• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2004.08a
• /
• pp.285-293
• /
• 2004

Oxidation behavior of 304 and 430 stainless steel were studied using thin film X-ray analysis and glow discharge spectrum analysis (here-after GDS). The oxidation layer of 304 stainless steel was composed of $Cr_2O_3\;and\;FeCrO_4$ and its thickness was about $1.5{\mu}m$ after $1\~5$ minutes of annealing at $1120^{\circ}C$ open air. However, the oxidation layer of 430 stainless steels was mainly composed of $Cr_2O_3$ and its typical thickness was 0.5um after $1\~5$ minutes of annealing at $1000^{\circ}C$ open air. Electro-chemical analysis revealed that the descaling of oxidation layer could be activated by Fe, Cr dissolution from the matrix behind the oxidation layer at the current density of $5\~10ASD$ and by Fe, Cr-oxide dissolution from the oxidation layer at the current density over than 10ASD. Electrolytic stripping of 430 and 304 revealed the intial incubation period of descaling by oxygen evolving at low current density range such as $5\~10ASD$. However the dissolution of oxide layer was occurred when applying the anodic current of $10\~20ASD$ on 430 and 304 stainless steels. It was suggested that the electrolytic pickling of high Cr bearing stainless steel such as 430 and 304 seemed to be the more effective in the high current density range such as $10\~20ASD$ than the low current density range such as $5\~10ASD$.

• Journal of the Korean institute of surface engineering
• /
• v.20 no.2
• /
• pp.49-59
• /
• 1987

The properties of $Cr_2O_3-Al_2O_3-SiO_2$ composite oxide coatings on steel surface were investigated. The results obtained were as follows: The microhardness of oxide coating layer increased with increasing heat-treatment temperature and $Cr_2O_3$ content in coating layer. The hardness showed the highest value (850Hv) treated at 700$^{\circ}C$ for $SiO_2:Al_2O_3:Cr_2O_3$=1:1:4. Increasing heat-treatment temperature, corrosion current density became lower and coating layer became denser. The corrosion current density showed the lowest value $(6.5{\times}10^{-5}\;Acm^2)$ treated at 750$^{\circ}C\;for\;SiO_2:Al_2O_3:Cr_2O_3$=1:1:3. These results were explained by protective layer which was formed during heat-treatment. The bonding between matrix and coating layer is expected to be made mechanically and chemically by the inter diffusion of Ni and Fe. The composite oxide coating was formed by softening of the binder with increasing heat-treatment temperature. The strengthening of coating layer is to be resulted from the dispersion of major oxide particles.

• Journal of the Korean institute of surface engineering
• /
• v.51 no.1
• /
• pp.34-39
• /
• 2018

Steel crucible used for molten Al has a problem of very limited lifetime because of the interaction between Fe and molten Al. This study was performed to improve the lifetime of steel crucible for molten Al by coating metallic Al and by further anodizing treatment to form thick and uniform anodic oxide films. The lifetime of the steel crucible was improved slightly by Al coating from 30 to 40 hours by metallic Al coating and largely to 120 hours by coating the surface with anodic oxide film. The improved lifetime was attributed to blocking of the reaction between Fe and molten Al with the help of anodic oxide layer with more than 20 um thickness on the crucible surface. The failure of the steel crucible arises from the formation of intermetallic compounds and pores at the steel/Al interface.

• Nuclear Engineering and Technology
• /
• v.40 no.2
• /
• pp.147-154
• /
• 2008

The general corrosion behavior of austenitic and ferritic steels(316L, 304, N controlled 304L, and 410) in supercritical water is investigated in this paper. After exposure to deaerated supercritical water at $480^{\circ}C$/25 MPa for up to 500 h, the four steels studied were characterized using gravimetry, scanning electron microscopy/energy dispersive X-ray spectroscopy(SEM/EDS), X-ray photoelectron spectroscopy(XPS), and X-ray diffraction(XRD). The results show that the 316L steel with a higher Cr and Ni content has the best corrosion-resistance performance among the steels tested. In addition to the oxide layer mixed with $Fe_{3}O_{4}$ and $(Fe,Cr)_{3}O_{4}$ that formed on all the samples, a $Fe_{3}O_{4}$ loose outer layer was observed on the 410 steel. The corrosion mechanism of stainless steels in supercritical water is discussed based on the above results.

• Korean Journal of Metals and Materials
• /
• v.47 no.7
• /
• pp.423-432
• /
• 2009

In the galvanizing coating process, the effects of the silicon content on the coatability and wettability of molten zinc were investigated on Dual-Phase High Strength Steels (DP-HSS) with various Si contents using the galvanizing simulator and dynamic reactive wetting systems. DP-HSS showed good coatability and a well-developed inhibition layer in the range of Si content below 0.5 wt%. Good coatability was the results of the mixed oxide $Mn_{2}SiO_{4}$, being formed by the selective oxidation on the surface, with a low contact angle in molten zinc and a large fraction of oxide free surface that provided a sufficient site for the molten zinc to wet and react with the substrate. On the other hand, with more than 0.5 wt%, DP-HSS exhibited poor coatability and an irregularly developed inhibition layer. The poor coatability was due to the poor wettability that resulted from the development of network-type layers of amorphous ${SiO}_{2}$, leading to a high contact angle in molten zinc, on the surface.

