• Journal of the Korean Applied Science and Technology
• /
• v.31 no.2
• /
• pp.296-304
• /
• 2014

For this research, prepared polyurethane dispersion of hard segment type and polyethylene emulsion wax. Use these resin, this article has been analyzed about mechanical properties variation by increasing amount of polyethylene emulsion wax on Lam skin leather and dried film. According to measure data for solvent resistance, PUD had good property. As known in the results, increase of polyethylene wax constant did not influence to big variation of hybrid resin properties. As test of tensile strength, PUD had good tensile characteristic($1.235kg_f/mm^2$) and PUD-EW4 had lowest tensile characteristic($1.022kg_f/mm^2$). As same as tensile characteristic, abrasion test determined PUD(52.225 mg.loss) had highest properties. In elongation case, PUD showed 698 % modulus which was best properties in this experiment.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.19 no.3
• /
• pp.42-50
• /
• 2020

This study explores the effects of repair width on the deposition characteristics and mechanical properties of stainless steel samples repaired using direct energy deposition (DED). In the DED repair process, defects such as pores and cracks can occur at the interface between the substrate and deposited material. In this study, we changed the width of the pre-machined zone for repair in order to prevent cracks from occurring at the inclined surface. As a result of the experiment, cracks of 10-40 ㎛ in length were formed along the inclined slope regardless of the repair width. Yield and tensile strength decreased slightly as the repair width increased, but the total and uniform elongation increased. This is due to the orientation of the crack. For specimens with a repair width of 20 mm, yield and tensile strength were 883 MPa and 1135 MPa, respectively. Total and uniform elongations were 14.3% and 8.2%, respectively. During observation of the fracture specimens, we noted that the fracture of the specimen with an 8 mm repair width occurred along the slope, whereas specimens with 14 mm and 20 mm repair depths fractured at the middle of the repaired region. In conclusion, we found that tensile properties were dependent upon the repair width and the inclination of the crack occurred at the interface.

• Journal of the Korean Society for Heat Treatment
• /
• v.5 no.2
• /
• pp.103-110
• /
• 1992

This study is aimed to investigate the effect of various thermomechanical treatments($T_6$, $T_8$ and ITMT) on the microstructure and mechanical properties of an Al-Cu-Li-Ag-Mg-Zr alloy (Weldalite 049) which has been known to strong natural aging response, good weldablity and high strength in $T_6$ sand $T_8$ temper. This experiment was performed by means of differential scaning calorimetry, tensile test, optical and transmission electron microscopy. The tensile strength in the peak aged condition shows 620, 650 MPa in $T_6$ and $T_8$(40% cold work), respectively. Also, The tensile strength is increased with cold working in $T_8$ but decreased at 60% cold working. However, the tensile strength of the intermediate thermomechanical treated speciman(ITMT) is lower than that of $T_6$ temper about 20% but the elongation is higher than two times. It might be predicted that the ITMT is effective processing to improve the toughness of this alloy. In $T_6$, $T_8$ and ITMT, the major strengthening phase is $T_1(Al_2CuLi)$ phases. and the fine $T_1$ phase which are homogeneously precipited in matrix was observed much more in $T_8$ than $T_6$ and ITMT.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.16 no.4
• /
• pp.69-78
• /
• 2012

This paper study on the physical property of naturally vulcanizing waterproofing synthetic rubber sheet for the underground concrete wall. In order to finding the naturally vulcanizing time, the relation of vulcanizing time and tensile strength is analysed from non-vulcanizing to naturally vulcanizing time. Physical tests such as tensile strength, tear strength: etc., under the thermal environment temperature at $-20^{\circ}C$, $-10^{\circ}C$, $20^{\circ}C$, $60^{\circ}C$. The result of experiment show that the developed rubber sheet has the delay time about 85 days and the curing time about 35 days. The tensile strength increased by about 692% and coefficient of expansion decreased by about 10% which value can be sufficiently compensate the demerit of vulcanized rubber sheet. Also, all of the physical properties of the naturally rubber sheet satisfy the KS standard and compare to the vulcanized rubber sheet, the developed naturally rubber sheet have excellent durability.

