• Journal of the Korea Institute of Building Construction
• /
• v.9 no.3
• /
• pp.95-101
• /
• 2009

Constructing large-scale mat foundation mass concrete is increasing for the stability of building structure, because a lot of high rise building are being built in order to make full use of limited space. However, It is of increasing concerns that because limited placing equipments, available job-site and systems for mass concete placement in construction field do not allow to place great quantity of concrete at the same time in large scale mat foundation, consistency between placement lift can not be secured. And also, it is likely to crack due to stress caused by the difference of hydration heat generation time. To find out the solution against above problems, this study is to reconfirm the performance of normal concrete designed by mix proportion and super retarding concrete. The Fundamental test shows what happens if low heat proportioning and control method of setting time are applied at the job-site of newly constructed high rise building. The test result show that slump flow of concrete has been somewhat increased as the target retarding time gets longer, while the air content has been slightly decreased but this is no great difference from normal concrete. The setting time shows to be retarded as target retarding time gets longer, the range of retarding time increases. It is necessary to increase the amount of mix of super retarding agent in the proportion ration by setting curing temperature high since outdoor curing is about 6 hours faster than standard curing, which means the temperature of the concrete will be higher than the temperature of the surrounding environment, due to its high hydration heat when applying in a construction site. The compressive strength of super retarding concrete appears to be lower than normal concrete due to the retarding action in the early stage. However, as the time goes by, the compressive strength gets higher, and by the 28th day the strength becomes the same or higher than normal concrete.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.19 no.12
• /
• pp.87-97
• /
• 2020

In this study, a UV-cured GFRP molding is made using a combination of hand lay-up and resin transfer molding, and its properties are analyzed. The molded plates produced using various vacuum pressures (0 mmHg, -450 mmHg, and -760 mmHg) are examined via a comparison of hand lay-up molding and resin transfer molding. Tests are conducted by processing tensile specimens (ASTM D-5083), flexural test specimens (ASTM D-790), and ILSS test specimens (ASTM D-2344) according to each ASTM standard with a molded plate. Similarly, the UV-cured GFRP molding is compared against GFRP using epoxy. It was confirmed that the mechanical strengths of all the specimens increased when the vacuum pressure was increased and when UV curing was applied. This is believed to be because as the vacuum pressure increases, the pores of the cured specimen are removed, thereby reducing defects, and the bonding force between the glass fiber and the resin is stronger than that of the epoxy resin. It is expected that if resin transfer molding methods and UV-cured resins are used for molding GFRP composites in industry, products with better mechanical properties and faster curing time will be produced.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2004.05a
• /
• pp.1-4
• /
• 2004

In this paper. applicability of high early strength type AE water reducing agent(HESAEWA) developed by the authors is discussed by applying Mock-up test. For fresh concrete properties, concrete using existing AE water reducing agent(EAEWRA) and HESAEW A meets the target slump and air content at jobsite. Setting time of concrete using HESAEWA is shorter than that using EAEWRA. Remarkable variance of bleeding and settlement is not observed with type of AE water reducing agent. For hardened concrete properties, use of HESAEW A results in higher strength development compared with that of EAEWRA at standard curing and in field curing condition. Reaching time to accomplish 5MPa of compressive strength. which is possible to remove side form. is taken using HESAEWA earlier than that of EAEWRA by 1day. Therefore, it is confirmed that use of HESAEWA can meet the requirements of general quality of concrete and achieve high early strength development as well as has a desirable field applicability.

• Journal of Environmental Science International
• /
• v.15 no.2
• /
• pp.185-191
• /
• 2006

In this paper, removal time of side form from concrete using OPC(ordinary Portland cement) and FAC(fly ash cement) are proposed by appling logistic model, which evaluates the strength development of concrete with maturity. W/B, types of cement and curing temperatures are adapted as test parameters. The estimation of strength development by logistic model has a good agreement between calculated values and measured ones. As for the removal times of form works suggested in this paper, as W/8 increases, curing temperature decreases and fly ash is used, removal time of side form is prolonged. Removal time of form from concrete using OPC suggested in this paper is shorter $2.5\~3.5$ days than those of KASS-5 (Korean Architectural Standard Specifications-5) in the range of over $20^{\circ}C$. And in the range of $10\~20^{\circ}C$ removal time of form is shorter than that of KASS-5 by as much as $4\~4.5$ days. The use of FAC results in an increase in removal time of form compared to that of OPC by about 1 day.

