurement results of the experiment are close to the simulation results. The results show that the laser cleaning of aluminum alloy oxide film is mainly based on the vaporization mechanism and the shock wave generated by the explosion.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.37 no.2
• /
• pp.119-132
• /
• 2024

Dielectric ceramic capacitors present high output power density due to the fast energy charge and discharge nature of dielectric polarization. By forming dense ceramic films with nano-grains through the Aerosol Deposition (AD) process, dielectric ceramic capacitors can have high dielectric breakdown strength, high energy storage density, and leading to high power density. Dielectric capacitors fabricated by AD process are expected to meet the increasing demand in applications that require not only high energy density but also high power output in a short time. This article reviews the recent progress on the dielectric ceramic capacitors with improved energy storage properties through AD process, including energy storage capacitors based on both leadbased and lead-free dielectric ceramics.

• Archives of Metallurgy and Materials
• /
• v.66 no.3
• /
• pp.751-754
• /
• 2021

Rutile-TiO₂ nanorod thin films were formed on Ti disks via alkali treatment in NaOH solutions followed by heat treatment at 700℃. Ag nanoparticles were loaded on nanorods using a photo-reduction method to improve the photocatalytic properties of the prepared specimen. The surface characterization and the photo-electrochemical properties of the Ag-loaded TiO₂ nanorods were investigated using a field-emission scanning electron microscope (FE-SEM), X-ray photoelectron spectroscopy (XPS), UV-Vis spectroscopy and electrochemical impedance spectroscopy (EIS). The TiO₂ nanorods obtained after the heat treatment were 80 to 180 nm thick and 1 ㎛ long. The thickness of the nanorods increased with the NaOH concentration. The UV-Vis spectra exhibit a shift in the absorption edge of the Ag-loaded TiO₂ to the visible light range and further narrowing of the bandgap. The decrease in the size of the capacitive loops in the EIS spectra showed that the Ag loading effectively improved the photocatalytic activity of the TiO₂ nanorods.

• Journal of the Korean Electrochemical Society
• /
• v.9 no.4
• /
• pp.141-150
• /
• 2006

Nanocrystalline CoW thin/thick film alloys were electodeposited from citrate baths to investigate the influences of metal ion concentration, current density and solution pH on chemical composition, current efficiency, residual stress, surface morphology, and microstructure of the film. Deposit W (tungsten) content in CoW thin/thick film increased with increasing W ion concentration, current density, and solution pH in the plating bath. It was observed that residual stress in CoW thin/thick film decreased with increasing W ion concentration and solution pH. CoW thin film exhibited mixed phases of hop Co [(100) and (002)] and hcp $Co_3W$ [(002) and (201)] at W ion concentration with 0.02 to 0.08 M. The microstructure of CoW thin film at W ion concentration of 0.1 to 0.2 M was close to amorphous phase. The dominant phases were found to be hop Co (002) and hop $Co_3W$ [(200), (002) and (201)] at the current densities of 5, 10, 25, and $100mA{\cdot}cm^{-2}$ CoW thin film at the current densities of 50 and $75mA{\cdot}cm^{-2}$ was close to amorphous phase. At solution pH 8.7, CoW thin film exhibited hcp Co (002) and hop $Co_3W$ [(200), (002) and (201)]. Below solution pH 8.7, CoW thin film exhibited amorphous microstructure. The optimum electrodeposition conditions for CoW thin/thick film were found to be W ion concentration of 0.08 M, current density of $10mA{\cdot}cm^{-2}$, and solution pH 8.7.

• Journal of the Korean Chemical Society
• /
• v.41 no.5
• /
• pp.223-233
• /
• 1997

Ultra-thin $TiO_2$ films are grown on the Mo(100) surface using evaporated Ti metal under ambient $O_2$ pressure. The thickness of the $TiO_2$ film is controlled by the dosing rate of Ti metal over Mo(100) which is determined from the Auger signal changes with dosing time. 30 ML, 5 ML, and 1.6 ML thick films are prepared and used to determine the growth mechanism, the chemical composition, and the surface structure of the films. The growth mechanism of the $TiO_2$ film on Mo(100) is observed to follow the layer-by-layer growth mechanism. The chemical composition of the film is found to be that of bulk $TiO_2$. The surface plane of the film is (001), which facets irreversibly at 1200 K. The LEED pattern obtained from the film can be explained with the faceted surface with {011} planes reconstructed to $(2\sqrt2{\times}\sqrt2)R45^{\circ}$ with respect to the $TiO_2$ (001) surface. The film is somewhat thermally unstable when annealed to 1300 K. The film sputtered with $Ar^+$ ion is also studied by XPS.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.13 no.5
• /
• pp.254-259
• /
• 2003

In the fabrication process of transparent conducting thin films of the ATO (antimony-doped tin oxide) on a soda lime glass substrate by a sol-gel dip coating method, the effects of the $SiO_2$ buffer layer formed on the substrate and $N_2$ annealing treatment were investigated by XPS (X-ray photoelectron spectroscopy) analysis. Optical transmittance and electrical resistivity of the 400 nm-thick ATO thin films which were deposited on $SiO_2$ buffer layer/soda lime glass and then annealed under nitrogen atmosphere were 84 % and $5.0\times 10^{-3}\Omega \textrm{cm}$ respectively. The XPS analysis confirmed that a $SiO_2$ buffer layer inhibited Na ion diffusion from the substrate, resulting in prohibiting the formation of a secondary phase such as $Na_2SnO_3$ and SnO and increasing Sb ion concentration and ratio of $Sb^{5+}/Sb^{3+}$ in the film. And it was also found that $N_2$ annealing treatment leads to the reduction of $Sn^{4+}$as well as $Sb^{5+}$ however the reduction of $Sn^{4+}$ is more effective and therefore consequently results in decrease in the electrical resistivity to produce an excellent electrical properties of the film.

• Applied Chemistry for Engineering
• /
• v.31 no.3
• /
• pp.291-298
• /
• 2020

ZITO/Ag/ZITO multilayer transparent electrodes at room temperature on glass substrates were prepared using RF/DC magnetron sputtering. Transparent conductive films with a sheet resistance of 9.4 Ω/㎡ and a transmittance of 83.2% at 550 nm were obtained for the multilayer structure comprising ZITO/Ag/ZITO (100/8/42 nm). The sheet resistance and transmittance of ZITO/Ag/ZITO multilayer films meant that they would be highly applicable for use in polymer-dispersed liquid crystal (PDLC)-based smart windows due to the ability to effectively block infrared rays (heat rays) and thereby act as an energy-saving smart glass. Effects of the thickness of the PDLC layer and the intensity of ultraviolet light (UV) on electro-optical properties, photopolymerization kinetics, and morphologies of difunctional urethane acrylate-based PDLC systems were investigated using new transparent conducting electrodes. A PDLC cell photo-cured using UV at an intensity of 2.0 mW/c㎡ with a 15 ㎛-thick PDLC layer showed outstanding off-state opacity, good on-state transmittance, and favorable driving voltage. Also, the PDLC-based smart window optimized in this study formed liquid crystal droplets with a favorable microstructure, having an average size range of 2~5 ㎛ for scattering light efficiently, which could contribute to its superior final performance.