Tensile, low cycle fatigue, and fatigue crack growth rate tests were conducted at RT and $300^{\circ}C$ for type 304 stainless steel. Tensile was tested under displacement control and low cycle fatigue was tested under strain control. Fatigue crack growth rate test was conducted under load control and crack was measured by DCPD method. Yield strength and elongation decreased at $300^{\circ}C$. Dynamic strain aging was not detected at $300^{\circ}C$. Low cycle fatigue life increased but fatigue strength decreased at $300^{\circ}C$. Fatigue crack growth rate increased at $300^{\circ}C$. Dislocation structures were mixed with cell and planar and did not change with temperature. Grain size did not change but plastic strain increased at $300^{\circ}C$. Strain induced martensite after low cycle fatigue test increased at RT but decreased at $300^{\circ}C$. It was concluded that the increase of low cycle fatigue life at $300^{\circ}C$ was due to the decrease of strain induced martensite at which crack was initiated.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.28 no.7
• /
• pp.977-985
• /
• 2004

An evaluation of fatigue life of welded components is complicated due to various geometrically complex welding details and stress raisers in vicinity of weld beads, ego under cuts, overlaps and blow holes. These factors have a considerable influence on the fatigue strength of welded joints, as well as the welding residual stress which is relaxed depending on the distribution of local stress at the front of the stress raisers. To reasonably evaluate fatigue life, the effect of geometries and welding residual stress should be taken into account. The several methods based on the notch strain approach have been proposed in order to accomplish this. These methods, however, result in differences between analytical and experimental results due to discrepancies in estimated amount of relaxed welding residual stress present. In this paper, an approach that involves the use of a modified notch strain approach considering geometrical effects and a residual stress relaxation model based on experimental results was proposed. The fatigue life for five types of representative welding details, ego cruciform, cover plate, longitudinal stiffener, gusset and side attachment joint, are evaluated using this method.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.15 no.1
• /
• pp.209-217
• /
• 1991

We have carried out a preliminary study to search for the new fracture mechanics parameter which can effectively estimate the fatigue life. In this study, the distribution of local fatigue strains near a fatigue crack tip was detailedly revealed using by fine dot grid strain measurement method. From these results, a single parameter (.DELTA.A), which characterize local fatigue strain field, was nearly proposed by the authors.

• Smart Structures and Systems
• /
• v.20 no.3
• /
• pp.343-350
• /
• 2017

An experimental study is presented of the application of fiber Bragg grating (FBG) interrogation method based on optical time-domain reflectometery (OTDR) to monitoring strain in bent reinforced concrete beams. The results obtained with the OTDR-based method are shown to agree well with the direct spectral measurements. Strain sensitivity, resolution and measurement range amounted to $0.0028dB/{\mu}strain$; $30{\mu}strain$; $4000{\mu}strain$, correspondingly. Significant differences are observed in surface and inner deformations of the test beams which can be attributed to different mechanical properties of concrete and steel reinforcement. The prospects of using OTDR-based FBG interrogation technique in real-life applications are discussed.

• Proceedings of the KSME Conference
• /
• 2001.06a
• /
• pp.169-174
• /
• 2001

Low cycle fatigue tests are performed on high strength low alloy steels that be developed for submarine material. The relation between absorbed plastic strain energy and numbers of cycle to failure is examined in order to predict the low cycle fatigue life of structural steels by using plastic strain energy method. The cyclic properties are determined by a least square fit techniques. The life predicted by the plastic strain energy method is found to coincide with experiment data and results obtained from the Coffin-Manson method. Also the cyclic behavior of structural steels is characterized by cyclic softening with increasing number of cycle at room temperature. Especially, low cycle fatigue characteristics and microstructural changes of structural steels are investigated according to changing tempering temperatures. In the case of PFS steels, the $\varepsilon$-Cu is formed in 550C of tempering temperature and enhances the low cycle fatigue properties.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.10 no.2
• /
• pp.141-149
• /
• 2002

Most of mechanical failures are caused by repeated loadings and therefore they are strongly related to fatigue. To avoid the failures caused by fatigue, determination of an optimal shape of a structure is one of the very important factors in the initial design stage. Shape optimization for three types of specimens, which are very typical ones in opening mode in fracture mechanics, was accomplished by the linear elastic fracture mechanics and the growth-strain method in this study. The linear elastic fracture mechanics was used to estimate stress intensity factors and fatigue lives. And the growth-strain method was used to optimize the shape of the initial shape of the specimens. From the results of the shape optimization, it was concluded that shapes of three types of specimens optimized by the growth-strain method prolong their fatigue lives very much.

• Mycobiology
• /
• v.44 no.4
• /
• pp.283-290
• /
• 2016

A double-stranded RNA (dsRNA) mycovirus was detected in malformed fruiting bodies of Pleurotus ostreatus strain ASI2792, one of bottle cultivated commercial strains of the edible oyster mushroom. The partial RNA-dependent RNA polymerase (RdRp) gene of the P. ostreatus ASI2792 mycovirus (PoV-ASI2792) was cloned, and a cDNA sequences alignment revealed that the sequence was identical to the RdRp gene of a known PoSV found in the P. ostreatus strain. To investigate the symptoms of PoV-ASI2792 infection by comparing the isogenic virus-free P. ostreatus strains with a virus-infected strain, isogenic virus-cured P. ostreatus strains were obtained by the mycelial fragmentation method for virus curing. The absence of virus was verified with gel electrophoresis after dsRNA-specific virus purification and Northern blot analysis using a partial RdRp cDNA of PoV-ASI2792. The growth rate and mycelial dry weight of virus-infected P. ostreatus strain with PoV-ASI2792 mycovirus were compared to those of three virus-free isogenic strains on 10 different media. The virus-cured strains showed distinctly higher mycelial growth rates and dry weights on all kinds of experimental culture media, with at least a 2.2-fold higher mycelial growth rate on mushroom complete media (MCM) and Hamada media, and a 2.7-fold higher mycelial dry weight on MCM and yeast-malt-glucose agar media than those of the virus-infected strain. These results suggest that the infection of PoV mycovirus has a deleterious effect on the vegetative growth of P. ostreatus.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.35 no.7
• /
• pp.753-758
• /
• 2011

The Ni-base super-heat-resistant alloy, GTD-111, is employed in gas turbines because of its high temperature strength and oxidation resistance. It is important to predict the fatigue life of this superalloy in order to improve the efficiency of gas turbines. In this study, low-cycle fatigue tests are performed as variables of total strain range and temperature. The relationship between the strain energy density and number of cycles to failure is examined in order to predict the low-cycle fatigue life of the GTD-111 superalloy. The fatigue life predicted by using the strain-energy methods is found to coincide with that obtained from the experimental data and from the Coffin-Manson method.

• Proceedings of the KSME Conference
• /
• 2004.11a
• /
• pp.178-183
• /
• 2004

For developing fatigue design curve of cast stainless steels that would be used in piping material of domestic nuclear power plants, a low-cycle fatigue test rig was built. It is capable of performing tests in pressurized high temperature water environment of PWR. Cylindrical specimens of CF8M were used for the strain-controlled environmental fatigue tests. Fatigue life was measured in terms of the number of cycles with the variation of strain amplitude at 0.04%/s strain rates. The disparity between target length and measured length of specimens was corrected by using finite element method. The corrected test results showed similar fatigue life trend with another previous results.