• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2004년도 추계학술대회 논문집 Vol.17
• /
• pp.341-344
• /
• 2004

The superconducting properties of $YBa_2Cu_3O_x$ with different content impurities of PbO and $BaPbO_3$ were studied. When the PbO was used as an additive in $YBa_2Cu_3O_x$, although the melting point could be reduced, the superconductivity became poor. From the XRD pattern of the sintered mixture of $YBa_2Cu_3O_x$ and PbO it was known that there is a reaction between $YBa_2Cu_3O_x$ and PbO, and the product is $BaPbO_3$. In the process of the reaction the superconducting phase of $YBa_2Cu_3O_x$ was decreased and $BaPbO_3$ would be the main phase in the sample. Therefore, $BaPbO_3$ was chosen as the impurity additive for the comparative study. The single phase of $BaPbO_3$ was synthesized by the simple way from both mixtures of $BaCO_3$ and PbO, $BaCO_3$ and $PbO_2$. Different contents of $BaPbO_3$ (10%, 20%, 30%) were added in the $YBa_2Cu_3O_x$. By the Phase analysis in the XRD patterns it was proved that there was no reaction between $YBa_2Cu_3O_x$ and $BaPbO_3$. When $BaPbO_3$ was used as impurity in $YBa_2Cu_3O_x$ the superconductivity was much better than PbO as an impurity additive in $YBa_2Cu_3O_x$.

• 동굴
• /
• 제78호
• /
• pp.17-22
• /
• 2007

The melting temperature and critical temperature (Tc) of $YBa_2Cu_3O_x$ with deferent content impurities of PbO and $BaPbO_3$ were studied. When the PbO was used as addition in $YBa_2Cu_3O_x$, although the melting point could be reduced, the superconductivity (the transition wide, ${\Delta}T_c$) became poor. From the XRD pattern of the sintered mixture of $YBa_2Cu_3O_x$ and PbO it was known that there is a reaction between $YBa_2Cu_3O_x$ and PbO, and the product is $BaPbO_3$. In the process of the reaction the superconducting phase of $YBa_2Cu_3O_x$ was decreased and in the sample $BaPbO_3$ became the main phase. Therefore the superconductivity was reduced. $BaPbO_3$ was chosen as the impurity for the comparative study. The single phase $BaPbO_3$ was synthesized by the simple way from both mixtures of $BaCO_3$ and PbO, $BaCO_3$ and $PbO_2$. Deferent contents of $BaPbO_3$ (10%, 20%, 30%) were added in the $YBa_2Cu_3O_x$. By the phase analysis in the XRD patterns it was proved that there were not reactions between $YBa_2Cu_3O_x$ and $BaPbO_3$. When $BaPbO_3$ was used as impurity in $YBa_2Cu_3O_x$ the superconductivity was much better than PbO as impurity in $YBa_2Cu_3O_x$. But the melting point of $YBa_2Cu_3O_x$ with $BaPbO_3$ could not be found when the temperature was lower than $1000^{\circ}C$ in the DTA measurement.

• 한국세라믹학회지
• /
• 제33권3호
• /
• pp.313-320
• /
• 1996

We have fabricated an in-plane aligned a-axis oriented YBa2Cu3O7-x (a-YBCO) thin film on a LaSrGaO4(100) substrate with a PrBa2Cu3O7-x(PBCO) template layer by two step plused laser deposition using 308 nm XeCl excimer laser. A YBCO layer and PBCO layer grown at low temperatures were used as template layers. We have investigated the effect of the deposition temperature of template layers on the superconducting and struc-tural properties of in-plane aligned a-YBCO thin films. An optimal deposition temperature of the PBCO template layers was 630. In-plane aligned a-YBCO thin films showed an anisotropy ratio in resistivity of 11.5 and a zero resistance temperature of 88 K.

• E2M - 전기 전자와 첨단 소재
• /
• 제8권1호
• /
• pp.6-12
• /
• 1995

High Tc superconducting YBa$_{2}$Cu$_{3}$$O_{7-x}$ thin films were prepared on various substrates by off-axis rf magnetron sputtering method to examine the substrate effects on the film structure and its R-T characteristics. The SEM analysis showed that the surface morphology of the grown YBa$_{2}$Cu$_{3}$O.sub 7-x/, film has different characteristic structure with different substrate used. The film on (100) SrTiO$_{3}$ substrate has critical current density of 3*10$^{5}$ A/cm$^{2}$ at 77K under zero magnetic field. The X-ray diffraction measurements revealed that the films on (100) SrTiO$_{3}$ substrate have mixed a-axis and c-axis normal to the substrate surface and the films on (100) MgO and ZrO$_{2}$/sapphire substrates have c-axis normal orientation to the substrate surface. However, YBa$_{2}$Cu$_{3}$$O_{7-x}$ films on (100) sapphire substrates showed no preferential orientation.ion.

