• Korean Journal of Materials Research
• /
• v.23 no.9
• /
• pp.495-500
• /
• 2013

Mo-based thin films are frequently used as back electrode materials because of their low resistivity and high crystallinity in CIGS chalcopyrite solar cells. Mo:Na/Mo bilayer thin films with $1{\mu}m$ thickness were deposited on soda lime glass by varying the thickness of each layer using dc-magnetron sputtering. The effects of the Mo:Na layer on morphology and electrical property in terms of resistivity were systematically investigated. The resistivity increased from $159{\mu}{\Omega}cm$ to $944{\mu}{\Omega}cm$; this seemed to be caused by increased surface defects and low crystallinity as the thickness of Mo:Na layer increased from 100 nm to 500 nm. The surface morphologies of the Mo thin films changed from a somewhat coarse fibrous structures to irregular and fine celled structures with increased surface cracks along the cell boundaries as the thickness of Mo:Na layer increased. Na contents varied drastically from 0.03 % to 0.52 % according to the variation of Mo:Na layer thickness. The change in Na content may be ascribed to changes in surface morphology and crystallinity of the thin films.

• Computers and Concrete
• /
• v.4 no.4
• /
• pp.285-298
• /
• 2007

Corrosion of Reinforcement (rebar) is nondestructively estimated by the half-cell potential measurement. As is the case with other nondestructive testings (NDT), understanding of the underlying principles should be clarified in order to obtain meaningful results. Therefore, the measurement of potentials in concrete is analytically investigated. The effect of internal defects on the potentials measured is clarified numerically by the boundary element method (BEM). Thus, a simplified inversion by BEM is applied to convert the potentials on concrete surface to those on rebars, taking into account the concrete resistivity. Because the potentials measured on concrete surface are so sensitive to moisture content, concrete resistivity and surface condition, an inverse procedure to convert the potentials on concrete surface into those on rebars is developed on the basis of BEM. It is found that ASTM criterion is practically applicable to estimate corrosion from the potential values converted. In experiments, an applicability of the procedure is examined by accelerated corrosion tests of reinforced concrete (RC) slabs. For practical use, the procedure is developed where results of IBEM are visualized by VRML (Virtual Reality modeling Language) in three-dimensional space.

• The Journal of Engineering Geology
• /
• v.31 no.2
• /
• pp.187-197
• /
• 2021

Clay mineral content of weathered zone is a key parameter for landslide studies. Electrical resistivity tomography is usually performed to delineate the geometry of complex landslides and to identify the sliding surface. In clay-bearing weathered zone, parallel resistivity Archie equation is employed to investigate the effect of conductivity added (resistivity reduced) by clay minerals of kaolinite and montmorillonite, which is dependent on their specific surface area and cation exchange capacities (CEC). A decrease of overall resistivity and apparent formation factor is observed with increasing pore-water resistivity, significantly in montmorillonite. Formation factor is found decreased with increasing porosity and decreasing cementation factor. Parallel Archie equation was applied to the electrical resistivity data from the test area (Sinjindo-ri, Taean-gun, Chungcheongnam-do, Korea) which experienced land creeping in the year of 2014. A panel test with varying clay-mineral contents provides the best fit section when the theoretical section constructed with the assumed contents approaches the field section, from which the clay-mineral content of the weathered zone is estimated to be approximately 10%. Resistivity interpretation schemes including the clay mineral contents for land creeping studies explored in this paper can be challenged more when porosity, saturation, and pore-water resistivity are provided and they are included in the numerical resistivity modeling.

• Economic and Environmental Geology
• /
• v.32 no.2
• /
• pp.161-167
• /
• 1999

Electric and electromagnetic surveys were conducted to investigate the deep structure of the Ulsan fault in Ipsil area, south of Kyeongju. On this study, especially high-frequency magnetotelluric method of electromagnetic survey in the frequency range of 10~100,000 Hz was mainly employed to study the deep subsurface configuration. High-frequency MT survey was performed at 70 points of spacing 30~50 m, making 3.8 km survey line. As a survey result, a 2-km-depth 2-D cross-section was achieved. It shows vertical and horizontal subsurface variations of resistivity values. Near-surface layer having low resistivity value becomes thicker eastward up to 800m. There is a steep low resistivity zone in the west side of survey line, and there exists two low resistivity zones dipping west in the east side of survey line. Two low resistivity zones are interpreted to be related to major movement pattern of the Ulsan fault. This suggests that major fault lines are developed on both peripheral sides of the broad fault zone.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2015.08a
• /
• pp.231.1-231.1
• /
• 2015

