• Corrosion Science and Technology
• /
• v.13 no.5
• /
• pp.178-185
• /
• 2014

Alloy 617 is considered as a candidate Ni-based superalloy for the intermediate heat exchanger (IHX) of a very high-temperature gas reactor (VHTR) because of its good creep strength and corrosion resistance at high temperatures. Helium is used as a coolant in a VHTR owing to its high thermal conductivity, inertness, and low neutron absorption. However, helium inevitably includes impurities that create an imbalance in the surface reactivity at the interface of the coolant and the exposed materials. As the Alloy 617 has been exposed to high temperatures at $950^{\circ}C$ in the impure helium environment of a VHTR, the degradation of material is accelerated and mechanical properties decreased. The high-temperature strength, creep, and corrosion properties of the structural material for an IHX are highly important to maintain the integrity in a harsh environment for a 60 year period. Therefore, an alloy superior to alloy 617 should be developed. In this study, the mechanical and high-temperature corrosion properties for Ni-Cr alloys fabricated in the laboratory were evaluated as a function of the grain boundary strengthening and alloying elements. The ductility increased and decreased by increasing the amount of Mo and Cr, respectively. Surface oxide was detached during the corrosion test, when Al was not added to alloy. However the alloy with Al showed improved oxide adhesive property without significant degradation and mechanical property. Aluminum seems to act as an anti-corrosive role in the Ni-based alloy.

• Journal of the Korean Geotechnical Society
• /
• v.24 no.8
• /
• pp.43-52
• /
• 2008

In this study, the verification test and creep test for both a single-rebar nail and a multi-rebar nail are carried out to investigate a tensile strength for both nails. The adhesion effects between a rebar and a cement grout, a mobilized frictional force induced by pull-out load, and load transfer characteristics are examined. The results obtained from the field pull-out tests and from the numerical analysis using $FLAC^{2D}$ which is one of the programs developed based on the finite difference method are analyzed and compared for a single-rebar nail and a multi-rebar nail. The field pull-out test results for a multi-rebar nail relative to a single-rebar nail show that a tensile failure load is relatively large and the pull-out loads are well transferred to the ground in deep depth.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 1999.03b
• /
• pp.180-183
• /
• 1999

It is well known that Fe3Al intermetallic compound shows an anomalous peak of the yield strength at about 50$0^{\circ}C$ and then decrease at higher temperatures The dislocation structure was examined by transmission electron microscopy and high temperatures. The dislocation structure was examined by transmission electron microscopy and high temperature mechanical properties were examined by tensile and load relaxation tests. The flow stress curves obtained from load relaxation tests were then analyzed in terms of internal variable deformation theory. it was found that the flow curves consisted of three micro-deformation mechanisms -i. e inelastic deformation mode plastic deformation mode and dislocation creep deformation mode depending on both dislocation structure and deformation temperature. The flow curves could be well described by the constitutive equations of these three micro-deformation mechanisms based on the internal variable deformation theory.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.221-222
• /
• 2007

The test method on materials of electrical power cable are used in accordance with 18 specifications of IEC, ICEA, KS and KEPCO Spec. The validation of test methods were checked and established by solving the problems occurred during the test. These tests are tensile strength, hot creep, shrink back, environmental stress cracking, flammability, oxygen index, absorption coefficient, differential scanning calorimetry, amount of ion in semiconductor, void, amber, contaminant and water tree etc. The performance test of power cable made by A, B, C, D company were evaluated and compared.

• 연구논문집
• /
• s.33
• /
• pp.167-174
• /
• 2003

Alloy 713LC was developed to improve the tensile strength and ductility by reducing the carbon content of Alloy 713C. As Alloy 713LC was designed to minimize the mechanical property change with process conditions, it is generally utilized in the parts which have thick and thin sections simultaneously. In the thick and the thin sections, quite different properties are required. Consequently it is essential to crucially control the local mechanical properties of a parts by optimizing the process condition and heat treatment. In this research, high temperature mechanical properties including creep-rupture and strain-control low cycle fatigue were investigated together with the microstructural variations with heat treatment. Failure mechanism was also analyzed by observing the fracture surface to correlate the variation of mechanical properties with the microstructural change.

