• New Physics: Sae Mulli
• /
• v.68 no.11
• /
• pp.1208-1214
• /
• 2018

The one-step spin coating method is reported as an excellent thin film process because it can be easily used to fabricate high-quality methyl-ammonium lead tri-iodide ($MAPbI_3$) perovskite layers. One of the important things in the one-step spin coating method towards obtaining high-quality $MAPbI_3$ layers is the anti-solvent (AS) engineering, which consists of an one-step deposition of the $MAPbI_3$ film and dripping of the AS. The properties of the $MAPbI_3$ layer were found to be strongly influenced by the amount, dispensing speed, and spraying time of the AS solution. The $MAPbI_3$ solution was prepared by dissolving lead iodide and methyl-ammonium iodide in N,N-dimethylformamide and adding N,N-dimethyl sulfoxide. Diethyl ether (DE) was used for the AS solution. The results indicate that a $MAPbI_3$ layer appropriately sprayed with DE is beneficial for improving film quality and device efficiency because nucleation of $MAPbI_3$ layer is affected by the characteristics of DE, which affect the film's crystallinity, density, and surface morphology. The $MAPbI_3$ layer, which was optimized by using 0.7 mL of DE, a 3.03 mL/sec dispensing speed, and a 7 second time to spray after spinning showed the best efficiency of 13.74%, which was reproducible.

• Journal of the Korean Ceramic Society
• /
• v.42 no.3 s.274
• /
• pp.150-154
• /
• 2005

Ferroelectric $Bi_{3.35}Sm_{0.65}Ti_{3}O_{12}(BSmT)$ thin films were synthesized by sol-gel process. In this experiments, $Bi(TMHD)_{3},\;Sm_{5}(O^{i}Pr)_{13},\;Ti(O^{i}Pr)_4$ were used as precursors, which were dissolved in 2-methoxyethanol. The BSmT thin films were deposited on the Pt/TiO/SiO/Si substrates by spin-coating. Thereafter, the thin films with the thickness of 240 nm were annealed from 600 to $720^{\circ}C$ in oxygen atmosphere for 1 h, and post-annealed in oxygen atmosphere for 1 h after deposition of Pt electrode to enhance the electrical properties. To investigate the effects of Sm-substitution in the BTO thin films, the BTO and BSmT thin films were prepared, respectively. The remanent polarization and coercive voltage of the BSmT thin films annealed at $720^{\circ}C$ were $19.48{\mu}C/cm^2$ and 3.40 V, respectively.

• Journal of the Korean Ceramic Society
• /
• v.31 no.7
• /
• pp.795-803
• /
• 1994

Ferroelectric BaTiO3 thin film was produced using BaTi-ethoxide sol. This sol was prepared from BaTi-ethoxide by a partial hydrolysis with ammonia as a basic catalyst and ethylene glycol as a chelating agent. BaTiO3 thin film was prepared from three continuous spin-coating layers of the sol on bare Si(100) wafer at 2500 rpm followed by pyrolysis at $700^{\circ}C$ for 30 min. After the heat treatment, the film was 0.200$\pm$0.010 ${\mu}{\textrm}{m}$ thick and its grain size was 0.059 ${\mu}{\textrm}{m}$. On the other hand, electrical properties were measured for BaTiO3 thin film separately prepared on Au-deposited silicon wafer. The dielectric constant and loss of the BaTiO3 thin film at room temperature was 150~160 and 0.04 respectively, which was measured at 10 kHz and oscillation level of 0.1 V. In the measurements of the dielectric properties at high temperatures, it was observed that the capacitance of the thin film increases steeply, while the dielectric loss reaches maximum around 1$25^{\circ}C$, which corresponds a phase transition from tetragonal to cubic BaTiO3.

• The Transactions of the Korean Institute of Electrical Engineers
• /
• v.44 no.7
• /
• pp.914-918
• /
• 1995

In this study, Pb(Zr$_{x}$ Ti$_{1-x}$ )O$_{3}$ (x=0.65, 0.52, 0.35) thin films were fabricated by Sol-Gel method. A stock solution with excess Pb 10[mol%] of Pb(Zr$_{x}$ Ti$_{1-x}$ )O$_{3}$ was made and spin-coated on the Pt/SiO$_{2}$/Si substrate at 4000[rpm] for 30[sec.]. Coated specimens were dried on the hot-plate at 400[.deg. C] for 10[min.]. Sintering temperature and time were 500~800[.deg. C] and 1~60[min.]. The coating process was repeated 6 times and the final thickness of the thin films were about 4800[A]. To investigate crystallization condition, PZT thin films were analyzed with sintering temperature, time and composition by the XRD. The microstructure of thin fulms were investigated by SEM. The ferroelectric perovskite phases precipitated under the sintering of 700[.deg. C] for 1 hours. In the PZT(52/48) composition, dielectric constant and dielectric loss were 2133, 2.2[%] at room temperature, respectively.ively.

