• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2007년도 춘계학술논문 발표대회
• /
• pp.55-58
• /
• 2007

This study investigates the spatting properties of high strength concrete, $60\sim80MPa$ class, designed with diverse aspect ratios and fiber content of nylon(NY). Test showed that increase of fiber content and aspect ratio in concrete decreased the fluidity of fresh concrete, especially for 1580 and 3000 aspect ratio of fiber. As for the compressive and tensile strength, adding NY fiber did not significantly affect the values In the range of high strength. After completing the fire test, the specimens containing both 750 and 1000 aspect ratios of fiber protected the spatting occurrence even in 0.05vol.% of fiber content. This specimens indicated the residual compressive strength ratio at 37%, showing the most favorable value among other specimens. Therefore, it is demonstrated that to protect the spalling in high strength concrete considering the effective fluidity, strength and economic efficiency altogether, adding 0.05vol.% of NY fiber with 750 aspect ratio Is beneficial.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2007년도 춘계학술논문 발표대회
• /
• pp.63-66
• /
• 2007

This study investigates the fire resistance properties of high strength concrete, around 60MPa class, designed with various admixture types and fiber content. Test showed that the increase of fiber content decreased the fluidity and slightly inclined the air content of fresh concrete. However, the fiber content in concrete did not affect the compressive strength. For the addition of admixture, specimens adding the shrinkage-reducing-agent (SR) indicated the strength value at 70MPa, which is followed by incorporating silica fume (SF) at 66MPa, the combination of expansive admixture (EA) and SR at 63MPa, only EA at 59MPa, blast furnace slag (BS) at 58MPa and fly ash (FA) at 50MPa in an order. After completing the fire test, all specimens adding 0.05vol.% of polypropylene fiber exhibited protection of spatting, except for the specimens incorporating loft of SF and incorporating 20% of SF with only SR and the combination of EP and SRA, respectively. Therefore the most effective result of this study was shown in the specimens incorporating love of FA and 30% of BS and incorporating 20% of SF with 5 % of EA. It is expected that this test results will be crucial references in near future to develope the spatting resistance method of high strength concrete.