• 한국초전도ㆍ저온공학회논문지
• /
• 제15권3호
• /
• pp.1-4
• /
• 2013

We investigated the effect of Nb substitution for Ru on the structural and magnetic properties of $(Ru_{1-x}Nb_x)\;Sr_2(Sm_{1.4}Ce_{0.6})Cu_2O_z$ Samples. X-ray diffraction measurements indicated that nearly single-phase samples are formed in the range from x = 0 to 1.0. The superconducting transition temperature determined from the inflection in the field-cooled magnetic susceptibility decreased only slightly from $T_c$ = 25 K for x = 0 to $T_c$ = 22 K for x = 1.0, in consistent with the change in room temperature thermopower of the samples. However, the Nb substitution for Ru above x = 0.25 significantly suppressed the weak ferromagnetic component of the field-cooled magnetic susceptibility. It was also found that the Nb substitution for Ru results in an enhanced diamagnetic susceptibility with Nb content above x = 0.5 in both zero field-cooled and field-cooled magnetization measurements, in contrast to the behavior of the samples with $x{\leq}0.5$ in which the diamagnetic susceptibility decreases as the Nb content increases.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2002년도 하계학술대회 논문집
• /
• pp.67-73
• /
• 2002

The development of high performance HTS wire is a key factor for various electrical applications of coils and cables. The purpose of this paper is to review and consider the main manufacturing technologies of HTS wire and its current status. A lot of efforts have been focused on the optimization of PIT parameters for Bi-2223/Ag wire. According to this, long Bi-2223 wires having Ic of 130 A were recently produced and their mass production has been underway in US. The current status performance of Bi-2223 wire is supposed to be used in power transmission cable because of its lower self-field property. Y-123 second generation conductor is extensively being developed throughout the world and many fabrication processes are competed with each other. 30 m-long Y-123 wire with Ic of 0.8 MA/$\textrm{cm}^2$ was recently fabricated using IBAD and PLD techniques in Japan. This result offers promise of scalable processing of practical multi-layer coated conductor.

• 한국초전도ㆍ저온공학회논문지
• /
• 제6권4호
• /
• pp.5-8
• /
• 2004

A low cost MOD processing using YBCO oxide powder as a starting precursor was employed for fabrication of YBCO thin films. YBCO oxide is advantageous over metal acetates or TFA salts which are popular starting precursors for conventional MOD-TFA process. YBCO thin films were prepared by oxide-precursor-based MOD process and annealing condition was optimized. The YBCO thin film annealed at 78$0^{\circ}C$ shows no transport $I_c$ and poor microstructure. However, the YBCO thin film annealed at higher temperature shows improvement in microstructure and current transport property. In order to improve critical current, YBCO thin film was prepared by double coating method. YBCO thin film prepared with double coating approach shows enhanced superconducting performance ($I_c$>100A/cm-w).

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2008년도 제39회 하계학술대회
• /
• pp.812-813
• /
• 2008

본 연구에서는 외부인가 자장을 위한 초전도 특성평가장 치용 레이스트랙형 초전도 마그네트의 개념설계를 하였다. 초전도 특성 평가장치는 외부인가 자장과 온도를 변화시켜가며 고온 초전도 선재의 특성을 측정할 수 있는 장치이다. 초전도 전력기기가 응용될 수 있는 온도범위인 $10K{\sim}77K$ 온도범위에서 초전도 선재의 특성을 평가하기 위해서 약 20cm 정도 길이의 시편이 차지하는 공간이 필요하고 이 공간에 1% 이하의 자장균일도와 최소 3T 이상을 가지는 마그네트가 필요하다. 이러한 조건을 만족시키는 초전도 마그네트는 필연적으로 레이스트랙형 마그네트를 가지는 split형이어야 한다. DI-BSCCO H type과 HT type 두 가지 선재에 대한 전자장 해석을 통하여 제한조건을 만족시키는 마그네트 설계를 하였다. 이렇게 설계된 초전도 마그네트는 초전도 특성평가장치 제작에 활용될 것이다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1988년도 춘계학술대회 논문집
• /
• pp.3-6
• /
• 1988

Electrical and magnetic properties of $Y_1Ba_2Cu_3O_7-y$ sintered with $Bi_2O_3$ have been investigated by levitation experiment and the measurement of electrical resistivity. The effects of $Bi_2O_3$ addition on the microstructure of the sintered specimens were also investigated. The electrical resistivity in the normal state is smaller in $Y_{0.85}Bi_{0.15}Ba_2Cu_3O_{7-y}$, where the Bi is substituted into Y site, than in the basic compound $Y_1Ba_2Cu_3O_{7-y}$ due to improved microstructure. On the other hand, the microstructure is poor and electrical resistivity is larger in the $Y_1Ba_2Cu_3O_{7-y}$ sintered with excess $Bi_2O_3$. It appears that the impurity in grain boundary affect the electrical properties significantly but has little effect on the magnetic property.

