• Journal of the Mineralogical Society of Korea
• /
• v.29 no.1
• /
• pp.11-22
• /
• 2016

The black fault gouge having 5-10 cm width occurs at the center of the fault fracture zone developed at the early Miocene basaltic rocks that is located at the Geumkwang-ri area in Donghae-myeon, Pohang city. The fault gouge was analyzed with XRD, FTIR, DTA/TGA, SEM, TEM, XRF, EPMA. Analyses reveal that the fault gouge is Fe-rich sepiolite having high iron content. Alteration minerals observed in the fault fracture zone are mainly smectite. The significant amount of smectite also observed in the basaltic parent rocks. The occurrence of constituent minerals indicates that the Fe-rich sepiolite was crystallized by faulting and hydrothermal alteration after the consolidation of basaltic rock at the deep place.

• Polymer(Korea)
• /
• v.39 no.1
• /
• pp.180-184
• /
• 2015

PP-grafted GO was prepared by the reaction of graphene oxide (GO) containing 2-bromoisobuyryl groups and polypropylene (PP) having hydroxyl groups (PP-OH) via a "grafting-to" method. GO-Br was synthesized by the reaction of GO and 2-bromoisobutyryl bromide under a basic condition. PP-MAH was reacted with ethanolamine to produce PP-OH. The melting temperature of PP-grafted GO was shifted to the higher temperature than that of PP-OH. Also, the thermal stability of PP-grafted GO was increased as compared to PP-OH and GO. These results demonstrated that the grafted coating polymer PP was effective for enhancing the thermal stability of GO. The higher surface roughness of PP-grafted GO was resulted from the chemical attachment of PP on the surface of GO. The characterization of PP-grafted GO was conducted from Fourier transform infrared spectroscopy (FTIR), Raman spectroscopy, differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), and scanning electron microscope (SEM).

• Polymer(Korea)
• /
• v.36 no.6
• /
• pp.816-821
• /
• 2012

In this study, silane-crosslinked proton exchange membranes were prepared by step-wise radiation grafting of styrene and 3-(trimethoxysilyl)propyl methacrylate (TMSPM) onto an poly(ethylene-co-tetrafluoroethylene) (ETFE) film and followed by sol-gel processing and sulfonation. The sequentially grafted films with styrene to provide the proton conductivity and TMSPM to form the crosslinked structure were prepared by different grafting order. The structural changes and thermal properties of the prepared films were investigated by FTIR and TGA, respectively. After the introduction of sulfonic acid functional groups, the distributions of sulfonic acid group and silicon atoms at the inside of the sulfonated membranes were analyzed by SEM-EDX.

• Applied Chemistry for Engineering
• /
• v.29 no.3
• /
• pp.264-269
• /
• 2018

PSf/D2EHPA/TBP/CNTs beads were prepared by immobilizing carbon nanotubes (CNTs) and two extractants, di-(2-ethylhexyl)-phosphoric acid (D2EHPA) and tributyl phosphate (TBP) on polysulfone (PSf). The prepared PSf/D2EHPA/TBP/CNTs beads were characterized by SEM, TGA, and FTIR. The removal rate of Sr(II) by PSf/D2EHPA/TBP/CNTs beads was well described by the pseudo-second-order kinetic model. The maximum removal capacity of Sr(II) obtained from Langmuir isotherm was found to be 5.52 mg/g. The results showed that the removal efficiency of Sr(II) by PSf/D2EHPA/CNTs beads prepared in this study was significantly improved compared to that of using PSf/D2EHPA/CNTs beads without TBP.

• Polymer(Korea)
• /
• v.31 no.1
• /
• pp.86-91
• /
• 2007

Polydimethylsiloxane branched HEMA (SH) was Prepared by reacting polydimethylsilorane prepolymer and 2-hydroxyethyl methacrylate (HEMA). Polyacrylate modified Polyorganosiloxane (SMPA) was prepared by polymerization of methacrylic acid(MA), allyl glycidyl ether(AGE), aminopro- pyltrimethoxysilane (APTS), and SH. Their structures were confirmed by the measurement of FTIR and $^1H-NMR$ and thermal properties of SMPA were studied from TGA. Residual weight of SMPA at $400^{\circ}C$ increased according to increasing content of the APTS to 63 from 55%. SMPA sealant was prepared by adding additives, such as viscosity increasing agent, crosslinking agent, and fillers. Adhesion characteristics of SMPA-3 sealant was determined to be maximum load elongation, 2.01 %, and break load elongation, 2.28%. Adhesion characteristics for SMPA sealant prepared from SMPA-3 were better than those for SMPA sealant prepared from SMPA-1 and SMPA-2.

