The Relationship between Microstructures and Mechanical Properties in Cold-drawn and Annealed Pearlitic Steel Wire

신선 가공한 펄라이트 강선의 어닐링시 미세 조직의 변화와 기계적 성질과의 관계

The effects of annealing temperature and time on mechanical properties and microstructures were studied in cold drawn pearlitic steel wires containing 0.84wt% Si. Annealing was performed from $200^{\circ}C$ to $450^{\circ}C$ with different time of 30sec, 1min, 15min and 1hr. The increase of tensile strength at low temperature was related with strain ageing. The decrease of tensile strength at high annealing temperature was related with spherodization of cementite and the occurrence of recovery of the lamellar ferrite in the pearlite. The improvement of ductility was connected with spherodization of cementite plate in pearlite and recovery process by reduction of high dislocation density at short time annealing temperature of $400^{\circ}C$.