• Elastomers and Composites
• /
• 제35권2호
• /
• pp.115-121
• /
• 2000

일반적인 고무가공 공정에 비해 열가소성 고무 (Thermoplastic Elastomer: TPE)의 가공은 재료가 공공정의 단축, 생산공정의 간소화, scrap의 재활용 둥의 장점과 이에 따른 불량률 저하에 의한 폐기물감소, 제조원가 감소 및 부가가치성을 높일 수 있어 국제 경쟁력 확보에 유리하다. 본 연구에서는 Ethylene propylene diene monomer (EPDM)고무와 polypropylene을 사용하여 동적가교 (dynamic vulcanization)에 의해 블렌드를 제조한 후, glass insert molding법을 이용하여 fixed glass weather-strip을 성형하였다. 성형품의 기계적인 특성을 조사하기 위하여 인장강도, 신장율. 경도, 비중을 측정하였으며, mixing 상태는 SEM 사진을 통하여 관찰하였다. TPE molding 부분과 glass를 일체 성형하므로써 공정의 효율성에 대한 기여 및 생산 자동화에 유리할 것으로 기대한다.

• Elastomers and Composites
• /
• 제31권5호
• /
• pp.341-346
• /
• 1996

The fracture mechanics investigation of the thermoplastic vulcanizates(TPV) from EPDM and PP/Ionomer ternary blends was performed in terms of the J-integral by measuring fracture energy via the locus method. The TPV from ternary blends consisting of EPDM, PP and ionomer were prepared in a laboratory integral mixer by blending and vulcanizing simultaneously. Vulcanization was performed with dicumyl peroxide (DCP) and the composition of EPDM and PP was fixed at 50/50 by weight. Two kinds of poly(ethylene-co-methacrylic acid) (EMA) lonomers were used. The J-integral values at crack initiation, Jc, of the dynamically vulcanized EPDM and PP/EMA Ionomer ternary blends were affected by the cation types $(Na^+\;or\;Zn^{2+})$ and contents(5-20wt%) of the added EMA Ionomers. The ternary blend containing 20wt% zinc-neutralized EMA Ionomer and 1.0phr DCP showed the highest Jc values of the blends.

• Elastomers and Composites
• /
• 제36권2호
• /
• pp.86-93
• /
• 2001

새로운 TPE(Thermoplastic Elastomer) 블렌드 재료로서 폐 EPDM(Ethylene Propylene Diene Monomer)분말의 사용에 따른 환경문제를 해결하고, TPE의 고부가 가치화를 위하여 PP (Polypropylene)와 폐 EPDM분말을 주원료로 하고, 동방향 이축압출기(Co-rotating Twin Screw Extruder)를 사용하여 동적가교를 이루어 TPE재료를 제조하였다. TPE 재료의 인장강도, 파단신율, 탄성율 등의 물성을 향상시킬 목적으로 스크류 조합별로 폐 EPDM/PP를 블렌드하여 기계적물성을 조사하였으며, 모폴로지를 조사하였다. 스크류 조합에서는 혼련판과 역 스크류 엘리먼트의 수가 증가할수록 블렌드물의 전단력과 체류시간이 증가하여 동적가교가 증가하였다.

• Macromolecular Research
• /
• 제11권4호
• /
• pp.267-272
• /
• 2003

The isothermal cure reactions of blends of epoxy (DGEBA, diglycidyl ether of bisphenol A)/anhydride resin with polyamide copolymer (poly(dimmer acid-co-alkyl polyamine)) or PEI were studied using differential scanning calorimetry (DSC). Rheological measurements have been made to investigate the viscosity and mechanical relaxation behavior of the blends. The reaction rate and the final cure conversion were decreased with increasing the amount of thermoplastics in the blends. Lower values of final cure conversions in the epoxy/thermoplastic blends indicate that thermoplastics hinder the cure reaction between the epoxy and the curing agent. Complete miscibility was observed in the uncured blends of epoxy/thermoplastics up to $120^{\circ}C$ but phase separations occurred in the early stages of the curing process at higher temperatures than $120^{\circ}C$. According to the rheological measurement results, a rise of G' and G" at the onset of phase separation is seen. A rise of G' and G" is not observed for neat epoxy system since no phase separation is seen during cure reaction. At the onset of phase separation the rheological behavior was influenced by the amount of thermoplastics in the epoxy/thermoplastic blends, and the onset of phase separation can be detected by rheological measurements.

• Elastomers and Composites
• /
• 제34권2호
• /
• pp.177-182
• /
• 1999

SBS thermoplastic elastomers offer an inexpensive alternative to vulcanised rubbers for many undemanding applications. They are, however, particularly susceptible to attack from atmospheric ozone leading to cracking as soon as any strain is applied. In most rubber applications some strain is unavoidable. In this paper a compounding approach to protecting SBS thermoplastic rubbers against ozone is described. An explanation is offered for why a protective effect Is observed only when certain combinations of additive are used. SBS elastomers are the most affordable class of thermoplastic rubbers. To achieve finished products resistant to ozone and without compromising the light colours often demanded, recourse must be made to blending with other saturated elastomers or replacement by hydrogenated (SEBS) types. The latter is a significantly more expensive alternative. Under laboratory conditions where the rate of ozone attack is increased by several decades, unprotected SBS begins to crack within a few hours. Several different protective agents are examined here, the best of which, a cyclic enol ether, $Vulkazon^{(R)}$ AFD, can extend the resistance to any cracking to several weeks by the use of a few percent by weight of additive. The systems reported neither discolour the polymer nor stain other materials with which it may be in contact. Use of the protective systems described here could enable SBS elastomers to compete in many applications with the more expensive SEBS polymers.

