• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 추계학술대회 논문집 Vol.14 No.1
• /
• pp.332-336
• /
• 2001

In this study, the reaction at UBM(Under Bump Metallurgy) and solder interface was investigated. The UBM employed in conventional optical packages, Au/Pt/Ti layer, were found to dissolve into molten Au-Sn eutectic solder during reflow soldering. Therefore, the reaction with different diffusion barrier layer such as Fe, Co, Ni were investigated to replace the conventional Pt layer. The reaction behavior was investigated by reflowing the solder on the pad of the metals defined by Cr layer for 1, 2, 3, 4, and 5 minutes at $330^{\circ}C$. Among the metals, Co was found to be most suitable for the diffusion barrier layer as the wettability with the solder was reasonable and the reaction rate of intermetallic formation at the interface is relatively slow.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 추계학술대회 논문집
• /
• pp.332-336
• /
• 2001

In this study, the reaction at UBM(Under Bump Metallurgy) and solder interface was investigated. The UBM employed in conventional optical packages, Au/Pt/Ti layer, were found to dissolve into molten Au-Sn eutectic solder during reflow soldering. Therefore, the reaction with different diffusion barrier layer such as Fe, Co, Ni were investigated to replace the conventional R layer. The reaction behavior was investigated by reflowing the solder on the pad of the metals defined by Cr layer for 1, 2, 3, 4, and 5 minutes at 330$^{\circ}C$. Among the metals, Co was found to be most suitable for the diffusion barrier layer as the wettability with the solder was reasonable and the reaction rate of intermetallic formation at the interface is relatively slow.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2002년도 Proceedings of the International Welding/Joining Conference-Korea
• /
• pp.469-474
• /
• 2002

Laser and hot air reflow soldering of PBGA solder ball was investigated. Experimental results showed that surface quality and shear strength of solder bumps reflowed by laser was superior than the solder bumps reflowed by hot air, and the microstructure inside the solder bumps reflowed by laser was much finer. Analysis on interfacial reaction showed that eutectic solder reacted with Au/Ni/Cu pad shortly after the solder was melted. Interface of solder bump reflowed by laser consists of a continuous AuSn$_4$ layer and remnant Au element. Needle-like AuSn$_4$ grew sidewise from interface, and then spread out to the entire interface region. A thin layer of Ni$_3$Sn$_4$ intermetallic compound was found at the interface of solder bump reflowed by hot air, AuSn$_4$ particles distributed inside the whole solder bump randomly. It is the combination effect of the continuous AuSn$_4$ layer and finer eutectic microstructure inside the solder bump reflowed by laser that resulted in higher shear strength.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2002년도 Proceedings of the International Welding/Joining Conference-Korea
• /
• pp.450-455
• /
• 2002

Cu-cored Sn-Ag solder balls were fabricated by coating pure Sn and Ag on Cu balls. The melting behavior and the solderability of the BGA joint with the Ni/Au coated Cu pad were investigated and were compared with those of the commercial Sn-Ag and Sn-Ag-Cu balls. DSC analyses clarified the melting of Cu-cored solders to start at a rather low temperature, the eutectic temperature of Sn-Ag-Cu. It was ascribed to the diffusion of Cu and Ag into Sn plating during the heating process. After reflow soldering the microstructures of the solder and of the interfacial layer between the solder and the Cu pad were analyzed with SEM and EPMA. By EDX analysis, formation of a eutectic microstructure composing of $\beta$-Sn, Ag$_3$Sn, ad Cu$_{6}$Sn$_{5}$ phases was confirmed in the solder, and the η'-(Au, Co, Cu, Ni)$_{6}$Sn$_{5}$ reaction layer was found to form at the interface between the solder and the Cu pad. By conducting shear tests, it was found that the BGA joint using Cu-cored solder ball could prevent the degradation of joint strength during aging at 423K because of the slower growth me of η'-(Au, Co, Cu, Ni)$_{6}$Sn$_{5}$ reaction layer formed at the solder, pad interface. Furthermore, Cu-cored multi-component Sn-Ag-Bi balls were fabricated by sequentially coating the binary Sn-Ag and Sn-Bi solders on Cu balls. The reflow property of these solder balls was investigated. Melting of these solder balls was clarified to start at the almost same temperature as that of Sn-2Ag-0.75Cu-3Bi solder. A microstructure composing of (Sn), Ag$_3$Sn, Bi and Cu$_{6}$Sn$_{5}$ phases was found to form in the solder ball, and a reaction layer containing primarily η'-(Au, Co, Cu, Ni)$_{6}$Sn$_{5}$ was found at the interface with Ni/Au coated Cu pad after reflow soldering. By conducting shear test, it was found that the BGA joints using this Cu-core solder balls hardly degraded their joint shear strength during aging at 423K due to the slower growth rate of the η'-(Au, Cu, Ni)$_{6}$Sn$_{5}$ reaction layer at the solder/pad interface.he solder/pad interface.