• Journal of the Korea Institute of Building Construction
• /
• v.7 no.1 s.23
• /
• pp.107-113
• /
• 2007

This study investigates the filed application in Daebul Free Trade Zone applying both a flowing method using drying shrinkage-reducing superplasticizer(SRS) and an insulating curing method using double layer bubble sheet. Test results showed that fresh concrete satisfied target slump and air content. A structure adding SRS significantly decreased the total bleeding capacity and accelerated the setting time. As for the crack occurrence, the structure applying the flowing method and double bubble sheets simultaneously exhibited the most favorable crack endurance, while conventional concrete showed more than 1mm size of crack in overall. In addition, a structure applying the flowing concrete method partially presented the micro crack. For the area proportion of crack occurrence, the structure using the double bubble sheets indicated 9.8%, while others applying flowing concrete method was 28%, compared with that of conventional one. For the compressive strength of specimens, standard curing specimens indicated $3{\sim}33%$ higher value than that of specimens cured besides the field construction. The specimens containing SRS improved the strength of $2{\sim}6MPa$, which is $10{\sim}22%$ higher than that of conventional concrete.

• Transactions of the Korean Society of Mechanical Engineers B
• /
• v.31 no.6 s.261
• /
• pp.499-506
• /
• 2007

This study aims to propose evaluation methods of chemical washing performance and estimate the washing capability by flowing detergent/water solution for application to home appliances such as dishwashers. Standard pollutant is stearic acid. A numerical study is also tried using a SIMPLER code. Preliminary experiments are performed by varying the concentration and temperature of the solution. From the pre-experiments, 10 minute pre-curing time is found to be necessary to remove the stearic acid. Stoichiometric ratio and detergent consumption coefficient of reaction between the detergent and stearic are estimated following a proposed method. Washing experiments of pollutant to compare with the numerical results are performed. The relative errors between the experimental and the numerical results with pre-curing time included are less than 7%. In conclusion, important mechanisms of chemical washing are revealed and methods of predicting washing performance are well established.

• Architectural research
• /
• v.20 no.1
• /
• pp.27-34
• /
• 2018

To improve the chloride ingress resistance of concrete, slag is widely used as a mineral admixture in concrete industry. And currently, most of experimental investigations about non steady state diffusion tests of chloride penetration are started after four weeks standard curing of concrete. For slag blended concrete, during submerged chloride penetration tests periods, binder reaction proceeds continuously, and chloride diffusivity decreases. However, so far the dependence of chloride ingress on curing ages are not detailed considered. To address this disadvantage, this paper shows a numerical procedure to analyze simultaneously binder hydration reactions and chloride ion penetration process. First, using a slag blended cement hydration model, degree of reactions of binders, combined water, and capillary porosity of hardening blended concrete are determined. Second, the dependences of chloride diffusivity on capillary porosity of slag blended concrete are clarified. Third, by considering time dependent chloride diffusivity and surface chloride content, chloride penetration profiles in hardening concrete are calculated. The proposed prediction model is verified through chloride immersion penetration test results of concrete with different water to binder ratios and slag contents.

• Journal of The Korean Society of Grassland and Forage Science
• /
• v.16 no.2
• /
• pp.169-176
• /
• 1996

An experiment was carried out to determine the effect of cultivar and tedding frequency on changes of moisture content of oat(Avena sativa L.) hay during field drying and on quality of baled oat hay after storage. The experimental design was a split-plot with the four oat cultivm such as 'Magnum', 'Cayuse', 'West' and 'Murray' as main plots and the two tedding frequencies such as 1 or 3 times a day as subplots in three replications. Moisture content of fresh cut oat cultivar was higher in the order of 'Magnum', 'Cayuse', 'West', and 'Murray' and the moisture content difference among the cultivm was maintained to the final curing day(P< 0.05). Moisture loss from the oat hay during the last 3 curing days was greater with 3 tedding a day than I tedding a day. Temperature of baled oat hay began to rise critically from the 6th day of storage and wa5 highest in 'Magnum' oat cultivar($45.3^{\circ}C$). Total nitrogen and ADIN contents of late maturing oat hay 'Magnum' and 'Cayuse' were higher than those of early maturing 'Murray' and 'West'. Tedding frequency did not influence total nitrogen and ADIN contents. ADF and NDF contents of early maturing oat hay were higher than those of late maturing oat hay. Relative feed value (RFV) of 'Magnum' oat hay was the highest(l06) and classified as Grade 2 in forage quality standard. Quality grade difference between early and late maturing oat cultivan was only 1 or 2.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2006.11a
• /
• pp.13-16
• /
• 2006

