• Elastomers and Composites
• /
• v.32 no.3
• /
• pp.157-165
• /
• 1997

The morphology of the thermoplastic vulcanizates prepared from ethylene-propylene-diene terpolymer, polypropylene and high density polyethylene(HDPE) or ethylene based ionomer were studied. Blends were prepared in a laboratory internal mixer where EPDM was cured in the presence of PP and HDPE or ionomer under shear with dicumyl peroxide(DCP). The effects of DCP concentration and rubber/plastics composition were studied. In the morphological analysis by scanning electron microscopy (SEM), a small amount of EPDM acted as a compatibilizer to HDPE and PP. It was also revealed that the dynamic vulcanization process could reduce the domain size of the crosslinked EPDM phase. When ionomer was added to EPDM/PP blend, the thermoplastic vulcanizate showed typical ductile fracture topology and the trend was more clearly observed when DCP contents and ionomer contents are higher.

• Elastomers and Composites
• /
• v.48 no.4
• /
• pp.256-262
• /
• 2013

We synthesized thermoplastic polyurethane elastomer (TPU) with different contents of sulfuric acid group, and characterized their physical properties such as mechanical, thermal and grip properties. And the results were compared with carboxylic acid-introduced TPU. Wet slip, tensile strength and abrasion properties were increased by the introduction of acid group. Mechanical properties increased with increasing the acid content up to 0.3 wt%. However, wet slip was continually increased as the acid content increased due to increase of hydrophilicity of TPU.

• Elastomers and Composites
• /
• v.49 no.3
• /
• pp.191-198
• /
• 2014

We synthesized thermoplastic polyurethane elastomer(TPU) with acid group and nano zinc oxide, and characterized their mechanical properties, thermal properties, contact angle and grip property. The effects of the zinc oxide content and size on the physical property of TPU were investigated. When the nano zinc oxide was introduced in TPU with acid group, it had excellent mechanical properties and grip by formation of hydrogen and ionic bonding. The wet slip of TPU with zinc oxide was increased continuously as ionization rate increased due to increase of hydrophilicity and ionic interaction, and mechanical properties were increased with increasing ionization rate up to 50%.

• Elastomers and Composites
• /
• v.38 no.1
• /
• pp.27-37
• /
• 2003

This work presents a comparative study of the morphology and structure related properties of thermoplastic elastomer blends based on SEBS/PP/Oil and dynamically vulcanized EPDM/PP/Oil. A combination of ruthenium oxide staining and low voltage scanning electron microscopy (LVSEM) was found to be suitable for the study of morphology of these highly oil extended blends. h close analogy was found in the mechanical, thermal and rheological properties of the two systems made in an internal Brabender mixer and co-rotating turin screw extruder. The morphology of the blends, as made by the two techniques, was found to be significantly different. In the case of TPVs, the blonds made in the extruder had smaller EPDM domains and better tensile properties. In the case of SEBS, the blends made in the Brabender had more co-continuous phases and showed better tensile properties. Crystallization behavior of the isotactic polypropylene in the blends was found to be influenced by the type of rubber. Blends of SEBS/PP crystallized at a lower temperature than the TPVs. These differences were probably caused by differences in the nucleating ability of the two rubbers.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.5 no.4
• /
• pp.46-52
• /
• 2006

From the past, most of the studies about thermoplastic elastomers(TPEs) have been conducted for theirs compounded materials and morphology. However these studies do not directly affect on injection molding processing. Therefor this study is focus on the variation of mechanical properties on TPEs moldings by increasing injection molding conditions which included injection molding conditions include injection pressure, holding pressure, melt temperature, mold temperature. The used experimental TPEs is a group of styrene(TPS). Injection pressure slightly affected on tensile strength, shrinkage and hardness. Holding pressure only affected on hardness. The melt temperature was the most affective condition on tensile strength.

