• Journal of the Korea Institute of Building Construction
• /
• v.20 no.4
• /
• pp.313-319
• /
• 2020

In this study, in order to confirm the applicability of Hollow Glass Powder(HGP) in 70MPa-class high strength concrete, the fresh and hardened states were examined according to the amount of HGP, and the results are as follows. The flow characteristics showed that the slump flow increased slightly as the amount of HGP was increased, and the T500 was slightly shortened as the amount of HGP was increased, and the rebar passing ability was improved due to the ball bearing effect of HGP. In particular, it showed the best rebar passing ability at a usage of 1.0kg/㎥. The use of HGP 1.0kg/㎥ resulted in a 40% reduction in plastic viscosity, but the viscosity increased at 2.0kg/㎥. Through experiments, it was confirmed that HGP was helpful in improving the workability of high-strength concrete, and the usage of 1.0kg/㎥ is considered to be the most appropriate. It was confirmed that HGP does not affect concrete compressive strength.

• Journal of the Korean Ceramic Society
• /
• v.38 no.9
• /
• pp.817-821
• /
• 2001

A new $Mg_{2-x}MN_xSnO_4$ phosphor with an inverse spinel structure was synthesized by the solid-state reaction technique. The photoluminescence properties of the $Mg_2SnO_4$:Mn phosphors were investigated under 147nm -vacuum ultraviolet ray excitation. The Mn-doped $Mg_2SnO_4$ phosphor exhibited high emission intensity with the spectrum centered at 500nm wavelength. It was explained that the green emission in $Mg_2SnO_4$:Mn phosphor has originated from energy transfer from $^4T_1$ to $^6A_1$ of $Mn^{2+}$ ion at tetrahedral site of the spinel structure. The $Mn^{2+}$ ion concentration exhibiting the maximum emission intensity under the excitation of 147nm-vacuum ultraviolet ray was 0.25mol%. And the decay time of the phosphor was shorter than 10ms.

• Journal of Digital Contents Society
• /
• v.19 no.7
• /
• pp.1297-1302
• /
• 2018

Propose of this study was to compared and analyzes the cranking between the newly developed hand cycle prototype and the hign-end hand cycle that are sold on the market for the disabled athletes. For this study, 10 male subjects, who had the same type of disability, were selected from the Korea Disabled Cycle Federation. 12 infrared camera(Oqus-500) was utilized to acquire the subjects' kinematic data. we have analyzed the data of 30 seconds - 15 seconds before and after cranking. SPSS 16 was used for a statistical verification and the difference of the sports biomechanical variable between RX and the prototype was verified by utilizing pared samples t-test. The significance level at the time of the experiment was ${\alpha}=.05$. The results show that there is a need to design the hand cycle crank in a curve shape to lessen the muscle fatigue that is measured the highest between the angle of 180 to 195. In addition, comparative analysis between the existing data and the data of modified crank must be researched since the hand cycle cranking is one of the main variables in performance enhancement.

• Korean Journal of Microbiology
• /
• v.27 no.1
• /
• pp.63-69
• /
• 1989

A pink-pigmented facultative methylotrophic bacterium, Methylobacterium sp. strain SY1, was isolated from soil through methanol-enrichment culture technique. The isolate was gram-negative, slightly curved rod, and motile by a single polarly inserted flagellum. The colony was smooth, bright pink, and slimy. The guanine plus cytosine content of the KNA was 66%. The cell was obigately aerobic and exhibited both catalase and oxidase activities. Carotenoid pigment and poly-$\beta$-hydroxybutyrate were present. It was found to have three kinds of plasmid with molecular weights 45,000, 38,500 and 23,000. Growth with methanol(0.5%) was fast ($t_{d}$=6.5h) and was optimal at $30^{\circ}C$ and at pH 7.0. The isolate could grow on several sugars, organic acids, amino acids, amines, and alcohols in addition to the methanol. Methanol was found to be assimilated through the serine pathway.

• Korean Journal of Crystallography
• /
• v.9 no.1
• /
• pp.15-20
• /
• 1998

Single crystals of lithium heptaborate, Li3B7O12(M=288.49), have been grown and their structure was determined by the x-ray powder diffraction and the single crystal diffraction technique. It is found that the borate anion consists of two(B3O7)3- and (B3O8)5- groups a unit cell. The space group was determined to be P-1(Ci1) with a=6.500(3) Å, b=7.839(2) Å, c=8.512(1) Å, α=92.07(2)˚, β=104.97(2)˚, γ=99.35(3)˚, V=412.0(2) Å3, Z=2 Dx=2.32 g cm-3, MoKα, λ=0.71069 Å, μ=2.15cm-1, T=293K. The structure was refined to R=0.0339 and wR=0.0882 for 2296 unique reflections by the single crystal diffraction. By the x-ray powder diffraction, we could obtain the similar results.

