• The Proceedings of the Korean Institute of Illuminating and Electrical Installation Engineers
• /
• v.2 no.1
• /
• pp.75-82
• /
• 1988

Epoxy, noticed as a new insulation material tor electrical installation, may become an excellent cured material from the crosslink reaction with some curing agents. The characteristics of cured Epoxy is determined by the kind of the curing agents and the method of lattice formation. The purpose of this paper, varing the process of lattice formation by various surrounding temperatures during the curing process, is to obtain the optimum curing temperature for electrical insulation from the results of investigation on the properties of cured Epoxy. In the experiment, Epoxy was cured at various temperatures between $20[^{\circ}C] and 50^[{\circ}C]$ which differ by $5^[{\circ}C]$, and then examined on the electrical insulation haracteristics as well as the thermal and mechanical stability. As a result, it is concluded that the optimum electrical insulation characteristis and mechanical strength of cured Epoxy can be obtained when cured at a surrounding temperature at $30[^{\circ}C]$.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2000.10a
• /
• pp.31-45
• /
• 2000

Because of the high unit cement content in the concrete mix, major concrete temperature rises are observed in the initial stages of hardening in structural members with large cross-sections made of high-strength concrete. While this temperature rise in the initial stages of hardening contributes to the initial development of the concrete strength, it also causes thermal cracking and obstructs medium to long-term increases of the concrete strength. In the study reports below, investigations were made on the effects of the concrete temperature rise in the initial stages of hardening on the medium to long-term development of the strength of structural concrete between the ages of 28 and 91 days. In the study, comparisons were made, for example, between the compressive strength of a control specimen subjected to standard curing at 28 days and the compressive strength of core specimens taken from structural members, and observations were made on the methods of evaluating the concrete strength in structure, defined here as the compressive strength of core specimens at 91 days. The results obtained indicate that, when the maximum temperature of the concrete is the structure does not exceed $60^{\circ}C$, the concrete strength in structure at the age of long-term will generally be greater than the compressive strength of the standard-curing specimens at 28 days, allowing one to evaluate the strength of the structural concrete in terms of the compressive strength of the 28-days standard-curing specimens. When, on the other hand, the maximum temperature of the concrete in the structure exceeds $60^{\circ}C$, the strength in concrete structure may be smaller than the compressive strength of the 28-days standard-curing specimens, creating risks in the evaluation of the concrete strength in structure by latter.

• Journal of the Korea Institute of Building Construction
• /
• v.16 no.6
• /
• pp.529-534
• /
• 2016

Calcium silicate inorganic insulating material is a porous material which is made of 90 wt% of cement. Unlike existing inorganic insulation materials, it is produced without high temperature curing process and also it costs much less than existing inorganic insulation materials. It is an innovative insulation material that supplemented disadvantages of conventional inorganic insulation material. Researches and developments about inorganic insulation materials have been actively researched abroad. Calcium silicate insulation has $0.13g/cm^3$ of specific gravity. Its heat conductivity is under 0.050W/mK, which it similar to conventional inorganic insulation. However, it has weak compressive strength compared to other inorganic insulation. The point of this research is to manifest that calcium silicate inorganic insulating material can have certain compressive strength after curing process with high insulating performance and to find out the proper curing methods and period.

• Composites Research
• /
• v.29 no.6
• /
• pp.395-400
• /
• 2016

Recently, many research groups have studied on the epoxy-based multifunctional electrolyte to develop the structural composite bearing high mechanical properties without sacrificing the ionic conductivity at the same time. The studies on the optimal content and material selection for structural electrolyte have been published, while its curing behavior has not much analyzed yet. In this study, epoxy-based structural electrolyte containing solid electrolyte was prepared by varying the curing temperature and time. In addition, the ionic conductivities and mechanical properties of specimens were measured. We also find out the optimal hardening condition where the epoxy domain enables to be hardened within the range of temperature at which the thermal decomposition of electrolyte does not occur. Finally, we propose the multifunctional structural electrolyte showing achievable electrical and mechanical properties (282 MPa and $9{\times}10^{-6}S/cm@25^{\circ}C$).

• Nuclear Engineering and Technology
• /
• v.4 no.4
• /
• pp.301-305
• /
• 1972

The polymerization rates of monomer or monomer mixture impregnated with catalyst into domestic soft woods such as pinus densiflora, pinus rigida and poplus deltoides e. t. c. were measured. The results were compared with those obtained by radiation curing method and the following conclusions were derived ; (1) Pinus densiflora and pinus rigida are superior to the poplus deltoides, and methyl methacrylate(M. M. A. ) is more effective than other monomers as far as the polymerization rates are only taken into account. (2) The polymerization rate of vinyl acetate is generally slow. And the polymerization rate of the monomer is the slowest in case of being impregnated into poplus deltoides. However, the polymerization rate of the comonomer composed of vinylacetate and M. M. A. is the fastest among the other monomers or monomer mixtures in woods regardless of the curing method. (3) The general trend of polymerization of monomer in wood is similar to that of monomers themselves in both curing methods if the woods contain not much resin.

