• Carbon letters
• /
• 제8권1호
• /
• pp.30-36
• /
• 2007

Oxidized PAN (OXI-PAN) fibers were used for the precursors of activated carbon fiber in study. How drying temperature affected the properties of carbon fibers on activating process of carbon fibers was investigated. The specific surface areas of activated carbon fibers have been determined on a series of chemically activated carbons with KOH and NaOH. The experimental data showed variations in specific surface area, iodine and silver adsorptions by the activated carbon fibers. The amount of iodine adsorption increases with increasing specific surface areas in both activation methods. This was because the ionic radius of iodine was smaller than the interior micropore size of activated carbon fibers. Silver adsorbed well in NaOH activated carbon fibers rather than KOH activated carbon fibers in this study.

• Journal of the Korean institute of surface engineering
• /
• 제53권5호
• /
• pp.241-248
• /
• 2020

The change of the deposition behavior of diamond through a pretreatment process of the base metal prior to diamond deposition using HFCVD was investigated. To improve the specific surface area of the base material, sanding was performed using sandblasting first, and chemical etching treatment was performed to further improve the uniform specific surface area. Chemical etching was performed by immersing the base material in HCl solutions with various etching time. Thereafter, seeding was performed by immersing the sanded and etched base material in a diamond seeding solution. Diamond deposition according to all pretreatment conditions was performed under the same conditions. Methane was used as the carbon source and hydrogen was used as the reaction gas. The most optimal conditions were found by analyzing the improvement of the specific surface area and uniformity, and the optimal diamond seeding solution concentration and immersion time were also obtained for the diamond particle seeding method. As a result, the sandblasted base material was immersed in 20% HCl for 60 minutes at 100 ℃ and chemically etched, and then immersed in a diamond seeding solution of 5 g/L and seeded using ultrasonic waves for 30 minutes. It was possible to obtain optimized economical diamond film growth rates.

• Bulletin of the Korean Chemical Society
• /
• 제20권12호
• /
• pp.1521-1523
• /
• 1999

• Analytical Science and Technology
• /
• 제24권6호
• /
• pp.503-509
• /
• 2011

Specific surface area is becoming a very important factor when newly developed advanced nano-materials are evaluated. But there have been many differences in results when measuring specific surface areas, depending on the measuring equipments and analysis method. To verify the reliability of the specific surface area measurement device supplied within the country, Round Robin Test (RRT) has been done at 21 affiliated research institutes. As a result, it was found that several institute had problems in measuring of gas adsorption amount in measuring equipment, and this proved the need for certified reference material (CRM). Furthermore, it was also found that the results from BET analysis is easily swayed by the analyst's subjectivism, and the calculated results may differ up to 16% in case of CRM I depending on the selection range of BET analysis. So this showed that a standard guideline for BET constant C value and fitting correlation coefficient R is needed, to properly select range in BET analysis. The experience in RRT, distribution of CRM, and standardized procedure would result in improved reliability in industrial processes, and thus, would contribute to the quality management, the productivity improvement, the safety evaluation, and the new material development.

• Journal of the Korean institute of surface engineering
• /
• 제49권5호
• /
• pp.416-422
• /
• 2016

We have investigated the effects of applied potential, deposition time and electrolyte types on shapes and physical properties of Cu dendrites by potentiostatic electrodeposition. Finer shape of dendrites was observed at less cathodic potential by 100mV than at the limiting current, due to 'effective overpotential'. The shape of copper dendrite is related to the deposition time, too. The dendrite depositing for 10 min showed the finest shape. The finer dendrite has the less apparent density and the larger specific surface area. Dendrite from chloride solution has the lowest density and the largest surface area among three plating solutions, sulfate, chloride and pyrophosphate.

• Composites Research
• /
• 제31권5호
• /
• pp.267-275
• /
• 2018

A facile method for the preparation of nitrogen-doped microporous carbon via the pyrolysis of poly(vinylidene fluoride) (PVDF) using polypyrrole (PPy) as a selective nitrogen source was developed. A PVDF/PPy-800 sample (carbonized at $800^{\circ}C$) with a 1:0.5 ratio of PVDF and PPy exhibited the highest micropore volume. The activated microporous carbon materials obtained from PVDF/PPy-800 prepared at $800^{\circ}C$ with KOH possessed a large specific surface area and narrow pore-size distribution. They were characterized using $N_2$ adsorption at 77 K and argon (Ar) adsorption at 87 K, which allowed for the characterization of the narrow microporosity of the prepared materials due to the absence of interactions between Ar and the sample surface. In addition, the activated microporous carbon material with a KOH/carbon ratio of 2:1 was found to exhibit the largest specific surface area ($1296m^2g^{-1}$ in $N_2$ at 77 K) and microporosity, and a high specific capacitance ($122.8F\;g^{-1}$).

