• Journal of the Korean Wood Science and Technology
• /
• v.42 no.1
• /
• pp.49-57
• /
• 2014

The pre-air-drying of Korean pine before the high-temperature and low-humidity drying was shown to be effective in uniform moisture content distribution and prevention of surface check. Our results suggest that initial moisture content of the timber also plays important role in high-temperature and low-humidity drying method. The pre-air-drying also helps in the reduction of surface checks in Korean pine when compared to the Korean pine dried by only high-temperature and low-humidity. End-coating was not effective in the prevention of twist, shrinkage, case hardening and internal checks. The pre-air-drying reduces the internal tension stresses which occur during high-temperature and low-humidity drying thus decreasing case hardening and also preventing internal checks. The pre-air-drying decreases the moisture content and causes shrinkage which leads to increased twist in the Korean pine.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.5 no.1
• /
• pp.53-58
• /
• 2017

FRP Hybrid Bar, composed of an embedded steel and the coated composites with epoxy and glass fiber, is an effective construction material with tension-hardening performance and lightweight. The epoxy exposed to UV(Ultra Violet Rays) and FT(Freezing and Thawing) action easily shows a surface deterioration, which can cause degradation of bonding strength between inside-steel and outside-concrete. In the present work, surface inspection for 3 different samples of normal steel, FRP Hybrid Bar before UV, and FRP Hybrid Bar after UV test was performed, then concrete samples with 3 reinforcement types were prepared for accelerated FT test. Through visual inspection on 3 typed reinforcement, no significant deterioration like chalking was evaluated. The results from FT test to 120 and 180 cycles showed FRP Hybrid Bar exposed to UV test has higher bonding strength than normal steel by 106.3% due to enlarged bond area by silica coating. The 3 cases showed a similar bond strength tendency with increasing FT cycles, however a relatively big deviations of bond strength were evaluated in FRP Hybrid Bar after UV test due to loss of silica coating.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.7 no.3
• /
• pp.224-234
• /
• 2019

Waterproof layers are installed in civil engineering structures and bridge construction is commonly finished by applying a layer of regular or asphalt concrete above the waterproof layer. However, asphalt materials are susceptible to melting at high temperature due to its superior temperature sensitivity, and this causes the waterproofing material to melt due to the high temperature of the asphalt concrete, thereby increasing the defect occurrence rate due to the thickness reduction. In this study, tensile strength and elongation of hard and soft type of MMA(Methyl Methacrylate) applied to bridges were compared in accordance to standard performance criteria based on different mixture ratios. Results of comparative testing showed that hard MMA resin can display a satisfactory tensile strength, and soft MMA resin displays satisfactory elongation properties, but as the two resin types are separately used, neither types are able to satisfy the standard requirements outlined in KS F 4932. When the amount of the powder exceeds 56.25% of the total amount, voids are generated on the surface after curing and self leveling was impossible and a heterogeneous surface is formed. Furthermore, when the hard resin: soft resin: powder mixture ratio was set to 15g: 85g: 150g. the tensile strength was $1.5N/mm^2$ and the elongation percentage was 133% which satisfy the tensile performance of KS F 4932.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.5 no.2
• /
• pp.130-136
• /
• 2017

The present work is for an evaluation of tension behavior and surface deterioration of FRP Hybrid Bar due to UV exposure and freezing/thawing(F/T) actions. For the work, FRP Hybrid Bar is subjected to UV exposure test, then F/T test is performed successively to 180 cycles. In FRP Hybrid Bar, no significant surface deterioration is evaluated after UV exposure. Tension hardening performance, a unique engineering advantage of FRP Hybrid Bar, is still maintained after F/T test. The performance in FRP Hybrid Bar exposed to UV is still effective. FRP Hybrid Bar exposed to UV have almost similar tension behavior of FRP Hybrid Bar without UV exposure. Although F/T cycles increase to 180, steel rebar, FRP Hybrid Bar, and FRP Hybrid Bar exposed to UV show no significant changes in tension behavior. In the work, UV exposure and F/T actions are evaluated to have little negative effect on surface deterioration and tensile performance in FRP Hybrid Bar, however spalling of silica coating due to impact should be considered since it affects bonding strength to outer concrete.