• Applied Chemistry for Engineering
• /
• v.26 no.5
• /
• pp.538-542
• /
• 2015

In this work, effects of the blend composition composed of 0, 10, 20, 30 and 40 wt% of nylon 6 to epoxy (diglycidylether of bisphenol-A, DGEBA) resin were investigated in terms of cure kinetics and thermal stability by differential scanning calorimeter (DSC) and thermogravimetric analysis (TGA). As the content of the nylon 6 increased, the maximum exothermic temperature ($T_{max}$) and the value of cure activation energy ($E_a$) decreased. The maximum exothermic temperature of the blending samples decreased with increasing in nylon 6 content, resulting in the decrease in curing activation energy of them due to the rapid curing reaction with epoxy resin in this system. From TGA analysis results of the DGEBA/nylon 6, the thermal stability based on the thermal stability index ($A^*{\cdot}K^*$) and integral procedure decomposition temperature (IPDT) increased with increase in the nylon 6 content. This was because of the combination of DGEBA and nylon 6 having good heat resistance, resulting in improving thermal stability of the DGEBA/nylon 6.

• Korean Journal of Optics and Photonics
• /
• v.22 no.2
• /
• pp.67-71
• /
• 2011

In the paper, we have demonstrated an azobenzene-coated fiber Bragg grating (FBG) for monitoring ultraviolet light (UV) intensity in remote measurement. The elasticity of the coated azobenzene polymer is changed by the UV light, which induces a center wavelength change corresponding to the change of the FBG's grating period. The wavelength shift resulting from both UV light and other light with the wavelength out of the UV range was about 0.18 nm. In order to improve the accuracy of the measurement, the center wavelength shift caused by radiant heat of the light source was sufficiently removed by using a thermal filter. The amount of the center wavelength shift was consequently reduced to 0.06 nm, compared to the result without the thermal filter. Also, the FBGs coated by using azobenzene polymer were produced by two different methods; thermal casting and UV curing. Considering temperature dependence, UV curing is more suitable than thermal casting in UV sensor application of the azobenzene-coated FBG. In addition, we have confirmed the wavelength dependence of the optical sensor by means of four different band pass filters. Thus, we found out that the center wavelength shift per unit intensity is 0.029 [arb. unit] as a maximum value at 370 nm wavelength region and that the absorption spectrum of the azobenzene polymer was very consistent with the wavelength dependence of the azobenzene-coated FBG.

• Journal of Adhesion and Interface
• /
• v.10 no.4
• /
• pp.191-198
• /
• 2009

UV-curable aliphatic epoxy acrylates were prepared by the reaction of glycerol diglycidyl ether (GDE) with 2-carboxyethyl acrylate (2-CEA) or 2-hydroxyethyl acrylate (2-HEA). The structures of the epoxy acrylates were characterized by FT-IR, $^1H$-NMR, and $^{13}C$-NMR and the yield was obtained by prep-LC. The UV- and the thermal-curing behaviors of the product were investigated using photo-DSC and DSC, respectively. The reactivity of 2-CEA was higher than 2-HEA and the yield of the product (GEA-C) which was prepared using 2-CEA was about 83%. The maximum UV-curing time ($T_{max}$) of the GEA-C contained non-reactive components and by-product was about 10 seconds. The GEA-C showed low color difference (${\Delta}E^*$), low viscosity, and good thermal stability - its value was 2.51, 192 cps, and $299^{\circ}C$ (at 5% weight loss), respectively. The activation energies ($E_a$) of thermal-curing reaction calculated from Kissinger and Ozawa-Flynn-Wall method were 91~92 kJ/mol.

• The Korean Journal of Rheology
• /
• v.11 no.2
• /
• pp.135-142
• /
• 1999

The effects of 1 wt.% N-benzylpyrazinium hexafluoroantimonate (BPH) as a thermal latent initiator and blend compositions composed of 0, 5, 10, 20 and 40 wt.% of phenol-novolac resin to epoxy resin were investigated in terms of cure kinetics, thermal stabilities and rheological properties. Thermal latent properties of BPH were measured from the conversion as a function of reaction temperature on a dynamic DSC. This cationic BPH system turned out to be an effective thermal latent initiator in the epoxy-phenol curing system. And the increase of phenol-novolac resin concentration led to the decrease in the latent temperature and to the increase of cure activation energy ($E_a$) of the blend system. The thermal stability and activation energy ($E_t$) for decomposition, gel-time and activation energy ($E_c$) for cross-linking from rheometer increased within the composition range of 20~40 wt.% of phenol-novolac resin. This implies that the three-dimensional cross-linking may take place among hydroxyl group within phenol resin, epoxide ring within epoxy resin and BPH.

• Design & Manufacturing
• /
• v.7 no.1
• /
• pp.60-63
• /
• 2013

Recently, Silicone that one of the thermo-sets is used to making optical products such as LED lenses because of excellent thermal properties. LED lenses are required to keep the precise dimensions, so they must be molded to have the minimum deformation. Thermo-sets have the expansion characteristic on the part of thermal property, it is important to optimize the cure condition so that the deformation of the part become minimum. In this study, to investigate the relationship between the shrinkage by the curing and expansion by the thermal properties of the resin, reactive injection experiment was performed by setting the variables such as mold setting temperature, cure time. As a result, it was confirmed that there was a interval while the thermal properties were transferred to more active during the cure process. It is expected to help in determining the reactive injection molding conditions of the thermo-set parts as well as LED lens in order to reduce the amount of deformation.