• 한국초전도ㆍ저온공학회논문지
• /
• 제1권1호
• /
• pp.15-21
• /
• 1999

Textured bulk $YBa_2Cu_3O_x$ superconductors samples were grown directionally using different precursors of $YBa_2Cu_3O_x$ power. and a mixture of $YBa_2Cu_3O_5, BaCuO_2 and CuO$ powder. The microstructures and superconducting properties of the samples were compared. The mixture powder produced better microstructures i.e. dense and crack-free so that a higher critical current density was achieved at the same hot-zone temperature of 115$0^{\circ}C$ than the reacted powder does. When the reacted powder used as a precursor, as the hot-zone temperature increased upto 1215$^{\circ}C$, the texture of the sample improved and the critical current density increased. The amount of melt in the sample is of secondary importance for the growth of superconducting $YBa_2Cu_3O_x$ grains. The microstructures and superconductivity of good quality superconductors grown directionally were more strongly influenced by the kind of precursor rather than the amount og melt in a sample.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2004년도 하계학술대회 논문집 Vol.5 No.1
• /
• pp.543-546
• /
• 2004

The melting temperature and critical temperature(Tc) of $YBa_2Cu_3O_x$ with deferent content impurities of PbO and $BaPbO_3$ were studied. When the PbO was used as addition in $YBa_2Cu_3O_x$, although the melting point could be reduced, the superconductivity(the transition width, ${\Delta}T_c$) became poor. From the XRD pattern of the sintered mixture of $YBa_2Cu_3O_x$ and PbO it was known that there is a reaction between $YBa_2Cu_3O_x$ and PbO, and the product is $BaPbO_3$. In the process of the reaction the superconducting phase of $YBa_2Cu_3O_x$ was decreased and in the sample $BaPbO_3$ became the main phase. Therefore the superconductivity was reduced. $BaPbO_3$ was chosen as the impurity for the comparative study. The single phase BaPbO3 was synthesized by the simple way from both mixtures of $BaPbO_3$ and PbO, $BaPbO_3\;and\;PbO_2$. Deferent contents of $BaPbO_3$(10%, 20%, 30%) were added in the $YBa_2Cu_3O_x$. By the phase analysis in the XRD patterns it was proved that there werenot reactions between $YBa_2Cu_3O_x$ and $BaPbO_3$. When $BaPbO_3$ was used as impurity in $YBa_2Cu_3O_x$ the superconductivity was much better than PbO as impurity in $YBa_2Cu_3O_x$. But the melting point of $YBa_2Cu_3O_x$ with $BaPbO_3$ could not be found when the temperature was lower than $1000^{\circ}C$ in the DTA measurement.

• 공업화학
• /
• 제7권4호
• /
• pp.639-644
• /
• 1996

원료물질인 $Y_2O_3$, $BaCO_3$, CuO 및 $AgNO_3$ 분말로부터 Y계 고온초전도체를 발화합성법으로 제조하였다 $YBa_2Cu_3O_{7-x}$와 Cu를 Ag로 부분 치환한 $YBa_2Cu_{3-y}Ag_yO_{7-x}$의 특성을 X-ray diffractometer, resistivity measuring equipment, SEM, and Vickers Hardness 등으로 분석하였다. $YBa_2Cu_3O_{7-x}$의 Tc,zero는 91K였고, 밀도는 $5.2g/cm^3$, 경도는 $590kg/mm^2$였다. Cu를 Ag로 0.15몰 이하 부분 치환한 $YBa_2Cu_{3-y}Ag_yO_{7-x}$의 경우 임계온도(Tc)는 거의 변하지 않으면서 미세구조, 밀도 및 경도가 향상되었다.

• 한국세라믹학회지
• /
• 제29권2호
• /
• pp.152-160
• /
• 1992

High-Tc superconductor thick films of YBa2Cu$\chi$O7-y (X=3, 3.5, 4) of which thickness varies from 100 $\mu\textrm{m}$ to 200 $\mu\textrm{m}$ were successfully prepared by plasma spraying method, and the characteristics of thick film depending on copper content and heat treatment conditions were investigated. Regardless of heat-treated temperature, the specimens with X=3 were composed of YBa2Cu$\chi$O7-y, Y2BaCuO5 and BaCuO3 phases. The specimens with X=4, however, were composed of YBa2Cu$\chi$O7-y phase at all heat treatment conditions. The specimens with X=4 composition showed the best superconducting characteristics after heat treatment at 925$^{\circ}C$, and the superconducting transition temperature with zero resistivity (Tc,zero) was 87K. The thick film lost superconductivity when the specimens were heat-treated at 950$^{\circ}C$ because of interdiffusion between superconductor elements and bond coating elements and Y2BaCuO5 phase was found was found to be main phase at the interface.

• 한국세라믹학회지
• /
• 제28권3호
• /
• pp.243-251
• /
• 1991

High-Tc YBa2Cu3O7-x superconducting thin films have been prepared by single-target off-axis RF magnetron sputtering. Optimal ratio of Y : Ba : Cu of the single-target was determined as 1 : 1.65 : 3.35 in order to obtain the stoichiometric films. Tc, crystalline phase, and microstructures of the surface and cross-section of the ex-situ YBa2Cu3O7-x thin films on MgO(100) had a Tc, zero of 80K, and the films on LaAlO3/Si had a Tc, on-set of 90 K and a Tc, zero of 70 K.

• 대한전기학회논문지
• /
• 제44권8호
• /
• pp.1063-1067
• /
• 1995

The superconducting properties of YBa$_{2}$Cu$_{3}$$O_{7-x}$(YBaCuO) thin films prepared by laser ablation have been investigated. The x-ray diffraction patterns and surface morphology of the films were substantially different from one another. The compositional ratios of YBaCuO films were controlled by the conditions of the target-substrate distance. The YBaCuO films manufactured on MgO(100) substrate were indicated T$_{c}$(zero)=91.2 K, T$_{c}$(onset)=93 K, and J$_{c}$=3.5*10$^{5}$ A/cm$^{2}$(at 77.3K). The optimum conditions were found to be a substrate temperature of 710 .deg. C, a energy density of 2 J/cm$^{2}$, and a target-substrate distance of 60 mm in an oxygen partial pressure of 200 mTorr.0 mTorr.