• Resources Recycling
• /
• v.28 no.6
• /
• pp.36-45
• /
• 2019

The spent petroleum catalysts contain rare metals such as vanadium, nickel, molybdenum, and cobalt. Therefore, the leaching of these rare metals from spent petroleum catalysts by organic acid was investigated in the present study. The leaching efficiency of metals by organic acid was in the following order: oxalic acid > tartaric acid > citric acid > maleic acid > ascorbic acid. Among the organic acids employed in this work, oxalic acid can be considered to be superior to the other acids in terms of metals leaching efficiency. The effect of several leaching conditions such as temperature, acid concentration, pulp density, stirring speed, and reaction time on the leaching of metals was investigated. Vanadium and molybdenum were selectively dissolved by oxalic acid from the spent catalysts. The leaching kinetics of vanadium by oxalic acid was also investigated. An activation energy of 8.76 kJ/mol indicated that the leaching kinetics of vanadium by oxalic acid solution was controlled by mass transfer.

• Proceedings of the IEEK Conference
• /
• 2001.10a
• /
• pp.472-477
• /
• 2001

Spent catalysts containing platinum were generated in petroleum refinery and other chemical industries. The reclamation of precious metals from such wastes has long been attempted in view of their rare, expensive and indispensable nature. In this study, the recovery of platinum from petroleum catalysts was attempted by a method consisting mainly of dissolving alumina substrate with sulfuric acid thereby concentrating insoluble platinum. Also, platinum dissolved partially in sulfuric acid was recovered by a cementation method using aluminum metal as a reductive agent. The effect of temperature, time, concentration of sulfuric acid. and pulp density on the dissolution of substrate was investigated. When the substrate of platinum catalyst was ${\gamma}$-AI$_2$O$_3$ about 95% alumina was dissolved in 6.0M sulfuric acid at 10$0^{\circ}C$ for 2 hours. When the substrate was the mixture of ${\gamma}$-A1$_2$O$_3$and $\alpha$-A1$_2$O$_3$about 92% was dissolved after 4 hours. As a result, more than 99% of platinum could be recovered by this method and aluminum sulfate was obtained as byproduct.

• Resources Recycling
• /
• v.13 no.1
• /
• pp.14-21
• /
• 2004

Spent catalysts containing platinum were generated in petroleum refinery and other chemical industries. The reclamation of platinum metals from such wastes has long been attempted in view of their rare, expensive and indispensable nature. In this study, the recovery of platinum from petroleum catalysts was attempted by a method consisting mainly of dissolving alumina carrier with sulfuric acid thereby concentrating insoluble platinum. Also, platinum dissolved partially in sulfuric acid was recovered by a cementation method using aluminum metal as a reductive agent. The effect of temperature, time, concentration of sulfuric acid, and pulp density on the dissolution of carrier was investigated. When the carrier of platinum catalyst was $\Upsilon-Al_2$O$_3$ about 95% alumina was dissolved in 6.0 M sulfuric acid at $100^{\circ}C$ for 2 hours. When the carrier was the mixture of $\Upsilon-Al_2$$O_3$ and $\alpha$-$Al_2$$O_3$ about 92% was dissolved after 4 hours. As a result, more than 99% of platinum could be recovered by this method and aluminum sulfate was also obtained as byproduct.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.19 no.10
• /
• pp.598-602
• /
• 2018

This study examined the characteristics of the waste catalyst used in the petroleum refinery operations. The total pore volume, specific surface area, and average pore size of the spent catalyst used in the petroleum refinery operations were 3.96cc/g, 13.81m2/g, and 1.15A, respectively. The weight loss observed in the range from $25^{\circ}C-700^{\circ}C$ for the spent catalysts using TG and DTA was approximately 23 wt. %. EDS analysis of the waste catalyst sample showed that the five major components were vanadium, nickel, manganese, iron, and copper. The extraction system is attractive for liquid-liquid extraction. In this study, Cynex 272 was used to extract vanadium from waste catalyst. The electrochemical characteristics of the extracted vanadium solution were measured by cyclic voltammetry (CV). As a result, an oxidation / reduction peak appeared, indicating the potential of an electrolytic solution.