• Journal of the Korean Ceramic Society
• /
• v.48 no.2
• /
• pp.160-167
• /
• 2011

Plasma sprayed ceramic coatings inherently contain pores and usually also cracks. Post-treatment of the plasma sprayed coatings is a way to close the connected pores and cracks. In this study, post-sealing treatment in plasma sprayed $Al_2O_3$ coatings was employed to overcome the reduction of coating properties. $Al_2O_3$ plasma thermal spray coating was made on aluminum alloys plate, $CrO_3$ post coating and heat treatment at $550^{\circ}C$ was carried out in order for final $Cr_2O_3$ to be saturated through phase transformation. Chromia sealing began at the fine defect in coated microstructure, while larger pores were permeated later. The increase in concentration and treatment frequency of sealing solution resulted in the decrease of porosity of coating layer, while cracks occurred partially after the third treatment. After twice treatment of 10M $CrO_3$ solution, microhardness and breakdown voltage of $Al_2O_3$ coatings were found to increase by ${\fallingdotseq}$ 50% and ${\fallingdotseq}$ 390% respectively than without post-treatment.

• Corrosion Science and Technology
• /
• v.11 no.1
• /
• pp.15-19
• /
• 2012

Both electrogalvanized and hot-dip galvanized steel sheets have been finally produced via organic-inorganic surface coating process on the zinc surface to enhance corrosion resistance and afford additional functional properties. Recently, POSCO has been developed a variety of chromate-free coated steels that are widely used in household, construction and automotive applications. New organic-inorganic hybrid coating solutions as chromate alternatives are comprised of surface modified silicate with silane coupling agent and inorganic corrosion inhibitors as an aqueous formulation. In this paper we have prepared new type of hybrid coatings and evaluated quality performances such as corrosion resistance, spot weldability, thermal tolerance, and paint adhesion property etc. The electrogalvanized steels with these coating solutions exhibit good anti-corrosion property compared to those of chromate coated steels. Detailed components composition of coating solutions and experimental results suggest that strong binding between organic-inorganic hybrid coating layer and zinc surface plays a key role in the advanced quality performances.

• Journal of Electrochemical Science and Technology
• /
• v.7 no.4
• /
• pp.263-268
• /
• 2016

This study describes the effect of coating the $Li[Ni_{0.8}Co_{0.15}Al_{0.05}]O_2$ cathode surface with a homogeneous carbon layer produced by carbonization of polyvinylidene fluoride (PVDF) as a novel organic source. The phase integrity of the above cathode was not affected by the carbon coating, whereas its rate capability and cycling performance were enhanced. Similarly, the cathode thermal stability was also improved after coating, which additionally protected the cathode surface against the reactive electrolyte containing hydrofluoric acid (HF). The results show that coating the $Li[Ni_{0.8}Co_{0.15}Al_{0.05}]O_2$ cathode with carbon using the PVDF precursor is an effective approach to enhance its electrochemical properties.

• Proceedings of the KAIS Fall Conference
• /
• 2010.11a
• /
• pp.478-481
• /
• 2010

Antimony doped tin oxide (ATO) nanoparticles were added as nanofillers to UV-curable polyester-acrylate (PEA) resin for coating to improve thermal, mechanical, and electrical properties. In this study, ATO nanoparticles were grafted by 3-glycidyloxypropyltrimethoxysilane and 3-methacryloxypropyltrimethoxysilane respectively to improve dispersion and interfacial adhesion. The physical properties and surface scratch hardness of the UV-curable nanocomposite coating were improved considerably by introducing the modified ATO nanoparticles.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2004.05a
• /
• pp.826-829
• /
• 2004

An increasing interest in fire safety engineering can currently be identified in Korea and overseas. The fire-resistant characteristics of spray coating material for fire protection with or without nano $Al(OH)_3$ colloid has been experimentally investigated and the results are presented in this paper. The fire-resistance characteristics of spray coating material with nano $Al(OH)_3$ were superior to those without $Al(OH)_3$. Especially, spray coating material with nano material showed that thermal characteristic in the early days was remarkably excellent.

• Proceedings of the Korean Ceranic Society Conference
• /
• 1986.12a
• /
• pp.211-225
• /
• 1986

Silicon carbide coating has been studied using a graphite substrate, a mixture of tetramethylsilane and hydrogen or argon at deposition temperature (T) of 950 to $1200^{\circ}C$ total pressure of 20 to 50 torr and carrier gas flow rate of 0 to 901/h. Deposition kinetic study has shown that a transition, from a surface reaction limited process to a diffusion limited one, takes place near $1100^{\circ}C$. Deposition rate depends directly upon the experimental parameters. The influence of the main process parameters is also discussed to relate the physiochemical properties of the coating to the deposition conditions.

• 한국신재생에너지학회:학술대회논문집
• /
• 2007.11a
• /
• pp.466-466
• /
• 2007

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2015.11a
• /
• pp.275-276
• /
• 2015

기존의 상용화된 Ni-Cr tie-coating 물질은 내열성 시험 후 강도가 저하되고, Cr 성분이 patterning후에 완벽하게 제거 되지 않아서 누설 전류를 만드는 단점을 갖고 있다. 따라서 이 연구에서는 기존의 Ni-Cr 과 삼원계 Ni-Cr-X(X는 Nb, V, Mo, Ti) 물질의 패터닝성과 내열성을 비교하였다.

• Journal of Information Display
• /
• v.5 no.4
• /
• pp.27-30
• /
• 2004

This paper investigates the effects of coating such as Invar (Fe-36% Ni), Fe-Ni Alloys and $WO_3$ on the doming property of aluminum killed (AK) shadow masks, which may be used for flat CPTs. Invar and Fe-Ni Alloys are deposited on AK shadow mask in plasma atmosphere and annealed. $WO_3$ is screen-printed on the deposited layer. The coating is observed to cause a decrease in the doming property of the shadow masks due to their lower thermal expansion coefficients and anti-doming properties.

• Journal of the Korean Ceramic Society
• /
• v.53 no.1
• /
• pp.81-86
• /
• 2016

The effect of substrate rotation speed on the phase forming behavior and microstructural variation of 8 wt% yttria ($Y_2O_3$) stabilized $ZrO_2$ (8YSZ) coatings as a thermal barrier coating has been investigated. 8YSZ coatings with $100{\sim}200{\mu}m$ thickness were deposited by electron beam-physical vapor deposition onto a super alloy (Ni-Cr-Co-Al) substrate with a bond coating (NiCo-CrAlY). The width of the columnar grains of the 8YSZ coatings increased with increasing substrate rotation speed from 1 to 30 rpm at a substrate temperature range of $900{\sim}950^{\circ}C$. In spite of the different growth behaviors of coatings with different substrate rotation speeds, the phases of each coating were not changed remarkably. Even after post heat treatments with various conditions of the coated specimens fabricated at 20 rpm, only a change of color was noticeable, without any remarkable change in the phase or microstructure.