• Corrosion Science and Technology
• /
• v.19 no.1
• /
• pp.43-50
• /
• 2020

In this study, the effects of KCl(s) and K₂SO₄(s) on the oxidation characteristics of 2.25Cr-1Mo steel were investigated for 500 h in 10O₂ + 10CO₂ (vol%) gas environmen at 650 ℃. Oxidation kinetics were characterized by weight gain, oxide layer thickness, and fitted models for the experiment data were proposed. The fitted models presented considerable agreement with the experimental data. The oxide layer was analyzed using the scanning electron microscope, optical microscope, and energy dispersive X-ray spectroscopy. The oxidation kinetics of 2.25Cr-1Mo steel with KCl and K₂SO₄ coatings showed significantly different oxidation kinetics. KCl accelerated the oxidation rate very much and had linear oxidation behavior. In contrast, K₂SO₄ had no significant effect, which had parabolic kinetics. The oxide layer was commonly composed of Fe₂O₃, Fe₃O₄, and FeCr₂O₄ spinel. KCl strongly accelerated the oxidation rates of 2.25Cr-1Mo steel in the high-temperature oxidation environment. Conversely, K₂SO₄ had little effect on the oxidation rates.

• Corrosion Science and Technology
• /
• v.6 no.3
• /
• pp.128-132
• /
• 2007

For a quantitative inspection on the performance of weathering steel bridges, we have investigated the relationship between the corrosion rate and the composition of the rust layers formed on weathering steel bridges located in various environments in Japan and applied a protective ability index (PAI) to the bridges. The corrosion rates were clearly classified by the PAI, ${\alpha}/{\gamma}*$ and sub index of $({\beta}+s)/{\gamma}*$, where $\alpha$, \gamma*, $\beta$ and s are the mass ratio of crystalline $\alpha-FeOOH$, the total of $\gamma$-FeOOH+ $\beta$-FeOOH + the spinel-type iron oxide (mainly $Fe_3O_4$), $\beta-FeOOH$ and spinel-type iron oxide, analyzed by powder X-ray diffraction, respectively. In the case of ${\alpha}/{\gamma}$*>1, the rust layer works protective enough to reduce the corrosion rate less than 0.01 mm/y. The sub index $({\beta}+s)/{\gamma}*$<0.5 or >0.5 classifies the corrosion rate of the non-protective rust layers, therefore the former state of the rust layer terms inactive and the latter terms active. The quantitative inspection of a weathering steel bridge requires a performance-inspection (PI) and periodical deteriorationinspections (DI). The PI can be completed by checking of the PAI, ${\alpha}/{\gamma}*$. The DI on the weathering steel bridges where deicing salt is sprinkled can be performed by checking the PAI, $({\beta}+s)/{\gamma}*$.

• Journal of the Korean institute of surface engineering
• /
• v.34 no.4
• /
• pp.321-326
• /
• 2001

The TiCrN Coatings haying three kinds of Compositions of $Ti_{36}$ $Cr_{26}$ $N_{38}$ , $Ti_{31}$ $Cr_{35}$ $N_{34}$ / and $Ti_{14}$ $Cr_{52}$ $N_{34}$ were deposited on STD 61 steel substrate by arc ion plating and were oxidized between 700 and 100$0^{\circ}C$ to identify the oxide scales formed on the coatings. The oxide scales were then analyzed using EPMA, XRD and GAXRD. During oxidation, the coatings consisting of TiN and CrN phases were reduced to TiO2 and $Cr_2$$O_3$, respectively. Titania tended to form at the outer oxide layer, whereas chromia tended to form at the inner oxide layer, owing to the different oxygen affinity. The substrate elements as well as coating elements diffused outwardly toward the oxide layer due to the concentration gradient. The growth of oxide from the TiCrN coatings was schematically expressed on the basis of thickness measurement of the reacted and unreacted coatings. The Cr element showed its stronger role to keep the TiCrN coatings from oxidation, when compared with Ni.

• Proceedings of the Korean Radioactive Waste Society Conference
• /
• 2018.11a
• /
• pp.474-475
• /
• 2018

• Journal of the Korean institute of surface engineering
• /
• v.28 no.1
• /
• pp.23-33
• /
• 1995

AISI 304 stainless steel has high resistance to corrosion due to the presence of a self-healing chromium oxide film on the surface, which also accounts for the difficulty in plating. Surface cleaning of this alloy is of fundamental importance in gold plating since its effectiveness puts an upper limit on the quality of the final coating. The cleaning of AISI 304 stainless steel was investigated with elimination of artificial passive oxide film and degreasing of remaining buffing wax as stearic acid. The familiar cleaning methods i.e. ultrasonic cleaning, electro-cleaning and activation treatment were fabricated in this study. Activation treatment showed best cleaning efficiency for elimination of passive oxide film among these methods, which was also confirmed by AES (Auger electron spectrometer) analysis. However, the best condition of cleaning was obtained by combining these methods. Electrocleaning time, for degreasing the stearic acid layer, was decreased with increasing amount of added KCN.