• Journal of Technologic Dentistry
• /
• v.26 no.1
• /
• pp.41-48
• /
• 2004

Ti-20%Zr(-5%Cr) alloys not containing harmful Al and V were newly designed in order to reveal their possibility for dental casting and melted in an arc melting and casting furnace under Ar atmosphere. The corrosion resistance was studied by anodic polarization test. From the observation of anodic polarization behavior, it was found that the corrosion resistance was markedly increased by the addition of Cr. The corrosion resistance of Ti-20%Zr-5%Cr alloy was superior to that in Ti-6%Al-4%V alloy but almost similar to that in CP Ti using in market place today.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2000.04a
• /
• pp.704-709
• /
• 2000

This study is to test effects of sulfate attack on deterioration of cement mortar. Four tests have been carried out with four types of mortars mixed by ordinary portland cement and sulfate-resistant portland cement containing blast-furnace slag and fly-ash. It was immersed in sulfate solution for 7, 28, 91, and 180 days. from the test results, sulfate attack resistance of cement mortar was improved by admixtures (blast-furnace slag and fly-ash), sulfate-resistance portland cement mortar showed high resistance than ordinarily portland cement at compressive strength, and similar the resistance of sulfate attack with ordinarily portland cement mortar with admixtures.

• 한국연소학회:학술대회논문집
• /
• 2006.04a
• /
• pp.121-127
• /
• 2006

It has become inevitable to search for alternative fuels due to severe energy crisis these days. Use of alternative fuels, which are typically of lower quality, tends to increase environmental pollution, including formation of nitrogen oxides (NOx). In this paper performance of vacuum residue has been investigated experimentally as well as numerically in typical operating conditions of a furnace. Heat release reaction is modeled as sequential steps of devolatilization, simplified gas phase reaction and char oxidation as that for pulverized coal. Thermal and fuel NOx are predicted by conditional estimation of elementary reaction rates and are compared against measured experimental data. On the overall reasonable agreement is achieved for spatial distributions of major species, temperature and NOx for all test cases.

• Journal of Ceramic Processing Research
• /
• v.20 no.4
• /
• pp.363-371
• /
• 2019

In this study, physical properties of normal concrete, magnetite concrete, EAF concrete, and EAF concrete with added iron powder were evaluated and a feasibility of radiation shielding is also evaluated through irradiation tests against X-rays and gamma-rays. While the unit weight of EAF concrete (3.21 t/㎥) appeared lower than that of magnetite concrete (3.50 t/㎥), the results in compressive strength of EAF concrete were greater than those in magnetite and normal concrete. While the radiation transmission rate of normal concrete reaches 26.0% in the X-ray irradiation test, only 6.0% and 9.0% of transmission rate were observed in magnetite concrete and linear relationship with unit volume weight and radiation shielding. In the gamma-ray irradiation test, the performance of EAF and magnetite concretes appeared to be similar. Through the results on the excellent physical properties and radiation shielding performance a potential applicability of EAF concrete to radiation shielding was verified.

• International Journal of Concrete Structures and Materials
• /
• v.8 no.2
• /
• pp.157-164
• /
• 2014

Ground granulated blast-furnace slag (GGBS) is a green construction material used to produce durable concrete. The secondary pozzolanic reactions can result in reduced pore connectivity; therefore, replacing partial amount of Portland cement (PC) with GGBS can significantly reduce the risk of sulfate attack, alkali-silica reactions and chloride penetration. However, it may also reduce the concrete resistance against carbonation. Due to the time consuming process of concrete carbonation, many researchers have used accelerated carbonation test to shorten the experimental time. However, there are always some uncertainties in the accelerated carbonation test results. Most importantly, the moisture content and moisture profile of the concrete before the carbonation test can significantly affect the test results. In this work, more than 200 samples with various water-cementitious material ratios and various replacement percentages of GGBS were cast. The compressive strength, electrical resistivity, chloride permeability and carbonation tests were conducted. The moisture loss and microstructure of concrete were studied. The partial replacement of PC with GGBS produced considerable improvement on various properties of concrete.

• Journal of Technologic Dentistry
• /
• v.42 no.2
• /
• pp.73-79
• /
• 2020

Purpose: The aim of this study was to investigate the influence of short and long duration sintering on microstructure and flexural strength of zirconia. Methods: To conduct three-point bending test, Zirconia specimens are milled according to ISO 6872 guidelines(N=18, n=9 per group). Two specimens group(n=8) is sintered for 10 hours(Standard schedule) and 3 hours(Speed schedule) at the peak temperature of 1550℃ with silicon carbide sintering furnace. Flexural strength of specimens are measured by instron. After coating each specimen(n=1), microstructure of specimens is observed using Scanning Electron Microscope(SEM). T-test was utilized to statistically assess the data. Results: The mean and standard deviation value of the flexural strength for standard schedule group are 578.15±57.48Mpa, that of speed schedule are 465.9±62.34Mpa. T-test showed significant differences in flexural strength between two zirconia specimen group which applied standard schedule and speed schedule respectively(p<0.05). Conclusion: The result of this study showed that the increase in sintering time led to increased grain size, and also to a positive effect on the flexural strength.

• Proceedings of the Korean Institute of Resources Recycling Conference
• /
• 1996.04a
• /
• pp.11-43
• /
• 1996

• Proceedings of the Korean Radioactive Waste Society Conference
• /
• 2017.05a
• /
• pp.407-408
• /
• 2017

• Journal of the Korea Institute of Building Construction
• /
• v.15 no.6
• /
• pp.597-605
• /
• 2015

The method of concrete mix design used in this study aims to achieve the identical specified design strength, applying different types and replacement ratio of mineral admixtures and afterwards, fire tests were conducted using the standard time-temperature curve specified in the ASTM E119 to identify the influences of the types of mineral admixtures on the fire resistance performance of high strength concrete(HSC). The least spalling was observed in the test specimen containing blast furnace slag as a partial replacement of cement, while the most significant spalling phenomena were observed in the blast furnace slag test specimen that silica-fume was added in. In particular, the reasonable volume of spalling was observed when solely replaced by silica fume. However, the influence of the cement replacement by silica fume and blast furnace slag on the increases of spalling can be explained through blocked pores by the fine particles of silica fume, leading to decreases in permeability.

• Journal of the Korea Concrete Institute
• /
• v.25 no.5
• /
• pp.477-484
• /
• 2013

In this study, eleven reinforced concrete beams, ground granulated blast furnace slag, replacing recycled coarse aggregate (BRS series) and recycled coarse aggregate with steel fiber (BSRS series), and standard specimen (BSS) were constructed and tested under monotonic loading. Experimental programs were carried out to improve and evaluate the shear performance of such test specimens, such as the load-displacement, the failure mode and the maximum load carrying capacity. All the specimens were modeled in 1/2 scale-down size. Test results showed that test specimens (BSRS Series) was increased the compressive strength by 9%, the maximum load carrying capacity by 1~6% and the ductility capacity by 1.02~1.13 times in comparison with the standard specimen (BSS). And the specimens (BSRS Series) showed enough ductile behavior and stable flexural failure.