• 한국주조공학회지
• /
• 제22권2호
• /
• pp.89-96
• /
• 2002

This study examined the effects of adding Zn to Sn-3.5Ag solder on the microstructure changes and behavior of interface reaction of the solder joint with Cu substrate. The solder/Cu joints were examined with microscope to observe the characteristics of microstructure changes and interfacial reaction layer with aging treatment for up to 120 days at $150^{\circ}C$. Results of the microstructure changes showed that the microstructures were coarsened with aging treatment, while adding 1%Zn suppresses coarsening microstructures. The Sn-3.5Ag/Cu had a fast growth rate of the reaction layer in comparison with the Sn-3.5Ag-1Zn at the aging temperature of $150^{\circ}C$. Through the SEM/EDS analysis of solder joint, it was proved that intermetallic layer was $Cu_6Sn_5$ phase and aged specimens showed that intermetallic layer grew in proportion to $t^{1/2}$, and the precipitate of $Ag_3Sn$ occur to both inner layer and interface of layer and solder. In case of Zn-containing composite solder, $Cu_6Sn_5$ phase formed at the side of substrate and Cu-Zn-Sn phase formed at the other side in double layer. It seems that Cu-Zn-Sn phase formed at solder side did a roll of banrier to suppress the growth of the $Cu_6Sn_5$ layer during the aging treatment.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2006년도 춘계 학술대회 개요집
• /
• pp.21-23
• /
• 2006

The microstructural investigation and thermo-mechanical reliability evaluation of the Sn-3.0Ag-0.5Cu solder bumped flip chip package were carried out during the thermal shock test of the package. In the initial reaction, the reaction product between the solder and Cu mini bump of chip side was Cu6Sn5 layer, while the two phases which were (Cu,Ni)6Sn5 and (Ni,Cu)3Sn4 were formed between the solder and Ni-P layer of the package side. The cracks were occurred at the corner solder joints after the thermal shocks of 400 cycles. The primary failure mechanism of the solder joints in this type of package was confirmed to be thermally activated solder fatigue failure.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2005년도 추계학술발표대회 개요집
• /
• pp.219-221
• /
• 2005

Sn-9Zn solder balls were bonded to Cu, ENIG (Electroless Nickel/Immersion Gold) and electrolytic Au/Ni pads, and the effect of aging on their joint reliability was investigated. The interfacial products were different from the general reaction layer formed in a Sn-base solder. The intermetallic compounds formed in the solder/Cu joint were $Cu_{5}Zn_{8}$ and $Cu_{6}Sn_{5}$. After aging treatment, voids formed irregularly at the bottom side of the solder because of Sn diffusion into the $Cu_{5}Zn_{8}$ IMC. In the case of the solder/ENIG joint, $AuZn_{3}$ IMCs were formed at the interface. In the case of the Au/Ni/Cu substrate, an $AuZn_{3}$ IMC layer formed at the interface due to the fast reaction between Au and Zn. In addition, the $AuZn_{3}$ IMC layer became detached from the interface after reflow. When the aging time was extended to 100 h, $Ni_{5}Zn_{21}$ IMC was observed on the Ni substrate.

