• 청정기술
• /
• 제24권3호
• /
• pp.206-211
• /
• 2018

Lead molybdate ($PbMoO_4$) were successfully synthesized using a facile surfactant-assisted hydrothermal process and characterized by XRD, Raman, PL, BET and DRS. We also investigated the photocatalytic activity of these materials for the decomposition of Rhodamine B under UV-light irradiation. From XRD and Raman results, well-crystallized $PbMoO_4$ crystals have been successfully synthesized with a facile surfactant-assisted hydrothermal process and had 52-69 nm particle size. The $PbMoO_4$ catalysts prepared at $160^{\circ}C$ showed the highest photocatalytic activity. The PL peak was appeared at about 540 nm at all catalysts and it was also shown that the excitonic PL signal was proportional to the photocatalytic activity for the decomposition of Rhodamine B.

• 공업화학
• /
• 제27권3호
• /
• pp.307-312
• /
• 2016

$PbMoO_4$를 계면활성제를 이용하여 수열합성법으로 합성하였고, XRD, Raman, TEM, PL, BET 및 DRS 등에 의해 특성 분석을 하였다. 이들을 사용하여 자외선 조사 하에서 Rhodamine B의 광분해 반응에서의 활성을 조사하였다. XRD 및 Raman의 분석 결과로부터 계면활성제를 이용한 손쉬운 수열합성에 의해 잘 결정화된 $PbMoO_4$ 구조를 가진 촉매들이 합성되었으며 52에서 69 nm의 크기를 나타내었다. cetyltrimethylammonium bromide (CTAB)를 계면활성제로 사용하여 합성된 $PbMoO_4$는 P-25와 순수한 $PbMoO_4$ 보다 높은 광촉매 활성을 나타내었다. pH 9에서 합성된 $PbMoO_4$ 촉매가 가장 높은 활성을 나타내었다. 모든 촉매들은 540 nm 부근에서 강하고 넓은 PL 흡수밴드가 나타났으며, 이 피크의 세기가 커질수록 Rhodamine B의 광분해 활성이 증가하는 것으로 나타났다.