• 접착 및 계면
• /
• 제9권2호
• /
• pp.16-23
• /
• 2008

본 연구에서는 산업현장에서 직물 제직 시 스크랩으로 버려지는 폐양모와 범용 열가소성수지인 폴리프로필렌(PP)으로 구성된 새로운 폐양모/PP NFRPs (Natural Fiber Reinforced Polymer Composites: 천연섬유강화 고분자복합재료)를 압축성형 방법으로 제조한 후 그들의 기계적, 열적 특성을 분석하였다. PP수지의 기계적 특성은 폐양모의 도입으로 두드러지게 향상되었다. 특히 폐양모의 함량을 50 vol%로 하여 NFRP를 제조하였을 때, PP 대비 NFRP의 굴곡강도는 약 20%, 굴곡탄성률은 약 143%까지 향상되었으며, 인장강도는 약 76%, 인장탄성률은 약 90% 크게 향상되었다. 그리고 열변형온도(HDT)는 최고 $138^{\circ}C$로 PP 대비 약 $21^{\circ}C$가 증가되는 결과를 보여주었다. 연구결과는 열가소성 매트릭스 수지의 보강소재로서 폐양모의 적용 가능성을 제시하였다.

• 폴리머
• /
• 제37권1호
• /
• pp.34-40
• /
• 2013

아민 작용기를 가진 POSS에 toluene diisocyanate(TDI)와 caprolactam(CL)의 반응물을 반응시켜 POSS 기반의 하이브리드 충전제(POSS-(TDI+CL))를 합성하였고 이를 상업용 폴리아미드계 열가소성 탄성체인 PA-TPE에 블렌딩하여 PA-TPE/POSS-(TDI+CL) 복합체를 제조하였다. POSS계 충전제의 화학구조는 FTIR과 $^1H$ NMR을 사용하여 확인하였다. PA-TPE/POSS-(TDI+CL) 복합체는 충전제를 PA-TPE에 7 wt%까지 첨가하여 제조하였고 이들은 순수 PA-TPE와 변성되지 되지 않은 PA-TPE/octaphenyl POSS의 복합체보다 낮은 tension set 값을 보여 탄성회복력이 향상되었다. 또한 하이브리드 충전제의 함량이 증가함에 따라 인장강도와 모듈러스가 증가하였다. 결론적으로 하이브리드 충전제인 POSS-(TDI+CL)는 원래 PA-TPE의 탄성에 나쁜 영향을 미치지 않고도 기계적 물성을 향상시킬 수 있는 적절한 충전제라 볼 수 있다.

• 한국산학기술학회논문지
• /
• 제19권9호
• /
• pp.77-83
• /
• 2018

열가소성 탄성체 (Thermo-Plastic Elastomer-TPE)는 우수한 탄성을 지니면서도 보통의 열가소성 플라스틱과 동일한 성형성과 재생 가능성 때문에 산업계 전반에 걸쳐 사용이 증가하고 있다. 현재 열가소성 탄성체와 관련된 연구는 다양한 소재와의 결합에 의한 복합탄성체 개발이나 이를 구현하기 위한 장비 개발 등에 집중되고 있다. 반면 중소기업 등의 현장에서는 이러한 신소재의 적용뿐만 아니라 저렴한 일축 스크류 장비에서 열가소성 탄성체의 압출이 가능하게 하는 공정조건에 대한 연구가 필요하다. 열가소성 탄성체는 일반적으로 트윈 스크류 방식으로 압출을 하게 된다. 반면에 중소기업 등에서는 단축 스크류 방식의 압출기를 주로 보유하고 있는데 단축 스크류 방식의 압출기에서 압출이 가능하게 하려면 정교한 공정제어를 통해 균일한 두께 유지가 중요하다. 본 논문에서는 열가소성 탄성체 TPE-800L 단축 압출가공에 있어서 압출공정변수인 출력부 가공 온도가 튜브의 성형성에 미치는 영향을 연구하였다. 열가소성 탄성체 TPE-800L의 압출에서는 출력부 온도가 가장 중요한 요소이며 165-170도일 때 가장 우수한 성형성을 확인하였다.

• 한국고분자학회:학술대회논문집
• /
• 한국고분자학회 2006년도 IUPAC International Symposium on Advanced Polymers for Emerging Technologies
• /
• pp.144-145
• /
• 2006

It is well known that the aromatic polycarbonate of bisphenol A (hereafter BPA polycarbonate) possesses superior transparency, exceptional toughness, high heat resistance and mechanical properties, which allow it to be diversely used for automotive, electrical, electronic, appliance and optical industries. In this paper, polycarbonate is reviewed on not only prospects of technology but market trend from the industrial point of view. It also demonstrates the diverse applications of polycarbonates with respect to its development history.

• 한국섬유공학회:학술대회논문집
• /
• 한국섬유공학회 1998년도 가을 학술발표회논문집
• /
• pp.49-52
• /
• 1998

Preparation of conducting Polymer composites by Polymerizing Polypyrrole in thermoplastic polymer matrices has been studied by many researchers in order to enhance the stability and the Physical Properties of polypyrrole. In the previous study4 we examined the effects of the ionic group content and the copolyester molecular structures on the electrical conductivity of conductivity of polypyrrole(PPy)/copolyester composite films. (omitted)