• Proceedings of the KIEE Conference
• /
• 1999.11d
• /
• pp.918-920
• /
• 1999

Recently, the ceramics of high permittivity are applied to DRAM and FRAM. In this study, (Ba, Sr)$TiO_3$ (BST) ceramics thin films were prepared by Sol-Gel method. BST solution was made and spin-coated on Pt/$SiO_2$/Si substrate at 4000[rpm] for 10 seconds. Coating process was repeated 3 times and then sintered at $750[^{\circ}C]$ for 30 minutes. Each specimen was analyzed structure and electrical characteristics. Thickness of BST ceramics thin films are about $2000[\AA]$. Dielectric constant and loss of thin films was little decreased at $1[kHz]{\sim}1[MHz]$. Dielectric constant and loss to frequency were 250 and 0.02 in BST3. In accordance with applied voltage, property of leakage current was stability when the was $0{\sim}3$[V]. According to voltage, leakage current was increased exponentially at $4{\sim}7$[V].

• Journal of the Korean Ceramic Society
• /
• v.38 no.9
• /
• pp.777-781
• /
• 2001

$LiCoO_{2}$ thin films have received attention as cathodes of thin film microbatteries in these days. In this study, $LiCoO_{2}$ thin films are fabricated by a sol-gel spin coating method followed by a post-annealing process. The thermal decomposition behaviour of precursor is investigated by TG/DTA analysis. The change of crystallinity, microstructure and electrochemical properties of final films as the drying temperature changes are also studied by XRD, SEM and galvanostatic charge/discharge cycling test. The relationship between the discharge capacity and the drying temperature are intensively investigated in this work.

• Korean Journal of Materials Research
• /
• v.28 no.7
• /
• pp.411-416
• /
• 2018

Tungsten oxide($WO_3$) films with uniform surface morphology are fabricated using a spin-coating method for applications of electrochromic(EC) devices. To improve the EC performances of the $WO_3$ films, we control the heating rate of the annealing process to 10, 5, and $1^{\circ}C/min$. Compared to the other samples, the $WO_3$ films fabricated at a heating rate of $5^{\circ}C/min$ shows superior EC performances for transmittance modulation(49.5 %), response speeds(8.3 s in a colored state and 11.2 s in a bleached state), and coloration efficiency($37.3cm^2/C$). This performance improvement is mainly related to formation of a uniform surface morphology with increased particle size without any cracks by an optimized annealing heating rate, which improves the electrical conductivity and electrochemical activity of the $WO_3$ films. Thus, the $WO_3$ films with a uniform surface morphology prepared by the optimized annealing heating rate can be used as a potential candidate for performance improvement of the EC devices.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.11 no.6
• /
• pp.252-258
• /
• 2001

($Ba_{0.7}Sr_{0.3})TiO_3$thin films were perpared on ITO-coated glass substrate by spin-coating method. The sol was sonicated in an ultrasonic bath to promote homogenization and the results were compared with untreated case. By application of the sonication process, crystallization temperatures of films were reduced, microstructers of films were more uniform and denser and the surface roughness of the films was lower from 8.4nm to 5.6nm. In addition, optical transmittances and electrical properties of films prepraed from sonicated sol were superior to those of films from untreated.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.11a
• /
• pp.132-135
• /
• 1999

Recently, the ceramics of high permittivity are applied to DRAM and FRAM. In this study, (B $a_{x}$ S $r_{l-x}$)Ti $O_3$(BST) ceramics thin films were prepared by Sol-Gel method. BST solution was made and spin-coated on Pt/ $SiO_2$/Si substrate at 4000 [rpm] for 10 seconds. Coated specimens were dried at 150[$^{\circ}C$] for 5 minutes. Coating process was repeated 3 times and then sintered at 750[$^{\circ}C$] for 30 minutes. Each specimen was analyzed structure and electrical characteristics. Thickness of BST ceramics thin films are about 2000($\AA$). Dielectric constant and loss of thin films was little decreased at 1[KHz] ~1[KHz]. Dielectric constant and loss to frequency were 250 and 0.02 in $Ba_{0.7}$S $r_{0.3}$Ti $O_3$. The properly of leakage current as the realation between the current and the voltage was that change of the leakage current was stable when the applied voltage was 0~3[V].

• Journal of the Korean Society for Precision Engineering
• /
• v.30 no.6
• /
• pp.567-572
• /
• 2013

In many electro-devices, the vacuum process is used as the manufacturing process. However, the vacuum process has a problem, it is difficult to apply to a continuous process such as a R2R(roll to roll) printing process. In this paper, we propose an ESD (electro static deposition) printing process has been used to apply an organic solar cell of thin film forming. ESD is a method of liquid atomization by electrical forces, an electrostatic atomizer sprays micro-drops from the solution injected into the capillary with electrostatic force generated by electric potential of about several tens kV. The organic solar cell based on a P3HT/PCBM active layer and a PEDOT:PSS electron blocking layer prepared from ESD method shows solar-to-electrical conversion efficiency of 1.42% at AM 1.5G 1sun light illumination, while 1.86% efficiency is observed when the ESD deposition of P3HT/PCBM is performed on a spin-coated PEDOT:PSS layer.