• Nuclear Engineering and Technology
• /
• v.53 no.7
• /
• pp.2295-2303
• /
• 2021

To investigate wall-thinning impact on axial load resistance of Zircaloy-4 cladding rods after a LOCA transient, axial tensile samples have been machined on as-received tubes with reduced thicknesses between 370 and 580 ㎛. After high temperature oxidation under steam at 1200 ℃ with measured ECR ranging from 10 to 18% and water quenching, machined samples were axially loaded until fracture. These tests were modeled using a fracture mechanics approach developed in a previous study. Fracture stresses are rather well predicted. However, the slightly lower fracture stress observed for wall-thinned samples is not anticipated by this modeling approach. The results from this study confirm that characterizing the axial load resistance using semi-integral tests including the creep and burst phases was the best option to obtain accurate axial strengths describing accurately the influence of wall-thinning at burst region.

• Elastomers and Composites
• /
• v.43 no.2
• /
• pp.113-123
• /
• 2008

Epoxy resins are thermoset polymers that exhibit good adhesion, creep resistance, heat resistance, and chemical resistance. These polymers, however, give poor resistance to crack propagation and low impact strength. In this study, epoxy/carboxyl-terminated butadiene acrylonitrile (CTBN) and epoxy/amine-terminated butadiene acrylonitrile (ATBN) composites were prepared with different ratio of CTBN and ATBN to improve low impact strength of epoxy resin. The impact strength of epoxy/elastomeric composites shows high values with increasting nonpolar surface free energy while the tensile strength and the glass transition are decreased. The highest surface free energy, impact strength observed when 15 phr CTBN and 15 phr ATBN added, respectively. It can be concluded that as liquid rubber to improve impact strength of epoxy resin, ATBN is more preferable to CTBN.

• International Journal of Precision Engineering and Manufacturing
• /
• v.9 no.2
• /
• pp.63-68
• /
• 2008

Hard and brittle materials, such as Ni- and Ti-based alloys, glass, and ceramics, are very useful in aerospace, marine, electronics, and high-temperature applications because of their extremely versatile mechanical and chemical properties. One Ni-based alloy, Inconel 718, is a precipitation-hardenable material designed with exceptionally high yield strength, ultimate tensile strength, elastic modulus, and corrosion resistance with outstanding weldability and excellent creep-rupture properties at moderately high temperatures. However, conventional machining of this alloy presents a challenge to industry. Ultrasonic vibration cutting (UVC) has recently been used to cut this difficult-to-machine material and obtain a high quality surface finish. This paper describes an experimental study of the UVC parameters for Inconel 718, including the cutting force components, tool wear, chip formation, and surface roughness over a range of cutting conditions. A comparison was also made between conventional turning (CT) and UVC using scanning electron microscopy observations of tool wear. The tool wear measured during UVC at low cutting speeds was lower than CT. UVC resulted in better surface finishes compared to CT under the same cutting conditions. Therefore, UVC performed better than CT at low cutting speeds for all measures compared.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• v.y2004m10
• /
• pp.77-81
• /
• 2004

The massive structures are not free to move with vibration, differential settlement, thermal stresses because, construction and expansion joint, crack etc., can be large enough to cause leakage as deformation of waterproofing. It has been depended on the test method of tensile/tear strength which is waterproofing performance as behavior of concrete structure crack. However, not to practically confirm the creep applied to concrete surface, even waterproofing membrane have more performance than definite strength and elasticity. Therefore, in this study will focus on the test method to consider a resistance performance about loose adhesion and deformation of waterproofing and behavior of concrete structure as construction/expansion joint, crack. Performance test method on the influence as behavior of concrete structure crack is to choose waterproofing materials and construction method which possible to confront with behavior of 50mm crack in the atmosphere and low temperature. Examine the deformation of waterproofing membrane and loose adhesion which can occur to structure in general job site, suggest standard testing method to analyze correlation waterproofing membrane and structure with 5-types of materials used in this study, such as Adhesion membrane and sheet complex, sheet and urethane complex, self-adhesive sheet, spray poly-urea, spray membrane of rubberized Asphalt.

• Journal of Welding and Joining
• /
• v.32 no.3
• /
• pp.102-107
• /
• 2014

Boiler equipment in power plant is always being operated in harsh conditions and severely exposed to the extreme environment of high temperature. Therefore periodically the state of devices should be checked, diagnosed, and analyzed to ensure the reliability of the equipment. Traditionally, such a diagnosis is based one or two physical properties of the sample taken from the equipment like hardness, microstructure, etc.. However, to enhance the confidence of the diagnosis, it is necessary to synthesize those properties together. This paper is to propose such a synthetic procedure for SA213-T12(1Cr-0.5Mo) which was developed to be used in $565^{\circ}C$ below condition. Creep test and accelerated degradation test were performed simultaneously, and the physical properties such as microstructure, tensile strength, yield strength, hardness, and indentation properties were measured. This paper proposes a method of determining the remaining life by quantitative comparison. It will provide the basis of evaluating life assessment more objective and reliable.