This study investigates filed application in Daebul Free Trade Zone of a flowing method using drying shrinkage-reducing superplasticizer(SRS) and an insulating curing method using double bubble sheets. Test showed that fresh concrete satisfied target slump and air content. A structure adding SRS significantly decreased the total bleeding capacity and accelerated the setting time. As for the crack occurrence, the structure applying the flowing method and double bubble sheets simultaneously exhibited the most favorable crack endurance, while conventional concrete showed more than 1mm size of crack in overall, and a structure applying only the flowing method partially presented micro crack. For the area proportion of crack occurrence, the structure using the double bubble sheets indicated 9.8%, while others applying flowing method was 28%, compared with 100% of conventional one. Standard curing specimens had about $3{\sim}6%$ higher compressive strength than that of specimens cured at adjacent field construction. In addition, using SRS improved about $5{\sim}7MPa$, than that of conventional concrete at 91 days elapse.

• Restorative Dentistry and Endodontics
• /
• v.23 no.1
• /
• pp.68-93
• /
• 1998

The physical properties of polymer are greatly influenced by the extent to which a resin cures. The presence of un reacted monomer can, have a plasticizing effect on the polymer, thereby altering the physical and mechanical properties of dentin bonding agent (DBA). If the DBA does not polymerize sufficiently, it will leave a weak bonding layer and lead to lower bond strength. The purpose of this study was to evaluate the shear bond strengths(SBS) and the degree of conversion (DC) of 4 commercialy avilable dentin bonding systems which are composed of 2 multi-bottle systems [Scotchbond Multi-Purpose (SMP), AeliteBond(AB)] and 2 onebottle systems [SingleBond(SB), One-Step(OS)]. For shear bond strength measurement, labial surfaces of freshly extracted bovine incisors were ground with # 600 grit SiC paper to expose dentin. Four different groups of samples were formed, with 10 samples. being made for each of the 4 commercial DBA in each group according to the curing sequences of DBA and overlayer thickness of composites: Group I (standard cure and 1mm thick composites) : The DBA was light cured and the composites of 1mm thickness was applied ; Group II (standard cure and 2mm thick composites) : The DBA was light cured and the composites of 2mm thickness was applied; Group III (simultaneous cure and 1mm thick composites) : The DBA was not light-cured and simultaneously cured with composites of 1mm thickness; Group N (simultaneous cure and 2mm thick composites) : The DBA was. not light-cured and simultaneously cured with composites of 2mm thickness. The SBS was measured immediately after the composites was bonded to the bovine dentin using an Instron machine. The DC of the DBA was examined in a thin film under simulated conditions of the experimental groups according to the curing sequences and overlayer thickness of composites in the SBS test. using a Fourier transform Infrared(FTIR) spectrometer. The following results were obtained from SBS tests and DC measurements 1. In SBS tests, the multi-bottle DBA(SMP, AB) had a generally higher bond strength values than the one bottle DBA(SB, OS). In DC measurements, the one bottle DBA(SB, OS) had a significantly higher DC than the multi-bottle DBA(SMP, AB). 2. In all DBAs except OS, there was no significant difference between the bond strength of group I (standard cure and 1mm thick composites) and that of group III (simultaneous cure and 1mm thick composites). SMP, SB in Group I had a significantly higher DC than those in group III, but AB, OS in group I had a significantly lower DC than those in group III 3. All DBAs in Goup II (standard cure and 2mm thick composites) had significantly higher bond strength and DC than those in Group N (simultaneous cure and 2mm thick composites). 4. In all DBAs, there was no significantly different SBS and DC between Group I and Group II, but all DBAs in Group III had significantly higher SBS and DC than those in Group IV.