• Proceedings of the Korean Fiber Society Conference
• /
• 2003.04a
• /
• pp.329-330
• /
• 2003

In general, the thermoplastic elastomers have the elastic recovery property caused by phyical crosslinks after the stress is applied. Segmented block copolyetheresters also have been used as elastomers. Many$\^$l-2/ tried to improve the elastic recovery of those which are less elastic than polyurethane. We confirmed that the copolyetherester based on poly(2,6-butylene naphthalate)(PBN) ha.4 segment had the high melting temperature, whcih was useable at the broader temperature range and the one based on poly(1,3-trimethylene terephthalate)(PTT) the high crystallinity, which would be expected to get the high elastic recovery. (omitted)

• Elastomers and Composites
• /
• v.26 no.1
• /
• pp.15-22
• /
• 1991

Blends of ethylene-propylene-diene terpolymer(EPDM) and high density polyethylene(HDPE) have been prepared in a roll mill by the process "dynamic curing" where both blending and a crosslinking reaction was carried out simultaneously. As a crosslinking agent, dicumyl peroxide(DCP) was used. Throughout the experimental ranges, the dynamically cured polyblends were shown to be thermoplastic elastomers except highly crosslinked blends of high compositions of EPDM. The increase of melt viscosity was observed as EPDM composition and DCP contents increased. From DSC determinations, the crystallinity decreased with increasing contents of DCP. The tensile strength and elongation at break generally increased with increasing DCP content and increasing HDPE compositions, but highly depended on the combined effects of decreasing crystallinity and increasing crosslinking density.

• Proceedings of the Korean Fiber Society Conference
• /
• 2002.04a
• /
• pp.93-96
• /
• 2002

Blending Is cheap and leads to new thermoplastics, many properties which can be predicted from those of the components. Due to the incompatibility of their components, most blends feature coarse phase morphologies with weak interfaces between the phases. Consequently the blends are brittle. Thermoplastic elastomers which have two kinds of segments in the chain have flexible(soft) and rigid(hard) segments and exhibit a unique combination of strength, flexibility, and processibility. (omitted)

• Applied Chemistry for Engineering
• /
• v.24 no.3
• /
• pp.305-313
• /
• 2013

In this study, we investigated effects of thermal annealing on the thermal properties and microphase separation behaviors of glycidyl azide-based thermoplastic polyurethane elastomers (ETPE). The GAP-based ETPEs were characterized by attenuated total reflectance-fourier transform infrared spectroscopy (ATR-FTIR), differential scanning calorimeter (DSC), dynamic mechanical analysis (DMA), and gel permeation chromatography (GPC). The effects of annealing temperature conditions ($80{\sim}130^{\circ}C$, 1 h or 24 h) on the properties of the ETPEs were investigated. The intensity of azide group absorption peak of ATR-FTIR spectra and the solubility of ETPE for methylene chloride and dimethylformamide solvent decreased after the annealing at $130^{\circ}C$ for 1 h and at $105^{\circ}C$ for 24 h. With increasing the annealing temperature from $80^{\circ}C$ to $110^{\circ}C$, the high temperature rubbery plateau region of storage modulus curves from DMA thermogram for GAP-based ETPEs was extended to the higher temperature.

• Elastomers and Composites
• /
• v.39 no.4
• /
• pp.286-293
• /
• 2004

Ester- and ether-based thermoplastic polyurethanes of different hardness were injection molded at different mold temperatures and effects of mold temperature on the physical properties of TPUs were investigated. Glass transition temperatures of soft segments of TPUs were hardly changed by mold temperatures. The phase separation of soft and hard segments of injection molded TPUs were affected little by mold temperatures. However, crystallinity of hard segments, temperature range of rubbery plateau, and tensile strength of injection molded TPUs decreased with increasing mold temperatures for TPUs of high hardness. However, injection molded TPUs of low hardness showed increases of crystallinity of hard segments, temperature range of rubbery plateau, and tensile strength with increasing mold temperatures. Different physical properties of injection molded TPUs depending on mold temperatures were attributed to different crystallization and physical crosslinking effects of hard segments.