• Fashion & Textile Research Journal
• /
• v.14 no.4
• /
• pp.635-640
• /
• 2012

In this study, thermoplastic urethane (TPU) coating yarns were prepared at various extruding temperatures. The fine structure and mechanical properties of resultant TPU coating yarns examined by the wide angle X-ray diffractometer (WAXD), differential scanning calorimetry (DSC), dynamic mechanical thermal analysis (DMTA), and tensile test. TPU coating yarns (prepared at extruding temperatures at $175^{\circ}C$) were confirmed as a stable fine structure that obtained excellent tensile strength and flexibility. The C samples prepared by optimized conditions made by TPU woven floor mat. The structure of the woven mat is $4{\times}4$ basket weave and have laminated with the EVA foam to obtained final TPU woven floor mat products. The resultant TPU woven floor mat was obtained to 1.5MN of tensile strength, 22% of the elongation, and 0.2MN of tear strength. The weight loss abrasion and the resilience by the ball rebound of the TPU-woven floor mat was prior to those of the PVC subsequently, we were able to develop a woven floor mat with TPU coating yarn and produce an eco-friendly high valuable woven floor mat using an interior product.

• Textile Coloration and Finishing
• /
• v.35 no.1
• /
• pp.20-28
• /
• 2023

In this study, TPU resin for coating was prepared by varying the mixing ratio of antistatic TPU and recycled TPU to manufacture permanent antistatic materials. The coated yarn was prepared by coating on the nylon yarn, and then the thermal, rheological, mechanical properties and antistatic properties were analyzed. In addition, antistatic properties and durability were confirmed after manufacturing UD fabrics using coated yarns. The mixing ratio of antistatic TPU and recycled TPU was most appropriate at 4:6, and the antistatic property had a surface resistance of 2.20 × 10⁹ Ω and a static charge of 398 V. In the coating process, the coating speed was most appropriate at 0.21 m/s, and the surface resistance of the UD fabric manufactured with the coated yarn manufactured under this condition was 6.80 × 10⁹ Ω and the static charge was 484 V. The UD fabric had a surface resistance of 7.21 × 10⁹ Ω and a static charge of 517 V after washing 10 times, and it was confirmed that the permanent antistatic property was excellent.