• YAKHAK HOEJI
• /
• 제29권4호
• /
• pp.176-182
• /
• 1985

As a part of the studies on adsorptive properties of Korean halloysite clays, Hadong white clays of premium grade were examined for geometric pore structured by mercury porosimetry and for specific surface areas by nitrogen adsorption according to the BET procedure. Three size fractions of the native clay sample were derived from passage BS #100, #200 and #325 meshes, respectively. Several parameters lhus observed in relation to the pore structures are shown below: 1. The size fraction of BS #100, #200 and #325 show internal pore volumes of 25.3, 30.2 and $35.0m^2g^{-1}$, respectively. 2. In the distribution curves of the cumulative pore volume against pore diameter, it has been shown that the larticle sizes, the steeper the distribution over the larger ranges of pore diameters. The converse is true the smaller particles. 3. Internal pore areas increase with decrease in pore sizes. It follows that the pores having diameters of $\leq$0.1$\mu\textrm{m}$ are responsible for more than 90% of the total pore area. 4. The behaviour of nitrogen adsorption can be best described by BET type IV isotherm. Further, the hysteresis loops of the adsorptiondesorption curves become narrower with decresing particle sizes. 5. The specific surface areas observed for the fractions of BS #100, BS #200 and BS #325 are 34.6, 35.4 and 43.2m $^2g^{-1}$, respectively. and the calcined clay of BS #325 has a specific surface area near $30.4m^2g^{-1}$.

• Journal of the Korean Applied Science and Technology
• /
• 제27권3호
• /
• pp.344-352
• /
• 2010

Magnetite and inorganic sludge were mainly composed of $Fe_2O_4$ and $Fe_2O_3$, respectively. Initial specific surface areas of magnetite and inorganic sludge were 130 $m^2$/g and 31.7 $m^2$/g. $CO_2$ decomposition rate for inorganic sludge was increased with temperature. Maximum $CO_2$ decomposition rates were shown 89% for magnetite at $350^{\circ}C$ and 84% for inorganic sludge at $500^{\circ}C$. Specific surface area for magnetite was not varied significantly after $CO_2$ decomposition. However, specific surface area for inorganic sludge was greatly decreased from initial 130 $m^2$/g to approximately 50~60 $m^2$/g after reaction. Therefore, it was estimated that magnetite could be used for $CO_2$decomposition for a long time and inorganic sludge should be wasted after $CO_2$ decomposition reaction.

• Korean Chemical Engineering Research
• /
• 제49권1호
• /
• pp.10-14
• /
• 2011

The electrode material performances of electric double layer capacitor(EDLC) were investigated using mesopous active carbon fiber(ACF), which was prepared by the iron exchange method. The mesoporous ACF had pore characteristics of specific surface area around 1249, 664 $m^2$/g, mesoporous fraction around 70.6-81.3% and meanpore size around 2.78-4.14 nm. The results showed that as HNO3 treatment time decreased, the specific surface area increased and mesoporous fraction decreased. To investigate electrochemical performance of EDLC, unit cell was manufactured using mesoporus ACF, conducting material and binder; organic elctrolyte was used on this experiment. The specific capacitance of ACF treated with HNO3 for 2 hours turned out to be 0.47 $F/cm^2$and the results of the cyclic charge-discharge tests were stable. Thus, the electrochemical performance of EDLC was mainly dependent on specific surface area of ACF electrode and the diffusion resistance of charge decreased as the mesopore increased.

• Journal of Korean Society of Water and Wastewater
• /
• 제8권1호
• /
• pp.34-43
• /
• 1994

It is well known that the adsorption character of activated carbon is dependent on the specific surface area and pore volume, but the relationship between the surface-chemical structure and the adsorption character has not been studied very often. The purpose of this study is to investigate the effect of the acidic surface functional groups of activated carbon and the adsorption characteristics of low concentration phenol. So three types of activated carbons and four different treatments were introduced to this isotherm experiment. These treatments were nontreatment, 1N $HNO_3$ treatment, 6N $HNO_3$ treatment, $H_2O_2$ treatment. The conclusions of this study are as followings. If the initial concentration of phenol is high as 5mg/l, the adsorption is dependent on the specific surface area. If the initial concentration of phenol is low as $100{\mu}g/l$, the adsorption is dependent on the average pore volume. The acidic surface functional groups prevent the adsorption of phenol molecules to activated carbon. And the adsorbed amount decreases more for $HNO_3$ treatment than for $H_2O_2$ treatment and more for concentrated $HNO_3$ treatment than for dilute $HNO_3$ treatment.