• 한국초전도ㆍ저온공학회논문지
• /
• 제16권3호
• /
• pp.7-9
• /
• 2014

Single-crystal like $MgB_2$ thin film was grown on (000l) $Al_2O_3$ substrate by using hybrid physical-chemical vapor deposition (HPCVD) system. Single crystal properties were studied by X-ray diffraction (XRD) and the full width at half maximum (FWHM) of the (0001) $MgB_2$ peak is $15^{\circ}$, which is very close to that has been reported for $MgB_2$ single-crystal. It indicates that the crystalline quality of thin film is good. Temperature dependence on resistivity was investigated by physical property measurement system (PPMS) in various applied fields from 0 to 9 T. The upper critical field ($H_{c2}$) and irreversibility field ($H_{irr}$) were determined from PPMS data, and the estimated values are comparable with that of $MgB_2$ single-crystals. The thin film shows a high critical temperature ($T_c$) of 40.4 K with a sharp superconducting transition width of 0.2 K, and a high residual resistivity ratio (RRR=21), it reflects that $MgB_2$ thin film has a pure phase structure.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2008년도 하계학술대회 논문집 Vol.9
• /
• pp.285-286
• /
• 2008

In practical applications of HTS tapes for electric devices such as coils and power cables, the jointing of HTS tapes is needed. In magnet applications superconducting joints are needed to achieve very low resistance at the joint, but for power device applications, a slightly higher joint resistance may be acceptable. In this study, an economical joint with good mechanical and electrical integrity could be achieved for Bi-2223 tapes which can be applicable to electric power applications. A lap joint method has been used. The joint resistance and strength of the jointed Bi2223 tapes have been evaluated. Electro-mechanical properties of the joint sample under tension have been examined and compared with the case of the single tapes.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2003년도 춘계학술대회 논문집 초전도 자성체 연구회
• /
• pp.73-76
• /
• 2003

Phase transformation of Bi-2223 tape during the final heat treatment has been investigated through the various duration time of heat treatment in a specially designed 3-step heat treatment. It was found that the phase assemblage in the sintering was determined by the sintering time and temperature. In this study, sintering time was changed to optimize the Bi-2223 phase assemblage, and acquire high critical current density. High critical current samples with Ic = 85 A and Je = 8.9 kA/$cm^2$ have been measured at 77K and self-field for 55-filament tapes sintered by optimum condition.

• 한국초전도ㆍ저온공학회논문지
• /
• 제12권1호
• /
• pp.1-5
• /
• 2010

Silver stabilizing layer of coated conductor has been prepared by dip coating method using organic silver complexes containing 10 wt% silver as a starting material. Coated silver complex layer was dried in situ with hot air and converted to crystalline silver by post heat treatment in flowing oxygen atmosphere. A dense continuous silver layer with good surface coverage and proper thickness of 230 nm is obtained by multiple dip coatings and heat treatments. The film heat treated at $500^{\circ}C$ showed good mechanical adhesion and crystallographic property. The interface resistivity between superconducting YBCO layer and silver layer prepared by dip coating was measured as $0.67\;{\times}\;10^{-13}\;{\Omega}m^2$. Additional protecting copper layer with the thickness of $20\;{\mu}m$ was successfully deposited by electroplating. The critical current measured with the specimen prepared by dip coating and sputtering on same quality YBCO layer showed similar value of ~140 A and proved its ability to replace sputtering method for industrial production of coated conductor.

• Progress in Superconductivity
• /
• 제12권2호
• /
• pp.118-123
• /
• 2011

The properties of $2^{nd}$ generation high temperature superconducting wire, coated conductor strongly depend on the quality of superconducting oxide layer and property of metal substrate is one of the most important factors affecting the quality of coated conductor. Good mechanical and chemical stability at high temperature are required to maintain the initial integrity during the various process steps required to deposit several layers consisting coated conductor. And substrate need to be nonmagnetic to reduce magnetization loss for ac application. Hastelloy and stainless steel are the most suitable alloys for metal substrate. One of the obstacles in using stainless steel as substrate for coated conductor is its difficulties in making smooth surface inevitable for depositing good IBAD layer. Conventional method involves several steps such as electro polishing, deposition of $Al_2O_3$ and $Y_2O_3$ before IBAD process. Chemical solution deposition method can simplify those steps into one step process having uniformity in large area. In this research, we tried to improve the surface roughness of stainless steel(SUS310). The precursor coating solution was synthesized by using yttrium complex. The viscosity of coating solution and heat treatment condition were optimized for smooth surface. A smooth amorphous $Y_2O_3$ thin film suitable for IBAD process was coated on SUS310 tape. The surface roughness was improved from 40nm to 1.8 nm by 4 coatings. The IBAD-MgO layer deposited on prepared substrate showed good in plane alignment(${\Delta}{\phi}$) of $6.2^{\circ}$.