• Journal of the Society of Naval Architects of Korea
• /
• v.55 no.3
• /
• pp.205-214
• /
• 2018

This paper deals with the experimental study on the hygrothermal ageing effect to the strength of Carbon Fiber Reinforced Plastics (CFRP) materials for marine leisure boat manufactured by vacuum assisted resin infusion method. The experiments performed consist of tensile, flexural and shear tests according to American Society for Testing and Materials (ASTM) and Korean Industrial Standards (KS) test methods. Test coupons are varied from uni-directional(UD, $0^{\circ}$, $90^{\circ}$), Bi-Directional (BD), and Double-Bias (DB) carbon fiber fabrics in conjunction with epoxy resin. The results of tensile test show that tensile strength reduces significantly while not the same degree of reduction is observed for elasticity modulus with respect to the existence of hygrothermal ageing effect. This implies that the tensile strain induced from external load holds steady values but ultimate strength values change widely under hygrothermal ageing effect. In case of the flexural test, $0^{\circ}$ UD shows more strength reduction than $90^{\circ}$ UD while BD has reduced values in both flexural strength and elasticity modulus under hygrothermal ageing effect. It is learned that the bending strain induced from external load and ultimate strength values are reduced with respect to hygrothermal ageing effect. Shear test performed only on DB materials, and the results show marginal reduction in ultimate strength and moderate reduction in elasticity modulus. This means that the shear strain varies more than ultimate shear strength with respect to hygrothermal ageing effect. The experiment conducted in this paper clearly demonstrates the differences in material properties of the CFRP for the consideration of hygrothermal ageing effect. Findings obtained from this experimental study can serve as a fundamental input data for the realistic structural responses of marine leisure boat built in CFRP materials.

• Carbon letters
• /
• v.5 no.1
• /
• pp.18-22
• /
• 2004

The failure behaviours of unidirectional pultruded carbon fiber reinforced polymer (CFRP) composites were monitored by the electrical resistance measurement during tensile loading, three-point-bending, interlaminar shear loading. The tensile failure behaviour of carbon fiber tows was also investigated by the electrical resistance measurement. Infrared thermography non-destructive evaluation was performed in real time during tensile test of CFRP composites to validate the change of microdamage in the materials. Experiment results demonstrated that the CFRP composites and carbon fiber tows were damaged by different damage mechinsms during tensile loading, for the CFRP composites, mainly being in the forms of matrix damage and the debonding between matrix and fibers, while for the carbon fiber tows, mainly being in the forms of fiber fracture. The correlation between the infrared thermographs and the change in the electrical resistance could be regarded as an evidence of the damage mechanisms of the CFRP composites. During three-point-bending loading, the main damage forms were the simultaneity fracture of matrix and fibers firstly, then matrix cracking and the debonding between matrix and fiber were carried out. This results can be shown in Fig. 9(a) and (b). During interlaminar shear loading, the change in the electrical resistance was related to the damage degree of interlaminar structure. Electrical resistance measurement was more sensitive to the damage behaviour of the CFRP composites than the stress/time curve.

• Journal of Welding and Joining
• /
• v.26 no.5
• /
• pp.49-59
• /
• 2008

Hastelloy C-276, corrosion resistant alloy at high temperature, is used in chemical plant and power generation industry. In this study, process parameter of laser welding for welding property in Hastelloy C-276 using a continuous wave Nd:YAG laser was studied. As the result of experiment, laser welding did not show segregation or crack at heat affected zone compared to conventional GTWA welding. The melting zone showed cell dendritic structure along with welding line. In addition, planer front solidification is occurred from welding structure, and it was progressed to cellular solidification. Optimal process parameter for butt welding was 1.2kW and 2.0 m/min for laser power and welding speed, respectively. While heat input, output density, tensile stress, and longitudinal strain was $441.98{\times}103$ J/cm2, $29.553{\times}103$ W/cm2, 768 MPa, and 0.689, respectively. Lap welding of the same material showed greater discrepancy in tensile property during 1 line and 2 line welding. For 1 line welding, tensile stress was about 320 MPa, and 2 line showed slightly larger tensile stress. However, strain was decreased by 20%. From this result, lap welding of the same material, Hastelloy C-276, with 2 line welding is considered to be more effective process than 1 line welding with consideration of mechanical property.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.14 no.7
• /
• pp.3562-3569
• /
• 2013