• Polymer(Korea)
• /
• v.38 no.3
• /
• pp.378-385
• /
• 2014

Multiwall carbon nanotubes (MWCNTs) were modified with a water soluble polymer, poly(vinyl alcohol), PVA, using a simple ultrasonic wave in water. Under the irradiation of ultrasound, PVA chains were severed as macroradicals and instantly grafted onto the surface of MWCNTs due to the radical scavenging effect of MWCNTs. To control the grafting PVA onto MWCNTs, the ultrasonication power and irradiation time were changed from 300 to 500 W and from 10 to 50 min, respectively. The grafted PVA onto MWCNTs was confirmed by FTIR, TGA, SEM, and TEM. Dispersion stability of the modified MWCNTs was monitored by Turbiscan. The amount of grafted PVA on MWCNTs increased with the increase in the sonication power and irradiation time. The grafted PVA on MWCNTs induced the improved dispersion stability of the modified MWCNTs in water. These findings exhibit that ultrasound can be readily used for the grafting polymer chains on MWCNTs.

• Polymer(Korea)
• /
• v.34 no.6
• /
• pp.495-500
• /
• 2010

Crosslinked PI films were synthesized from 4,4'-(hexafluoro isopropylidene)diphthalic anhydride (6FDA) and bis[4-(3-aminophenoxy) phenyl] sulfone(BAPS) with various ratios of the reactive monomer cis-4-cyclohexene-1,2-dicarboxylic anhydride(CDBA). We prepared crosslinked poly(amic acid) (PAA) using a 0.1 wt% Grubbs catalyst as a crosslinking agent. The crosslinked PAA was heat-treated at different temperatures to give PI films. The thermo-mechanical properties and optical transparency of the PI films were investigated. The thermal properties of the PI films were examined using Fourier transform infrared (FTIR) spectroscopy, differential scanning calorimetry(DSC), thermogravimetric analysis(TGA), thermo-mechanical analysis(TMA), and universal tensile machine(UTM), and their optical transparencies were investigated using UV-vis. spectrophotometry. The thermomechanical properties of the PI films improved with increasing CDBA content. However, the optical transparency of the PI films decreased slightly with increasing CDBA content.

• Journal of Korean Society of Environmental Engineers
• /
• v.29 no.7
• /
• pp.810-819
• /
• 2007

Investigation of alkali activation of fly ash and blast furnace slag was carried out using waterglass and sodium hydroxide. XRD, FTIR, $^{29}Si$ and $^{27}Al$ NMR, TGA and SEM were used to observed the reaction products and microstructure of the fly ash/slag cement (FSC) pastes. The reaction products were amorphous or low-ordered calcium silicate hydrate and aluminosilicate gel produced from alkali activation of blast furnace slag and fly ash, respectively. On the basis of this investigation, waterglass solution with a modulus(Ms) of 1.0 and 1.2 is recommended for alkali activation of fly ash and blast furnace slag. Morphology of FSC pastes alkali-activated with Ms of 1.0 and 1.2 shows a more solid and continuous matrix due to restructuring of gel-like reaction products from alkali-activated fly ash and blast furnace slag together with another hydrolysis product(i.e., silica gel) from water glass.

• Polymer(Korea)
• /
• v.34 no.5
• /
• pp.464-468
• /
• 2010

In this study, a vinylbenzyl chloride (VBC) monomer was successfully grafted onto the several fluoropolymer films including poly(tetrafluoroethylene-co-hexafluoropropylene) (FEP), poly(tetrafluoroethylene-co-perfluoropropylvinyl ether) (PFA), and poly(ethylene-co-tetrafluoroethylene) (ETFE) films by using a simultaneous irradiation method. The results indicated that PVBC graft polymer can be easily grafted onto the ETFE film than other fluorinated films under the same irradiation condition. The grafted films were characterized by using FTIR, TGA, and SEM-EDS instruments. The elongation at the breaking of the grafted films was found to decrease with an increase of degree of grafting (DOG). The PVBC-grafted ETFE films were found to have better mechanical properties than other PVBC-grafted fluorinated films.

• Korean Chemical Engineering Research
• /
• v.53 no.1
• /
• pp.83-90
• /
• 2015

In this study, we investigated optimum conditions for the introduction of a lot of free radical polymerizable methacrylate groups on the multi-walled carbon nanotube (MWCNT) surface. Carboxyl groups were introduced first on MWCNT surfaces by treating with a mixture of sulfuric acid and nitric acid with ultrasonic bath for 2 hours, and oxidized MWCNTs were reacted further with thionyl chloride followed by triethylenetetramine (TETA) to introduce amino groups on the oxidized MWCNT surface, to make MWCNT-$NH_2$. To introduce free radical polymerizable methacrylate groups on the MWCNT-$NH_2$, MWCNT-$NH_2$ was reacted with 3-(acryloyloxy)-2-hydroxypropyl methacrylate (AHM) by Michael addition reaction. We investigated progress of modification reactions for MWCNT by fourier transform infrared spectroscopy (FTIR), thermogravimetric analysis (TGA) and elemental analysis (EA). We found maximum degree of Michael addition reactions between AHM and TETA grafted on MWCNT-$NH_2$ for 10:1 mol ratio and 8 hour reaction time in our reaction conditions.