Surface energy, being an important material parameter to control its interactions with the other surfaces plays a key role in bio-related application. Carbon films are found very promising due to their characteristics such as wear and corrosion resistant, high hardness, inert, low resistivity and biocompatibility. The present work deals with the deposition of carbon films using unbalanced facing target magnetron sputtering technique. The discharge characteristics were studied using optical emission spectroscopy and correlated with the film properties. Surface energy was investigated through contact angle measurement. The ID/IG ratio as calculated from Raman spectroscopy data increases with the increase in power density due to the higher number of sp2 clusters embedded in the amorphous matrix. The deposited films were smooth and homogeneous as observed by Atomic force microscopy having RMS roughness in the range of 1.74 to 2.25 nm. It is observed that electrical resistivity and surface energy varies in direct proportionality with operating pressure and has inverse relation with power density. The surface energy results clearly exhibited that these films can have promising applications in cell cultivation.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.7 no.2
• /
• pp.141-148
• /
• 2003

Concrete surface is a part that resists chiefly to carbonation by carbonic acid gas, affluence of rainwater and air, deterioration by freezing thawing, salt damage by seawater, and other chemical erosion etc. Therefore, this research analyzed physical characteristic and durable characteristic of concrete eliminated glut water and bubble of concrete surface using CON-SILK that is permeated with dehydration. As a research result, concrete using CON-SILK was improved, in comparison with concrete using general formwork, in physical performance and durability of concrete, as surface hardness, carbonation resistivity, and salt content permeation resistivity etc. Therefore, we could know that it is effective to use CON-SILK in performance elevation of concrete surface.

• Journal of the Korean Vacuum Society
• /
• v.11 no.3
• /
• pp.171-175
• /
• 2002

The change in work function was studied on Indium-Tin-Oxide(ITO) surface after O-plasma treatment using $\gamma$-Focused ion Beam($\gamma$-FIB). As the surface of ITO experienced more O-plasma treatment, both the surface resistivity and the work function got higher. Auger Electron Spectroscopy identified the increase of oxygen as well as the decrease of Sn. The rise of work function and surface resistivity is considered to be due to the change in oxygen and Sn on the surface of ITO.

• Journal of the Korean Vacuum Society
• /
• v.9 no.3
• /
• pp.279-284
• /
• 2000

In order to analysis the degradation process of epoxy/glass fiber for outdoor condition, FRP laminate was exposed to high temperature and water. Then the degradation process was evaluated by comparing contact angle, surface potential decay, and surface resistivity. For the change of wettability, the contact angle of thermal-treated specimen with the high temperature of $200^{\circ}C$ increased. But that of water-treated specimen decreased. The characteristic of surface potential decay shows the tendency of the remarkable decrease on water-treated specimens, but increase on thermal-treated specimen compared with untreated one. Also, for the surface resistivity, it shows the same trend compared with the change of contact angle.

• Proceedings of the KSR Conference
• /
• 2011.10a
• /
• pp.2435-2438
• /
• 2011

Steel bar is used for as a reinforcing material in a concrete slab track. Bacuase the steel re-bar could provide passes for current transition, all the cross points of steel re-bars should be insulated by using plastic materials. This is due to the loss of signal intensity of track-circuit. In this study, GFRP bars are adopted in place of the traditional steel reinforcing bars for a concrete slab track to minimize the loss of the signal intensity. In order to evaluate the replacing effect on eletrical characteristic of slab track, measurements of surface resistivity are conducted on steel and GFRP reinforced precast slab tracks. In the results, the GFRP reinforced slab strack shows the higher resistivity than the steel reinforced slab track.

• Journal of the Korean Ceramic Society
• /
• v.37 no.2
• /
• pp.194-200
• /
• 2000

Sb-doped tin oxide films were deposited on Corning glass 1737 substrate by plasma enhanced chemical vapor deposition(PECVD) technique using a gas mixture of SnCl4/SbCl5/O2/Ar. The deposition behaviors of tin oxide films by PECVD were compared with those by thermal CVD, and effects of deposition temperature, r.f. power and Sb doping on the electrical properties of tin oxide films were investigated. PECVD technique largely increased the deposition rate and smoothed the surface of tin oxide films compared with thermal CVD. Electrical resistivity decreased with doping of Sb due to the increase of carrier concentration. However, large doping of Sb diminished carrier concentration and mobility due to the decrease of crystallinity, which resulted in the increase of electrical resistivity. As the deposition temperature and r.f. power increased, Cl content in the film decreased.