• 한국주조공학회지
• /
• 제20권2호
• /
• pp.116-121
• /
• 2000

Interfacial reaction and mechanical properties between Sn-Zn-X ternary alloys(X : 3wt.%In, 4wt.%Bi) and Cu-substrate were studied. Cu/solder joints were subjected to aging treatments for up to 50days to see interfacial reaction at $100^{\circ}C$ and then were examined changes of microstructure and interfacial compound by optical microscopy, SEM and EDS. Cu/solder joints were aged to 30days and then loaded to failure at cross head speed of 0.3 mm $min^{-1}$ to measure tensile strength. According to the results of the solderability test, additions of In and Bi in the Sn-9wt.%Zn solder improve the wetting characteristics of the alloy and lower the melting temperature. Through the EDS and XRD analysis of Cu/Sn-9wt.%Zn solder joint, it was concluded that the intermetallic compound was the ${\gamma}-Cu_5Zn_8$ phase. Cu-Zn intermetallics at Cu/solder interfaces played an important role in both the microstructure evolution and failure of solder joints. Cu/solder joint strength was decreased by aging treatment, and those phenomenon was closely related to the thickening of intermetallic layer at Cu/solder joints.

• 마이크로전자및패키징학회지
• /
• 제22권1호
• /
• pp.69-74
• /
• 2015

첨단 전자기기에 사용되는 전자부품의 크기와 접속피치가 감소하면서 리플로우 공정 후 플럭스 잔사의 세정이 어려워짐에 따라 무세정 솔더 페이스트에 대한 요구가 증가하고 있다. 본 연구에서는 SAC305 솔더분말과 에폭시 레진을 주성분으로 하는 경화성 플럭스를 혼합하여 제조한 에폭시 경화형 솔더 페이스트에 대하여 리플로우 공정성, 플럭스 잔사의 부식성, 솔더볼 및 보드레벨 BGA 패키지 솔더 접합부의 기계적 거동을 기존 로진계 솔더 페이스트와 비교하여 평가하였다. 에폭시 경화형 솔더 페이스트는 솔더 접합부 주변에 경화물 필렛을 형성한 것으로 보아 플럭싱 작용에 의해 솔더 접합부가 형성된 이후에 경화반응이 진행되는 것을 확인할 수 있었으며, 동판에 대한 젖음성 시험을 통해 기존상용 솔더 페이스트 정도의 납퍼짐성을 갖는 것을 알 수 있었다. 리플로우 후 동판에 대한 고온 고습 시험을 통해 에폭시 경화형 솔더 페이스트는 동판 부식을 전혀 발생시키지 않는 것으로 나타났는데, 이는 FT-IR 분석결과 에폭시 경화반응을 통해 단단히 고정된 결과로 생각되었다. 볼전단, 볼당김 및 다이전단 시험 결과, 솔더 접합부 주변에 형성된 경화물 필렛은 솔더 표면과 접착본딩을 형성하며, 다이전단강도를 15~40% 정도 향상시키는 것으로 보아 에폭시 경화형 솔더 페이스트는 플럭스 잔사 세정공정의 생략과 함께 솔더 접합부 보강효과를 통해 패키지 신뢰성 향상에도 기여할 수 있을 것으로 생각되었다.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2002년도 Proceedings of the International Welding/Joining Conference-Korea
• /
• pp.475-480
• /
• 2002

The reliability of the solder joint is affected by type and extent of the interfacial reaction between solder and substrates. Therefore, understanding of intermetallic compounds produced by soldering in electronic packaging is essential. In-based alloys have been favored bonding devices that demand low soldering temperatures. For photonic and fiber optics packaging, m-based solders have become increasingly attractive as a soldering material candidate due to its ductility. In the present work, the interfacial reactions between indium solder and bare Cu Substrate are investigated. For the identification of intermetallic compounds, both Scanning Electron Microscopy(SEM) and X-Ray Diffraction(XRD) were employed. Experimental results showed that the intermetallic compounds, such as Cu$_{11}$In$_{9}$ was observed for bare Cu substrate. Additionally, the growth rate of these intermetallic compounds was increased with the reaction temperature and time. We found that the growth of the intermetallic compound follows the parabolic law, which indicates that the growth is diffusion-controlled.d.