The performance of concrete structure decreases with change in time and the external environment. In order to reinforce the structure, the research about new material development and application of newly developed materials are widely conducted. In the case of composite FRP, it received good attention in the academia due to its high intensity-weight ratio, excellent corrosion resistency as well as good workability. When applying at the construction field, however, the utilization of FRP did not increase as much due to lack of reliability and design standard. Current study investigated the material characteristics during the temperature change at high temperature and the structural behavior from restraint effect for GFRP reinforcing materials. Two experimental variables were set in this study: GFRP reinforcements due to tensile properties of temperature and restraint compression effects. Three concrete specimen were selected for each set temperatures. For this reason, as a variable to experiment with the effects confined compression concrete members value and tensile properties with temperature reinforcement GFRP, experiment produced three pieces each for each set temperature, the concrete specimen, which is confined in the GFRP was selected each I did. For the temperature change during the experiment, the concrete specimen were mounted in order to expose to experimental high temperature for certain period of time. For compression performance evaluation, reinforcement effect from horizontal constraint of the fiber were measured using an Universal Material Testing Machine (UTM). Finally, this study revealed that the binding characteristics of GFRP materials from temperature change decreased. Also, this study showed that the maximum compression intensity decreased as the temperature increased up to $150^{\circ}C$ in the constraints ability of the GFRP reinforcements during the horizontal constraint of concrete.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.5 no.2
• /
• pp.91-96
• /
• 2010

The purpose of this study is to find problems about pedestrian road of tourist resort and to make new type of sidewalk pavement with wood chip and binder using urethane resin on the parks and tourist resort. The wood chip pavement has new economics and durability with comfortable texture. Samples of these pavement materials were tested for tensile strength, permeability and ball rebound value. Also, after immersion for 24 hours, tensile strength, samples' thickness and weight were measured and discussed the strength reduction according to the water immersion. Tensile strength experimentation was examined on dry condition and water immersion. The result of examination on dry condition was 1.06MPa and on water immersion was 0.67MPa. The results showed 36.8% decreasing rate of tensile strength. Permeability experiment test based on field permeability method of pavement were conducted as a result, permeability coefficients were in the range of 0.67~0.78mm/s that all exceeds object permeability coefficient. Elasticity experiment was based on elasticity test method of Japan road association. GB coefficient was 21% and SB coefficient was 10%. GB coefficient and SB coefficient increased if fine aggregate were increased.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.30 no.5
• /
• pp.471-478
• /
• 2010

Thin films play an important role in many technological applications including microelectronic devices, magnetic storage media, MEMS and surface coatings. It is well known that a thin film's material properties can be very different from the corresponding bulk properties and thus there has been a strong need for the development of a reliable test method to measure the mechanical properties of a thin film. We have developed an alternative and convenient test method to overcome the limitations of previous membrane deflection experiment and uniaxial tensile test by adopting a white light interferometer having sub-nanometer out-of-plane displacement resolution. The freestanding aluminium specimens are tested to verity the effectiveness of the test method developed and get the tensile properties. The specimens are 0.5 rum wide, $1{\mu}m$ thick and fabricated through MEMS processes including sputtering. 1 to 5 specimens are fabricated on Si dies. The membrane deflection experiments are carried out by using a homemade tester consisted of a motor-driven loading tip, a load cell, and 6 DOF alignment stages. The test system is compact enough to set it up beneath a commercial white light interferometric microscope. The white light fringes are utilized to align a specimen with the tester. The Young's modulus and yield point stress of the aluminium film are 62 GPa and 247 MPa, respectively.