• Journal of the Korean Chemical Society
• /
• v.33 no.1
• /
• pp.90-96
• /
• 1989

A new series of $dioxo-di-{\mu}-oxo-dimolybdate(V)(*image)$, has been prepared by the reaction of pyridinum oxoisothiocyanato-molybdate(V) with 1, 6-diaminohexane-N, N, N', N'-tetraacetic acid derivatives containing amine carboxyl groups. The properties and possible molecular structure of these complexes were discussed by elemental analysis, spectroscopic studies and magnetic susceptibility measurements. The infrared spectra of these complexes show two strong Mo=$O_t$ stretching modes in the $900-965cm^{-1}$, MoO$_2$Mo stretching bands at around 450∼500 and $740-765 cm^{-1}$ to symmetrical and asymmetrical O-bridge stretching, a coordinated $COO^-$ asymmetrical band in the $1600-1635 cm^{-1}$. The complexes synthesized were yellow or orange and diamagnetic.

• Journal of the Korea Institute of Building Construction
• /
• v.15 no.3
• /
• pp.291-297
• /
• 2015

In this study, the evaluation and the analysis of the correlation between rheological properties and pumpability of high performance concrete, C80A which was applied to the height of from 200 m to 350 m in a super tall building, was carried out by measuring pumping pressure and flow rate, testing concrete properties at before and after pumping. As the results, C80A had satisfactory properties of fresh and hardened concrete to the requirements even after pumping and the maximum pumping pressure showed increase of 10~15% at every 50m higher pumping and the average flow rate showed the above $25m^3$ per hour which means proper productivity. Additionally it was verified that pumping pressure and friction factor in pipeline are inversely proportional to slump flow and showed a tendency to increase according to the higher T-500 value.

• Proceedings of the Korean Institute of Navigation and Port Research Conference
• /
• 2005.10a
• /
• pp.5-10
• /
• 2005

T.S. HANBADA will navigate to maintain the adequate distance between own ship and other ships safely for about 17 hours on the about 2 kts. On the above situation, M broadcasting station requires to maintain the distance from 100m to 500m between ships. This paper aims to calculate the minimum safe distance between ships, the distance is assessed by using ES Model which is a quantitative model for evaluating the difficulty of shiphandling. After marine traffic flow simulation, minimum safe distance for HANBADA on the 2kts is about 260m based ES value. On this paper, the result was compared about its distance to the actual navigating distance.

• Resources Recycling
• /
• v.3 no.1
• /
• pp.9-16
• /
• 1994

Fine cobalt metal powders was produced from domestic Stellite scrap by decomposing it with molten sodium hydroxide. Complete decomposition of the scrap could be obtained with the weigth ratio of sodium hydroxide to Stellite being about 2 at the temperature ranges of $750~800^{\circ}C$ for an hour. The cobalt-bearing compound was identified as $Co_2O_3{\dot}H_2O$ by X-ray analysis and D.T.-T.G.a.. The compound was then digested in HCI to form cobalt chloride, and after iron removal by adjusting the pH of the solution, cobaltous or cobaltic hydroxide was precipitated at the pH of about 13 or 4, respectively. The precipitates were reduced by hydrogen in the temperatures of $400~500^{\circ}C$ to fine cobalt powders of high purity with the size of 1.0 to $1.5\mu\textrm{m}$. The recovery of cobalt from Stellite scrap was about 75~86% by weight.

• Journal of Korea Multimedia Society
• /
• v.19 no.8
• /
• pp.1260-1274
• /
• 2016

To obtain good summarization algorithms, we need first understand how people summarize videos. 'Semantic gap' refers to the gap between semantics implied in video summarization algorithms and what people actually infer from watching videos. We hypothesized that ERP responses to real time videos will show either N400 effects to topic-irrelevant shots in the 300∼500ms time-range after stimulus on-set or P600 effects to topic-relevant shots in the 500∼700ms time range. We recruited 32 participants in the EEG experiment, asking them to focus on the topic of short videos and to memorize relevant shots to the topic of the video. After analysing real time videos based on the participants' rating information, we obtained the following t-test result, showing N400 effects on PF1, F7, F3, C3, Cz, T7, and FT7 positions on the left and central hemisphere, and P600 effects on PF1, C3, Cz, and FCz on the left and central hemisphere and C4, FC4, P8, and TP8 on the right. A further 3-way MANOVA test with repeated measures of topic-relevance, hemisphere, and electrode positions showed significant interaction effects, implying that the left hemisphere at central, frontal, and pre-frontal positions were sensitive in detecting topic-relevant shots while watching real time videos.