• Journal of the Korean Society for Heat Treatment
• /
• v.17 no.6
• /
• pp.327-335
• /
• 2004

Effect of spherodization of cementite on static and dynamic deformation behaviors of SCM415 steels was investigated in this study. Dynamic torsional test was conducted using torsional Kolsky bar with the strain rate of $1.6{\times}10^3/s$. Three type of specimens were used with different spherodization degree of cementite. Dynamic test results were analyzed comparing with static tensile results and microstructural changes. The obtained results are as follows; 1) All the specimens of static and dynamic tests showed a ductile fracture mode of dimple. Specimens of the dynamic test showed adiabatic shear bands on the beneath of fracture surface. 2) In static tensile test, decreased tensile strength and increased uniform and non-uniform elongations appeared as spherodization degree of cementite increased. 3) In dynamic torsional test, decreased shear strength and increased uniform elongation appeared as spherodization degree of cementite increased. 4) Due to the largest uniform elongation, superior cold forgeability at high speed is expected on high spherodization degree of cementite.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2006.05a
• /
• pp.159-163
• /
• 2006

The effects of annealing temperature and time on mechanical properties and microstructures were studied in cold drawn pearlitic steel wires containing 0.84wt% Si. Annealing was performed from $200^{\circ}C$ to $450^{\circ}C$ with different time of 30sec, 1min, 15min and 1hr. The increase of tensile strength at low temperature was related with strain ageing. The decrease of tensile strength at high annealing temperature was related with spherodization of cementite and the occurrence of recovery of the lamellar ferrite in the pearlite. The improvement of ductility was connected with spherodization of cementite plate in pearlite and recovery process by reduction of high dislocation density at short time annealing temperature of $400^{\circ}C$.

• Journal of the Korean Society for Heat Treatment
• /
• v.17 no.4
• /
• pp.211-215
• /
• 2004

Conventional spheroidization process of cold heading quality steels requires long heat treatment time, and reduction of the heat treatment time is important for improving productivity in the industry. Recently, hot deformation method has been proposed as a means of increasing spherodization kinetics. In this study, the influences of hot deformation on the spherodization behavior of cold heading quality steels were investigated. Hot deformation at the temperature range of $700^{\circ}C$ significantly enhances the spheroidization kinetics. Hot deformation can lead to a substantial reduction of spherodization process time as low as 1~5 hrs.

• Journal of the Korean Society for Heat Treatment
• /
• v.4 no.2
• /
• pp.1-8
• /
• 1991

The spheroidization of cold rolled lamellar pearlite in annealing at the temperatures between 600 and $700^{\circ}C$ has been studied by quantitative micrography. It was foud that the spheroidization proceeded as two stageh. The first stage was the stage of relieving the stored energy by cold work, the second was the stage of reducing the interface energy between ferrite and cementite. The spheroidization rate combining the spheroidization rate of each stages is described by the following equation : $$d(1/S)/dt=k_3{\cdot}D/_{(1/s)}\{{\sigma}V/_{(1/s)}+k_4{\cdot}{\exp}(-bt)\}$$ Where, S is the total area of the interface between ferrite and cementite per unit volume, D is the diffusion coefficient, ${\sigma}$ is the boundary energy, V is the volume fraction of the cementite, and $k_3$, $k_4$, b are constants.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2008.05a
• /
• pp.543-546
• /
• 2008

In the present study, the effect of cold reduction ratio on the spherodization rate of SK85 high carbon steel sheet was investigated. High carbon steel sheet fabricated by POSCO was soaked at $800^{\circ}C$ for 2 hr in a box furnace and then treated at $570^{\circ}C$ for 5 min in a salt bath furnace followed by water quenching to obtain a fine pearlite structure. Cold rolling was conducted on the sheets of fine pearlite by reduction ratios of 20, 30, and 40 % and heat treatment for spheroidization was carried out at $720^{\circ}C$ for the various time intervals from 0.1 to 32 hrs. Area fraction of spheroidized cementite was measured with an image analyzer as a function of cold reduction ratios and duration times.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2009.10a
• /
• pp.350-353
• /
• 2009

In the present study, the effect of initial microstructure, cold reduction ratio, and annealing temperature on the spherodization rate of SK85 high carbon steel sheet was investigated. High carbon steel sheet fabricated by POSCO was soaked at $800^{\circ}C$ for 2 hr in a box furnace and then treated at $570^{\circ}C$ for 5 min in a salt bath furnace followed by water quenching to obtain a fine pearlite structure. Cold rolling was conducted on the sheets of fine pearlite by reduction ratios of 20, 30, and 40% and heat treatment for spheroidization was carried out at 600 and $720^{\circ}C$ for the various time intervals from 0.1 to 32 hrs. Area fraction of spheroidized cementite was measured with an image analyzer as a function of cold reduction ratios and duration times.